Abstract
Although TiO2 was formerly a common material for photocatalysis reactions, its wide band gap (3.2 eV) results in absorbing only ultraviolet light, which accounts for merely 4% of total sunlight. Modifying TiO2 has become a focus of photocatalysis reaction research, and combining two metal oxide semiconductors is the most common method in the photocatalytic enhancement process. When MoO3 and TiO2 come into contact to form a heterogeneous interface, the photogenerated holes excited from the valence band of MoO3 should be transferred to the valence band of TiO2 to effectively reduce the charge recombination of photogenerated electron–hole pairs. This can efficiently separate the pairs and promote photocatalysis efficiency. In addition, photocurrent enhancement is attributed to the strong near-field and light-scattering effects from plasmonic Ag nanoparticles. In this work, we fabricated MoO3-coated TiO2 nanotube heterostructures with a 3D hierarchical configuration through two-step anodic oxidation and a facile hydrothermal method. This 3D hierarchical structure consists of a TiO2 nanotube core and a MoO3 shell (referred to as TNTs@MoO3), as characterized by field emission scanning electron microscopy and X-ray photoelectron spectroscopy.
Avoid common mistakes on your manuscript.
Background
Rapid technological development has been accompanied by an increased demand for energy. Consequently, research into alternative energy sources has become popular over the past decade, with many scientists focused on renewable energy sources with low carbon emissions and minimal environmental impact. These include solar energy [1, 2], geothermal heat [3, 4], tides [5], and various forms of biomass [6, 7]. Photocatalytic water splitting, as the most direct method for achieving the goal of clean and renewable energy [8], is also the most investigated method of directly converting solar energy into chemical energy. Some common means of promoting energy conversion efficiency include increasing the reaction area, catalyst deposition, and compositing with secondary materials; for example, synthesizing specific microstructures [9,10,11], depositing Pt as a catalyst [12, 13], and combining two different metal oxides [14,15,16].
TiO2 nanotube (TNT) arrays have received considerable attention for their large surface area, robust photocatalytic activity, and vectorial charge transfer properties [17,18,19]. However, the practical application of TiO2 is restricted by its wide band gap (3.2 eV). This results in absorbing only UV light, which accounts for 4% of total sunlight, greatly limiting its photocatalytic activity in the visible light region. In addition, the high recombination rate of TiO2 lowers the efficiency of photocatalytic activity. To solve these problems, many studies have focused on extending the absorption edge of TiO2 into the visible light region, including doping with nitrogen or other nonmetals [20, 21], surface modification with noble metals [22, 23], and coupling with narrow-band-gap semiconductors [14,15,16].
Molybdenum trioxide (MoO3) is a p-type metal oxide semiconductor with a high work function and excellent hole conductivity; therefore, it is widely used in organic solar cells and organic light-emitting diodes [24, 25]. MoO3 has a band gap of approximately 2.8 eV, with 20–30% ionic character and the capacity to absorb both UV and visible light [26]. The valence and conduction band positions of MoO3 are both lower than those of TiO2. Hence, a heterojunction between TiO2 and MoO3 might enhance photocatalytic activity by decreasing the charge recombination and promoting the charge transfer process [27]. Under visible light irradiation, the holes excited from the valence band of MoO3 should be transferred to the valence band of TiO2, to reduce the charge recombination of photogenerated electron–hole pairs.
Plasmonic photocatalysis has recently facilitated the rapid enhancement of photocatalytic efficiency under visible light irradiation [28, 29]. A surface plasmon is a surface electromagnetic wave on the metal–dielectric interface, widely used in optical, chemical, and biological sensing for the high sensitivity of its resonant waves. The surface plasmon resonance effect is confined to the metal surface to form a highly enhanced electric field [30]. When the particular resonance frequency of plasmonic metal nanoparticles matches that of the incident photon, strong electric field forms near the surface of the metal. Furthermore, tunable interactions between incident visible light and excited plasmonic nanoparticles are achieved by controlling their sizes and shapes, as well as the dielectric constant of the surrounding environment [31,32,33].
