Abstract
Simultaneous transport and scanning nanoSQUID-on-tip magnetic imaging studies in Cr-(Bi,Sb)2Te3 modulation-doped films reveal the presence of superparamagnetic order within the quantum anomalous Hall regime. In contrast to the expectation that a long-range ferromagnetic order is required for establishing the quantum anomalous Hall state, superparamagnetic dynamics of weakly interacting nanoscale magnetic islands is observed both in the plateau transition regions, as well as within the fully quantized C = ±1 Chern plateaus. Modulation doping of the topological insulator films is found to give rise to significantly larger superparamagnetic islands as compared to uniform magnetic doping, evidently leading to enhanced robustness of the quantum anomalous Hall effect. Nonetheless, even in this more robust quantum state, attaining full quantization of transport coefficients requires magnetic alignment of at least 95% of the superparamagnetic islands. The superparamagnetic order is also found within the incipient C = 0 zero Hall plateau, which may host an axion state if the top and bottom magnetic layers are magnetized in opposite directions. In this regime, however, a significantly lower level of island alignment is found in our samples, hindering the formation of the axion state. Comprehension and control of superparamagnetic dynamics is thus a key factor in apprehending the fragility of the quantum anomalous Hall state and in enhancing the endurance of the different quantized states to higher temperatures for utilization of robust topological protection in novel devices.
Similar content being viewed by others
Introduction
The quantum Hall (QH) and the recently demonstrated quantum anomalous Hall (QAH) effects are prime examples of topological states of matter driven by time-reversal symmetry braking (TRSB).1,2,3 In the QH state the TRSB is induced by high magnetic field applied perpendicular to a high-mobility 2D electron gas. The QAH state, in contrast, can be formed in thin films of topological insulators (TI) even in the absence of magnetic field.3,4,5,6,7,8,9,10 In this case the TRSB is induced by magnetic order attained by doping the TIs with transition metal elements like Cr, V, or Mn,3,4,5,6,7,8,11,12 which open a mass gap Δ in the helical Dirac surface states.13,14,15
In order to establish a TRSB topological state on a macroscopic scale the magnetic order should be long ranged and therefore a robust ferromagnetic (FM) state is believed to be a necessary condition for the experimental observation of the QAH effect with dissipationless chiral edge states.2,13,16 Indeed, a number of studies using global magnetization measurements14,17,18 and magnetic force microscopy19,20 have observed FM-like response in magnetically doped TI thin films. Surprisingly, however, recent scanning SQUID magnetic imaging21 and transport studies,22,23 as well as analysis of Kerr microscopy imaging,24 have suggested the presence of a superparamagnetic (SPM) state in Cr-doped (Bi,Sb)2Te3 films in which instead of a long-range FM order the magnetism is comprised of single-domain magnetic islands. These islands are of characteristic size of few tens of nanometers and are only weakly coupled to each other.21
The possible presence of a SPM order has important implications for the properties of the QAH state. The first key consideration is that if the QAH state can indeed be induced by a SPM order, such coexistence can be present only at temperatures well below the SPM blocking temperature, T≪T B, since at higher temperatures the QAH state will be destroyed by thermally activated magnetization reversals of the SPM islands. At T≪T B the overall magnetic response of a SPM is hysteretic similarly to a FM, making it difficult to discern the two types of magnetic order using global magnetization studies. Moreover, the distinction between SPM and FM states may seem to be of minor importance, since in both cases a full alignment of the magnetic moments can be attained at low temperatures and at sufficiently high fields above the coercive field H c. This aligned magnetization may then be preserved upon decreasing the field back to zero. However, in addition to causing nontrivial dynamics,22,23,25 the SPM state has two essential repercussions. The first pertains to the existing puzzle of the fragility of the QAH that limits the observation of conductance quantization, σ xx = 0 and σ xy = e 2/h, to only very low temperatures that are significantly lower than the magnetic ordering temperature T c ≅ 20 K and the size of the magnetically induced gap in the surface Dirac states,14,15,26 Δ ≈ 30 meV. The fact that the SPM islands are only weakly coupled implies reduced magnetism in the regions between the islands which may lead to suppressed Δ in the inter-island matrix, providing a possible explanation for the observed fragility of the global QAH state.
