Abstract
The design of monomer sequences in polymers has been a challenging research subject, especially in making vinyl copolymers by free-radical polymerization. Here, we report a strategy to obtain sequence-regulated vinyl copolymers, utilizing the periodic structure of a porous coordination polymer (PCP) as a template. Mixing of Cu2+ ion and styrene-3,5-dicarboxylic acid (S) produces a PCP, [Cu(styrene-3,5-dicarboxylate)] n , with the styryl groups periodically immobilized along the one-dimensional channels. After the introduction of acrylonitrile (A) into the host PCP, radical copolymerization between A and the immobilized S is performed inside the channel, followed by decomposing the PCP to isolate the resulting copolymer. The predominant repetitive SAAA sequence in the copolymer is confirmed by monomer composition, NMR spectroscopy and theoretical calculations. Copolymerization using methyl vinyl ketone also provides the same type of sequence-regulated copolymer, showing that this methodology has a versatility to control the copolymer sequence via transcription of PCP periodicity at the molecular level.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Natural biopolymers contain perfectly defined monomer sequences in the polymer chain to execute essential biogenic functions. The nucleotide sequence in DNA plays a critical role in genetic inheritance, where the DNA strands with complementary sequences are accurately replicated from the original DNA template within DNA polymerase. According to the nucleotide sequence of the DNA, a peptide chain with a specific structure is produced efficiently via translation of RNA in a ribosome1. Thus, nature tells us that the utilization of informative templates in confined spaces would be the key to accomplishing precisely controlled synthesis of polymers with well-defined sequences.
In contrast to the elegant operations of the polymerizations in biological systems, the monomer sequence in a polymer chain is poorly regulated by synthetic chemical processes. Although several approaches with the aid of iterative reactions2,3, multicomponent reactions4,5, preprogrammed monomers6,7 and templates8 have successfully allowed the control of monomer sequences in polymers or oligomers, sequence regulation in vinyl polymers via the chain-growth mechanism has been rather limited. In conventional chain-growth radical polymerization, which is widely used in industry, the composition and sequence distribution of copolymers are governed generally by the inherent relative monomer reactivities, resulting in the production of statistically random copolymers with irregular sequences. For the preparation of vinyl copolymers with regulated sequences, the formation of primitive periodic sequences (XY-, XYY-type sequences) could only be achieved using specific co-monomer pairs9,10, additives11,12 and small template molecules13,14. Sequential additions of donor and acceptor monomer feeds in living polymerization could virtually allow for controlled placement of the monomers at a chain location15. Therefore, sequence-defined radical copolymerization is recognized as the current holy grail of polymer synthesis16, with strong requirements for protocols that enable the precise positioning of monomers in copolymer chains with high molecular weight17,18.
Inspired by biological polymerizations, we were drawn to polymer synthesis in confined artificial nanospaces to accomplish the precise control of polymer structures. Porous coordination polymers (PCPs), built up by the self-assembly of metal ions with organic ligands, have received much attention because of their diverse topologies and unique properties in areas such as storage, exchange and conversion19,20,21. Polymerization reactions could also be induced in PCPs, imposing specific nanoconfinement effects on the reaction kinetics and selectivity22,23. In our effort to develop an effective methodology for controlling copolymerization, we performed radical polymerization of multiple vinyl monomers accommodated in PCP nanochannels, revealing the compositional changes of monomer units compared with those obtained from conventional free-radical conditions24,25. However, sequence regulation in the resultant copolymers was unsuccessful because of inadequate spatial arrangement of monomers in the nanochannels. Here, we disclose a methodology that utilizes the periodic structure of PCPs for sequence control in radical copolymerization. The structural periodicity of PCPs is precisely transcribed into products at the molecular level, which is distinguished from other examples using PCPs as reaction templates26,27,28. Owing to the high designability of PCPs as well as many applicable monomers, this method can be utilized to fabricate a wide variety of vinyl copolymers with controlled sequences.