In the present work, we first synthesized MoS2 coating on the surface of TNTs through a hydrothermal method. MoS2 was then oxidized to MoO3 through a simple annealing process (Scheme 1). This process enabled high coverage of MoO3 nanoscale particles with a highly ordered structure. To further enhance the photocatalytic water-splitting performance, we introduced a surface plasmon resonance (SPR) effect.
Methods
Fabrication of the TiO2 Nanotubes
The TNTs were fabricated by a two-step anodic oxidation method. Prior to the anodic oxidation process, the titanium foil was cut to size and placed in acetone, then ethanol, then deionized (DI) water, and then subjected to ultrasonic vibration for 5 min. Anodic oxidation was carried out using a conventional two-electrode system with the Ti foil as an anode and a carbon rod as a cathode. All electrolytes consisted of 0.3 wt% ammonium fluoride (NH4F) in ethylene glycol (C2H6O2, EG) solution with 5 vol% water. All processes were carried out at room temperature.
In the first step of anodic oxidation, the Ti foil was anodized at 60 V for 30 min; the as-grown nanotubes were subsequently removed in 1 M HCl by ultrasonic vibration. The same Ti foil then underwent a second anodic oxidation process at 60 V for 30 min. After both steps were completed, the prepared TNTs were washed with ethanol and DI water. The TNTs were annealed in air at 450 °C for 4 h at a heating rate of 2 °C/min to form the anatase TNTs.
Synthesis of TNTs@MoO3 Core–Shell Structure
The TNTs@MoO3 core–shell structure was synthesized with a hydrothermal method and a simple annealing process. MoS2 nanosheets were synthesized by the following procedures: 0.12 g of sodium molybdate (Na2MoO4·2H2O) and 0.24 g of thioacetamide (TAA) were dissolved in 80 mL of DI water under vigorous stirring for 15 min. Subsequently, the transparent solution and as-grown TNTs were transferred into a 100-mL Teflon-lined stainless steel autoclave, which was sealed and heated to 200 °C at a heating rate of 3 °C/min and held for 24 h. After the autoclave was cooled to room temperature, the prepared TNTs@MoS2 were washed with DI water. The TNTs@MoS2 were annealed in air at 450 °C for 4 h with a heating rate of 2 °C/min to form the TNTs@MoO3 core–shell structure.
Deposition of Au Nanoparticles
The plasmonic cocatalyst photoelectrodes (Au/TNTs@MoO3) were fabricated with the prepared TNTs@MoO3 cocatalytic core–shell structure through the hydrothermal method, followed by the standard sputtering deposition of Au nanoparticles.
Characteristic Analysis and Photocurrent Measurements
The microstructures and morphologies of the samples were examined using field emission scanning electron microscopy (FE-SEM) and energy-dispersive X-ray spectroscopy (EDS). To confirm the bonding energy of the developed TiO2, MoS2, and MoO3 photoelectrodes, X-ray photoelectron spectroscopy (XPS) was employed. Finally, the photocatalytic reaction was measured in 1 M NaOH solution by operating three terminal potentiostats at room temperature under 532-nm laser irradiation with a 1-mm diameter spot size.
Results and Discussion
Figure 1 shows the SEM images and EDS mapping of the prepared samples. Figure 1a–c shows the SEM images of the TNTs, TNTs@MoS2, and TNTs@MoO3. The SEM image of TNTs obtained by two-step anodic oxidation of Ti foil in 0.3 wt% NH4F contained in ethylene glycol solution (Fig. 1a) exhibited uniform pore size (100–120 nm). After the core–shell structure was formed with MoS2 covered through the hydrothermal method, the porous structure of TNTs was not blocked to reduce the active reaction sites (Fig. 1b). Subsequently, the TNTs@MoO3 core–shell structure was formed by a simple annealing process in the tube furnace (Fig. 1c). Figure 1d shows the SEM image and EDS mapping of Au/TNTs@MoO3, providing clear information about the Ti, O, Mo, and Au. The uniform deposition of the island-like Au nanoparticles, observable on top of the TNTs@MoO3, facilitated the generation of the SPR effect.
