Abstract
Tin niobate photocatalysts with the phase structures of froodite (SnNb2O6) and pyrochlore (Sn2Nb2O7) were obtained by a facile solvothermal method in order to explore the impact of phase structure and electronic structure on the charge kinetics and photocatalytic performance. By employing tin niobate as a model compound, the effects of phase structure over electronic structure, photocatalytic activity toward methyl orange solution and hydrogen evolution were systematically investigated. It is found that the variation of phase structure from SnNb2O6 to Sn2Nb2O7 accompanied with modulation of particle size and band edge potentials that has great consequences on photocatalytic performance. In combination with the electrochemical impedance spectroscopy (EIS), transient photocurrent responses, transient absorption spectroscopy (TAS), and the analysis of the charge-carrier dynamics suggested that variation of electronic structure has great impacts on the charge separation and transfer rate of tin niobate photocatalysts and the subsequent photocatalytic performance. Moreover, the results of the X-ray photoelectron spectroscopy (XPS) indicated that the existent of Sn4+ species in Sn2Nb2O7 could result in a decrease in photocatalytic activity. Photocatalytic test demonstrated that the SnNb2O6 (froodite) catalyst possesses a higher photocatalytic activity toward MO degradation and H2 evolution compared with the sample of Sn2Nb2O7 (pyrochlore). On the basis of spin resonance measurement and trapping experiment, it is expected that photogenerated holes, O2−•, and OH• active species dominate the photodegradation of methyl orange.
Avoid common mistakes on your manuscript.
Background
Energy and environment problems have limited the sustainable development of human society, with the enhancement of the utilization of fossil resources [1,2,3]. Photocatalysis based on semiconductors attracts great attention owning to its potential application in solving the global energy crisis and environmental pollution [4,5,6,7]. The light absorption and photogenerated charge carriers may be the mainly limitations of photocatalytic efficiency, both of which are intrinsically controlled by the electronic structure [8,9,10,11]. In this regard, research on engineering appropriate electronic structure of the photocatalyst showing controllable photocatalytic performance is emerged as a lucrative way to dissolve the above issues [12,13,14]. As we all know, that the electronic structure is dependent on the crystal structure of semiconductors in a degree [15]. A series of studies on the oxide semiconductors with different crystal structures, as well as their optimal photocatalytic performance, have been reported, such as NaTaO3/Na2Ta2O6, SrNb2O6/Sr2Nb2O7, Ba5Ta4O15/Ba3Ta5O15, and SrTa2O6/Sr4Ta2O9/Sr5Ta4O15 [16,17,18,19,20]. In principle, the detailed crystallographic and structural variations determine the native photocatalytic performance of semiconductors. To uncover the native structure-dependent properties, the investigation of the photocatalytic activity of photocatalysts with different crystal structures is fundamentally important.
Layered niobates and tantalates are regarded as the promising photocatalysts which are usually applied to the reaction of water splitting and the photodegradation of organic pollution [21]. Especially, tin niobate which exists in two crystal structures: the froodite (SnNb2O6) [22, 23] and the pyrochlore (Sn2Nb2O7) [24, 25] have attracted much attention for the visible light-responsive photocatalysts. Either SnNb2O6 or Sn2Nb2O7 exhibits close structural relations to many semiconductors. The identification of the structural variation is advantageous for regulation of photochemical and photophysical properties of tin niobate and other semiconductors. Foordite (SnNb2O6) as a typical 2D layered niobate semiconductor material where two corner-sharing NbO6 sheets linked together at their edges and a distorted SnO8 sheet due to the existence of a lone-pair electron is alternating [23, 26]. SnNb2O6 can be active under visible light irradiation because of narrow band-gap (~ 2.3 eV) [27]. Furthermore, as a result of the conduction band which consists of Nb 4d orbitals and the valence band which contains hybridized orbitals of Sn 5s and O 2p, a narrower band gap is observed in SnNb2O6 compared with other niobate compounds [28, 29]. Hence, the particular band structure results in SnNb2O6 being used as the photocatalysts for the hydrogen evolution reaction under visible light irradiation [27,28,29,30,31]. The pyrochlore oxides are different from foordite structure which has eight formula units of the general formula A2B2O7 in the cubic unit cell [32]. A three-dimensional network in corner-sharing tetrahedral was formed with A and B atoms individually, and O atoms were located around these atoms [33]. The valence band of Sn2Nb2O7 was composed with Sn 5s orbitals as same as that of SnNb2O6. Whereas, the differentiation of Sn/Nb molar ratio and phase structure cause the variation of conduction and valence band potentials between Sn2Nb2O7 and SnNb2O6 [28]. Although the pyrochlore structure has a similar band gap to that of froodite and the photocatalytic activity of these reported metal oxide photocatalysts does not seem high [34,35,36]. Therefore, both the phase structure and electronic structure may always play an important role in the photocatalytic performances. Hence, tin niobate photocatalysts with the phase structures of froodite (SnNb2O6) and pyrochlore (Sn2Nb2O7) were systematically investigated to uncover the nature of phase structure-dependent properties, including the size, shape, optical absorption, the activity of photo-induced carriers, and the photocatalytic activity.
In this work, a series of tin niobate photocatalysts were synthesized via a facile solvothermal method in order to explore the roles that phase structure and electronic structure played on the charge kinetics and photocatalytic performance. The characters of the obtained products, such as morphology, structure and optical/electric properties, were investigated systematically with various physicochemical techniques. The photocatalytic properties of the obtained photocatalysts were investigated by the photocatalytic hydrogen evolution reaction and the degradation of MO under visible light irradiation. Meanwhile, the photocatalytic reaction mechanism was proposed based on the exploration of actives species and ESR analysis over the obtained SnNb2O6 photocatalyst.
Methods/Experimental
Synthesis of SnNb2O6 and Sn2Nb2O7
K7HNb3O19•13H2O was obtained as precursor for the synthesis of photocatalysts. For the synthesis of the target materials, K7HNb3O19•13H2O (0.360 g) was dissolved into distilled water (8 mL) whose pH value was adjusted to 7 by adding HCl solution (2.4 mol•L− 1) under magnetic stirring. Meanwhile, the white suspension was formed. As SnCl2•2H2O (0.225 g) solution which was dissolved with deionized water (2 mL) adding into the above suspension, a yellow suspension was generated. Meanwhile, the pH value of this suspension was about 1. Moreover, the pH values (3, 5, 7, 9, and 11) of the above suspension were adjusted by 1 mol•L− 1 KOH under vigorous stirring. Then, the mixture was statically heated at 180 °C for 24 h. The resultant products were washed with deionized water consecutively and dried 12 h at 80 °C.