Results
Preparation of template PCP
The key to success in this system is pre-immobilization of the vinyl moieties at regular intervals along the one-dimensional nanochannels of a PCP framework via covalent bonding. After the introduction of another free guest monomer into the nanochannels, copolymerization between the immobilized and free monomers provided a copolymer containing a highly periodic sequence because of the regular positioning of monomers in the nanochannels (Fig. 1). To arrange vinyl groups periodically along PCP nanochannels, we focused on a kagomé-type PCP, [Cu(ipa)] n (1; ipa = 5-substituted isophthalates), with one-dimensional nanochannel structure29,30,31. Use of different ipa ligands can allow for the regular alignment of substituents on the ligands along the channels. Here, we employed styrene-3,5-dicarboxylic acid (S) as the organic linker to produce [Cu(styrene-3,5-dicarboxylate)] n (1S) for the periodic positioning of the styryl groups in the framework. Mixing of the S ligand and Cu2+ ion in methanol at room temperature gave the functional host PCP containing coordinated water (1S⊃H2O). Single-crystal X-ray diffraction analysis showed that the as-synthesized host has two types of one-dimensional channels with pore diameters of ca 6 Å (hexagonal channels) and 4 Å (triangular channels) along the c-axis (Fig. 2a, Supplementary Figs. 1, 2 and Supplementary Table 1). In the larger hexagonal channels, two crystallographically independent styryl groups are arranged alternatively along the channels while the styryl groups of adjacent wall planes point in opposite directions. Thus, styryl groups on each plane of the hexagonal channels were regularly aligned at a distance of 6.8 Å along the channel direction (Fig. 2b), resulting in the periodic arrangement of polymerizable units along the one-dimensional channels.
Schematic illustration of sequence-regulated radical copolymerization using PCPs. A vinyl monomer (X) is pre-immobilized at a regular interval along the nanochannels of a PCP (PCP⊃X). Another vinyl monomer (Y) is then incorporated into the PCP, giving a host–guest composite (PCP⊃(X + Y)). Polymerization of the monomers in the composite followed by the removal of host structure produces sequence-regulated copolymers reflecting on the periodicity of the PCP nanochannels
Crystal structure of host PCP. Views of the nanochannel structure of 1S⊃H2O along the c-axis (a) and a-axis (b). Atoms: Cu (purple), O (red), C (grey). Styryl groups are periodically aligned along the c-axis at a distance of 6.8 Å on each face of the hexagonal channel. H atoms and one of the disordered vinyl moieties have been omitted for clarity
Radical copolymerization of acrylonitrile in PCP
For the copolymerization in 1S, we used acrylonitrile (A) as a guest monomer with molecular dimensions (4.3 × 5.6 Å2) comparable to the size of the hexagonal channel in 1S⊃H2O. According to the well-established relative reactivities in vinyl copolymerization, the terminal radical group of A would preferentially react with the styrene derivatives32, facilitating smooth chain growth along the hexagonal channels of 1S. As the first step for the copolymerization, the A monomer was fully introduced into a degassed host (1S) by soaking 1S in neat A and subsequent removal of excess A outside the host crystals by evacuation, giving a host–guest composite (1S⊃A). X-ray powder diffraction (XRPD) measurement showed that the peak positions of 1S⊃A are the same as those of the hydrated host (1S⊃H2O), showing the maintenance of the crystalline framework structure upon monomer inclusion (Fig. 3, Supplementary Fig. 3). The A/S feed ratio in 1S⊃A was found to be 42/58, as determined by 1H nuclear magnetic resonance (NMR) measurement (Supplementary Fig. 4). Radical copolymerization in the pores of 1S was induced by heating 1S⊃A with 2,2′-azobis(isobutyronitrile) (AIBN) at 70 °C for 48 h under nitrogen atmosphere. The lack of change in the XRPD profiles of the composite before and after heating clearly indicated that the crystal structure of the host was retained during the copolymerization (Fig. 3). In addition, scanning electron microscopy and particle size analysis showed the maintenance of morphology and particle size distribution of 1S, indicating that the copolymerization proceeded only inside the host (Supplementary Figs. 5 and 6). The addition of dilute HCl to the heated composite led to the decomposition of the framework of 1S, followed by washing with ethanol to give a poly(A-co-S) copolymer denoted as P1. In this polymerization system, gram scale synthesis of P1 was possible if we employed a larger amount of 1S. In addition, the host PCP framework could be recycled efficiently by the recrystallization of unreacted S monomer with Cu ion after the decomposition process (Supplementary Methods).
