Abstract
In this work, we demonstrate a facile successive ionic layer adsorption and reaction process accompanied by hydrothermal method to synthesize CdS nanoparticle-modified α-Fe2O3/TiO2 nanorod array for efficient photoelectrochemical (PEC) water oxidation. By integrating CdS/α-Fe2O3/TiO2 ternary system, light absorption ability of the photoanode can be effectively improved with an obviously broadened optical-response to visible light region, greatly facilitates the separation of photogenerated carriers, giving rise to the enhancement of PEC water oxidation performance. Importantly, for the designed abnormal type-II heterostructure between Fe2O3/TiO2, the conduction band position of Fe2O3 is higher than that of TiO2, the photogenerated electrons from Fe2O3 will rapidly recombine with the photogenerated holes from TiO2, thus leads to an efficient separation of photogenerated electrons from Fe2O3/holes from TiO2 at the Fe2O3/TiO2 interface, greatly improving the separation efficiency of photogenerated holes within Fe2O3 and enhances the photogenerated electron injection efficiency in TiO2. Working as the photoanodes of PEC water oxidation, CdS/α-Fe2O3/TiO2 heterostucture electrode exhibits improved photocurrent density of 0.62 mA cm− 2 at 1.23 V vs. reversible hydrogen electrode (RHE) in alkaline electrolyte, with an obviously negatively shifted onset potential of 80 mV. This work provides promising methods to enhance the PEC water oxidation performance of the TiO2-based heterostructure photoanodes.
Avoid common mistakes on your manuscript.
Background
To solve the severe problem of pollution and limited resources of fossil, photoelectrochemical (PEC) water splitting to produce hydrogen has been regarded as one of the most promising strategies for solar energy conversion. Since the first report on PEC water oxidation based on TiO2 [1], TiO2 has drawn much attention as the photoanode materials for PEC water oxidation, due to its stable PEC properties, strong optical response, and suitable energy band position [2, 3]. However, the PEC performance of pristine TiO2 photoanode is greatly confined by the slow water oxidation kinetics originated from the poor photogenerated carrier separation capability and insufficient light absorption ability [4, 5].
Therefore, various strategies have been taken to improve the PEC water oxidation performance of pristine TiO2, such as surface modification [6], quantum dot sensitization, and heterojunction construction [7, 8]. One efficient method to improve the photogenerated carrier separation performance is to construct heterostructured photoanode. For instance, constructing heterojunction between TiO2 and other metal oxide semiconductors with matched energy band structures (like Co3O4/TiO2 [9] and ZnIn2S4/TiO2 [10, 11]) can effectively facilitate the separation of photogenerated electrons and holes; therefore, PEC water splitting performance of the pristine TiO2 can be obviously enhanced. Among various metal oxide semiconductors, hematite (α-Fe2O3) is regarded as a promising photoanode material because of the suitable band gap (~ 2.0 eV) for sunlight harvesting, excellent stability, and low cost [12]. In addition, the theoretical power conversion efficiency (PCE) of α-Fe2O3 can reach 15.3%, with a photocurrent density of 12.6 mA cm− 2 at 1.23 V vs. reversible hydrogen electrode (RHE) under the standard sun irradiation [13]. Therefore, constructing α-Fe2O3/TiO2 heterostructured photoanode cannot only enhance the carrier separation performance in TiO2 but also effectively extend the light absorption range of TiO2. Meanwhile, according to some latest research, α-Fe2O3 photoanodes suffer from short electron-hole pair lifetime and hole diffusion length (2–4 nm), which results in high recombination rate of photogenerated carriers, hindering the improvement of the PEC performance [12]. In that case, to further enhance the PEC water splitting performance of Fe2O3/TiO2 photoanodes, some narrow band gap semiconductors, like CdS [14, 15] and PbS [16], can be coupled to facilitate the separation of photogenerated carriers. Among them, CdS/Fe2O3/TiO2 heterostructured photoanode is considered to be a promising choice with matched band gap and expanded light absorption range. Also, carrier transport process can be effectively improved because photogenerated carriers can be quickly separated at the interface of CdS/Fe2O3/TiO2, thereby greatly decreasing the carrier recombination rates.
