Abstract
Cobalt oxide (Co3O4) was homogeneously coated on multiwalled carbon nanotube through a simple chemical deposition method and employed in supercapacitor electrodes. SEM image indicated the uniform distribution of Co3O4 nanoparticles on the surface of the multiwalled carbon nanotube. A maximum specific capacitance of 273 Fg−1 was obtained at the charge–discharge current density of 0.5 Ag−1. After 500 cycles of continuous charge–discharge process, about 88% of the initial capacity could be retained.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Background
Electrochemical capacitors (ECs) are causing great concern due to their long cycle life and safety tolerance to high-rate charge and discharge [1]. The electrochemical capacitors have higher power density than secondary batteries and higher energy density than conventional capacitors. With the development of nanoscience and technology, nanoscaled cobalt oxide (Co3O4) has received great attention for its use in diverse applications such as catalysis, energy storage devices, and electrochemical sensors due to its peculiar properties and controllable morphology compared with the bulk phase [2-4]. In particular, extensive efforts have been devoted to utilize Co3O4 for supercapacitors because of its high reversibility and theoretical specific capacitance (3560 Fg−1) [5,6]. Recently, cobalt oxide has been proven to be a potential alternate to expensive RuO2 which is broadly used as the electrochemically active material in electrochemical capacitors [7-12].
It is well known that Co3O4 is an important p-type semiconductor. Co3O4 has been used in lithium-ion batteries, heterogeneous catalysis, electrochemical capacitor devices, and other applications. For this purpose, Co3O4 has been synthesized using a variety of methods such as sol–gel, reflux, microwave, and hydrothermal methods [13-16]. Furthermore, much work has been done on the controlled synthesis of nanostructure Co3O4 and Co3O4 cubes, rods, wires, tubes, and sheets [17-21]. Although electrochemical capacitors based on Co3O4 have shown excellent electrochemical capacity, its practical application in supercapacitors is still limited in part due to its poor electrical conductivity. In order to improve the electrical conductivity, one of the most common ways is to mix the Co3O4 with conductive additives. Introduction of carbon-based composites may be a promising way to improve the electrical conductivity of Co3O4. Carbonaceous materials, such as activated carbon, carbon nanotubes (CNTs), and grapheme nanosheets (GNs), can provide matrices for structural stability and fine electron transfer property due to their excellent mechanical flexibility and high electrical conductivity [22-24]. Fu et al. [25] synthesized spherical cobalt oxide nanoparticles along CNTs in supercritical fluid (containing ethanol and CO2) and studied their electrical transport properties as a Schottky-junction diode. Huang et al. and Tang et al. obtained hybrid MnO2/carbon nanotube through facile redox and hydrothermal methods, respectively, which both showed high-rate capacitility and fine stability [26,27]. Wang synthesized Co3O4@MWCNT composites through a hydrothermal procedure. This hybrid showed superior electrochemical performance as a cathode material in aqueous supercapacitors, which gave 590 Fg−1 at 15 Ag−1 in 0.5 M KOH aqueous solution [28]. Su et al. [29] electrodeposited Co3O4 and NiO on the carbon nanotube and obtained a high capacitance of 52.6 mF cm−2.
In this work, we describe a general method to synthesize Co3O4/MWCNTs through a simple chemical deposition method. Co3O4 nanoparticles can be evenly and tightly attached on the surface of multiwalled carbon nanotubes (MWCNTs), through a long time of constant temperature heating. The obtained samples showed high specific capacitance (273 Fg−1 at a current density of 0.5 Ag−1) though just few Co3O4 was deposited on the MWCNTs. This method could significantly decrease the consumption of rare cobalt element.