The second important implication of SPM is related to the recent observation of the C = 0 Chern state in which both σ xx and σ xy vanish17,27,28 resulting in zero Hall conductivity plateau (ZHP). In contrast to the C = ±1 QAH case, this intricate insulating state requires the existence of a gap in the TI helical states on the film surfaces but an absence of a global chiral state at the sample edges.29 One interesting possible mechanism for realization of such a state is the axion insulator,27,30,31 which requires the out-of-plane magnetization to point in opposite directions on the top and bottom surfaces of the film. In this configuration gap opening is induced at the surfaces, as well as along the film edges, leading to vanishing σ xx and σ xy . Such a unique magnetic state can be attained in modulation-doped (Bi,Sb)2Te3 films with asymmetric structure resulting in different coercive fields in the top and bottom Cr-doped layers.27 The recent observation of the enhancement of the ZHP upon increasing the asymmetry of the heterostructures lends strong support to the axion insulator model27 over other suggested mechanisms, such as the hybridization between the top and bottom surfaces of the TI in presence of disorder.13 Similarly to the QAH C = ±1 state, however, the stability of the axion insulator is also crucially dependent on the establishment of a long-large magnetic order. Resolving the microscopic magnetic structure in doped TIs is thus paramount for our understanding of the mechanisms leading to the C = 0 and C = ±1 states and for enhancing the robustness of the QAH effect and of the ZHP for device applications.
The degree of the magnetic order in magnetically doped TI films, whether FM, SPM, or disordered, can critically depend on material parameters, doping level, growth conditions, and temperature.11,18,32,33 In this context, it is important to note that none of the previous studies of doped TI films have directly probed the microscopic magnetic structure within the QAH state.19,20,21 The FM state was reported to be present in films that either do not show QAH at all due to non-optimal doping or composition, or at temperatures substantially higher than those required for the formation of the QAH.19,20 Similarly, the SPM was demonstrated locally in films that do show QAH but at elevated temperatures at which no quantization was present.21,24
Here we report scanning SQUID-on-tip (SOT) magnetic imaging of modulation-doped (Bi,Sb)2Te3 films performed concurrently with transport measurements that show full QAH quantization. We observe unambiguous SPM behavior both in the magnetization reversal process in the plateau transition regions near H c, as well as within the macroscopically quantized state. No conventional FM domain wall motion is detected under any conditions. Moreover, our results indicate that SPM order is present also in the incipient C = 0 state providing an essential insight into the microscopic nature of the different Chern number topological states.
Results and discussion
In this work we studied (Bi,Sb)2Te3 heterostructures with Cr modulation doping which gives rise to a significantly more robust QAH state34 sustained up to 2 K and in addition renders a clearly developed C = 0 state.27 Figure 1a shows a schematic structure of the film containing two 2 nm thick 12%-Cr-doped layers separated by a 3 nm undoped layer. The bottom-doped layer is separated from the InP substrate by a 1 nm undoped layer of (Bi,Sb)2Te3. The heterostructure was coated with 23 nm of AlO x and 10 nm of Ti/Au top-gate electrode and patterned into a Hall bar structure (Fig. 1b). Imaging of the local out-of-plane magnetic field B z (x,y) employing a scanning SOT35,36,37 was carried out simultaneously with transport measurements at T = 300 mK. The Indium SOT with effective diameter of 115 nm (Fig. 1c) was scanned at a constant height of about 300 nm above the sample surface at a typical scan rate of 9 μm/s.
Characterization of Cr–(Bi,Sb)2Te3 modulation-doped heterostructure.a Schematic structure of the MBE grown thin film sample. b False color optical image showing the edges of the Cr–(Bi,Sb)2Te3 Hall bar pattern (bright), top gate (yellow), and metallic contacts (blue). Scale bar length is 100 μm. The green arrow points to the area at the heterostructure edge imaged in e. c Scanning electron microscope micrograph of the In SOT used for the scanning magnetic imaging. Scale bar length is 100 nm. d Transport measurements of ρ xx (black) and ρ yx (red) showing the QAH state with full quantization at T = 300 mK at gate voltage of V g = 4 V. e Scanning SOT image of the out of plane magnetic field B z (x,y) above the sample surface at T = 300 mK in applied field of μ 0 H = 166.4 mT slightly above the coercive field μ 0 H c = 137 mT. The dotted line indicates the location of the edge of the patterned heterostructure. Image area 8×4 μm2, pixel size 50 nm, sampling time 5.5 ms/pixel. Scale bar length is 1 μm
The four-probe transport characteristics of the sample show hysteretic behavior (Fig. 1d) and a clear QAH effect. Full quantization is attained at top-gate bias V g = 4 V when the Fermi energy is tuned into the gap. The apparent coercive field H c, defined by the location of the peaks in ρ xx , depends on the sweep rate of the applied field μ 0 H due to the time relaxation of the magnetization in the film.21 It reduces from μ 0 H c = 160 mT for the faster sweep dμ 0 H/dt = 95.2 mT/min used for transport measurements in Fig. 1d to μ 0 H c = 137 mT at slower effective sweep rate of dμ 0 H/dt = 40 μT/min employed for the simultaneous magnetic imaging and transport (Fig. 1e).