What is more, in order to construct an advanced electrode for PEC water splitting system, the electrode materials should possess the characteristics like sufficient incident light capture capability and tunnels for charge transport. Comparing with general planar photoanodes, one dimensional (1D) nanorod (NR) array photoanodes exhibit good incident light harvesting performance due to the enhanced multi-scattering processes [17], which would lead to an enhanced PEC water oxidation performance. Besides, it is reported that 1D NR array also exhibits excellent carrier transport performance since the photogenerated carriers can directly transport along the NR, thus direct carrier recombination at the crystal boundary can be effectively avoided [18]. Also, in order to further enlarge the surface area of such 1D NR arrays, which can bring more PEC reaction sites and enhance the PEC performance, 1D NR with branched nanostructures is expected [19]. Such integrated architecture offers a long optical path for effective light harvesting, short diffusion distance for excellent charge transport, and large surface area for fast interfacial charge collection, which is of great benefit for the enhancement of PEC performance. Hence, it would be of particular interest to design a CdS-modified Fe2O3/TiO2 heterostructure NR array for PEC water oxidation.
Herein, we reported a facile successive ionic layer adsorption and reaction (SILAR)-hydrothermal method to synthesize CdS-modified Fe2O3/TiO2 NR array for efficient PEC water oxidation. UV-vis study confirms the CdS/Fe2O3/TiO2 NR array displays excellent optical response performance with an obvious broadened light absorption range. Improved charge transfer process and declined charge recombination rate can be evidenced by means of PL spectrum and EIS plots. Applied as the photoanode for PEC water oxidation, CdS/Fe2O3/TiO2 NR array exhibits greatly enhanced photocurrent density of 0.62 mA cm− 2 (1.23 V vs. RHE) in alkaline electrolyte compared with pristine TiO2 (0.32 mA cm− 2 at 1.23 V vs. RHE). It is believed that the synthesis route and the application of CdS/Fe2O3/TiO2 NR array presently reported is of great importance and can be applied in other photovoltaic and photoelectronic devices.
Methods
Preparation of CdS/Fe2O3/TiO2 NR Heterostructured Photoanode
Synthesis of TiO2 NR Array
To synthesize TiO2 NR array on the FTO glass, the FTO was cut into rectangle and ultrasonically cleaned with deionized water, acetone, and ethanol, successively. Then, the FTO was put into the autoclave containing a mixed solution of deionized water (20 ml), hydrochloric acid (20 ml), and titanium isopropoxide (1.1 ml) and baked at 160 °C for 6 h. After the reaction, the FTO was washed with deionized water and ethanol for several times and then was annealed in air at 450 °C for 0.5 h.
Synthesis of Fe2O3/TiO2 NR Array
To grow α-Fe2O3 on TiO2 NR, as obtained TiO2 NR array was put into a mixed solution of FeCl3 (15 ml, 0.1 M) and NaNO3 (15 ml, 0.5 M) and then transferred to the autoclave. Heating at 100 °C for 2 h, the autoclave was cooled to room temperature and the FTO substrate was washed with deionized water and ethanol for several times. Finally, the FTO substrate was annealed in air at 450 °C for 1 h.
Synthesis of CdS/Fe2O3/TiO2 NR
The obtained α-Fe2O3/TiO2 NR array was pretreated with an ethanol solution of mercaptopropinioc acid (MPA, 0.3 M) overnight at 50 °C and then washed with ethanol to remove the excess MPA. In order to deposit CdS layer, a facile successive ionic layer adsorption and reaction (SILAR) method is applied. Pretreated NR array was successively immersed into four different solutions for 30 s, including Cd(NO3)2·4H2O (ethanol, 0.1 M), pure ethanol, Na2S·9H2O (methanol, 0.2 M) and pure methanol, respectively. The SILAR process was repeated for five times and then the substrate was washed with methanol to remove the extra CdS.
Materials Characterization
The phase structures were characterized by X-ray powder diffractometer (XRD) in a 2θ range of 20 to 80°. The morphology of the products was studied with field emission scanning electron microscopy (FE-SEM) attached energy-dispersive X-ray spectroscopy (EDS). Transmission electron microscopy (TEM) images were collected via Tecnai 20 U-Twin equipment. The absorption and photoluminescence (PL) spectra were tested with TU-1900 and Hitachi U-4100, respectively.
Photoelectrochemical Performance Characterization
The PEC water oxidation performance was characterized with CHI660E electrochemical station with a three-electrode mode. The applied electrolyte was consisted of 1M NaOH. Before testing, the system was bubbled with argon for 30 min to remove the electrolyte dissolved gas. The linear sweep voltammograms (LSV) and chronoamperometric I-t curves were recorded under standard sunlight illuminations (100 mW cm− 2). Mott-Schottky plots were measured in the dark at an AC frequency of 1.0 kHz.