Morphology, Structure, and Optical Properties Characterization
In order to study the crystal phase structures of the prepared samples, the wide-angle X-ray power diffraction (XRD) was used by performing on a Rigaku DMAX2500 X-ray diffractometer with Cu Kα radiation. Scanning electron microscopy (SEM) was performed on a HITACHI S-4800 apparatus, which applied to investigate the morphologies of the obtained photocatalysts. For the purpose of confirming the lattice spacing and the morphologies of the obtained samples, transmission electron microscopy (TEM) was recorded using a FEI Tecnai G2 F20 S-TWIN field emission microscope apparatus with an acceleration voltage of 200 kV. The ultraviolet-visible DRS of the samples were measured with a Perkin Elmer UV/VS/NIR Lambda 750 s spectrometer. The surface structures of the samples were measured by using Perkin Elmer IR spectrometer. The specific surface areas of the samples were measured on a Micromeritics ASAP 2020 Surface Area and Porosity Analyzer by Brunauer-Emmett-Teller (BET) technique. X-ray Photoelectron Spectroscopy (XPS) analyses were performed on an ESCALab220i-XL with a monochromatic Al Kα and charge neutralizer. The C 1 s peak at 284.6 eV was the referenced binding energy for all the samples. EPR spectra for superoxide radicals (sample, 4 mg; DMPO, 0.22 M; methanol solution volume, 2.0 mL) and hydroxyl radicals (sample, 4 mg; DMPO, 0.22 M; aqueous solution volume, 2.0 mL) were obtained on an ER200-SRC electron spin resonance spectrometer (Bruker, Germany) at 3186 G and 9056.895 MHz, which was performed in dark and visible light irradiation. Transient absorption spectroscopy (TAS) measurements were performed on a home-made setup equipped with a laser beam (532 nm, 1 mJ, 1 Hz), which was investigated in the range from 550 to 800 nm.
Electrochemical Measurements
Electrochemical analysis was performed on a conventional three-electrode cell which was consisted in the working (the fabricated electrode), counter (a platinum wire), and reference electrodes (Ag/AgCl, 3M KCl). The synthesized photocatalysts powder was deposited on the FTO (F-doped tin oxide) glass by electrophoretic deposition. The depositional solution was composed by the acetone (50 mL) which contains photocatalysts power (40 mg) and iodine (10 mg). Two clean FTO glasses with a distance (2 cm) were immersed in the solution in parallel and a potential (20 V) was applied between the electrodes for 120 s using a DC power supply [37]. Electrochemical impedance spectroscopy (EIS) measurements were performed in the frequency from 0.1 Hz to 100 KHz, and the applied voltage was the open circuit voltage. The electrolyte was Na2SO4 aqueous solution (0.2 M, pH = 7) [38]. Mott-Schottky plot of SnNb2O6 was performed at the frequency of 1000 Hz in the dark.
Evaluation of Photocatalytic Activity
Photocatalytic water splitting reactions were carried out by the suspension which was contained 0.1 g of the as-prepared photocatalyst, 80 mL deionized water, 20 mL triethanolamine (TEOA) which was the sacrificial electron donor. The reaction solution was evacuated several times to remove the air and ensure the reactor in an inert atmosphere before irradiation. A 300 W Xenon lamp with a filter (λ ≥ 420 nm) was used as light source in this photocatalytic system. The generated H2 gases were analyzed by an online gas chromatograph (GC2014C, TCD, Ar as the carrier).
The photocatalytic performance of semiconductors was measured using the photodegradation of methyl orange (MO) under visible light irradiation. Herein, the photocatalytic experimental procedure was as follows: the 50 mL reaction suspension was contained 2 × 10− 5 mol/L MO (50 mL), and the obtained photocatalysis (25 mg) which was continuously stirred for 2 h in dark to achieve the equilibrium of MO absorption/desorption on the sample surface before illumination. Then, the suspensions were irradiated by a 300 W mercury lamp with a filter (λ ≥ 420 nm). At given intervals, 5 mL solution was centrifuged, which was used to test the UV-vis absorption spectra by a UVIKON XL/XS Spectrometer.
Results and Discussion
Figure 1a shows the XRD patterns of the products obtained by hydrothermal method. The phases of the samples were changed with increase of pH values. It is clearly seen that the diffraction peaks concurred with the pure phase of monoclinic SnNb2O6 (JCPDS 01-048-1810) as the pH values were 1, 3, and 5. The sample obtained at pH = 7 was the mixed phases of SnNb2O6 and Sn2Nb2O7 which also can be observed from the SEM (Additional file 1: Figure S2). And the phases were the pure phase of Sn2Nb2O7 (JCPDS 00-023-0593) when the pH values were 9 and 11. And no impurity peaks from other phases can be detected. This may be ascribed to their different Sn precursors as the description in the previous report [39]. The change of the phase structure was also investigated via the infrared spectra (Additional file 1: Figure S1). The average crystallite sizes of the synthesized samples was calculated using the Debye-Scherrer formula D = kλ/βcosθ [40]. Figure 1b presents that the average particle sizes of the prepared photocatalysts were increased from 7.6 to 24.7 nm for the crystal structure of SnNb2O6 with increase of pH from 1 to 7 and decreased from 47.0 to 17.4 nm for Sn2Nb2O7 with the pH value up to 11. It is commonly recognized that materials possess a smaller particle size which always have a higher specific surface area and the better photocatalytic activity of the catalysts will be achieved, which can be further confirmed by the results of photocatalytic performance [41]. In addition, we found that the reaction temperature had an influence on the formation of pyrochlore (Sn2Nb2O7) as shown in Additional file 1: Figure S2.
The morphologies and crystal structures of SnNb2O6 and Sn2Nb2O7 photocatalysts were investigated by field emission scanning electron microscopy (SEM) and transmission electron microscopy (TEM) (Fig. 2). It is clearly seen that the sample of SnNb2O6 was consisted of numerous irregular nanosheets (Fig. 2a, c) and the Sn2Nb2O7 was composed of uniform clumps (Fig. 2b, d). Meanwhile, the size of the clumps gradually decreased as the pH value increase (Additional file 1: Figure S3), which was consistent with the result of the average crystallite size in Fig. 1b. To identify the fine crystalline nature of the obtained samples, the high-resolution TEM was taken (inset images). As shown in Fig. 2c, the lattice plane space was about 0.285 nm corresponding to the (600) plane of SnNb2O6, and the lattice space of 0.611 nm was identical to the (111) plane of Sn2Nb2O7 illustrated in Fig. 2d.