Characterizations of copolymer synthesized in PCP
Formation of the copolymer between A and S in the channels of 1S was fully confirmed by infrared, 1H NMR and 13C NMR spectroscopies of P1 (Supplementary Figs. 7–10). The homopolymer of A (polyacrylonitrile) was not obtained, despite the possible accommodation of A in the small triangular pores of 1S, because of the unpolymerizable monomer arrangement as well as the inaccessibility of the initiator (AIBN) to the narrow channels. In fact, a characteristic peak for polyacrylonitrile was not detectable at 2θ = 17° in the XRPD pattern of P1 (Supplementary Fig. 11)33. Gel permeation chromatography measurement of P1 after methylation of the carboxylic group34 of S showed that the number-average molecular weight (Mn) and polydispersity (Mw/Mn) of P1 were 20,000 and 1.6, respectively (Supplementary Figs. 12 and 13). It should be noted that the compositional ratio in P1 was calculated to be A/S = 75/25, as determined by peak integration of 1H NMR and elemental analysis (Supplementary Fig. 8), which was greatly different from the initial A/S feed ratio (42/58) in 1S⊃A (Supplementary Fig. 4). This result contrasted highly with those obtained from copolymerization between free A and S monomers in N,N-dimethylformamide (DMF) solution, where statistically random copolymers (R1–6) with A/S compositions close to their monomer feed ratios were obtained.
Sequence analysis of copolymer
Analysis of the 1H NMR spectrum in the aromatic region of P1 implied the feasibility of the sequence regulation in the host–guest copolymerization between 1S and A (Fig. 4). In the spectra of the random copolymers with the composition of S unit higher than 17 mol% (R3–6), the peak for aromatic protons of S was found to broaden with a shift towards higher magnetic field, as was also seen in the spectrum of the homopolymer of S, because of the shielding effect from the neighbouring bulky S units in the polymer chains35. In contrast, the aromatic proton peaks for the S units in P1 were relatively sharp and only detectable at a lower magnetic field (δ = 7.8–8.4 ppm) despite the adequate content of the S unit (25 mol%), suggesting the distribution of solitary S units in continuous A linkages. 13C NMR spectroscopy is also a powerful method to prove the regulation of monomer sequences in copolymers14,36,37. The predominant triad sequences of P1 could be determined by analyzing the shape and chemical shift of signals in comparison with those of homopolymers and random copolymers (R1–6). Figure 5a shows the spectra in the region for the C=O group of the S unit (δ = 165–168 ppm). In this analysis, a peak for CC=O in the homopolymer of S comprising only the SSS triad appeared at 166.0 ppm, and this carbonyl peak shifted to lower magnetic field with increasing content of A unit in the random copolymers. Note that the CC=O peak for P1 was found at 166.5 ppm, and the location of this signal was almost the same as that of R1 (A/S = 95/5) and R2 (A/S = 87/13) with the statistically preferred triad of ASA. Thus, the formation of ASA should be predominant in the structure of P1, as is also supported by the 1H NMR result (Fig. 4). In a similar manner, the A-centred triad of P1 could be estimated by analysis of the CCH signals of A appearing in the aliphatic region (Fig. 5b). Although copolymers with a lower composition of A (R5, R6) showed featureless broad peaks at 26.5–27.0 ppm, copolymers with high A content (R1–R4) presented three clear peaks in this region. These characteristic peaks were also observed in the spectrum of P1, showing that the composition of P1 is similar to R1–R4 with the predominant triads of AAA and SAA.