XPS was used to investigate the chemical states of the TNTs@MoO3 after conversion from TNTs@MoS2 through a simple annealing process (Fig. 2). Three characteristic peaks of Ti and O can be observed in Fig. 2a, b. The binding energies at the Ti2p1, Ti2p3, and O1s peaks are 464.6, 458.9, and 530.4 eV, respectively. In Fig. 2c, a Mo3d3 peak at 231.6 eV and Mo3d5 peak at 228.9 eV can be identified, indicating the chemical composition of MoS2 in the TNTs@MoS2. In addition, a weak peak appearing at approximately 226 eV is the signal peak of S2s. The Mo3d3 and Mo3d5 peaks in Fig. 2d with binding energies of 235.6 and 232.6 eV are ascribed to Mo6+ in MoO3. Therefore, the XPS investigations confirm that the red shift of the spectrum reflects the conversion of the Mo element valence from tetravalent to hexavalent.
The photocatalytic water-splitting performance of the prepared photoelectrodes was measured under 532-nm laser irradiation. Figure 3a, b shows the photocurrent response (I–V curves) of TNTs@MoO3 and Au/TNTs@MoO3. According to the results, TiO2@MoO3 exhibits a higher photocurrent because of the enhanced charge separation rate at the TiO2@MoO3 heterogeneous interface (shown in Fig. 3a). Furthermore, with the integration of Au nanoparticles, Au/TNTs@MoO3 presented a photocurrent response approximately 1.5 times higher than TNTs@MoO3 at the bias voltage of −1 V. Figure 3c shows the I–T curves of the TNTs, TNTs@MoO3, and Au/TNTs@MoO3 at the bias voltage of 0 V. As shown in Fig. 3c, the photocurrent response was higher again in the Au/TNTs@MoO3 structure compared to the TNTs@MoO3 photoelectrode without the application of bias voltage. The photocurrent response of Au/TNTs@MoO3 could be enhanced through the simple SPR effect.
To further investigate the photocatalytic activity of the prepared photoelectrodes, we also examined the extended photocurrent responses and electrochemical impedance spectroscopy to understand the photocurrent stability and the charge transfer at the photoelectrode–electrolyte interfaces (Fig. 3d, e). The extended stability of the photoelectrode with the optimal performance, Au/TNTs@MoO3, was examined under 532-nm laser irradiation for approximately 1.5 h (Fig. 3d). At the applied voltage of 0.8 V, the photocurrent remained at 57% of its initial value. Figure 3e shows the Nyquist plots of all three tested photoelectrodes under 532-nm laser irradiation recorded at a DC potential of 1.23 V versus RHE and an AC potential frequency range of 106–1 Hz with an amplitude of 1 V under 532-nm laser irradiation. According to the results, smaller semicircle diameters can be observed in the Au/TNTs@MoO3 sample, indicating a lower transport impedance for charge carriers. The formation of a heterogeneous interface between TiO2 and MoO3 is confirmed to facilitate charge transfer and enhance photocatalytic activity through the excellent carrier conduction properties of the Au nanoparticles.
Conclusions
Supporting information
In the supporting information (Additional file 1) we performed the Raman spectra analysis of MoS2 layer, the related thickness and average pore size of SEM images of TNTs, and the enhancement mechanism of the system.
In this study, we successfully fabricated a TNTs@MoS2 core–shell heterostructure by a two-step anodic oxidation process and a facile hydrothermal method to form a TNTs@MoO3 core–shell structure through a simple annealing process. According to the results, a MoO3 coating on a photoelectrode can enhance its utilization of photons in the visible region. Moreover, with the integration of plasmonic Au nanoparticles, a significant improvement in the water-splitting photocurrent was observed compared to pure TiO2 nanotubes under visible light irradiation. The energy band engineering of the TNTs@MoO3 heterostructure favors charge transfer and suppresses photogenerated electron–hole pair recombination between MoO3 and TiO2, leading to enhanced photocatalytic activity.