In general, the band gap and energy level of a semiconductor are pivotal in determining the photocatalytic activity. It can be seen that all of the obtained samples had absorption in the visible region (Additional file 1: Figure S4). Meanwhile, the band gap transition from valence band to the conduction band was indicated by the steep edges in the DRS (Fig. 3a) [42]. The band gap energy E g of the semiconductors (SnNb2O6 and Sn2Nb2O7) with an indirect electronic transition can be determined by the following equation: αhν = A (hν−Eg)1/2, where α, ν, Eg, and A are the absorption coefficient, incident light frequency, band gap, and constant, respectively [25, 43]. As illustrated in Fig. 3b, the band gap energy of Sn2Nb2O7 (2.22 eV) was larger than that of SnNb2O6 which was estimated to be ~ 2.12 eV. Meanwhile, the experimental data was closed to the calculated band gap of SnNb2O6 (~ 2.10 eV) which was different from Sn2Nb2O7 (~ 2.3 eV), and the difference between the band energies of the samples may be owing to the Sn:Nb ratio and the crystal structure were different from each other [28].
The XPS measurement was performed to investigate the surface chemical compositions and chemical states of the photocatalysts. The survey XPS spectrum (Fig. 4a) of the as-prepared samples showed that Sn, Nb, O, and C were existed. The high-resolution XPS spectrum of Sn 3d (Fig. 4b) showed that Sn 3d XPS spectrum can be divided into two peaks with binding energies of ~ 486.4 and ~ 494.8 eV in SnNb2O6, which attributed to the Sn 3d5/2 and Sn 3d3/2 of Sn2+, respectively [44]. The binding energy of Sn 3d orbital for Sn2Nb2O7 exhibited four peaks as Sn2+ 3d5/2 at 486.4 eV, Sn4+ 3d5/2 at 487.2 eV, Sn2+ 3d3/2 at 494.8 eV, and Sn4+ 3d3/2 at 495.6 eV [45,46,47,48]. It indicated that Sn was present in the Sn2+ and Sn4+ chemical state on the surface of Sn2Nb2O7. The generation of the Sn4+ chemical state may be due to the oxidation of Sn2+ by the reaction system of strong alkalinity. As illustrated in Fig. 4c, the peaks located at ~ 206.9 and ~ 209.7 eV for all samples which correspond to the Nb 3d5/2 and Nb 3d3/2 and the structure splitting distance was about 2.8 eV, indicating that the Nb ions were existed in the form of Nb5+ [49]. Figure 4d illustrates XPS spectra of O 1s. We inferred that the variety of surface oxygen species was at least three kinds, on account of the three peaks in the O 1s spectrum for all the samples. The binding energy in O 1s spectra at about 530.1, 531.2, and 532.2 eV was assignable to the lattice oxygen (OL), surface hydroxyl groups (OS), and surface chemisorbed O2 which might be related to surface oxygen vacancies (Oad), respectively [50]. It is seen that the Oad content in SnNb2O6 (11.8%) was higher than that in Sn2Nb2O7 (8.3%). Generally, a higher Oad content implies a higher oxygen adsorption ability, which may expect a higher photocatalytic performance [51]. As a consequence, SnNb2O6 may display a greater photocatalytic activity than Sn2Nb2O7.
In principle, different crystal structures shows difference on the photocatalytic activity, on account of their unique structure and electronic properties [16, 18,19,20]. The photocatalytic performance of the obtained samples was estimated by methyl orange (MO) decomposition as the model reaction. Before irradiation, all suspensions were stirred in dark for 120 min to ensure the establishment of adsorption/desorption equilibrium of methyl orange on the sample surfaces. Little adsorption of the MO molecules was observed for all samples. Moreover, the photodegradation of methyl orange in the absence of catalyst was also investigated. It is clearly showed that little change in the MO concentration was observed, which implied that visible light irradiation had little impact on the self-degradation of MO (Additional file 1: Figure S5). However, a continuous decrease of the characteristic absorption peaks of MO was observed as an addition of tin niobate samples under visible light irradiation (Additional file 1: Figure S5). As shown in Fig. 5a, all the tin niobate products had the photocatalytic performance toward the degradation of MO. Remarkably, SnNb2O6 obtained in the pH = 1 showed the highest photocatalytic activity with 99.6% degradation efficiency after illumination for 40 min. Meanwhile, with the increase of the pH value, the photocatalytic activity was highly decreased (Additional file 1: Figure S5). The curves of kinetics over different photocatalysts were shown in Fig. 5b. It is seen that there existed a linear relationship between the ln (C0/C) plot and the visible light irradiation time, suggesting a first-order kinetic reaction feature of methyl orange degradation [52]. And the SnNb2O6 possessed the maximal degradation rate constant (0.112 ± 0.008 min− 1). Moreover, the prepared samples also exhibited photocatalytic water splitting property under visible light irradiation. The photocatalytic H2 evolution activity of the as obtained samples had been evaluated from water in the presence of triethanolamine (TEOA) as a sacrificial electron donor and 1.0 wt.% Pt as co-catalytic to promote the H2 evolution activities. Additional file 1: Figure S6 presents the H2 evolution amount of the samples obtained at different pH value. The result revealed that the H2 evolution amount of SnNb2O6 prepared in pH = 1 was much higher than others. The optimal photocatalytic H2 evolution rate achieved for SnNb2O6 to be 5.94 μmol g− 1 h− 1, which was 3.2 and 11.4 times higher than that of the mixed phases of SnNb2O6 and Sn2Nb2O7 obtained in the pH value of 7 and Sn2Nb2O7 obtained in pH = 11 (Fig. 5a).
Having the aforementioned results in mind, it is highly necessary to explore the origination of the difference photocatalytic activity between the samples of SnNb2O6 and Sn2Nb2O7. As we all know, there basically exists three key steps in the overall potocatalysis process related to charge kinetics, i.e., generation, transfer, and consumption [53]. The first step is the generation of charge carriers which is mainly dominated by the energy band structure of the light-responding semiconductor. In order to maximize the number of photons converted into electron-hole pairs that participated in the photocatalytic process, the narrow band gap semiconductors for absorbing broader spectrum of solar energy was necessary. As mentioned above, the band gap energy of SnNb2O6 (2.12 eV) was smaller than Sn2Nb2O7 (2.22 eV). Furthermore, as shown in Fig. 4b, Sn presented the Sn2+ and Sn4+ chemical state on the surface of Sn2Nb2O7. As a result of the existent of Sn4+ ions, the photocatalytic activity was decreased, which could be attributed to the Nb5+ ions can be replaced with the Sn4+ ions and then a formed electron trap site by Sn4+ species was located below the conduction band [23, 28]. Hence, SnNb2O6 possessed of the advantage in the charge generation compared with Sn2Nb2O7 under visible light irradiation.