Structural characterization of polymers using 1H NMR. The 1H NMR spectra of (co)polymers synthesized in 1S (P1) and in DMF (R1-6 and polyS). With decreasing S unit in polymers prepared in DMF, peaks for the aromatic protons of the S unit (6.5–8.5 ppm) shifted to lower magnetic field because of the lower shielding effect around S in A-rich copolymers. Although the composition of S in P1 is larger than those of R3 and R4, peaks at 6.5–7.6 ppm were not observed, indicating that S units in P1 are solitary among the repeating A units
Structural characterization of polymers using 13C NMR. 13C NMR spectra focusing on carbonyl (a) and methine carbons (b) of polymers, from which S- and A-centred triads can be analyzed, respectively. Plausible monomer sequences of random copolymers (R1–6) are shown together with their NMR spectra. The predominant triads of P1 could be estimated to be ASA, AAS and AAA by comparison of the peak shapes and peak positions for P1, random copolymers (R1–6) and polyS
The preferential formation of ASA, AAA and SAA triads in the P1 chains was strongly supported by the crystal structure of 1S⊃H2O. As shown in Fig. 2, styryl groups in 1S are regularly aligned at a distance of 6.8 Å towards the channel direction, which cannot induce the direct reaction between the styryl units. Thus, for the S-centred triad, formation of the ASA triad was only allowed during the copolymerization in 1S⊃A. In the same way, the distance between the styryl units along the channels is too long to form the SAS triad, resulting in the selective formation of AAA and SAA for the A-centred triad in P1. Based on the A/S composition (75/25) and detected triads (Fig. 5), the formation of repetitive SAAA is the most likely sequence in the structure of P1.
Radical copolymerization at different monomer feed ratios provides an insight into the monomer sequence in the resulting copolymer. Loading amount of A was controlled by co-introduction with acetonitrile in the host, followed by the copolymerization of A with the S units in the pores. This polymerization reaction proceeded smoothly, showing that the non-polymerizable solvent molecules do not interfere with the diffusion of the free A monomers in the nanochannels. Note that both 1H and 13C NMR spectra of the resulting copolymers were similar to those of P1, showing the predominant ASA, AAS and AAA triads in the copolymer chains (Supplementary Figs. 14 and 15). In contrast to the solution copolymerization system, the A/S ratio in the copolymers from 1S was close to that of P1 (A/S = 3/1) regardless of the initial monomer feed ratio, as determined by peak integration of the 1H NMR spectra (Fig. 6 and Supplementary Fig. 14). Independency of the copolymer composition is a key behaviour to prove the regulation of monomer sequence in polymers11,12, and the constant A/S ratio of the copolymers strongly supports the predominant repetitive SAAA sequence in the copolymer chains.
Copolymer composition plots for the copolymerization of A with S. A series of A ratio in the generated copolymers were plotted against their initial A ratio for the copolymerization of A with S in 1S (filled red circle) and in DMF (open circle). Note that the maximum initial ratio of A is 0.42 in the channels of 1S due to the limitation of introduction amount of A into the host
Computational simulation
To clarify the mechanism of this highly regulated reaction system, we performed a computational analysis on the copolymerization of A with 1S using replica-exchange molecular dynamics (REMD) simulations38,39 and density functional theory (DFT) calculations40. In spite of the possible multiple connectivity between S units via A chains, REMD simulations suggested that a propagation reaction involving two adjacent styryl groups at different planes of the hexagonal channels causes large steric hindrance for A around the terminal S radical, resulting in no further polymerization, as is expected from the host crystal structure (Supplementary Figs. 16 and 17a). In contrast, copolymerization of A with 1S can proceed smoothly along the arrays of the styryl units at one face of the channel, picking the regularly positioned styryl moieties into the P1 chains (Supplementary Fig. 17b and c). Based on this reaction position, we executed DFT calculations on the reaction barriers for the propagation reaction of the terminal A radicals in ~SA n • (n = 2, 3; radicals are denoted by a dot) chains with free A or styryl monomer immobilized in the host. Taking the difference in the reaction barriers together with the collision frequency estimated from REMD simulations into account, the ~SAA• is likely to react with free A monomer to form ~SAAA• radical with very high selectivity (>99%). Note that the resulting ~SAAA• would favour a reaction with the immobilized S monomer rather than free A, giving a ~SAAAS• chain (Supplementary Fig. 18). These results are fairly consistent with those of the NMR analysis and copolymer composition of P1, which shows the validity of the formation of the SAAA repeat unit as a predominant sequence.
