Abstract
A real-time humidity sensor based on a microwave resonator coupled with a poly(3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS) conducting polymer (CP) film is proposed in this paper. The resonator is patterned on a printed circuit board and is excited by electromagnetic field coupling. To enhance the sensitivity of the sensor, the CP film is located in the area with the strongest electric field in the resonator. To investigate the performance, the proposed sensor is placed alongside a reference sensor in a humidity chamber, and humidity is injected at room temperature. The experimental results indicate that the electrical properties of the resonator with the CP film, such as the transmission coefficient (S 21) and resonance frequency, change with the relative humidity (RH). Specifically, as the RH changes from 5% to 80%, S 21 and the resonance frequency change simultaneously. Moreover, the proposed sensor exhibits great repeatability in the middle of the sensing range, which is from 40% to 60% RH. Consequently, our resonator coupled with the CP film can be used as a real-time humidity-sensing device in the microwave range, where various radio-frequency devices are in use.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Humidity sensors have recently been receiving considerable attention due to their usefulness in various fields, such as agriculture, manufacturing, environmental sciences, medicine1,2, and so on. These humidity sensors should possess good performance characteristics, such as high accuracy, good repeatability, wide sensing range, fast response time, easy fabrication process, and low production cost. To satisfy these requirements, various sensing mechanisms and materials have been studied. The sensing mechanisms are classified based on the components used for the measurement. The first class includes optical fibre sensors3,4,5, which measure the reflectivity by adding a sensing layer to the end of an optical fibre. The second class includes sensors based on nanowires6 and bulk acoustic wave resonators7, which coat the sensing layers on the components and measure the resonance frequencies at very low frequencies. The third class measures the impedance change by depositing the sensing layer on interdigitated electrode (IDT)8,9. The fourth class measures the capacitance change of a dielectric membrane by filling the disk witg the sensing material10,11. The final class includes chemically sensitive field-effect transistor (ChemFET)12,13 sensors, which substitute the gate region of the transistor with the sensing material and measure the drain current. Various sensing materials such as carbon nanotubes14,15, crystals16, graphene17,18,19, ceramics20,21, silicon22, organic polymers23,24, and composite materials25,26, have been studied. However, despite these studies, more investigations are required to achieve high sensitivity, real-time sensing, easy fabrication, and great repeatability characteristics.
Among the sensing materials, poly(3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS) has been receiving considerable attention for use in sensors because of its outstanding properties, such as high conductivity, good processability, low price, low redox potential, and ability to operate at room temperature27,28,29. Most previous studies that used PEDOT:PSS as an analyte focused on FETs30,31 or electrodes32,33 at the DC level or on a surface acoustic wave (SAW) filter34 at low frequencies. However, these methods could measure only one parameter, such as the current, resistance, or resonance frequency, to deduce the result. In addition, it was difficult to fabricate and enhance the sensitivity of FET and nanowire-based sensors, and it was difficult to integrate SAW filter-based sensors into a single integrated circuit (IC); it was also difficult to miniaturize the sensors.
Meanwhile, microwave resonators can measure two parameters, namely, the transmission coefficient passing through the resonator (S 21) and the resonance frequency, to enhance the detection capacity. Moreover, their sizes can be reduced due to their high operating frequencies, and they can easily be linked with commercial mobile communication systems. Because of these advantages, microwave resonators have been applied in a variety of sensing applications, such as glucose measurement35,36, biomolecular sensing37,38,39, gas sensing40,41, wrist pulse detection42,43,44, vital sign monitoring45,46,47, and breast tumour detection48,49. Additionally, relative humidity detection using microwave components has also been studied50,51. In contrast to previous works, a PEDOT:PSS coupled microwave resonator is proposed in this paper. It is determined that by replacing a part of the conductor, the sensitivity of the sensor can be enhanced and its fabrication becomes easy. Moreover, the proposed sensor can be used in real time (<0.5 s) in cases where the relative humidity (RH) ranges from 5% to 80%, with excellent repeatability. When the RH changes from 5% to 80%, S 21 and the resonance frequency are immediately changed by 0.18 dB and −35.4 MHz,respectively.