Another most important step is the charge separation in the process of photocatalysis, which is the determination factor for the photocatalytic activity of a semiconductor, generally. Therefore, it is highly necessary to suppress detrimental electron-hole recombination during the charge-transfer. The electrochemical impedance spectroscopy (EIS) (Fig. 6a) was taken to investigate the charge-transfer resistance and separation efficiency of samples. The Nyquist plot data can be well-reproduced into solution-spreading resistance (Rs), charge-transfer resistance (Rct) (inset of Fig. 6a) in parallel with a constant phase-element (CPE) [54, 55]. Rct for a (SnNb2O6), b (the mixed phases of SnNb2O6 and Sn2Nb2O7), and c (Sn2Nb2O7) samples were 16.1, 35.5, and 41.7 KΩ, respectively. The SnNb2O6 sample with the smallest Rct usually presented the lower resistance than others. According to the previous report, semiconductor own a smaller Rct which always achieved a higher separation efficiency of the photogenerated carriers and a faster transfer of interfacial charge during the photocatalytic process [56]. Furthermore, by way of transient photocurrent responses, we can give a profound understand for the separation efficiency and the transfer of photogenerated carriers. As shown in Fig. 6b, all of the samples exhibited prompt and reproducible photocurrent responses on each illumination. As observed, the transient photocurrent density of the SnNb2O6 was higher than others. In general, high photocurrent density typically indicated a stronger ability to promote electron shuttling and suppressing charge recombination, which eventually contributed to the enhancement in photocatalytic performance [57, 58]. Based on the analysis of the EIS and transient photocurrent response, the efficient charge separation and the improvement of electrical conductivity were achieved in SnNb2O6 compared with others, which may predict the enhancement of the photocatalytic performance.
Basically, the photocatalytic mechanism and the carrier dynamics also can be investigated by the time-resolved spectroscopy [59]. In order to further determine the excited state dynamics including charge separation, electron trapping and the recombination at materials surface, transient absorption spectroscopy (TAS) measurement was used [15]. As shown in Fig. 6c, all samples showed a broad and continuous absorption in the range of 550–800 nm with the excitation by pulse laser at 532 nm. According to previous literature, the broad absorption in visible light region could be ascribed to the effective separation of the photoinduced charges at different trap states in semiconductors [60,61,62]. As the transient absorption intensity at the same monitoring delay time and wavelength often represents the relative charge separation efficiency [63]. From Fig. 6c, it is clearly seen that the charge separation efficiency was highly improved in SnNb2O6 compared with the Sn2Nb2O7 sample. The home-made setup with an excitation wavelength of 600 nm was used to analyze the charge-carrier dynamics of the obtained samples. The results in Fig. 6d clearly suggested that a multi-exponential feature was exhibited from the decay curves for all samples. Furthermore, the effective time of the samples can be calculated according the previous research [64]. The effective lifetime τ for a (SnNb2O6), b (the mixed phases of the SnNb2O6 and Sn2Nb2O7), and c (Sn2Nb2O7) samples were 0.273, 0.271, and 0.264 ms, respectively. Clearly, the lifetime τ of the SnNb2O6 sample was larger than others. We all know that the longer lifetime always indicated the enhancement of the photogenerated electron-hole separation efficiency [65, 66]. Hence, the relatively long lived charge separation state of SnNb2O6 promised a higher charge separation efficiency and photocatalytic activity.
Usually, the enhancement of the surface adsorption and the increase of the active sites on the surface have very important impact on the charge-consumption step during the photocatalytic process. It has been commonly recognized that the surface active sites play a key role in the photocatalytic activity of semiconductor. Hence, the surface area may have an important influence on the photocatalytic performance of the prepared products. In general, larger surface area often possesses a higher photocatalytic activity because of the more active sites on the surface. The isotherm curves of the obtained samples showed a feature of type IV in the classification of Brunauer-Deming-Deming-Teller, as illustrated in Fig. 7. The BET surface area of a (SnNb2O6), b (the mixed phases of SnNb2O6 and Sn2Nb2O7), and Sn2Nb2O7 were 44, 37, and 60 m2/g, respectively (inset of Fig. 7). Obviously, the BET surface area of the SnNb2O6 was smaller than Sn2Nb2O7 and lager than the other one. Generally speaking, the samples with a smaller particle size always lead to higher specific surface area. However, the result of BET area was inconsistent with the particle size shown in Fig. 1b and the photocatalytic performance as shown in Fig. 5, which predicted the BET surface area had a minor impact on the photocatalytic performance of the semiconductors. Moreover, photocatalyst with a planar structure and a smaller size usually was beneficial to accelerating the transfer of photogenerated charge carriers from semiconductor interior to the reaction sites on surface and as a consequence the photocatalytic activity was improved [19, 67]. Thus, the SnNb2O6 sample which possessed the structure of nanosheets and the smallest average crystallite size shown in Fig. 1b had the superiority in the photocatalytic activity.
As reported, it included four types of reactive species such as holes (h+), electron (e−), superoxide radicals (O2−•), and/or hydroxyl radicals (OH•) during the photocatalytic degradation of organic pollution [68]. In order to trace the effective radical species in the photocatalytic process, a series of controlled experiments by adding corresponding active species scavengers were carried out [69]. Briefly, 0.001 g of benzoquinone (BQ) was added to trap superoxide radical (O2−•), and 0.1 g of ammonium oxalate (AO) was added to trap hole (h+). Furthermore, the controlled experiments was proceeded by adding 2.5 mL carbon tetrachloride (CCl4) as an electron scavenger (e−) and 2.5 mL of tert-butyl alcohol (TBA) as a hydroxyl radical scavenger (OH•) [70, 71]. It was clear that the photodegradation rate of MO decreased significantly when TBA, BQ, and AO were added under visible light irradiation (Fig. 8a). Meanwhile, the photocatalytic activity was improved with the addition of CCl4. This may be due to the separation efficiency of photogenerated carriers that was enhanced with the addition of CCl4 as the electron scavenger, and then more holes and the corresponding active species were participated in the photocatalytic reaction, which would improve the degradation rate [72]. Based on the above result, the main active species in the photocatalytic decomposition of MO were included the oxidation reaction of the holes which generated in the valence and the formed O2−• and OH• on the surface of semiconductor. To further elucidate the actives involved in the photocatalytic process, electron paramagnetic resonance (EPR) technique was taken. 5, 5-Dimethyl-1-pyrroline-N-oxide (DMPO) was used as a spin trap to capture hydroxyl radical and superoxide species [73]. As shown in Fig. 8b, the characteristic EPR signal of DMPO-O2−• was detected under the visible light irradiation and the intensity gradually increased with the increase of irradiation time. The result of the investigation of DMPO-OH• adduct was presented in Fig. 8c which indicated that the active species of OH• was generated in the process of photocatalytic under visible light irradiation and the signal increased with prolonged irradiation time. The formation of the OH• and O2−• active species in the process of the photocatalytic was determined by EPR technique. Meanwhile, the EPR analysis gave a direct evidence that the dominated active species during the photocatalytic decomposition MO were OH• and O2−•.