References
Yang Y, Yang WZ, Tang WD, Sun CD (2013) High-temperature solar cell for concentrated solar-power hybrid systems. Appl Phys Lett 103:8
Zhang Y, Wang H, Liu Z, Zou B, Duan CY, Yang T, Zhang XJ, Zheng CJ, Zhang XH (2013) Optical absorption and photoelectrochemical performance enhancement in Si tube array for solar energy harvesting application. Appl Phys Lett 102:16
Bojadgieva K, Benderev A, Berova-Andonova A, Tsanov T (2013) Aspects of current geothermal application in Bulgaria. J Renew Sustain Ener 5:4
Self SJ, Reddy BV, Rosen MA (2013) Geothermal heat pump systems: status review and comparison with other heating options. Appl Energ 101:341–348
Wang L, Li CN (2011) Dynamic stability analysis of a tidal power generation system connected to an onshore distribution system. Ieee T Energy Conver 26(4):1191–1197
Laihanen M, Karhunen A, Ranta T (2013) Possibilities and challenges in regional forest biomass utilization. J Renew Sustain Ener 5:3
Lei TZ, Wang ZW, Li ZF, Xu JF, He XF, Zhu JL (2013) A biomass briquetting fuel machine and its large-scale operation system. J Renew Sustain Ener 5:1
Hung WH, Chien TM, Tseng CM (2014) Enhanced photocatalytic water splitting by plasmonic TiO2-Fe2O3 cocatalyst under visible light irradiation. J Phys Chem C 118(24):12676–12681
Chae SY, Sudhagar P, Fujishima A, Hwang YJ, Joo OS (2015) Improved photoelectrochemical water oxidation kinetics using a TiO2 nanorod array photoanode decorated with graphene oxide in a neutral pH solution. Phys Chem Chem Phys 17(12):7714–7719
Yantara N, Pham TTT, Boix PP, Mathews N (2015) Modulating light propagation in ZnO-Cu2O-inverse opal solar cells for enhanced photocurrents. Phys Chem Chem Phys 17(33):21694–21701
Liu XY, Huang JA, Yang B, Zhang XJ, Zhu YY (2015) Highly reproducible SERS substrate based on polarization-free Ag nanoparticles decorated SiO2/Si core-shell nanowires array. AIP Adv 5:5
Wang CC, Hsueh YC, Su CY, Kei CC, Perng TP (2015) Deposition of uniform Pt nanoparticles with controllable size on TiO2-based nanowires by atomic layer deposition and their photocatalytic properties. Nanotechnology 26:25
Haldorai Y, Rengaraj A, Lee JB, Huh YS, Han YK (2015) Highly efficient hydrogen production via water splitting using Pt@MWNT/TiO2 ternary hybrid composite as a catalyst under UV-visible light. Synthetic Met 199:345–352
Kapoor MP, Inagaki S, Yoshida H (2005) Novel zirconium-titanium phosphates mesoporous materials for hydrogen production by photoinduced water splitting. J Phys Chem B 109(19):9231–9238
Luca V, Blackford MG, Finnie KS, Evans PJ, James M, Lindsay MJ, Skyllas-Kazacos M, Barnes PRF (2007) Sol-gel tungsten oxide/titanium oxide multilayer nanoheterostructured thin films: structural and photoelectrochemical properties. J Phys Chem C 111(50):18479–18492
Zhou W, Fu HG, Pan K, Tian CG, Qu Y, Lu PP, Sun CC (2008) Mesoporous TiO2/alpha-Fe2O3: bifunctional composites for effective elimination of arsenite contamination through simultaneous photocatalytic oxidation and adsorption. J Phys Chem C 112(49):19584–19589
Chen KS, Feng XR, Tian H, Li Y, Xie K, Hu R, Cai YX, Gu HS (2014) Silver-decorated titanium dioxide nanotube arrays with improved photocatalytic activity for visible light irradiation. J Mater Res 29(11):1302–1308
Liu H, He YH, Liang X et al (2014) J Mater Res 29(1):98–106
Shaislamov U, Yang BL (2013) CdS-sensitized single-crystalline TiO2 nanorods and polycrystalline nanotubes for solar hydrogen generation. J Mater Res 28(3):418–423