Methods
Materials preparation
MWCNTs (purity, >95%; diameter, 40 to 60 nm; specific surface area, 200 m2g−1) were purchased from Chengdu Organic Chemicals Co. Ltd., Chengdu, China. All of the other chemicals were of analytical grade and were used as purchased without further purification. Firstly, MWCNTs were acid-treated with concentrated nitric at 140°C for 10 h. The treated MWCNTs were rinsed with distilled water until the PH was 7 and dried at 60°C for 24 h. It is well known that the surface of MWCNTs possesses a great deal of functional carboxyl groups and becomes negatively charged after functioned with nitric acid [30]. This extraordinary change of the tubular structure for MWCNTs was familiar to be coated with inorganic nanomaterials. Secondly, 80 mg of acid-treated MWCNTs was dispersed into 50 ml ethanol by stirring and ultrasonic treatment, then 2.5 ml of 0.5 M Co(OAC)2 aqueous solution was added to the above solution in a state of agitation, followed by the addition of 1 ml of NH4OH (30% solution) and 1.4 ml of distilled water an hour later. Thirdly, the reaction was kept at 80°C with stirring for 10 h. After that, the reaction mixture was transferred and sealed in a 100-ml Teflon-lined stainless steel autoclave for a hydrothermal reaction at 150°C for 3 h. After cooling to room temperature, the product was collected by centrifugation and rinsed with deionized water and absolute ethyl alcohol in sequence several times until pH was equal to 7, then dried at 80°C for 12 h. The content of Co3O4 on the surface of MWCNTs was controlled through the regulation of the Co(OAC)2 content. The Co(OAC)2 contents were controlled to be 0.125, 0.25, 0.5, and 1 mmol. The prepared samples were denoted as Co3O4-0.125/MWCNTs, Co3O4-0.25/MWCNTs, Co3O4-0.5/MWCNTs, and Co3O4-1/MWCNTs, accordingly. Pure Co3O4 sample was also prepared through the same preparation process as the Co3O4/MWCNTs samples.
Structural characterization and electrochemical measurements
The morphology and structure of the samples were characterized by JSM-7001 F field emission scanning electron microscope (FESEM) and DX-2700 X-ray diffractometer (XRD) with a monochromatized Cu K irradiation (k = 0.154145 nm), respectively. The composition was characterized by the thermogravimetric (TG) analysis method through Netzsch-STA 449C, from 25°C to 900°C at a heating rate of 10°C min−1 in air.
The electrochemical measurements were carried out using a three-electrode system with a 6 M KOH electrolyte in which platinum foils and a saturated calomel electrode (SCE) were used as the counter and reference electrodes, respectively. The working electrodes were fabricated by mixing the as-prepared composite, acetylene black, and polytetrafluoroethylene (1% wt.) with a mass ratio of 85:10:5. N-methyl pyrrolidinone (NMP) was also added to form slurry for the spreading on nickel sheets (1.0 cm × 1.0 cm). The working electrodes were pressed at 10 MPa and dried under vacuum at 60°C for 24 h [31]. Cyclic voltammetry (CV) measurement was performed with a CHI660B (Chen Hua Co., Shanghai, China) workstation. The scan rates of CV were in the range from 5 to 100 mVs−1. Electrochemical impedance spectroscopy (EIS) measurement was performed with the electrochemistry workstation IM6 (Zahner Co., Kronach, Germany).
Results and discussion
XRD patterns of the Co3O4/MWCNT samples obtained with different cobalt contents are shown in Figure 1. The diffraction peak of the (002) plane for the pure MWCNT sample is sharp. But this peak is gradually weakened with the increasing of Co(OAC)2 content, which indicated that the content of Co3O4 increases accordingly. When the added Co(OAC)2 content was 0.25 mmol, new diffraction peaks appeared. These diffraction peaks appeared at 18.9, 31.3, 36.8, 44.9, 59.4, and 65.4°. These peaks belong to the characteristic peaks of spinel Co3O4, which could be indexed with a JCPDS card (No.43-1003). These diffraction peaks were corresponded to the reflection planes (111), (220), (311), (400), (511), and (440), respectively. These peaks were all in accordance with the pure Co3O4 nanomaterial, except the peak at 2θ = 26°, which is corresponding to the (002) reflection of the MWCNTs. This indicated that the coated Co3O4 on the surface of MWCNTs has the same crystal phase with the pure Co3O4 nanoparticles.