Results
Simulation of microwave resonator
In this work, we designed a microwave resonator, namely, a double split-ring resonator (DSRR), that is compatible with a CP film for a real-time humidity sensor. The operating frequency of the resonator was chosen to be 2.45 GHz, which is a specific frequency in the industrial-scientific-medical (ISM) band, for applications in wireless sensing platforms. The resonance frequency of the DSRR is generally determined using the following equation52,53:
where a0 is the distance between the centre of the square and the middle of the inner and outer squares, as indicated in Fig. 1c. L eff , L m , C S1, C S2, and Cg are the effective inductance obtained from a0, the mutual inductance between the two squares, the capacitance between the split of each ring, and the capacitance between the two rings, respectively, as illustrated in Fig. 1a.
To prepare the sample, the proposed sensor was fabricated on a printed circuit board (PCB) substrate, which was 0.762 mm thick with a dielectric constant (ε r ) of 6.15 and loss tangent (tanδ) of 0.0028. After electroplating nickel (Ni) as an adhesion layer, the resonator with a copper pattern was coated with gold to prevent oxidation from humidity and then with a PEDOT:PSS CP film. To deposit the CP film at the specific site and to prevent overflow, a mask layer was added to the substrate, which covered all parts except for the copper line, and to the sensing region. This layer was to form a well structure, as shown in Fig. 1b. The mask layer was composed of photoimageable solder resist ink, which is widely used in the PCB process. Furthermore, to enhance the sensitivity, the sensing region was positioned between the outer electrodes, which is the region with the strongest electric field, as shown in Fig. 1d. This is because the material properties, namely, permittivity and conductivity, are dependent on the electric field, and the electric field effects can sensitively change the resonance frequency and the gain level of the transmission coefficient (S 21). For this reason, when a CP film is exposed to humidity, its permittivity and conductivity change simultaneously. Consequently, the resonator with a CP film can exhibit real-time deviations in frequency and a gain level of S 21. After selecting the sensing region, the CP film was deposited onto two squares with a side of length b and gap size of gi. The dimensions of the other resonator sections are presented in Fig. 1c. Here, the feed line had a characteristic impedance of 50 Ω to avoid an impedance mismatch with the measuring vector network analyser (VNA). The distance between the feed line and the resonator, which controlled the amount of signal coupling to the resonator, was determined to be 0.2 mm. Physically, as this spacing increases, the signal coupling to the resonator decreases as presented in supplementary information Fig. S1.Therefore, keeping this distance short provides an advantage to the sensor. A ground plane was added to both sides of the feed line to reduce the radiation losses, dispersion, and parasitic wave propagation in the resonator.
Validation of the sensor
The proposed RH sensor was fabricated using the well-defined PCB technology, as illustrated in Fig. 2a. To connect the sensor with the VNA, sub-miniature version A (SMA) connectors were mounted on the input and output feed lines. CP film deposition was confirmed using an optical microscope at 300x magnification, as shown in Fig. 2b. Due to the manual deposition of PEDOT:PSS, an imperfect square shape was obtained; specifically, near the gap region, the PEDOT:PSS layer was also detached when the polyimide film was removed. Therefore, the dimensions of the sensing region were deformed and caused ripples in the characteristics of the sensor in the frequency range of 2.55 GHz to 2.95 GHz, as shown in Fig. 2d. Atomic force microscopy (AFM) images of the deposited CP film surface are shown in Fig. 2c. The AFM images show that the PEDOT:PSS is evenly deposited on the substrate and that the average roughness of the PEDOT:PSS is 1.933 nm. Moreover, morphologies of the PEDOT:PSS observed using a the scanning electron microscope (SEM) are shown supplementary information Fig. S2. X-ray photoelectron spectroscopy (XPS) survey spectra of deposited PEDOT:PSS film are presented in supplementary information Fig. S3. A comparison of the frequency responses of the bare resonator and the PEDOT:PSS coupled resonator is presented in Fig. 2d. A simulation was conducted using a three-dimensional full-wave electromagnetic field solver, and measurements were conducted using the VNA. The microwave properties of the circuit modelling PEDOT:PSS used in the simulation are presented in supplementary information S4. After depositing the CP film on the resonator, the resonance frequency was shifted from 2.45 GHz to 2.4 GHz. This is because the film is a conductive material, and the deposition of the film caused an increase in the capacitance (C S1). Thus, the resonance frequency was slightly shifted to a lower frequency region. Figure 2e shows the measured isotherm characteristics of the sensor before and after the introduction of humidity. After the humidity reacted with the PEDOT:PSS CP film and was adsorbed by the film, the magnitudes of both S 21 and the resonance frequency were affected. The gain level of S 21 increased, and the resonance frequency slightly shifted towards a lower frequency.