Hereafter, the electrode potential was converted into the RHE potential with the Nernst equation:
where E RHE was the converted potential vs. RHE, E Ag/AgCl was the measured potential vs. the Ag/AgCl electrode, and E o Ag/AgCl = 0.1976 V at 25 °C.
Result and Discussion
Structure and Morphology Characterization
The phase structures of the synthesized products are characterized by the XRD patterns in Fig. 1. As shown in Fig. 1a, the rutile TiO2 nanorod arrays (NR) are successfully synthesized. The diffraction peaks at 36.0°, 44.1°, 54.3°, 62.7°, 64.0°, 65.4°, and 69.8° correspond well to (101), (210), (211), (002), (310), (221), and (112) planes of rutile TiO2 (JCPDS. 21-1276). After deposition of Fe2O3, the additional XRD diffraction peaks at 32.9° and 45.2° can be indexed to (222) and (332) planes of Fe2O3 (JCPDS. 39-0238). SILAR process is applied to grow CdS nanoparticles, the diffraction peaks at 26.4°, 28.2° corresponding well to (002) and (101) planes of CdS (JCPDS. 65-3414) confirm the success growth of CdS nanoparticles on Fe2O3/TiO2. The SEM image in Fig. 1b shows that TiO2 NRs are uniformly grown on the FTO substrate with a diameter of 50 nm. The NR surface is relatively smooth. After growth of Fe2O3 on surface of TiO2, the diameter of Fe2O3/TiO2 gests larger and increases to 60 nm. Furthermore, the surface of the NRs gets much rougher. Further deposition of CdS nanoparticles can cause an increase in diameter of the Fe2O3/TiO2 composite NR. To further confirm element distribution of the obtained CdS/Fe2O3/TiO2 NR, the cross-view EDS mapping images are recorded and shown in Additional file 1: Figure S1, Additional file 2: Figure S2. It can be seen that Ti, Fe, Cd, and S elements are uniformly distributed among samples.
The HRTEM image and selected area electron diffraction (SAED) pattern of CdS/Fe2O3/TiO2 NR are shown in Fig. 2. It can be seen that the both TiO2 and Fe2O3 are well crystallized and the CdS nanoparticles are grown on surface of Fe2O3. The lattice spacing of 0.31, 0.27, and 0.21 nm can be corresponded well to the (101), (222), and (210) plane of CdS, Fe2O3, and TiO2, respectively (Fig. 2a). The diffraction rings from the recorded SAED pattern in Fig. 2b can be seen, which can be indexed well to (101), (210) planes of rutile TiO2, (222), (332) planes of Fe2O3, and (002), (101) planes of CdS, respectively. The TEM results are in good agreement with the XRD characterization results.
a HRTEM image of CdS/Fe2O3/TiO2 NR. The marked d-spacing of 0.31 nm corresponds well to the (101) plane of CdS, the d-spacing of 0.27 nm correspond well to the (222) plane of Fe2O3 and the d-spacing of 0.21 nm correspond well to the (210) plane of TiO2. b Selected area electron diffraction pattern of CdS/Fe2O3/TiO2 NR, the diffraction rings correspond to the (002), (101) planes of CdS, (222), (332) planes of Fe2O3 and (101), (210) planes of TiO2
The chemical composition and valence states of the CdS/Fe2O3/TiO2 hybrid NRs are studied by XPS spectra. Figure 3a shows the survey spectra, the existence of Ti, Fe, O, Cd, and S elements are demonstrated. The appearance of element C is assigned to the carbon-based containment. For the Ti 2p XPS spectrum in Fig. 3b, these splitted two distinct peaks at 458.2 and 464.2 eV can be assigned to Ti 2 p3/2 and 2 p1/2 of TiO2 [20]. The XPS spectrum of Fe 2p is shown in Fig. 3c. Two distinct peaks at 710.6 and 724.10 eV can be seen, which correspond well to Fe 2 p3/2 and 2 p1/2 peaks of α-Fe2O3 [21]. The core level XPS spectrum of O 1s is shown in Fig. 3d, where the peak at 531.2 eV is attributed to the Ti–O bond between titanium and oxygen, and the peak at 531.9 eV can be attributed to the Fe–O bond between iron and oxygen [20, 21]. Figure 3e shows XPS spectrum of Cd, which is attributed to the Cd 3d5/2 at 405.2 eV. The XPS spectrum of S 2P is shown in Fig. 3f [22]. The center peak is splitted into two peaks of S 2p1/2 and 2p3/2 at 161.5 and 162.6 eV [22].