Figure 1e shows an example of scanning SOT magnetic image of 8 × 4 µm2 acquired at an applied field of μ 0 H = 166.4 mT, slightly above μ 0 H c = 137 mT. The imaged area includes the edge of the Cr–(Bi,Sb)2Te3 film (dotted). Since the SOT response is periodic in magnetic field (see Fig. S1) the value of the measured local magnetic field can be determined only up to a constant offset. Here we are interested in studying the variations in local field B z (x,y) stemming from the spatial fluctuations in the local magnetic structure in the film. We therefore define B z = 0 at ~3 µm from the edge of the sample (at the left end of the imaged area) where the stray field from the magnetized film, which decays as ~x/d, where x is the distance from the edge and d = 7 nm is the magnetic thickness of the film, is negligible. The attained B z (x,y) thus describes the magnetic field above the surface of the sample, which arises from the variations in local magnetic structure, while the total magnetic field is given by μ 0 H + B z (x,y). At μ 0 H = 166.4 mT > μ 0 H c the net average magnetization M of the film is positive resulting in the negative stray field immediately to the left of the sample edge (blue in Fig. 1e). The interior of the sample, however, shows a highly inhomogeneous structure with both positive and negative values of B z (x,y) reflecting microscopic regions with correspondingly positive and negative out-of-plane magnetization M z .
The magnetism in Cr-doped (Bi,Sb)2Te3 films is strongly anisotropic with an out-of-plane easy magnetization axis.17 The inhomogeneous magnetic structure in Fig. 1e could therefore arise either from coexistence of FM domains with positive and negative magnetization M z near H c or from single-domain SPM islands with random positive and negative moments m z . In order to address this question we acquire a sequence of B z (x,y) images upon increasing the applied field by small increments of 0.2 mT. In the FM case this procedure should result in expansion of the positive M z domains into the negatively magnetized regions through domain wall motion. In the case of weakly interacting SPM islands, in contrast, no domain walls should be present and the magnetization process is expected to occur through uncorrelated flipping of the magnetic moments m z of the different islands determined by their individual coercive fields. Figure 2a, b show an example of two consecutive B z (x,y) images acquired at μ 0 H = 137.4 and 137.6 mT, which appear to be almost identical. In order to determine the small changes we subtract numerically the two images. The resulting ΔB z (x,y) image (Fig. 2c) reveals seven distinct circular peaks of positive differential field that are clearly above the background noise level. These peaks can be fitted by point dipoles with magnetic moments of 2m i ranging from 2 × 105 to 8 × 105 µ B as shown in Fig. 2d. This means that seven islands have flipped their magnetic moment m z from −m i to +m i upon increasing the applied field by 0.2 mT. Movie S1 presents a sequence of B z (x,y) and ΔB z (x,y) images upon such incremental sweep of μ 0 H from 132.6 to 144.2 mT. The same reversal mechanism is revealed at the rest of investigated fields. All the observable magnetization changes thus occur through a random flipping of uncorrelated magnetic islands without any domain wall dynamics, revealing the SPM nature of the magnetic order in the modulation-doped (Bi,Sb)2Te3 films.