The Mott-Schottky analysis was carried out to determine the flat band potential (Efb) and conduction band (CB) edges of the photocatalysts [74,75,76]. The positive slope was observed in the Schottky plots of all the products shown in Additional file 1: Figure S7 which demonstrated that the photocatalysts were assigned to n-type semiconductors [77, 78]. The flat band potentials (Efb) of the samples can be estimated using the extrapolation of the Mott-Schottky plot at the frequency of 1000 Hz and found to be − 0.685 eV for the SnNb2O6, − 0.67 eV for the mixed phases of SnNb2O6 and Sn2Nb2O7, and − 0.626 eV for the Sn2Nb2O7. It was known that the conduction band potentials of n-type semiconductors were closed to the flat potential [39, 79, 80]. Hence, the positions the conduction band of the prepared samples were − 0.685, − 0.67, and − 0.626 eV for SnNb2O6, the mixed phases of SnNb2O6 and Sn2Nb2O7, and the Sn2Nb2O7, respectively (inset of Additional file 1: Figure S6). From the results of the MS analysis, we can see that the variation of the phase structure from SnNb2O6 to Sn2Nb2O7 accompanied with the change of the band edge potentials. Meanwhile, the valence band of the sample can be evaluated by the band gap data (E g = 2.12 eV) determined by the UV-vis spectra (Fig. 3), and the valence band of SnNb2O6 was 1.435 eV. This result was closed to previous reported results of the conduction band (− 0.68 eV) and valence band (1.42 eV) edge potentials of SnNb2O6 [43].
On the basis of the above experimental results, a possible photocatalytic mechanism was described as follows. For SnNb2O6, the conduction band (CB) and valence band (VB) edge potentials are − 0.685 and 1.435 eV, respectively. Under visible light irradiation, the photogenerated electrons were excited from the valence band to the conduction band of SnNb2O6 to reduction oxygen, while the photogenerated holes on the valence band of SnNb2O6 reacted with the contaminant and lead to the decomposition of methyl orange. The photogenerated electrons in the conduction band of SnNb2O6 reacted with electron acceptors including O2 existed in the system, leading to the formation of O2−• active species and the subsequent degradation of methyl orange. The generated O2−• radical species reacted with electrons in succession to produce active OH•, leading to the degradation of MO [81].
Conclusions
In summary, we systematically investigated the tin niobate photocatalysts of SnNb2O6 (froodite) and Sn2Nb2O7 (pyrochlore) in order to uncover the impact of phase structure and electronic structure on the charge kinetics and the subsequent improvement of photocatalytic activity. The band gap was changed with the transformation of phase structure, which contributed to the advantage for SnNb2O6 in charge generation compared with Sn2Nb2O7. The existent of Sn4+ in Sn2Nb2O7 resulted in a decrease in the photocatalytic activity, because part of the Nb5+ ions can be replaced with Sn4+ ions in tin niobates, and the Sn4+ species formed an electron trap site which located below the conduction band. On the other hand, the efficient charge separation, the reduction of resistance, and the improvement of charge transfer rate, which dramatically enhanced the photocatalytic activity toward water reduction and MO degradation. The optimal photocatalytic activity toward H2 evolution of SnNb2O6 showed 11.4 times improvement with respect to that of the Sn2Nb2O7. Meanwhile, the SnNb2O6 possessed the maximal degradation rate constant (0.112 ± 0.008 min− 1). Additionally, the quenching effects of different scavengers suggested that the dominated active species in the photodegradation reaction were holes, O2−•, and OH•.
Abbreviations
- BET:
-
Brunauer-Emmett-Teller
- DRS:
-
Diffuse reflection spectroscopy
- EIS:
-
Electrochemical impedance spectroscopy
- EPR:
-
Electron paramagnetic resonance
- FTO:
-
Fluorine-doped tin oxide
- SEM:
-
Scanning electron microscopy
- TAS:
-
Transient absorption spectroscopy
- TEM:
-
Transmission electron microscopy
- XPS:
-
X-ray photoelectron spectroscopy
- XRD:
-
X-ray power diffraction
References
Lan Z-A, Zhang G, Wang X (2016) A facile synthesis of Br-modified g-C3N4 semiconductors for photoredox water splitting. Appl Catal B Environ 192:116–125
Lei C, Zhu X, Zhu B, Jiang C, Le Y, Yu J (2017) Superb adsorption capacity of hierarchical calcined Ni/Mg/Al layered double hydroxides for Congo red and Cr(VI) ions. J Hazard Mater 321:801–811
Lin L, Ou H, Zhang Y, Wang X (2016) Tri-s-triazine-based crystalline graphitic carbon nitrides for highly efficient hydrogen evolution photocatalysis. ACS Catal 6:3921–3931
Jiang W, Bai S, Wang L, Wang X, Yang L, Li Y, Liu D, Wang X, Li Z, Jiang J, Xiong Y (2016) Integration of multiple Plasmonic and co-catalyst nanostructures on TiO2 Nanosheets for visible-near-infrared photocatalytic hydrogen evolution. Small 12:1640–1648
Hu Y, Chen G, Li C, Zhou Y, Sun J, Hao S, Han Z (2016) Fabrication of {010} facet dominant BiTaO4 single-crystal nanoplates for efficient photocatalytic performance. J Mater Chem A 4:5274–5281
Choi Y, Kim H-i, Moon G-h, Jo S, Choi W (2016) Boosting up the low catalytic activity of silver for H2 production on ag/TiO2 photocatalyst: thiocyanate as a selective modifier. ACS Catal 6:821–828
Zhu G, Lin T, Cui H, Zhao W, Zhang H, Huang F (2016) Gray Ta2O5 nanowires with greatly enhanced photocatalytic performance. ACS Appl Mater Interfaces 8:122–127