The sensing response of the sensor was verified in a custom-made acrylic humidity chamber. The experimental setup for the fabricated sensor is illustrated in Fig. 3. A DSRR was placed along with a commercial sensor inside the humidity chamber, and the performance of the sensor was evaluated by comparing with the commercial sensor. The frequency response of the DSRR was measured using a VNA, and the measured data were sent to a computer every 0.5 s. The commercial sensor was connected to a micro-controller board, and the board also sent data to the computer every 0.5 s. The RH inside the chamber was increased by the humidifier and decreased by pure argon (Ar), where the controllable RH range is from 5% to 80%.
To analyse the performance of the proposed humidity sensor quantitatively, the following parameters are defined:
where S 21 is the transmission coefficient at the resonance frequency. S 21,Humidity and F Humidity are the values when the sensor reacts to humidity. S 21, Ref and F Ref are the reference values when humidity is very low (3%). Here, ΔS 21 and ΔF are the differences in the transmission coefficient and resonance frequency, respectively.
The performance of the sensor was tested using two methods. First, the available operating range of the sensor was evaluated. The operating range was verified by venting most of the humidity in the chamber using argon (Ar) and injecting humidity into the dehumidified custom-made chamber at room temperature (RT). The RH was increased using a humidifier for 130 s until it reached 80%. ΔS 21 and ΔF were tracked in the time domain as functions of the RH values. As the RH increased, ΔS 21 increased by 0.18 dB and ΔF decreased by −35.4 MHz, as shown in Fig. 4a. It was found that the changes in S 21 and the resonance frequency exhibited opposite trends with the RH level and that the microwave sensor was suitable for a real-time humidity sensor when the RH was in the range between 5% and 80%.
Next, the repeatability of the sensor was tested by controlling the RH in the middle of sensor’s operating range, which is from 40% to 60%. The test consisted of seven cycles, with each cycle lasting 60 s. In each cycle, half of the cycle was designated for the injection of humidity, while the other half was for ventilation. As the RH changed, ΔS 21 changed from 0.04 dB to 0.1 dB, while ΔF shifted from −7 MHz to −15 MHz, as shown in Fig. 4b. The result showed that the proposed sensor responded to humidity in real time and that it had an outstanding repeatable response.
In addition to the repeatability test, ten samples with separately deposited CP films were prepared for testing, and each sample was measured three times. The statistical distributions of the measured data are shown in the box plot in Fig. 4c and summarized in Table 1. As the RH increased, ΔS 21 and ΔF changed quite rapidly, and the difference between each sample (i.e., the standard deviation) increased because of the PEDOT:PSS saturation54. Nevertheless, it was clearly observed that the proposed microwave sensor could be used to detect RH by measuring the changes in S 21 and those in the resonance frequency. Comparisons with other microwave-based RH sensors are shown in supplementary information Table S1.
Discussion
A chemical reaction between the PEDOT:PSS CP film and humidity can clearly be observed via the microwave electrical properties, S 21 and the resonance frequency. The S 21 is related to the conductivity of the PEDOT:PSS CP film, which is inversely proportional to the square of the ohmic loss. Meanwhile, the resonance frequency is related to the capacitance between the PEDOT:PSS CP films (C S1), which is inversely proportional to the square of the resonance frequency. Moreover, the changes in the conductivity and capacitance are independent, meaning that they can provide twice the amount of information.
The chemical reaction can be verified in two ways. First, the changes in capacitance can be identified by measuring the change in the resonance frequency. This variation is a consequence of the deposited film deformation and the effective permittivity change. As the RH increases, water molecules around the PEDOT:PSS are accumulated and capillary action occurs. This fills the intergrain crevices of PEDOT:PSS with H2O. This process causes swelling of the film, which subsequently increases the film size55. Additionally, the adsorption of H2O increases the effective permittivity because H2O has high permittivity (ε r = 80)56. Because the capacitance is proportional to the areas of the two conductors and the permittivity, an enhancement in the capacitance can be observed. Consequently, the resonance frequency shifts to a lower frequency region, which is consistent with the result in Fig. 4.