Superparamagnetism in the modulation-doped Cr–(Bi,Sb)2Te3 heterostructure.a,b Scanning SOT B z (x,y) images 8×4 μm2 at 300 mK at μ 0 H = 137.4 mT a and 137.6 mT b. c Differential image \(\Delta B_z(x,y)\) obtained by numerically subtracting image a from image b, showing the magnetization reversal of seven SPM islands (green–red) in response to the 0.2 mT increase in the applied field. d Best fit numerical simulation of \(\Delta B_z(x,y)\) due to seven point dipoles with indicated values of out-of-plane magnetic moment of 2m i = 2.2×105 μ B (bottom-right island) to 8.9×105 μ B (top-right island). e Residual \(\Delta B_z(x,y)\) after subtracting d from c showing the quality of the fit and the noise level of the measurement. Scale bar length is 1 μm. f Histogram of the magnetization reversal moment sizes m i in four field ranges centered at μ 0 H = 48.1 (blue), 97.3 (yellow), 141.7 (green), and 245.9 mT (red). The top axis shows the corresponding calculated diameter d of the SPM islands. g Comparison between the moment size histograms of the uniform doped (from ref. 21) and the modulation-doped samples in the vicinity of H c showing significantly larger SPM islands in the modulation-doped heterostructure. h Cumulative magnetization change M = ∑ i m i due to island reversals upon sweeping the applied field in seven ranges (color coded, left axis) and the simultaneously acquired ρ yx (black, right axis). The blue arrow at μ 0 H ≅ 80 mT indicates the field at which ρ yx starts deviating from quantized value, corresponding to a cumulative change in M of ~5% of the full saturation
The statistical analysis of 785 detected flipping events in four segments of field sweeps are presented in Fig. 2f. An incremental field sweep over 16.2 mT centered around 48.1 mT (blue) revealed 33 events with average magnetic moment of \(\bar m_i =\) 1.2×105 µ B and a quite narrow distribution of m i . As the field is increased, the flipping rate grows significantly reaching 485 events in 23.4 mT interval around 141.7 mT (green). In this range, which includes μ 0 H c = 137 mT, \(\bar m_i\) increased to 2.1×105 µ B and the distribution becomes significantly broader with few islands reaching m i ≅ 106 µ B. Upon further increase of the field to 246 mT (red) the rate drops substantially, the distribution narrows down, and \(\bar m_i\) decreases to 1.1×105 µ B.
It is interesting to compare the SPM magnetization reversal process in our modulation-doped samples with the previously reported behavior in uniformly doped Cr–(Bi,Sb)2Te3 films.21 Fig. 2g shows the distribution of the reversal moments in the vicinity of H c in the two samples. The modulation-doped film displays much larger reversal moments reaching 8×105 μ B as compared to about 3×105 μ B for uniform doping. Similarly, \(\bar m_i =\) 2.1×105 µ B in the modulation-doped film is three times larger than \(\bar m_i =\) 7.1×104 µ B in the uniform sample. Taking the similar total Cr doping level, 7 nm film thickness, and assuming 3 µ B per Cr atom, the \(\bar m_i =\) 7.1×104 µ B in the uniformly doped film translates into SPM island size of 4.9×103 nm2. In our current modulation-doped sample, the Cr doping level was comparable but the doped layers were only 2 nm thick. The observed \(\bar m_i =\) 2.1×105 µB thus translates into 2.4×104 nm2 area of a typical SPM island, which is five times larger than in the uniform film. The larger area of the SPM islands implies a substantial reduction of the relative area of the inter-island regions and a more homogeneous magnetization with a likely smaller suppression of Δ in the inter-island matrix, thus providing a possible explanation for the enhanced robustness of the QAH in our modulation-doped samples.
By integrating the reversing moments m i for each field increment, we can derive the magnetization curve M(H) = ∑ i m i (Fig. 2h) along with the simultaneously measured ρ yx . Comparison of M(H) and ρ yx (H) curves unveils two significant observations. The first is that in the C = −1 plateau region for μ 0 H < 80 mT the magnetization M grows appreciably with H while ρ yx remains quantized. A similar behavior is observed in the C = + 1 plateau at H ≅ 250 mT. Fig. 2f shows that at these plateau fields substantial island flipping occurs (blue and red distributions) providing a direct observation of SPM dynamics within the QAH C = ±1 plateau regions. This implies that the global QAH state is preserved in the presence of oppositely magnetized islands as long as their density is low. In Fig. 2h the onset of deviation from quantized ρ yx value occurs at μ 0 H ≅ 80 mT (blue arrow), where the relative magnetization of the oppositely magnetized islands reaches about 5%. Above this fraction the edge states surrounding the islands of opposite magnetization apparently start percolating across the sample13 giving rise to finite ρ xx and a drop in |ρ yx |. Our results thus show that the establishment of quantized conductance requires a very large fraction of over 95% of the SPM islands’ magnetization to be aligned, significantly higher than required for conventional percolation threshold. The second observation in Fig. 2h is that near the coercive field ρ yx (H) displays a sharper plateau transition than the M(H) curve. This behavior could be ascribed to the enhancement of ρ xx in the C = 0 state, similarly to the behavior in the regular anomalous Hall effect where \(\rho _{yx} \propto M\rho _{xx}^2\) is commonly found.25
We now address the C = 0 plateau and its magnetic state. Fig. 3a shows σ xx and σ xy attained for the faster field sweep (black) and along several segments of slower sweeps acquired simultaneously with the magnetic imaging (color). At H c a pronounced suppression of σ xx and a plateau-like feature in σ xy are visible. Supplementary Fig. S4 shows a more complete set of transport measurements acquired on another sample of the same structure emphasizing the emergence of the ZHP in the C = 0 state. A recent study has shown that the σ xx = 0 and σ xy = 0 characteristic property of the C = 0 state becomes fully developed at low temperatures in modulation-doped structures with higher asymmetry between the top and bottom layers.27 The SOT magnetic imaging in Fig. 2 and Movie S1 acquired concurrently with the transport data clearly show that the magnetic structure of the Cr–(Bi,Sb)2Te3 film in this incipient C = 0 state near μ 0 H c = 137 mT is in SPM state, resulting in highly disordered magnetic configuration and in the absence of domain wall dynamics.