Liu G, Niu P, Sun C, Smith SC, Chen Z, Lu GQ, Cheng H-M (2010) Unique electronic structure induced high photoreactivity of sulfur-doped graphitic C3N4. J Am Chem Soc 132:11642–11648
Yang Y, Liu G, Irvine JTS, Cheng H-M (2016) Enhanced photocatalytic H2 production in core–shell engineered rutile TiO2. Adv Mater 28:5850–5856
Lei F, Sun Y, Liu K, Gao S, Liang L, Pan B, Xie Y (2014) Oxygen vacancies confined in ultrathin indium oxide porous sheets for promoted visible-light water splitting. J Am Chem Soc 136:6826–6829
Yang Y, Wang Y, Yin S (2017) Oxygen vacancies confined in SnO2 nanoparticles for desirable electronic structure and enhanced visible light photocatalytic activity. Appl Surf Sci 420:399–406
Su Y, Peng L, Guo J, Huang S, Lv L, Wang X (2014) Tunable optical and photocatalytic performance promoted by nonstoichiometric control and site-selective codoping of trivalent ions in NaTaO3. J Phys Chem C 118:10728–10739
Elgh B, Yuan N, Cho HS, Nilsson E, Terasaki O, Palmqvist AEC (2013) Correlating photocatalytic performance with microstructure of mesoporous titania influenced by employed synthesis conditions. J Phys Chem C 117:16492–16499
Kumar V, Govind A, Nagarajan R (2011) Optical and photocatalytic properties of heavily F-doped SnO2 nanocrystals by a novel single-source precursor approach. Inorg Chem 50:5637–5645
Bai S, Jiang J, Zhang Q, Xiong Y (2015) Steering charge kinetics in photocatalysis: intersection of materials syntheses, characterization techniques and theoretical simulations. Chem Soc Rev 44:2893–2939
Marschall R, Soldat J, Wark M (2013) Enhanced photocatalytic hydrogen generation from barium tantalate composites. Photoch Photobio Sci 12:671–677
Yoshioka K, Petrykin V, Kakihana M, Kato H, Kudo A (2005) The relationship between photocatalytic activity and crystal structure in strontium tantalates. J Catal 232:102–107
Tüysüz H, Chan CK (2013) Preparation of amorphous and nanocrystalline sodium tantalum oxide photocatalysts with porous matrix structure for overall water splitting. Nano Energy 2:116–123
Chen D, Ye J (2009) Selective-synthesis of high-performance single-crystalline Sr2Nb2O7 nanoribbon and SrNb2O6 nanorod photocatalysts. Chem Mater 21:2327–2333
Grewe T, Meier K, Tüysüz H (2014) Photocatalytic hydrogen production over various sodium tantalates. Catal Today 225:142–148
Noureldine D, Takanabe K (2016) State-of-the-art Sn2+-based ternary oxides as photocatalysts for water splitting: electronic structures and optoelectronic properties. Catal Sci Technol 6:7656–7670
Ercit TS, Černý P (1988) The crystal structure of foordite. Acta Crystallogr 26:493–498
Cruz LP, Savariault JM, Rocha J, Jumas JC, Pedrosa de Jesus JD (2001) Synthesis and characterization of tin Niobates. J Solid State Chem 156:349–354
Stewart DJ, Knop O, Meads RE, Parker WG (2011) Pyrochlores. IX. Partially oxidized Sn2Nb2O7 and Sn2Ta2O7: a Mössbauer. Can J Chem 51:1041–1049
Zhou C, Zhao Y, Bian T, Shang L, Yu H, Wu L-Z, Tung C-H, Zhang T (2013) Bubble template synthesis of Sn2Nb2O7 hollow spheres for enhanced visible-light-driven photocatalytic hydrogen production. Chem Commun 49:9872–9874
Saito K, Kudo A (2013) Fabrication of highly crystalline SnNb2O6 shell with a visible-light response on a NaNbO3 nanowire core. Inorg Chem 52:5621–5623
Yasuhiro H, Kentaro T, Hideki K, Hisayoshi K, Akihiko K (2004) Energy structure and photocatalytic activity of niobates and tantalates containing Sn(II) with a 5s2 electron configuration. Chem Lett 33:28–29
Hosogi Y, Shimodaira Y, Kato H, Kobayashi H, Kudo A (2008) Role of Sn2+ in the band structure of SnM2O6 and Sn2M2O7(M=Nb and ta) and their photocatalytic properties. Chem Mater 20:1299–1307
Seo SW, Noh TH, Park S, Chan WL, Sang HK, Kim HJ, Park HK, Hong KS (2014) Solvothermal synthesis of SnNb2O6 nanoplates and enhanced photocatalytic H2 evolution under visible light. Int J Hydrog Energy 39:17517–17523
Noureldine D, Anjum DH, Takanabe K (2014) Flux-assisted synthesis of SnNb2O6 for tuning photocatalytic properties. PCCP 16:10762–10769
Zhou C, Zhao Y, Shang L, Shi R, Wu L-Z, Tung C-H, Zhang T (2016) Facile synthesis of ultrathin SnNb2O6 nanosheets towards improved visible-light photocatalytic H2-production activity. Chem Commun 52:8239–8242
Subramanian MA, Aravamudan G, Subba Rao GV (1983) Oxide pyrochlores—a review. Prog Solid State Chem 15:55–143
Taira N, Kakinuma T (2012) Photocatalytic activity of Sn2M2O7 (M = Nb and ta) pyrochlore oxides with blue LEDs irradiation. J Ceram Soc Jpn 120:551–553
Ikeda S, Itani T, Nango K, Matsumura M (2004) Overall water splitting on tungsten-based photocatalysts with defect pyrochlore structure. Catal Lett 98:229–233
Abe R, Higashi M, Sayama K, Abe Y, Sugihara H (2006) Photocatalytic activity of R3MO7 and R2Ti2O7 (R = Y, Gd, La; M = Nb, Ta) for water splitting into H2 and O2. J Phys Chem B 110:2219–2226
Ikeda S, Fubuki M, Takahara YK, Matsumura M (2006) Photocatalytic activity of hydrothermally synthesized tantalate pyrochlores for overall water splitting. Appl Catal A Gen 300:186–190
Kim ES, Kang HJ, Magesh G, Kim JY, Jang J-W, Lee JS (2014) Improved photoelectrochemical activity of CaFe2O4/BiVO4 heterojunction photoanode by reduced surface recombination in solar water oxidation. ACS Appl Mater Interfaces 6:17762–17769
Zhang G, Lan Z-A, Lin L, Lin S, Wang X (2016) Overall water splitting by Pt/g-C3N4 photocatalysts without using sacrificial agents. Chem Sci 7:3062–3066