Figure 4a shows the absorption spectra of different photoelectrodes. TiO2 shows a typical absorption band edge at 400 nm, which can be attributed to the intrinsic band gap absorption of TiO2 (3.2 eV). After coupling with Fe2O3, Fe2O3/TiO2 shows enhanced absorption in the visible light region at about 540 nm. The extension of absorption band edge is due to the visible-sensitive component of Fe2O3 (2.0–2.2 eV). After further modification of CdS nanoparticles, the light absorption edge can be further extended to 580 nm. It confirms that coupling TiO2 with Fe2O3 and CdS can effectively tune the light absorption property to visible light region. Photoluminescence (PL) spectrum is applied to study the influence of incorporation of CdS and Fe2O3 in the CdS/Fe2O3/TiO2 hybrid on photogenerated carriers’ transport and recombination behavior. The lower the intensity of PL peak, the higher separation efficiency of photogenerated carrier pairs in the samples. Figure 4b shows the PL spectra of TiO2, Fe2O3/TiO2, and CdS/Fe2O3/TiO2 samples. It is obvious that Fe2O3/TiO2 NR achieves lower carrier recombination rate than pristine TiO2, and CdS/Fe2O3/TiO2 NR achieves the best carrier transport performance.
In order to further confirm this conclusion, the picosecond-resolved fluorescence transient plots are tested and shown as Additional file 3: Figure S3. The average lifetime τ is calculated according to τ = (B1τ1 [2] + B 2 τ 2 [2])/(B1τ1 + B2τ2) and the time constant of the fluorescence transients at 511 nm is listed in the Additional file 4: Table S1 [23]. It can be seen that after modifying pristine TiO2 with Fe2O3, the photogenerated carrier lifetime is prolonged. Coupled with CdS, the carrier lifetime can be further enhanced. This result obviously demonstrates the charge separation performance can be effectively enhanced by forming CdS/Fe2O3/TiO2 multi-junction.
The possible carrier transport process is illustrated in Fig. 5. In the CdS/Fe2O3/TiO2 ternary system, because both the conduction band position and valence band position of CdS are higher than that of Fe2O3, the photoinduced electrons in CdS will be transported to conduction band of Fe2O3, while the photoinduced holes in valence band in Fe2O3 will be transported to CdS. For the designed abnormal type-II heterostructure between Fe2O3/TiO2, the conduction band position of Fe2O3 is higher than that of TiO2. Under sunlight illumination, photoexcited electron-hole pairs will generate both in TiO2 and Fe2O3. Photogenerated electrons in the conduction band of Fe2O3 will immediately move to the valence band of TiO2 to recombine with the photogenerated holes, thus greatly improving the separation efficiency of photogenerated holes within Fe2O3 and enhances the photogenerated electron injection efficiency in TiO2 [24, 25]. It implies that the coupling of TiO2 with Fe2O3 and CdS can effectively reduce the recombination rate of the photogenerated carrier pairs. Meanwhile, the photogenerated electrons in TiO2 move to the counter electrode where the reduction reaction takes place. So, the abnormal type-II heterostructure between Fe2O3/TiO2 plays an important role in the enhanced PEC water oxidation performance.
Figure 6 depicts linear sweep voltammograms (LSV) and chronoamperometric I-t curves of CdS/Fe2O3/TiO2, Fe2O3/TiO2, and TiO2 samples. As shown in Fig. 6a, the photocurrent density of photoanodes under illumination gradually increases after coupling with α-Fe2O3 and CdS nanoparticles, and the CdS/Fe2O3/TiO2 NR sample exhibits the largest photocurrent density of 0.61 mA cm− 2 at 1.2 V vs. RHE, which is almost twice of bare TiO2 sample. I-t curves at a bias potential of 1.2 V vs. RHE under chopped illumination are shown in Fig. 6b, it can be seen that the samples remain excellent stability and good optical-response property under chopped illumination. CdS/Fe2O3/TiO2 NR sample maintains a photocurrent density of about 0.6 mA cm− 2, which is in accordance with the LSV curves.