Guo W, Shen YH, Wu LQ, Gao YR, Ma TL (2011) Effect of N dopant amount on the performance of dye-sensitized solar cells based on N-doped TiO2 electrodes. J Phys Chem C 115(43):21494–21499
Xu Z, Yin M, Sun J, Ding G, Lu L, Chang P, Chen X, Li D (2016) 3D periodic multiscale TiO2 architecture: a platform decorated with graphene quantum dots for enhanced photoelectrochemical water splitting. Nanotechnology 27(11):115401
Chen L, He S, He BY, Wang TJ, Su CL, Zhang C, Jin Y (2012) Synthesis of iron-doped titanium oxide nanoadsorbent and its adsorption characteristics for fluoride in drinking water. Ind Eng Chem Res 51(40):13150–13156
Kumaresan L, Mahalakshmi M, Palanichamy M, Murugesan V (2010) Synthesis, characterization, and photocatalytic activity of Sr2+ doped TiO2 nanoplates. Ind Eng Chem Res 49(4):1480–1485
Zhao DW, Sun XW, Jiang CY, Kyaw AKK, Lo GQ, Kwong DL (2008) Efficient tandem organic solar cells with an Al/MoO3 intermediate layer. Appl Phys Lett 93:8
Hamwi S, Meyer J, Winkler T, Riedl T, Kowalsky W (2009) p-type doping efficiency of MoO3 in organic hole transport materials. Appl Phys Lett 94:25
Chithambararaj A, Sanjini NS, Velmathi S, Bose AC (2013) Preparation of h-MoO3 and alpha-MoO3 nanocrystals: comparative study on photocatalytic degradation of methylene blue under visible light irradiation. Phys Chem Chem Phys 15(35):14761–14769
Lu MX, Shao CL, Wang KX, Lu N, Zhang X, Zhang P, Zhang MY, Li XH, Liu YC (2014) p-MoO3 nanostructures/n-TiO2 nanofiber heterojunctions: controlled fabrication and enhanced photocatalytic properties. ACS Appl Mater Interfaces 6(12):9004–9012
Zhang XM, Chen YL, Liu RS, Tsai DP (2013) Plasmonic photocatalysis. Rep Prog Phys 76:4
Yang W, Xiong Y, Zou L, Zou Z, Li D, Mi Q, Wang Y, Yang H (2016) plasmonic Pd nanoparticle-and plasmonic pd nanorod-decorated BiVO4 electrodes with enhanced photoelectrochemical water splitting efficiency across visible-NIR region. Nanoscale Res Lett 11(1):1–8
Hou WB, Cronin SB (2013) A review of surface plasmon resonance-enhanced photocatalysis. Adv Funct Mater 23(13):1612–1619
Hung WH, Lai SN, Su CY, Yin M, Li DD, Xue XZ, Tseng CM (2015) Combined Au-plasmonic nanoparticles with mesoporous carbon material (CMK-3) for photocatalytic water splitting. Appl Phys Lett 107:7
Ringe E, Sharma B, Henry AI, Marks LD, Van Duyne RP (2013) Single nanoparticle plasmonics. Phys Chem Chem Phys 15(12):4110–4129
Link S, El-Sayed MA (2000) Shape and size dependence of radiative, non-radiative and photothermal properties of gold nanocrystals. Int Rev Phys Chem 19(3):409–453
Funding
The authors acknowledge financial support from the Ministry of Science and Technology Foundation (MOST 105-2221-E-035-015-). The authors appreciate the Precision Instrument Support Center of Feng Chia University for providing the facilities for production and measurement.
Author information
Authors and Affiliations
Contributions
CJL carried out the experiments and drafted the manuscript. SNL participated in the design of the study and performed the analysis. CRY participated in the measurements. CMT and WHH supervised the overall study and polished the manuscript. All authors read and approved the final manuscript.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Additional file
Additional file 1:
Supporting information. (DOCX 1074 kb)
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Li, CJ., Tseng, CM., Lai, SN. et al. Photocatalytic Activities Enhanced by Au-Plasmonic Nanoparticles on TiO2 Nanotube Photoelectrode Coated with MoO3 . Nanoscale Res Lett 12, 560 (2017). https://doi.org/10.1186/s11671-017-2327-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-017-2327-y