Donaldson JD, Moser W, Simpson WB (1963) 321. Basic tin(II) chloride. J Chem Soc (Resumed) 3:1727–1731
Wu JM, Chen Y-R, Kao WT (2014) Ultrafine ZnO nanoparticles/nanowires synthesized on a flexible and transparent substrate: formation, water molecules, and surface defect effects. ACS Appl Mater Interfaces 6:487–494
Chen J, Zhong J, Li J, Huang S, Hu W, Li M, Du Q (2017) Synthesis and characterization of novel Ag2CO3/g-C3N4 composite photocatalysts with excellent solar photocatalytic activity and mechanism insight. Mol Catal 435:91–98
Liang S, Zhu S, Chen Y, Wu W, Wang X, Wu L (2012) Rapid template-free synthesis and photocatalytic performance of visible light-activated SnNb2O6 nanosheets. J Mater Chem 22:2670–2678
Huang S, Lang J, Du C, Bian F, Su Y, Wang X (2017) Enhanced driving force and charge separation efficiency in disordered SnNbxOy: boosting photocatalytic activity toward water reduction. Chem Eng J 309:313–320
He Y, Zhang L, Fan M, Wang X, Walbridge ML, Nong Q, Wu Y, Zhao L (2015) Z-scheme SnO2−x/g-C3N4 composite as an efficient photocatalyst for dye degradation and photocatalytic CO2 reduction. Sol Energy Mater Sol Cells 137:175–184
Yamaguchi M, Ide-Ektessabi A, Nomura H, Yasui N (2004) Characteristics of indium tin oxide thin films prepared using electron beam evaporation. Thin Solid Films 447-448:115–118
Zhai P, Qin J, Guo L, Zhao N, Shi C, Liu E-Z, He F, Ma L, Li J, He C (2017) Smart hybridization of Sn2Nb2O7/SnO2@3D carbon nanocomposites with enhanced sodium storage performance through self-buffering effects. J Mater Chem A 5:13052–13061
Wang C-H, Shen W-Y, Sheng P-S, Lee C-Y, Chiu H-T (2007) Deposition of mesoporous silicon carbide thin films from (Me3Si)4Sn: tin nanoparticles as in situ generated templates. Chem Mater 19:5250–5255
Nayral C, Viala E, Fau P, Senocq F, Jumas J-C, Maisonnat A, Chaudret B (2000) Synthesis of tin and tin oxide nanoparticles of low size dispersity for application in gas sensing. Chem Eur J 6:4082–4090
Sasahara A, Tomitori M (2013) XPS and STM study of Nb-doped TiO2(110)-(1 × 1) surfaces. J Phys Chem C 117:17680–17686
Su Y, Huang S, Wang T, Peng L, Wang X (2015) Defect-meditated efficient catalytic activity toward p-nitrophenol reduction: a case study of nitrogen doped calcium niobate system. J Hazard Mater 295:119–126
Chang J, Ahmad M, Wlodarski W, Waclawik E (2013) Self-assembled 3D ZnO porous structures with exposed reactive {0001} facets and their enhanced gas sensitivity. Sensors 13:8445
Luo B, Xu D, Li D, Wu G, Wu M, Shi W, Chen M (2015) Fabrication of a ag/Bi3TaO7 plasmonic photocatalyst with enhanced photocatalytic activity for degradation of tetracycline. ACS Appl Mater Interfaces 7:17061–17069
Yang J, Wang D, Han H, Li C (2013) Roles of cocatalysts in photocatalysis and photoelectrocatalysis. Acc Chem Res 46:1900–1909
Kang S, Zhang L, Yin C, Li Y, Cui L, Wang Y (2017) Fast flash frozen synthesis of holey few-layer g-C3N4 with high enhancement of photocatalytic reactive oxygen species evolution under visible light irradiation. Appl Catal B Environ 211:266–274
Li K, Huang Z, Zeng X, Huang B, Gao S, Lu J (2017) Synergetic effect of Ti3+ and oxygen doping on enhancing photoelectrochemical and photocatalytic properties of TiO2/g-C3N4 heterojunctions. ACS Appl Mater Interfaces 9:11577–11586
Hung W-H, Yang K-L, Lai S-N, Yang C-R, Shyue J-J, Ku C-S, Cronin SB (2017) Demonstration of enhanced carrier transport, charge separation, and long-term stability for photocatalytic water splitting by a rapid hot pressing process. J Mater Chem A 5:10687–10695
Khan MM, Ansari SA, Pradhan D, Ansari MO, Han DH, Lee J, Cho MH (2014) Band gap engineered TiO2 nanoparticles for visible light induced photoelectrochemical and photocatalytic studies. J Mater Chem A 2:637–644
Hou Y, Wen Z, Cui S, Guo X, Chen J (2013) Constructing 2D porous graphitic C3N4 Nanosheets/nitrogen-doped graphene/layered MoS2 ternary nanojunction with enhanced photoelectrochemical activity. Adv Mater 25:6291–6297
Bhunia MK, Melissen S, Parida MR, Sarawade P, Basset J-M, Anjum DH, Mohammed OF, Sautet P, Le Bahers T, Takanabe K (2015) Dendritic tip-on polytriazine-based carbon nitride photocatalyst with high hydrogen evolution activity. Chem Mater 27:8237–8247
Pendlebury SR, Wang X, Le Formal F, Cornuz M, Kafizas A, Tilley SD, Grätzel M, Durrant JR (2014) Ultrafast charge carrier recombination and trapping in hematite photoanodes under applied bias. J Amer Chem Soc 136:9854–9857
Barroso M, Mesa CA, Pendlebury SR, Cowan AJ, Hisatomi T, Sivula K, Grätzel M, Klug DR, Durrant JR (2012) Dynamics of photogenerated holes in surface modified α-Fe2O3 photoanodes for solar water splitting. PNAS 109:15640–15645
Barroso M, Cowan AJ, Pendlebury SR, Grätzel M, Klug DR, Durrant JR (2011) The role of cobalt phosphate in enhancing the photocatalytic activity of α-Fe2O3 toward water oxidation. J Ame Chem Soc 133:14868–14871
Ye C, Li J-X, Li Z-J, Li X-B, Fan X-B, Zhang L-P, Chen B, Tung C-H, Wu L-Z (2015) Enhanced driving force and charge separation efficiency of protonated g-C3N4 for photocatalytic O2 evolution. ACS Catal 5:6973–6979
Su Y, Li G, Wang X, Li L (2012) Bridging between structure and optimum luminescence for nearly monodispersed Ce1−xGdxF3:Eu3+ nanoparticles. J Lumin 132:1407–1413
Wang X, Kafizas A, Li X, Moniz SJA, Reardon PJT, Tang J, Parkin IP, Durrant JR (2015) Transient absorption spectroscopy of Anatase and rutile: the impact of morphology and phase on photocatalytic activity. J Phys Chem C 119:10439–10447