To quantify the amount of Co3O4 in the composites, TG analysis was carried out in air. The sample was heated from 25°C to 900°C at a rate of 10°C min−1. Figure 2 gives the TG curves for the Co3O4/MWCNT hybrid and the pure MWCNT powder. It can be seen that the bare MWCNTs are burned off at around 650°C. On the contrary, the Co3O4-0.5/MWCNT hybrid began to lose the weight significantly at around 400°C due to the catalysis of the Co3O4 sheath. According to the TG curves, the content of Co3O4 can be estimated to be about 35% (wt.%) for the Co3O4-0.5/MWCNTs. The Co3O4 content of other Co3O4/MWCNT samples were also decided to be about 13%, 24%, and 43% (wt.%) for the Co3O4-0.125/MWCNTs, Co3O4-0.25/MWCNTs, and Co3O4-1/MWCNTs, respectively. It can be seen that the content of Co3O4 could be handily controlled through this preparation method.
To investigate the surface morphology of Co3O4/MWCNT composites, SEM measurement was employed. Figure 3 shows the morphologies of the pure MWCNTs (Figure 3a), pure Co3O4 (Figure 3b), and Co3O4-0.5/MWCNTs (Figure 3c,d). From Figure 3b, we can see that the as-prepared Co3O4 particle is small and homogeneous. But the small particles agglomerate with each other to form large powders, which is inconvenient for contact with the electrolyte during the charging and discharging process. It can be seen from Figure 3a that the pure MWCNTs are smooth and flexible, forming strong intertwined entanglements with a three-dimensional (3-D) network structure. Compared with the pure MWCNTs, the surface of Co3O4-particle-coated MWCNTs (Co3O4-0.5/MWCNTs) became unsmooth with well-distributed small particles. The particle size is in the range of 5 to 10 nm. The most important thing is that there are no unabsorbed Co3O4 particles in the samples. It can be seen that the adopted preparation method is a practical way to coat inorganic nanoparticles on MWCNTs. The MWCNTs could provide a conductive frame network for the Co3O4 electrode for electrochemical capacity. On the other hand, coated Co3O4 could improve the specific capacity of MWCNT electrode. The SEM spectra of other samples, such as Co3O4-0.125/MWCNTs, Co3O4-0.25/MWCNTs, and Co3O4-1/MWCNTs, are given in the supporting information. It can be seen that the Co3O4 particles keep increasing with the addition of Co(OAC)2 (Additional file 1: Figure S1).
In order to evaluate the supercapacitor performance of the electrodes, electrochemical studies were performed using cyclic voltammetry in 6 M KOH aqueous electrolyte. Figure 4a illustrates the CV curves of pure MWCNT electrode at different scan rates in the voltage range of −1 to 0 V. The pure MWCNT electrode has deviated from idealized double layer because of the redox reactions of the functional groups on the surface. The paragraph shows high symmetry between the negative curves and the positive ones, so the MWCNT electrode behaves as a pseudocapacitor. With the increase of the sweep rate, the CV curves have no obvious distortion, indicating a highly reversible system.
Figure 4b shows the cyclic voltammograms of Co3O4/MWCNT composites with different Co3O4 contents at a scan rate of 50 mV/s between −0.4 and 0.35 V in the 6 M KOH aqueous electrolyte. Compared with the bare MWCNT electrodes, the shapes of the cyclic voltammogram curves in all of the cases are not close to rectangular. The non-rectangular form of the cyclic voltammogram is due to the role of the introduction of Co3O4 particles which provide higher pseudocapacitive capacity. It is well known that the capacitive behavior of Co3O4 results from the following redox reactions [32]:
Compared with the pure MWCNT electrode, the Co3O4-coated MWCNT electrodes show significant higher current density in the CV curves. When the content of added Co(OAC)2 was 0.5 M, the obtained samples (Co3O4-0.5/MWCNTs) give the highest current density which indicated that the Co3O4-0.5/MWCNT electrode has the highest specific capacitance. When the content of added Co(OAC)2 solution was increased to 1 mmol (Co3O4-1/MWCNTs), the current density decreased abruptly.