Second, the changes in the conductivity can be deduced by measuring S 21. This change is a result of the chemical structure of PEDOT. PEDOT:PSS is a conjugated conducting polymer, which is composed of poly(3,4-ethylenedioxythiophene) (PEDOT) and polystyrene sulfonate (PSS). PEDOT:PSS has a two-chemical conformation with benzoid and quinoid structures, which are two resonance structures of PEDOT. There are two conjugated π electrons on the C α =C β bond in the benzoid structure, and there are no conjugated π electrons on the C α -C β bond in the quinoid structure, as illustrated in Fig. 5. Thus, the quinoid structure has delocalized ions, and these ions make the quinoid structure more conductive than the benzoid structure. Without additives, both benzoid and quinoid structures are present in PEDOT:PSS. However, adding organic compounds with certain chemical conditions transforms the benzoid structure into the quinoid structure. The additives must have two or more polar groups in a molecule, and they must enable the formation of hydrogen bonds with the PSS of PEDOT:PSS57,58. Thus, when PEDOT:PSS reacts with humidity, an enhancement in conductivity can be observed. This increases S 21, which is consistent with the result in Fig. 4.
In summary, a humidity sensor device based on a microwave resonator coupled with a PEDOT:PSS CP film was successfully demonstrated. The performance of the proposed sensor was verified by comparing it with a commercial sensor in two aspects: operating range and repeatability. As the RH changed, both S 21 and the resonance frequency varied faster than 0.5 s. Note that similar results were obtained for different samples. Our results demonstrated that the microwave resonator with a CP film was suitable for humidity monitoring at room temperature in real time.
Methods
Sensing Material Synthesis and Deposition
Poly(3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS) solution (Clevios PH 1000) was purchased from Heraeus. The solid content was 1.1 wt%, and the weight ratio of PEDOT to PSS was 1:2.5. Dimethyl sulfoxide (DMSO, 99%) was purchased from Samchun Pure Chemicals (S. Korea). To enhance the electrical conductivity of the PEDOT:PSS film, the typical DMSO doping procedure was followed. DMSO was added to the aqueous PEDOT:PSS solution (5.0 v/v%) and stirred gently at room temperature. Then, the solution was filtered using a syringe filter (0.45 μm pore-size Nylon membrane).
The PEDOT:PSS films were deposited as follows. First, polyimide tape was attached to the surface of the sensor as a shield to prevent the analyte region from overflowing. Although the substrate was inherently hydrophobic, the surface could be temporarily rendered hydrophilic upon exposure to oxygen plasma for adhesion improvement. Then, the polymer solution was dropped onto the substrate and bar coated to stabilize the roughness.
Equipment
The 2D surface view of the deposited film was observed by AFM (Nanowizard I, JPK instrument). The morphologies of the deposited film were observed by SEM (JSM-7001F, JEOL). The XPS survey spectra of the deposited PEDOT:PSS film were obtained using an XPS (K-alpha, Thermo Scientific). The characteristics of the sensor were measured using a VNA (E5071B, Agilent), which was controlled by LabView (NI) through a general-purpose interface bus (GPIB) cable. A commercial reference sensor (DHT22) was connected to a microcontroller board (Arduino), which interfaced the sensor with a computer. The DHT22 is a capacitive humidity sensor, whose operating range is from 0% to 100% and response time is 2 s. The resolution is 0.1% RH, and the accuracy is ±2 RH.
References
Chen, Z. & Lu, C. Humidity sensors: a review of materials and mechanisms. Sensor Letters 3, 274–295 (2005).
Farahani, H., Wagiran, R. & Hamidon, M. N. Humidity sensors principle, mechanism, and fabrication technologies: a comprehensive review. Sensors 14, 7881–7939 (2014).
Corres, J. M., Matias, I. R., Hernaez, M., Bravo, J. & Arregui, F. J. Optical fiber humidity sensors using nanostructured coatings of sio2 nanoparticles. IEEE Sensors Journal 8, 281–285 (2008).
Yeo, T. L., Sun, T. & Grattan, K. T. V. Fibre-optic sensor technologies for humidity and moisture measurement. Sensors and Actuators, A: Physical 144, 280–295 (2008).
Chen, L. H. et al. Chitosan based fiber-optic fabry–perot humidity sensor. Sensors and Actuators, B: Chemical 169, 167–172 (2012).