EIS measurement is performed under illumination and the Nyquist plots are shown in Fig. 7a and Additional file 5: Figure S4. They demonstrate that the Nyquist plots have two semicircles with a contact series resistance (R s ) on the FTO substrate. The small semicircle in the Nyquist plots is attributed to the charge transport resistance at the electrode/electrolyte interface, and the large semicircle represents the charge transfer resistance related to the electron transport/recombination within the photoanode materials. The sheet resistance (R s ) of the substrate, the charge transfer resistance of the counterelectrode (R ct1), and the charge transfer resistance (R ct2) were simulated by the Zview software and the corresponding data are shown in Additional file 6: Table S2. The fitted R s and R ct1 values for all samples are similar due to the same configuration and growing substrates are applied, while the R ct2 values show obviously variation of 1079.5, 880.6, and 679.5 Ω for TiO2, Fe2O3/TiO2, and CdS/Fe2O3/TiO2, respectively. It can be seen that after modifying TiO2 with Fe2O3 and CdS, the interfacial charge transfer kinetics are greatly enhanced.
The Mott-Schottky plots of the as obtained samples are listed in Fig. 7b. The slopes determined from the Mott-Schottky plots are used to estimate the carrier density according to the following equation [26]:
Nd = \( \frac{2}{e_0{\varepsilon \varepsilon}_0}\times \left[\frac{dV}{d\left(1,/,{C}^2\right)}\right] \)
where e 0 is the electronic charge, ε is the dielectric constant of the sample, ε 0 is the permittivity of the vacuum, Nd is the donor density, and V is the applied voltage. In general, relatively smaller the slope represents higher carrier density.
The flat band potential can be estimated by the following equation:
The flat band potential (E fb) is determined by taking the x intercept of a linear fit to the Mott-Schottky plot, 1/C 2, as a function of applied potential (E). Additionally, a remarkable cathodic shift in the flat potential from 0.44 V for TiO2 sample to 0.36 V for the CdS/Fe2O3/TiO2 NR sample was observed. This suggests a larger accumulation of electrons in the heterojunction and reflects decreased charge recombination.
It should be noticed that the PEC water oxidation performance of as synthesized CdS/ Fe2O3/TiO2 sample is comparable to some related works. For instance, Sharma et al. reported Fe-TiO2/Zn-Fe2O3 thin films with a performance of 0.262 mA cm− 2 at 0.95 V (vs. SCE) [27], while the FTO/Fe2O3/ZnFe2O4 photoanode achieves a photocurrent density of 0.4 mA cm− 2 [28]. In addition, for the reported Fe2O3/TiO2 nanotube photoanodes, a photocurrent density of 0.5 mA cm− 2 is achieved [29, 30]. Comparing with the related works, it can be seen that obtained CdS/Fe2O3/TiO2 photoanode does obtain outstanding and reliable PEC water splitting performance here.
Conclusions
In conclusion, a facile successive ionic layer adsorption and reaction (SILAR)-hydrothermal method is developed to fabricate CdS-modified Fe2O3/TiO2 NR array for efficient PEC water oxidation. UV-vis study confirms the CdS/Fe2O3/TiO2 NR array displays excellent optical response performance with an obvious broadened light absorption range. Applied as the photoanode for PEC water oxidation, CdS/Fe2O3/TiO2 NR array photoanode exhibits greatly enhanced photocurrent density of 0.62 mA cm− 2 (1.23 V vs. RHE) in alkaline electrolyte compared with pristine TiO2 (0.32 mA cm− 2 at 1.23 V vs. RHE).