The charge–discharge properties of the electrodes were also tested in 6 M KOH aqueous electrolyte. The charge–discharge curves of pure MWCNT, pure Co3O4, and Co3O4/MWCNT composite electrodes are all shown in Figure 5. The charge–discharge current density is 0.5 Ag−1. Figure 5a shows the charge–discharge curve of pure MWCNT electrode within a potential window of −1 to 0 V. The shape of the curve is closely linear and shows a typical triangle symmetrical distribution indicating a good double layer capacitive property. Figure 5b shows the charge–discharge curve of the pure Co3O4 electrode within a potential window of −0.4 to 0.35 V. It can be seen that the curve has significant bend which indicates a pseudocapacitive capacity for the electrodes. Figure 5c shows the charge–discharge of the Co3O4/MWCNT composites with different cobalt content in the potential range of −0.4 to 0.35 V. The shape of the charge–discharge curves is similar with that of the pure Co3O4 electrode. The average specific capacitances for the electrodes can be calculated on the basis of Equation 3:
where C is the specific capacitance (Fg−1), i (A) is the discharge current, △V (V) is the potential window during the discharge process, △t (s) is the discharge time, and m (g) is the mass of electroactive material [33]. The average specific capacitances for the pure MWCNT, pure Co3O4, Co3O4-0.125/MWCNT, Co3O4-0.25/MWCNT, Co3O4-0.5/MWCNT, and Co3O4-1/MWCNT composite electrodes, which were obtained from charge–discharge curves on the basis of Equation 3, were calculated to be about 33, 150, 103, 137, 273, and 118 Fg−1, respectively. The results are identical to that estimated from the cyclic voltammogram curves. This result indicates that it is valuable to combine the high electric conduction of MWCNTs with the large specific capacity of Co3O4. Meanwhile, the content of the coated Co3O4 should be appropriate.
Figure 5d displays the charge–discharge curves of the Co3O4-0.5/MWCNT composite at various current densities in the range of 0.5 to 1.5 Ag−1. The specific capacitances were calculated to be about 273, 160, 134, 88, and 69 Fg−1, respectively. It can be seen that the specific capacitances gradually decreases with the increasing of the discharging current density. This phenomenon might be due to the diffusion limits of the OH− ion movement.
The electrochemical performance of the electrode was further investigated by the EIS measurements. Figure 6 shows the Nyquist plots of the EIS spectra of pure Co3O4 electrode and Co3O4-0.5/MWCNT electrode, in the frequency range of 1 Hz to 100 KHz. The obtained EIS spectra are composed of a half semicircle at high frequency and a line at low frequency. The small arc observed at the high frequency is related to the process at the electrode material electrolyte interface (R ct), and the line at the low frequency indicates a capacitive behavior related to the charging mechanism. High-frequency intercepts of the real axis gives the serial resistance (R s) for the working electrode. It can be seen that the Co3O4-0.5/MWCNT has smaller R ct and R s, indicating a lower electrochemical reaction resistance and electron transfer resistance. Furthermore, the straight line of the Co3O4-0.5/MWCNT spectra is more close to 90° compared with the pure Co3O4 spectra which shows that the Co3O4-0.5/MWCNTs possess a more ideal capacitive behavior.
Figure 7 shows the cycle life of the pure Co3O4 and Co3O4-0.5/MWCNT electrodes at 0.5 Ag−1. It is clearly seen that the specific capacitance of the Co3O4-0.5/MWCNT electrode is much higher than that of pure Co3O4 under the same current density. The two electrodes show similar charge–discharge performance in the first 500 cycle times. The process of charging and discharging are both relatively stable. After 500 times charge–discharge, the specific capacity of Co3O4-0.5/MWCNT electrodes remains to be about 219 Fg−1 which is about 88% of the first discharge capacity.
Conclusions
Co3O4 was homogeneously coated on a multiwalled carbon nanotube through a simple chemical deposition method. The contents of Co3O4 on the surface of MWCNTs were handily controlled through the regulation of the Co(OAC)2 content. Furthermore, the Co3O4 nanoparticles were homogeneously distributed on the surface of multiwalled carbon nanotubes. The coating of Co3O4 could significantly increase the specific capacity of MWCNTs. The optimized samples were obtained when the Co(OAC)2 content was 0.5 mmol. The maximum specific capacitance of 273 Fg−1 was obtained at the charge–discharge current density of 0.5 Ag−1. After 500 cycles of charge–discharge process, about 88% of the initial capacity could be retained.