Magnetic imaging of the C = 0 and C = ±1 states.a The conductivity coefficients σ xx and σ xy at 300 mK showing the incipient C = 0 plateau measured upon a faster field sweep (black) and in a slow sweep acquired simultaneously with the SOT magnetic imaging (color). The slower sweep allows for larger magnetic relaxation and decrease in the apparent coercive field. b The B z (x,y) profiles showing the individual scanning SOT line traces within the marked rectangular areas in c–e. c–e Scanning SOT B z (x,y) images at μ 0 H = 260 mT c, 137 mT d, and 40 mT e, corresponding to the C = + 1, C = 0, and C = −1 states, respectively. Scale bar length is 1 μm. f–h Schematic configuration of the SPM islands showing high degree of magnetic alignment in the C = + 1 f and C = −1 h states. In the incipient C = 0 axion state g majority of the islands are positively (negatively) magnetized in the top (bottom) layers but the degree of alignment is insufficient for attaining quantization of transport coefficients
Figure 3b–d compare the magnetic structure in the C = ±1 and C = 0 states. The line cuts in Fig. 3e demonstrate that in the C = + 1 state most of the SPM islands are magnetized along the positive field direction resulting in an enhanced B z (x,y) on the inner side of the film and a negative stray B z outside the edge. Similarly in the C = −1 state most of the islands are negatively magnetized resulting in a negative B z (x,y) on the inner side and a positive stray field outside the film edge. In the C = 0 state, on the other hand, the densities of the positively and negatively magnetized islands are comparable resulting in zero average B z (x,y) both inside and outside the film. Moreover, while in the C = ±1 states in Fig. 3b, d the magnetization is not entirely uniform due to variations in local doping and remaining low density of oppositely oriented islands (see the statistical analysis in Fig. 2f), the degree of the inhomogeneity is relatively small (Fig. 3e). In the C = 0 state, in contrast, the variations in the local field are substantially larger and B z (x,y) crosses zero many times, revealing a random distribution of SPM islands with positive and negative values of m i .