References
Fujishima A, Honda K (1972) Electrochemical photolysis of water at a semiconductor electrode Nature 238:37-38
Khan SU, Al-Shahry M, Ingler WB (2002) Efficient photochemical water splitting by a chemically modified n-TiO2 Science 297:2243-224
Tang R, Yin L (2015) Enhanced photovoltaic performance of dye-sensitized solar cells based on Sr-doped TiO2/SrTiO3 nanorod array heterostructures J Mater Chem A 3:17417-17425
Tang R, Yin R, Zhou S, Ge T, Yuan Z, Zhang L, Yin L (2017) Layered MoS2 coupled MOF-derived dual-phase TiO2 for enhanced photoelectrochemical performance J Mater Chem A 5:4962-4971
Resasco J, Zhang H, Kornienko N, Becknell N, Lee H, Guo J, Briseno AL, Yang P (2016) TiO2/BiVO4 nanowire heterostructure photoanodes based on type II band alignment ACS Cent Sci 2:80-88
Reichert R, Jusys Z, Behm R (2015) Au/TiO2 Photo (electro) catalysis: The Role of the Au Cocatalyst in Photoelectrochemical Water Splitting and Photocatalytic H2 Evolution J Phys Chem C 119:24750-24759
Das RK, Kar JP, Mohapatra S (2016) Enhanced Photodegradation of Organic Pollutants by Carbon Quantum Dot (CQD) Deposited Fe3O4@mTiO2 Nano-Pom-Pom Balls Ind Eng Chem Res 55:5902-5910
Yang W, Yu Y, Starr MB, Yin X, Li Z, Kvit A, Wang S, Zhao P, Wang X (2015) Ferroelectric polarization-enhanced photoelectrochemical water splitting in TiO2-BaTiO3 core-shell nanowirephotoanodes Nano Lett 15:7574-7580
Huang B, Yang W, Wen Y, Shan B, Chen R (2014) Co3O4-modified TiO2 nanotube arrays via atomic layer deposition for improved visible-light photoelectrochemical performance ACS Appl Mater Interfaces 7:422-431
Hoang S, Guo S, Hahn NT, Bard AJ, Mullins CB (2011) Visible light driven photoelectrochemical water oxidation on nitrogen-modified TiO2 nanowires Nano Lett 12:26-32
Liu Q, Lu H, Shi Z, Wu F, Guo J, Deng K, Li L (2014) 2D ZnIn2S4 nanosheet/1D TiO2 nanorod heterostructure arrays for improved photoelectrochemical water splitting ACS Appl Mater Interfaces 6:17200-17207
Peerakiatkhajohn P, Yun JH, Chen H, Lyu M, Butburee T, Wang L (2016) Stable hematite nanosheet photoanodes for enhanced photoelectrochemical water splitting Adv Mater 28:6405-6410
Quynh LT, Van CN, Bitla Y, Chen J-W, Do TH, Tzeng W-Y, Liao S-C, Tsai K-A, Chen Y-C, Wu C-L, Lai C-H, Luo C-W, Hsu Y-J, Chu Y-H (2016) Self-Assembled BiFeO3-ε-Fe2O3 Vertical Heteroepitaxy for Visible Light Photoelectrochemistry Adv Energy Mater 6:1600686
Zhou S, Yin L (2017) CdS quantum dots sensitized mesoporous BiVO4 heterostructures for solar cells with enhanced photo-electrical conversion efficiency J Alloys Compd 691:040-1048
Bai Z, Yan X, Li Y, Kang Z, Cao S, Zhang Y (2016) 3D-Branched ZnO/CdS Nanowire Arrays for Solar Water Splitting and the Service Safety Research Adv Energy Mater 6:1501459
Jin-nouchi Y, Hattori T, Sumida Y, Fujishima M, Tada H (2010) PbS Quantum Dot-Sensitized Photoelectrochemical Cell for Hydrogen Production from Water under Illumination of Simulated Sunlight ChemPhysChem 11:3592–3595
Zhan Q, Qian J, Li X, He S (2009) A study of mesoporous silica-encapsulated gold nanorods as enhanced light scattering probes for cancer cell imaging Nanotechnol 21:055704
Feng X, Shankar K, Varghese OK, Paulose M, Latempa TJ, Grimes CA (2008) Verticallyaligned single crystal TiO2 nanowire arrays grown directly on transparent conducting oxide coated glass: synthesis details and applications Nano Lett 8:3781–3786
Cho IS, Chen Z, Forman AJ, Kim DR, Rao PM, Jaramillo TF, Zheng X (2011) Branched TiO2 nanorods for photoelectrochemical hydrogen production Nano Lett 11:4978–4984
Bai S, Wang L, Chen X, Du J, Xiong Y (2015) Chemically exfoliated metallic MoS2 nanosheets: A promising supporting co-catalyst for enhancing the photocatalytic performance of TiO2 nanocrystals Nano Res 8:175–183