References
Simon P, Gogotsi Y. Materials for electrochemical capacitors. Nature. 2008;7:845.
Yang G, Gao D, Zhang J, Zhang J, Zhu Z, Xue D. Synthesis and characterization of shape-controlled mesoporous Co3O4 hierarchical nanostructures. RSC Adv. 2013;3:508.
Battumur T, Ambade SB, Ambade RB, Pokharel P, Lee DS, Han SH, et al. Addition of multiwalled carbon nanotube and graphene nanosheet in cobalt oxide film for enhancement of capacitance in electrochemical capacitors. Current Appl Phys. 2013;13:196.
Wang K, Shi ZQ, Wang YY, Ye ZG, Xia HY, Liu GW, et al. Co3O4 nanowires@MnO2 nanolayer or nanoflakes core–shell arrays for high-performance supercapacitors: the influence of morphology on performance. J Alloys Compd. 2015;624:85.
Yuan C, Yang L, Shen L, Zhang X, Lou XW. Growth of ultrathin mesoporous Co3O4 nanosheet arrays on Ni foam for high-performance electrochemical capacitors. Energy Environ Sci. 2012;5:7883.
Cheng H, Lu ZG, Deng JQ, Chung CY, Zhang K, Li YY. A facile method to improve the high rate capability of Co3O4 nanowire array electrodes. Nano Res. 2010;3:895.
Wei TY, Chen CH, Chang KH, Lu SY, Hu CC. Cobalt oxide aerogels of ideal supercapacitive properties prepared with an epoxide synthetic route. Chem Mater. 2009;21:3228.
Hu CC, Chang KH, Lin MC, Wu YT. Design and Tailoring of the Nanotubular Arrayed Architecture of Hydrous RuO2 for Next Generation Supercapacitors. Nano Lett. 2006;6:2690.
Kandalkar SG, Lokhande CD, Mane RS, Han SH. A non-thermal chemical synthesis of hydrophilic and amorphous cobalt oxide films for supercapacitor application. Appl Surf Sci. 2007;253:3952.
Yuan AB, Zhang QL. A novel hybrid manganese dioxide/activated carbon supercapacitor using lithium hydroxide electrolyte. Electrochem Commun. 2006;8:1173.
Pang H, Gao F, Chen Q, Liu RM, Lu QY. Dendrite-like Co3O4 nanostructure and its applications in sensors, supercapacitors and catalysis. Dalton Trans. 2012;41:5862.
Xiong SL, Yan CZ, Zhang XG, Xi BJ, Qian YY. Controllable synthesis of mesoporous Co3O4 nanostructures with tunable morphology for application in supercapacitors. Chem Eur J. 2009;15:5320.
Santos GA, Santos CMB, Silva SWD, Urquieta-Gonzalez EA, Sartoratto PPC. Sol–gel synthesis of silica–cobalt composites by employing Co3O4 colloidal dispersions. Colloids Surf A Physicochem Eng Aspects. 2012;395:217.
Meher SK, Rao GR. Effect of microwave on the nanowire morphology, optical, magnetic, and pseudocapacitance behavior of Co3O4. J Phys Chem C. 2011;115:25543.
Bilecka I, Djerdj I, Niederberger M. One-minute synthesis of crystalline binary and ternary metal oxidenanoparticles. Chem Commun. 2008;886.
Meher SK, Rao GR. Ultralayered Co3O4 for high-performance supercapacitor applications. J Phys C. 2011;115:15646.
He T, Chen DR, Jiao XL, Wang YL, Duan YZ. Solubility-controlled synthesis of high-quality Co3O4 nanocrystals. Chem Mater. 2005;17:4023.
Liu Y, Wang G, Xu C, Wang W. Fabrication of Co3O4 nanorods by calcination of precursor powders prepared in a novel inverse microemulsion. Chem. Commun. 2002;1486.
Li Y, Tan B, Wu Y. Mesoporous Co3O4 nanowire arrays for lithium ion batteries with high capacity and rate capability. Nano Lett. 2008;8:265.