In order to realize a robust axion state in TI heterostructures with two doping layers, the magnetic properties of the layers have to meet two requirements: (i) the coercive field of one of the layers, \(H_{\rm c}^{\rm l}\), has to be lower than \(H_{\rm c}^{\rm h}\) of the second layer, and (ii) in the field range \(H_{\rm c}^{\rm l} < H < H_{\rm c}^{\rm h}\), where the two layers have opposite magnetization, the magnetic structure within each of the layers has to be sufficiently homogeneous similarly to the structure attained in the C = ±1 states with over 95% island alignment. Since in the SPM case the width δH c over which the global magnetization reversal occurs is finite, the second requirement necessitates the separation between the two coercive fields, \(\Delta H_{\rm c} = H_{\rm c}^{\rm h} - H_{\rm c}^{\rm l}\), to be substantially larger than the width of the magnetization reversal transition of each of the layers, \(\Delta H_{\rm c} \gg \delta H_{\rm c}\). In such a case, upon sweeping the magnetic field from C = −1 state with both layers negatively magnetized (Fig. 3h), the first layer undergoes a transition at \(H_{\rm c}^{\rm l}\) accompanied by reversal events of the SPM islands. The axion state is established when most of the islands in the first layer have reversed their magnetization, accompanied by a drop in the rate of the magnetization reversals. As the field is further increased upon approaching \(H_{\rm c}^{\rm h}\), the SPM m i reversal events in the second layer will set in, leading to the destruction of the axion state. Since our SOT imaging cannot distinguish between the SPM islands in the two layers, we expect to observe two peaks in the rate of m i reversals at \(H_{\rm c}^{\rm l}\) and \(H_{\rm c}^{\rm h}\) and the integrated magnetization curve M(H) = ∑ i m i should display two step-like features and a plateau at intermediate fields \(H_{\rm c}^{\rm l} < H < H_{\rm c}^{\rm h}\). The transport data showing two peaks in σ xx in Fig. 3a is indicative of the positions of the two coercive fields \(H_{\rm c}^{\rm l}\) and \(H_{\rm c}^{\rm h}\). In our magnetic imaging data, however, we observe only one broadened range of fields over which the rate of m i events is large (Fig. S3a) and the corresponding M(H) curve shows a single smoothed step-like behavior with no observable intermediate plateau (Fig. S3b). These results thus indicate that in our modulation-doped Cr–(Bi,Sb)2Te3 films the two magnetization reversal transitions overlap substantially, \(\delta H_{\rm c}\sim \Delta H_{\rm c}\), with no intermediate region in which one layer is close to full positive magnetization and the other close to full negative magnetization (Fig. 3g) thus preventing the establishment of a global axion state. This finding is consistent with the absence of a fully developed ZHP in the transport measurements in Figs. 3a and S4.
In conclusion, by performing simultaneous transport and magnetic imaging we reveal that in modulation-doped Cr–(Bi,Sb)2Te3 films the SPM state coexists with the QAH state in the C = ±1 plateaus, in the plateau transition regions, and in the incipient C = 0 state. The size of the SPM islands in the modulation-doped heterostructures is substantially larger than in comparable homogeneously doped TI films. This points to a more uniform magnetization which apparently lessens the suppression of Δ in the inter-island matrix leading to the observed large enhancement in the temperature robustness of the QAH in modulation-doped structures.34 In order to attain a full conductance quantization, over 95% of the SPM islands’ magnetization in each layer have to be magnetized along the same direction. In the C = ±1 state such an alignment can be attained by applying magnetic field that is substantially higher than H c. A similarly high degree of island alignment is required in order to attain a robust axion state. To achieve this, however, the difference in the coercive fields of the two doped layers should be significantly larger than the width of the SPM transition in each of the layers, \(\Delta H_{\rm c} \gg \delta H_{\rm c}\). The difficulty in attaining this requirement in modulation-doped TI films in which the two layers are both Cr doped renders the C = 0 state to be significantly more fragile than the counterpart C = ±1 states. Very recently, two independent studies38,39 have attained much larger \(\Delta H_{\rm c}\) by doping one layer by Cr and the other layer by V leading to a significantly more robust ZHP providing strong support to this conclusion. Control of the materials properties in terms of doping homogeneity, enlarging the size and the uniformity of the SPM islands, and increasing the difference in the coercive fields of the top and bottom magnetically doped layers thus emerges as the key challenge for attaining robust QAH and axion states and extending their temperature range for novel electronic applications.
Methods
Fabrication of modulation-doped Cr–(Bi,Sb)2Te3 heterostructures
The Cr–(Bi,Sb)2Te3 films were grown by molecular beam epitaxy (MBE) on semi-insulating InP(111) substrates using the same procedures as described in ref. 27. The 3-nm-thick AlO x capping layer was deposited by atomic layer deposition (ALD) system immediately after the removal from the MBE chamber. Using standard photolithography and Ar ion milling processes, the films were patterned into the Hall-bar geometry: 600 nm long and 300 nm wide (Fig. 1b). The top 20-nm-thick AlO x dielectric layer and 10-nm-thick Ti/Au electrode were deposited by ALD and electron beam evaporation, respectively.
SOT imaging
The magnetic imaging was performed using Indium SOT device35,36,37 with an effective diameter of 115 nm (see Supplementary Note 1). The SOT was mounted in a home-built scanning probe microscope employing a series SQUID array amplifier40 for signal readout. Scanning was performed using Attocube integrated xyz scanner with xy range of 30 μm and z range of 15 μm. Magnetic imaging measurements were performed at 300 mK in Oxford Heliox He3 refrigerator.