Xia H, Xiong W, Lim CK, Yao Q, Wang Y, Xie J (2014) Hierarchical TiO2-B nanowire@α-Fe2O3 nanothorn core-branch arrays as superior electrodes for lithium-ion microbatteries Nano Res 7:1797–1808
Cao S, Yan X, Kang Z, Liang Q, Liao X, Zhang Y (2016) Band alignment engineering for improved performance and stability of ZnFe2O4 modified CdS/ZnO nanostructured photoanode for PEC water splitting Nano Energy 24:25–31
Yang P, Murase N (2010) Preparation-Condition Dependence of Hybrid SiO2-Coated CdTe Nanocrystals with Intense and Tunable Photoluminescence Adv Funct Mater 20:1258–1265
Mahadik MA, Subramanian A, Ryu J, Cho M, Jang JS (2017) A hydrothermally grown CdS nanograin-sensitized 1D Zr: α-Fe2O3/FTO photoanode for efficient solar-light-driven photoelectrochemical performance Dalton Trans 46:2377–2386
Zhang X, Xie Y, Chen H, Guo J, Meng A, Li C (2014) One-dimensional mesoporous Fe2O3@TiO2 core-shell nanocomposites: Rational design, synthesis and application as high-performance photocatalyst in visible and UV light region Appl Surf Sci 317:43–48
Kim JY, Magesh G, Youn DH, Jang J-W, Kubota J, Domen K, Lee JS (2013) Single-crystalline,wormlike hematite photoanodes for efficient solar water splitting Sci Rep 3:2681
Sharma P, Kumar P, Solanki A, Shrivastav R, Dass S, Satsangi VR (2012) Photoelectrochemical performance of bilayered Fe-TiO2/Zn-Fe2O3 thin films for solar generation of hydrogen J Solid State Electrochem 16:1305–1312
McDonald KJ, Choi K-S (2011) Synthesis and photoelectrochemical properties of Fe2O3/ZnFe2O4 composite photoanodes for use in solar water oxidation Chem Mater 23:4863–4869
Kuang S, Yang L, Luo S, Cai Q (2009) Fabrication, characterization and photoelectrochemical properties of Fe2O3 modified TiO2 nanotube arrays Appl Surf Sci 255:7385–7388
Han H, Riboni F, Karlicky F, Kment S, Goswami A, Sudhagar P, Yoo J, Wang L, Tomanec O, Petr M, Haderka O, Terashima C, Fujishima A, Schmuki P (2017) Nano 9:134–142
Acknowledgements
The authors acknowledge support from the project supported by the Sate Key Program of National Natural Science of China (grant no. 51532005), the National Nature Science Foundation of China (grant nos. 51472148 and 51272137), and the Tai Shan Scholar Foundation of Shandong Province.
Funding
This study received funding from the Sate Key Program of National Natural Science of China (grant no. 51532005), National Nature Science Foundation of China (grant nos. 51472148 and 51272137), and Tai Shan Scholar Foundation of Shandong Province.
Author information
Authors and Affiliations
Contributions
LWY and RT designed and supervised this work. RYY and MYL performed the simulation and wrote the manuscript. All authors read and approved the final manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Additional Files
Additional file 1: Figure S1.
Cross-sectional SEM image of CdS/Fe2O3/TiO2 NR. (JPEG 742 kb)
Additional file 2: Figure S2.
The cross-view EDS mapping images of CdS/Fe2O3/TiO2 NR in Fig. S1. (JPEG 585 kb)
Additional file 3: Figure S3.
The picosecond-resolved fluorescence transients of TiO2, Fe2O3/TiO2 and CdS/Fe2O3/TiO2 samples. (JPEG 1602 kb)
Additional file 4: Table S1.
Dynamics of picosecond-resolved fluorescence transients of TiO2, Fe2O3/TiO2 and CdS/Fe2O3/TiO2 samples. (DOCX 11 kb)
Additional file 5: Figure S4.
The amplified Nyquist plot of the obtained TiO2, Fe2O3/TiO2 and CdS/Fe2O3/TiO2 photoanodes. (JPEG 933 kb)
Additional file 6: Table S2.
Series resistance of the obtained TiO2, Fe2O3/TiO2 and CdS/Fe2O3/TiO2 photoanodes. (DOCX 13 kb)
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Yin, R., Liu, M., Tang, R. et al. CdS Nanoparticle-Modified α-Fe2O3/TiO2 Nanorod Array Photoanode for Efficient Photoelectrochemical Water Oxidation. Nanoscale Res Lett 12, 520 (2017). https://doi.org/10.1186/s11671-017-2278-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-017-2278-3