Erol, A., Okur, S., Yağmurcukardeş, N. & Arlkan, M. Humidity-sensing properties of a zno nanowire film as measured with a qcm. Sensors and Actuators B: Chemical 152, 115–120 (2011).
Ashley, G., Kirby, P., Butler, T., Whatmore, R. & Luo, J. Chemically sensitized thin-film bulk acoustic wave resonators as humidity sensors. Journal of The Electrochemical Society 157, J419–J424 (2010).
Yao, Z. & Yang, M. A fast response resistance-type humidity sensor based on organic silicon containing cross-linked copolymer. Sensors and Actuators B: Chemical 117, 93–98 (2006).
Su, P.-G. & Huang, L.-N. Humidity sensors based on tio2 nanoparticles/polypyrrole composite thin films. Sensors and Actuators B: Chemical 123, 501–507 (2007).
Viviani, M., Buscaglia, M., Buscaglia, V., Leoni, M. & Nanni, P. Barium perovskites as humidity sensing materials. Journal of the European Ceramic Society 21, 1981–1984 (2001).
Wang, A. hua Wang, X. & dong Wang, X. Study on dielectric properties of humidity sensing nanometer materials. Sensors and Actuators B: Chemical 108, 445–449 (2005).
Zhuo, M. et al. Humidity sensing properties of a single sb doped sno2 nanowire field effect transistor. Sensors and Actuators B: Chemical 186, 78–83 (2013).
Tai, H., Jiang, Y. & Xie, G. Fabrication of integrated chemical field-effect transistor humidity sensor array and signal processing using artificial neural network. In 2006 IEEE International Conference on Networking, Sensing and Control, 1102–1105 (2006).
Na, P. S. et al. Investigation of the humidity effect on the electrical properties of single-walled carbon nanotube transistors. Applied Physics Letters 87, 093101 (2005).
Yoo, K.-P. et al. Novel resistive-type humidity sensor based on multiwall carbon nanotube/polyimide composite films. Sensors and Actuators B: Chemical 145, 120–125 (2010).
Qian, J. et al. Positive impedance humidity sensors via single-component materials. Scientific Reports 6, 25574 (2016).
Xuan, W. et al. Fast response and high sensitivity zno/glass surface acoustic wave humidity sensors using graphene oxide sensing layer. Scientific Reports 4, 7206 (2014).
Bi, H. et al. Ultrahigh humidity sensitivity of graphene oxide. Scientific Reports 3, 2714 (2013).
Zhang, D., Chang, H., Li, P., Liu, R. & Xue, Q. Fabrication and characterization of an ultrasensitive humidity sensor based on metal oxide/graphene hybrid nanocomposite. Sensors and Actuators B: Chemical 225, 233–240 (2016).
Yadav, B. C. & Singh, M. Morphological and humidity sensing investigations on niobium, neodymium, and lanthanum oxides. IEEE Sensors Journal 10, 1759–1766 (2010).
Kassas, A. et al. Humidity sensitive characteristics of porous li-mg-ti-of ceramic materials. American Journal of Analytical Chemistry 4, 83 (2013).
Litovchenko, V., Gorbanyuk, T., Solntsev, V. & Evtukh, A. Mechanism of hydrogen, oxygen and humidity sensing by cu/pd-porous silicon–silicon structures. Applied Surface Science 234, 262–267 (2004).
Li, Y., Chen, Y., Zhang, C., Xue, T. & Yang, M. A humidity sensor based on interpenetrating polymer network prepared from poly (dimethylaminoethyl methacrylate) and poly (glycidyl methacrylate). Sensors and Actuators B: Chemical 125, 131–137 (2007).
Sun, A., Li, Z., Wei, T., Li, Y. & Cui, P. Highly sensitive humidity sensor at low humidity based on the quaternized polypyrrole composite film. Sensors and Actuators B: Chemical 142, 197–203 (2009).
Zhang, D., Sun, Y., Li, P. & Zhang, Y. Facile fabrication of mos2-modified sno2 hybrid nanocomposite for ultrasensitive humidity sensing. ACS Applied Materials & Interfaces 8, 14142–14149 (2016).
Olenych, I. B., Aksimentyeva, O. I., Monastyrskii, L. S., Horbenko, Y. Y. & Yarytska, L. I. Sensory properties of hybrid composites based on poly(3,4-ethylenedioxythiophene)-porous silicon-carbon nanotubes. Nanoscale Research Letters 10, 187 (2015).