Data availability
The datasets generated during the current study are available from the corresponding authors on reasonable request.
References
Hasan, M. Z. & Kane, C. L. Colloquium: topological insulators. Rev. Mod. Phys. 82, 3045–3067 (2010).
Qi, X.-L. & Zhang, S.-C. Topological insulators and superconductors. Rev. Mod. Phys. 83, 1057–1110 (2011).
Chang, C.-Z. et al. Experimental observation of the quantum anomalous hall effect in a magnetic topological insulator. Science 340, 167–170 (2013).
Checkelsky, J. G. et al. Trajectory of the anomalous Hall effect towards the quantized state in a ferromagnetic topological insulator. Nat. Phys. 10, 731–736 (2014).
Kou, X. et al. Scale-invariant quantum anomalous hall effect in magnetic topological insulators beyond the two-dimensional limit. Phys. Rev. Lett. 113, 137201 (2014).
Bestwick, A. J. et al. Precise quantization of the anomalous Hall effect near zero magnetic field. Phys. Rev. Lett. 114, 187201 (2015).
Chang, C.-Z. et al. High-precision realization of robust quantum anomalous Hall state in a hard ferromagnetic topological insulator. Nat. Mater. 14, 473–477 (2015).
Kandala, A., Richardella, A., Kempinger, S., Liu, C.-X. & Samarth, N. Giant anisotropic magnetoresistance in a quantum anomalous Hall insulator. Nat. Commun. 6, 7434 (2015).
Yu, R. et al. Quantized anomalous Hall effect in magnetic topological insulators. Science 329, 61–64 (2010).
Nomura, K. & Nagaosa, N. Surface-quantized anomalous hall current and the magnetoelectric effect in magnetically disordered topological insulators. Phys. Rev. Lett. 106, 3–6 (2011).
Chang, C.-Z. et al. Thin films of magnetically doped topological insulator with carrier-independent long-range ferromagnetic order. Adv. Mater. 25, 1065–1070 (2013).
Peixoto, T. R. F. et al. Impurity states in the magnetic topological insulator V:(Bi,Sb)2Te3. Phys. Rev. B. 94, 195140 (2016).
Wang, J., Lian, B. & Zhang, S.-C. Universal scaling of the quantum anomalous Hall plateau transition. Phys. Rev. B. 89, 85106 (2014).
Xu, S. et al. Hedgehog spin texture and Berry’s phase tuning in a magnetic topological insulator. Nat. Phys. 8, 616–622 (2012).
Lee, I. et al. Imaging Dirac-mass disorder from magnetic dopant atoms in the ferromagnetic topological insulator Crx (Bi0.1Sb0.9)2-xTe3. Proc. Natl. Acad. Sci. 112, 1316–1321 (2015).
Checkelsky, J. G., Ye, J., Onose, Y., Iwasa, Y. & Tokura, Y. Dirac-fermion-mediated ferromagnetism in a topological insulator. Nat. Phys. 8, 729–733 (2012).
Kou, X. et al. Metal-to-insulator switching in quantum anomalous Hall states. Nat. Commun. 6, 8474 (2015).
Li, B. et al. Carrier dependent ferromagnetism in chromium doped topological insulator. Phys. Lett. A. 377, 1925–1929 (2013).
Wang, W. et al. Visualizing ferromagnetic domains in magnetic topological insulators. APL Mater. 3, 83301 (2015).
Wang, W., Chang, C.-Z., Moodera, J. S. & Wu, W. Visualizing ferromagnetic domain behavior of magnetic topological insulator thin films. npj Quantum Mater. 1, 16023 (2016).
Lachman, E. O. et al. Visualization of superparamagnetic dynamics in magnetic topological insulators. Sci. Adv. 1, e1500740 (2015).
Grauer, S. et al. Coincidence of superparamagnetism and perfect quantization in the quantum anomalous Hall state. Phys. Rev. B. 92, 201304 (2015).
Liu, M. et al. Large discrete jumps observed in the transition between Chern states in a ferromagnetic topological insulator. Sci. Adv. 2, e1600167–e1600167 (2016).
Yeats, A. L. et al. Local optical control of ferromagnetism and chemical potential in a topological insulator. Proc. Natl. Acad. Sci. 114, 10379–10383 (2017).