Lou XW, Deng D, Lee JY, Feng J, Archer LA. Self-supported formation of needlelike Co3O4 nanotubes and their application as lithium-ion battery electrodes. Adv Mater. 2008;20:258.
Cao AM, Hu JS, Liang HP, Song WG, Wan LJ, He XL, et al. Hierarchically structured cobalt oxide (Co3O4): the morphology control and its potential in sensors. J Phys Chem B. 2006;110:15858.
Yang XL, Fan KC, Zhu YH, Shen JH, Jiang X, Zhao P, et al. Tailored graphene-encapsulated mesoporous Co3O4 composite microspheres for high-performance lithium ion batteries. J Mater Chem. 2012;22:17278.
Lang JW, Yan XB, Xue QJ. Facile preparation and electrochemical characterization of cobalt oxide/multi-walled carbon nanotube composites for supercapacitors. J Power Sourc. 2011;196:7841.
Su L, Jing Y, Zhou Z. Li ion battery materials with core–shell nanostructures. Nanoscale. 2011;3:3967.
Fu L, Liu Z, Han B, Han P, Hu P, Cao L, et al. Beaded cobalt oxide nanoparticles along carbon nanotubes: towards more highly integrated electronic devices. Adv Mater. 2005;17:217.
Tang W, Hou YY, Wang XJ, Bai Y, Zhu YS, Sun H, et al. Beaded cobalt oxide nanoparticles along carbon nanotubes: towards more highly integrated electronic devices. J Power Sourc. 2012;197:330.
Huang HJ, Zhang WY, Fu YS. Controlled growth of nanostructured MnO2 on carbon nanotubes for high-performance electrochemical capacitors. Electrochim Acta. 2015;152:480.
Wang XW, Li MX, Chang Z, Yang YQ. Co3O4@MWCNT nanocable as cathode with superior electrochemical performance for supercapacitors. ACS Appl Interf. 2015;7:2280.
Su F, Lv X, Miao M. High-performance two-ply yarn supercapacitors based on carbon nanotube yarns dotted with Co3O4 and NiO nanoparticles. Small. 2015;11:854.
Nethravathi C, Rajamathi M. Chemically modified graphene sheets produced by the solvothermal reduction of colloidal dispersions of graphite oxide. Carbon. 2008;46:1994.
Sahoo S, Karthikeyan G, Nayak GC, Das CK. Electrochemical characterization of in situ polypyrrole coated graphene nanocomposites. Synth Met. 2011;161:1713.
Liao MX, Liu YF, Hu ZH, Yu Q. Novel morphologic Co3O4 of flower-like hierarchical microspheres as electrode material for electrochemical capacitors. J Alloys Compd. 2013;562:106.
Devaraj S, Munichandraiah N. High capacitance of electrodeposited MnO2 by the effect of a surface-active agent. Electrochem Solid State Lett. 2005;8:A373.
Acknowledgements
This work was supported by the Natural Science Foundation of China (No.51304062, 21403056, and U1404202), the Program for Innovative Research Team in Science and Technology in University of Henan Province (IRTSTHN) (Grant No.2012IRTSTHN004), and the Basic and Frontier Technology Research Programs of the Department of Science & Technology of Henan Province (No. 122300410107). Research Plan for Natural Science in the Education Department of Henan Province (No. 13B150920).
Author information
Authors and Affiliations
Corresponding authors
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors’ contributions
LT carried out the sample synthesis and data analysis and wrote the manuscript. LSJ designed the experiments, analyzed the data, and modified the manuscript. ZBW contributed to the data analysis and manuscript-revising work. WB, NDY, CZ, YY, and WN provided helpful discussion of the experiment. ZWF modified the manuscript. All authors read and approved the final manuscript.
Additional file
Additional file 1:
SEM images. It can be seen that the Co3O4 particles keep increasing with the addition of Co(OAC)2.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.
The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
To view a copy of this licence, visit https://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Tao, L., Shengjun, L., Bowen, Z. et al. Supercapacitor electrode with a homogeneously Co3O4-coated multiwalled carbon nanotube for a high capacitance. Nanoscale Res Lett 10, 208 (2015). https://doi.org/10.1186/s11671-015-0915-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-015-0915-2