Nardes, A. et al. Conductivity, work function, and environmental stability of pedot:pss thin films treated with sorbitol. Organic Electronics 9, 727–734 (2008).
Seekaew, Y. et al. Low-cost and flexible printed graphene–pedot:pss gas sensor for ammonia detection. Organic Electronics 15, 2971–2981 (2014).
Aziz, S., Chang, D. E., Doh, Y. H., Kang, C. U. & Choi, K. H. Humidity sensor based on pedot:pss and zinc stannate nano-composite. Journal of Electronic Materials 44, 3992–3999 (2015).
Bihar, E. et al. A disposable paper breathalyzer with an alcohol sensing organic electrochemical transistor. Scientific Reports 6, 27582 (2016).
Gualandi, I. et al. Textile organic electrochemical transistors as a platform for wearable biosensors. Scientific Reports 6, 33637 (2016).
Khalil, R., Homaeigohar, S., Häußler, D. & Elbahri, M. A shape tailored gold-conductive polymer nanocomposite as a transparent electrode with extraordinary insensitivity to volatile organic compounds (vocs). Scientific Reports 6, 33895 (2016).
Lim, J.-E. et al. Brush-paintable and highly stretchable ag nanowire and pedot:pss hybrid electrodes. Scientific Reports 7, 14685 (2017).
Peng, W. et al. Performance improvement of zno nanowire based surface acoustic wave ultraviolet detector via poly(3, 4-ethylenedioxythiophene) surface coating. Sensors and Actuators A: Physical 199, 149–155 (2013).
Kim, S. et al. Noninvasive in vitro measurement of pig-blood d-glucose by using a microwave cavity sensor. Diabetes Research and Clinical Practice 96, 379–384 (2012).
Kim, N.-Y. et al. Rapid, sensitive, and reusable detection of glucose by a robust radiofrequency integrated passive device biosensor chip. Scientific Reports 5, 7807 (2015).
Lee, H.-J. et al. Asymmetric split-ring resonator-based biosensor for detection of label-free stress biomarkers. Applied Physics Letters 103, 053702 (2013).
Kim, S.-G., Lee, H.-J., Lee, J.-H., Jung, H.-I. & Yook, J.-G. A highly sensitive and label free biosensing platform for wireless sensor node system. Biosensors and Bioelectronics 50, 362–367 (2013).
Hong, Y. et al. A label-free biosensing platform using a pll circuit and biotin-streptavidin binding system. IEEE Transactions on Biomedical Circuits and Systems 9, 345–352 (2015).
Bailly, G., Harrabi, A., Rossignol, J., Stuerga, D. & Pribetich, P. Microwave gas sensing with a microstrip interdigital capacitor: Detection of nh3 with tio2 nanoparticles. Sensors and Actuators B: Chemical 236, 554–564 (2012).
Kim, B. H. et al. A gas sensor using double split-ring resonator coated with conducting polymer at microwave frequncies. In IEEE SENSORS 2014 Proceedings, 1815–1818 (2014).
An, Y.-J., Yun, G.-H., Kim, S. W. & Yook, J.-G. Wrist pulse detection system based on changes in the near-field reflection coefficient of a resonator. IEEE Microwave and Wireless Components Letters 24, 719–721 (2014).
An, Y.-J. et al. Flexible non-constrained rf wrist pulse detection sensor based on array resonators. IEEE Transactions on Biomedical Circuits and Systems 10, 300–308 (2016).
Kim, B.-H. et al. A proximity coupling rf sensor for wrist pulse detection based on injection-locked pll. IEEE Transactions on Microwave Theory and Techniques 64, 1667–1676 (2016).
Kim, S.-G., Yun, G.-H. & Yook, J.-G. Compact vital signal sensor using oscillation frequency deviation. IEEE Transactions on Microwave Theory and Techniques 60, 393–400 (2012).
Hong, Y. et al. Noncontact proximity vital sign sensor based on pll for sensitivity enhancement. IEEE Transactions on Biomedical Circuits and Systems 8, 584–593 (2014).
An, Y.-J., Yun, G.-H. & Yook, J.-G. Sensitivity enhanced vital sign detection based on antenna reflection coefficient variation. IEEE Transactions on Biomedical Circuits and Systems 10, 319–327 (2016).