Nagaosa, N., Sinova, J., Onoda, S., MacDonald, A. H. & Ong, N. P. Anomalous Hall effect. Rev. Mod. Phys. 82, 1539–1592 (2010).
Yue, Z. & Raikh, M. E. Smearing of the quantum anomalous Hall effect due to statistical fluctuations of magnetic dopants. Phys. Rev. B. 94, 1–7 (2016).
Mogi, M. et al. A magnetic heterostructure of topological insulators as a candidate for an axion insulator. Nat. Mater. 16, 516–521 (2017).
Feng, Y. et al. Observation of the zero Hall plateau in a quantum anomalous Hall insulator. Phys. Rev. Lett. 115, 126801 (2015).
Qi, X.-L., Hughes, T. L. & Zhang, S. Topological field theory of time-reversal invariant insulators. Phys. Rev. B. 78, 195424 (2008).
Wilczek, F. Two applications of axion electrodynamics. Phys. Rev. Lett. 58, 1799–1802 (1987).
Essin, A. M., Moore, J. E. & Vanderbilt, D. Magnetoelectric polarizability and axion electrodynamics in crystalline insulators. Phys. Rev. Lett. 102, 10–13 (2009).
Hor, Y. S. et al. Development of ferromagnetism in the doped topological insulator Bi 2-x MnxTe3. Phys. Rev. B. 81, 195203 (2010).
Feng, X. et al. Thickness dependence of the quantum anomalous Hall effect in magnetic topological insulator films. Adv. Mater. 28, 6386–6390. (2016).
Mogi, M. et al. Magnetic modulation doping in topological insulators toward higher-temperature quantum anomalous Hall effect. Appl. Phys. Lett. 107, 182401 (2015).
Finkler, A. et al. Self-aligned nanoscale SQUID on a tip. Nano. Lett. 10, 1046–1049 (2010).
Finkler, A. et al. Scanning superconducting quantum interference device on a tip for magnetic imaging of nanoscale phenomena. Rev. Sci. Instrum. 83, 73702 (2012).
Vasyukov, D. et al. A scanning superconducting quantum interference device with single electron spin sensitivity. Nat. Nanotechnol. 8, 639–644 (2013).
Mogi, M. et al. Tailoring tricolor structure of magnetic topological insulator for robust axion insulator. Sci. Adv. 3, eaao1669 (2017).
Xiao, D. et al. Realization of the axion insulator state in quantum anomalous hall sandwich heterostructures. Preprint at http://arxiv.org/abs/1710.00471 (2017).
Huber, M. E. et al. DC SQUID series array amplifiers with 120 MHz bandwidth. IEEE Trans. Appl. Supercond. 11, 1251–1256 (2001).
Acknowledgements
We thank Karen Michaeli for helpful discussions. This work was supported by the NSF/DMR-BSF Binational Science Foundation—BSF No. 2015653 and NSF No. 1609519, by Rosa and Emilio Segré Research Award, and by JST CREST (No. JPMJCR16F1).
Author information
Authors and Affiliations
Contributions
E.O.L. performed the scanning SOT and transport measurements at 300 mK and constructed the scanning SOT microscope. M.M., A.T., M.K., and Y.T. designed, fabricated, and characterized the samples. J.S. performed transport measurements and participated in sample fabrication. A.U. and K.B. fabricated the SOTs. Y.A. and Y.M. developed the SOT fabrication technique. Y.A. and E.O.L. developed the data analysis software. M.E.H. developed the SOT readout system. E.Z. and E.O.L. wrote the manuscript with contributions from other authors.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Lachman, E.O., Mogi, M., Sarkar, J. et al. Observation of superparamagnetism in coexistence with quantum anomalous Hall C = ±1 and C = 0 Chern states. npj Quant Mater 2, 70 (2017). https://doi.org/10.1038/s41535-017-0072-1
Received:
Revised:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41535-017-0072-1
- Springer Nature Limited
This article is cited by
-
Direct visualization of electronic transport in a quantum anomalous Hall insulator
Nature Materials (2023)
-
Laughlin charge pumping in a quantum anomalous Hall insulator
Nature Physics (2023)
-
Visualization of ferromagnetic domains in vanadium-doped topological insulator thin films and heterostructures
Tungsten (2023)
-
Nanoscale imaging of equilibrium quantum Hall edge currents and of the magnetic monopole response in graphene
Nature Physics (2020)
-
Axion physics in condensed-matter systems
Nature Reviews Physics (2020)