Lei F, Zhang L, Sun Y, Liang L, Liu K, Xu J, Zhang Q, Pan B, Luo Y, Xie Y (2015) Atomic-layer-confined doping for atomic-level insights into visible-light water splitting. Angew Chem Int Ed 54:9266–9270
Bai S, Xiong Y (2015) Recent advances in two-dimensional nanostructures for catalysis applications. Sci Adv Mater 7:2168–2181
Zhang L-S, Wong K-H, Yip H-Y, Hu C, Yu JC, Chan C-Y, Wong P-K (2010) Effective photocatalytic disinfection of E. coli K-12 using AgBr−Ag−Bi2WO6 nanojunction system irradiated by visible light: the role of diffusing hydroxyl radicals. Environ Sci Technol 44:1392–1398
Wang T, Lang J, Zhao Y, Su Y, Zhao Y, Wang X (2015) Simultaneous doping and heterojunction of silver on Na2Ta2O6 nanoparticles for visible light driven photocatalysis: the relationship between tunable optical absorption, defect chemistry and photocatalytic activity. CrystEngComm 17:6651–6660
Lang J, Li C, Wang S, Lv J, Su Y, Wang X, Li G (2015) Coupled heterojunction Sn2Ta2O7@SnO2: cooperative promotion of effective Electron–hole separation and superior visible-light absorption. ACS Appl Mater Interfaces 7:13905–13914
Qu L, Lang J, Wang S, Chai Z, Su Y, Wang X (2016) Nanospherical composite of WO3 wrapped NaTaO3: improved photodegradation of tetracycline under visible light irradiation. Appl Surf Sci 388:412–419
Sun M, Su Y, Du C, Zhao Q, Liu Z (2014) Self-doping for visible light photocatalytic purposes: construction of SiO2/SnO2/SnO2:Sn2+ nanostructures with tunable optical and photocatalytic performance. RSC Adv 4:30820–30827
Li M, Li X, Jiang G, He G (2015) Hierarchically macro-mesoporous ZrO2–TiO2 composites with enhanced photocatalytic activity. Ceram Int 41:5749–5757
Rettie AJE, Lee HC, Marshall LG, Lin J-F, Capan C, Lindemuth J, McCloy JS, Zhou J, Bard AJ, Mullins CB (2013) Combined charge carrier transport and photoelectrochemical characterization of BiVO4 single crystals: intrinsic behavior of a complex metal oxide. J Amer Chem Soc 135:11389–11396
Nurlaela E, Ould-Chikh S, Harb M, del Gobbo S, Aouine M, Puzenat E, Sautet P, Domen K, Basset J-M, Takanabe K (2014) Critical role of the semiconductor–electrolyte Interface in photocatalytic performance for water-splitting reactions using Ta3N5 particles. Chem Mater 26:4812–4825
Shang J, Hao W, Lv X, Wang T, Wang X, Du Y, Dou S, Xie T, Wang D, Wang J (2014) Bismuth oxybromide with reasonable photocatalytic reduction activity under visible light. ACS Catal 4:954–961
Yan J, Zhang Y, Liu S, Wu G, Li L, Guan N (2015) Facile synthesis of an iron doped rutile TiO2 photocatalyst for enhanced visible-light-driven water oxidation. J Mater Chem A 3:21434–21438
Kandi D, Martha S, Thirumurugan A, Parida KM (2017) Modification of BiOI microplates with CdS QDs for enhancing stability, optical property, electronic behavior toward rhodamine B decolorization, and photocatalytic hydrogen evolution. J Phys Chem C 121:4834–4849
Wu X, Ng YH, Wang L, Du Y, Dou SX, Amal R, Scott J (2017) Improving the photo-oxidative capability of BiOBr via crystal facet engineering. J Mater Chem A 5:8117–8124
Bao S, Wang Z, Gong X, Zeng C, Wu Q, Tian B, Zhang J (2016) AgBr tetradecahedrons with co-exposed {100} and {111} facets: simple fabrication and enhancing spatial charge separation using facet heterojunctions. J Mater Chem A 4:18570–18577
Liu W, Wang M, Xu C, Chen S (2012) Facile synthesis of g-C3N4/ZnO composite with enhanced visible light photooxidation and photoreduction properties. Chem Eng J 209:386–393
Funding
This work is financially supported by the National Natural Science Foundation of China (grants 21563021), the Inner Mongolia Natural Science Foundation (grant no. 2016JQ01), and Program for Young Talents of Science and Technology in Universities of Inner Mongolia Autonomous Region (NJYT-18-A01).
Availability of Data and Materials
The datasets supporting the conclusions of this article are included within the article.
Author information
Authors and Affiliations
Contributions
SH synthesized and characterized the samples. YS, SH, CW, HS, and XW analyzed and discussed the results of the experiments. SH wrote the manuscript, and YS revised the manuscript. All authors read and approved the final manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Additional file
Additional file 1:
Figure S1. FT-IR spectra of the as-prepared photocatalysts. Figure S2. X-ray diffraction patterns of tin niobate prepared under different reaction temperature of 140°C (a), 160°C (b), 180°C (c), and 200°C (d). Figure S3. Typical SEM images of photocatalysts prepared at different pH values (1~ 11) of the reaction solution. Figure S4. UV-visible diffuse reflectance spectra of the as-prepared photocatalysts. Figure S5. Normalized concentration of methyl orange (MO) versus visible light irradiation time in the presence of as-prepared photocatalysts. Figure S6. The time course of photocatalytic H2 evolution of all prepared samples under visible light irradiation (λ ≥ 420) by using TEOA as sacrificial agent and 1.0 wt.% of Pt as cocatalyst. Figure S7. Mott-Schottky plots of the samples collected at the frequency of 1000 Hz. (DOC 2510 kb)
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Huang, S., Wang, C., Sun, H. et al. Steering Charge Kinetics of Tin Niobate Photocatalysts: Key Roles of Phase Structure and Electronic Structure. Nanoscale Res Lett 13, 161 (2018). https://doi.org/10.1186/s11671-018-2578-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-018-2578-2