Huang, W. & Kishk, A. Compact dielectric resonator antenna for microwave breast cancer detection. IET Microwaves, Antennas Propagation 3, 638–644 (2009).
Aguilar, S. M., Al-Joumayly, M. A., Burfeindt, M. J., Behdad, N. & Hagness, S. C. Multiband miniaturized patch antennas for a compact, shielded microwave breast imaging array. IEEE Transactions on Antennas and Propagation 62, 1221–1231 (2014).
Bernou, C., Rebièe, D. & Pistré, J. Microwave sensors: a new sensing principle. application to humidity detection. Sensors and Actuators B: Chemical 68, 88–93 (2000).
Nair, R., Perret, E., Tedjini, S. & Barron, T. A novel relative humidity sensor based on microwave resonators and a customized polymeric film. 29–33 (2012).
Saha, C., Siddiqui, J. Y., Guha, D. & Antar, Y. M. M. Square split ring resonators: Modelling of resonant frequency and polarizability. In 2007 IEEE Applied Electromagnetics Conference (AEMC), 1–3 (2007).
Saha, C. & Siddiqui, J. Y. A comparative analyis for split ring resonators of different geometrical shapes. In 2011 IEEE Applied Electromagnetics Conference (AEMC), 1–4 (2011).
Kuş, M. & Okur, S. Electrical characterization of pedot: Pss beyond humidity saturation. Sensors and Actuators B: Chemical 143, 177–181 (2009).
Wegler, B., Schmidt, O. & Hensel, B. Influence of pedot:pss on the effectiveness of barrier layers prepared by atomic layer deposition in organic light emitting diodes. Journal of Vacuum Science & Technology A: Vacuum, Surfaces, and Films 33, 01A147 (2015).
Koch, N., Vollmer, A. & Elschner, A. Influence of water on the work function of conducting poly(3,4-ethylenedioxythiophene)/poly(styrenesulfonate). Applied Physics Letters 90, 043512 (2007).
Ouyang, J. et al. On the mechanism of conductivity enhancement in poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) film through solvent treatment. Polymer 45, 8443–8450 (2004).
Ouyang, J., Chu, C.-W., Chen, F.-C., Xu, Q. & Yang, Y. High-conductivity poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) film and its application in polymer optoelectronic devices. Advanced Functional Materials 15, 203–208 (2005).
Acknowledgements
This research was supported by the MSIP(Ministry of Science, ICT and Future Planning), Korea, under the ITRC(Information Technology Research Center) support program (IITP-2017-2013-0-00680) supervised by the IITP(Institute for Information & Communications Technology Promotion). This research was also supported by the Basic Science Research Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Science, ICT & Future Planning (NRF-2015R1C1A1A02037804) and by the Mid-career Researcher Program through the National Research Foundation of South Korea (NRF) funded by the Science and Engineering. (NRF-2017R1A2B4012051).
Author information
Authors and Affiliations
Contributions
J.K.P. conducted most of the investigations on the samples and wrote the main paper. T.G.K., H.J.L., and B.H.K. provided valuable suggestions on the research and performed the experiments. H.H.C. deposited the PEDOT:PSS film and provided suggestions related to chemistry. Y.J.G. supervised the project and provided valuable advice on conducting the work. All authors contributed to writing the final manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Park, JK., Kang, TG., Kim, BH. et al. Real-time Humidity Sensor Based on Microwave Resonator Coupled with PEDOT:PSS Conducting Polymer Film. Sci Rep 8, 439 (2018). https://doi.org/10.1038/s41598-017-18979-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-18979-3
- Springer Nature Limited
This article is cited by
-
The quality monitoring of paracetamol medicament using a noninvasive microwave sensor
Scientific Reports (2023)
-
Chemical sensor based on a novel capacitive microwave flexible transducer with polymer nanocomposite-carbon nanotube sensitive film
Microsystem Technologies (2022)
-
All printed wide range humidity sensor array combining MoSe2 and PVOH in series
Journal of Materials Science: Materials in Electronics (2020)
-
An overview on the synthesis and recent applications of conducting poly(3,4-ethylenedioxythiophene) (PEDOT) in industry and biomedicine
Journal of Materials Science (2020)
-
Transition from positive to negative electrical resistance response under humidity conditions for PEDOT:PSS-MoS2 nanocomposite thin films
Journal of Materials Science: Materials in Electronics (2019)