Radical copolymerization of another guest monomer in PCP
The generality of our methodology for the preparation of XYYY copolymers was confirmed using methyl vinyl ketone (M) as another guest monomer, where this monomer also has a tendency to crosspropagate with styryl monomers during the copolymerization. Radical polymerization of M was performed in 1S, giving a copolymer (P2) with the composition of M/S = 76/24, as determined by 1H NMR spectroscopy (Supplementary Figs. 19–23). Clearly, this M/S ratio is comparable to the A/S composition in P1. 1H and 13C NMR studies on P2 showed that the S units in P2 were solitary among M units with the probable triad sequences of MSM, MMS and MMM, similar to the case of P1. These results strongly suggested that the formation of P2 in the channels of 1S would also be regulated to give a repetitive SMMM sequence (Supplementary Figs. 24 and 25).
Discussion
We have established an approach to sequence-controlled radical copolymerization using the regular structure of a PCP as a template. The capability of PCPs to transcribe their periodic structure into a product was demonstrated. The S monomer anchored into the host PCP was copolymerized with guest vinyl monomers, producing copolymers with a predominant XYYY sequence. Our methodology exploiting crystalline templates constructed by self-assembly of metal ions and ligands provides an easy access to the sequence-regulated polymerization with scalability and recyclability. In addition, this work achieved successfully sequence-controlled radical copolymerization using an artificial polymeric template. Preparation of polymeric templates with well-defined structures is generally quite difficult because of the requirement for complicated organic synthesis with many reaction steps. Moreover, use of small templates in solution copolymerizations often led to undesired crosslinking reactions41. Our methodology using PCP templates could overcome these problems, showing the remarkable advancement in this field. Owing to the high designability of PCPs, predetermination of monomer units in PCP frameworks can allow for materials platforms to accomplish many other periodic sequences for copolymers. We believe that this study opens the door to the utilization of crystalline templates for controlled monomer sequences in copolymers.
Methods
Synthesis of 1S⊃H2O
Single crystals of 1S⊃H2O were synthesized as follows. Slow diffusion of a methanol solution of S into a methanol solution of Cu(NO3)2•3H2O and pyridine afforded sky-blue polycrystals in a few days. They were cut into small single crystals and then used for the single-crystal X-ray diffraction. A crystalline powder sample of 1S⊃H2O was prepared as follows. Methanol (200 mL) solutions of S (4.00 g, 20.8 mmol) and Cu(NO3)2•3H2O (5.03 g, 20.8 mmol) were mixed and stirred for 12 h after the addition of pyridine (1.68 mL, 20.8 mmol). The mother liquor was decanted and the light blue solid was washed with methanol to remove unreacted materials. Light blue powder (2.85 g) was obtained after drying under vacuum for 2 h at room temperature.
Copolymerization of guest vinyl monomers with S in 1S
A typical procedure for copolymerization of A and S in the nanochannels of 1S. The degassed host compound 1S was obtained (168 mg) by evacuation (<0.2 kPa) at 110 °C for 2 h, and was then immersed in the solution of A (1 mL) and AIBN (3 mg) in a 30-mL flask under nitrogen atmosphere. The mixture was left for 30 min to incorporate the monomer and the initiator into 1S. The host–guest composite (1S⊃A) was obtained after removing excess monomer outside the PCP crystals completely by evacuation at 8.0 kPa. 1S⊃A was heated at 70 °C for 48 h to copolymerize A with the styryl groups immobilized in the frameworks of 1S. The reaction was quenched by the addition of methanol. After removing the supernatant solution and drying the compound, 1 M HCl was added to decompose the PCP framework of 1S as well as to acidify the carboxylate group of the resulting copolymer. P1 was obtained by washing the product with ethanol, followed by drying under reduced pressure at room temperature (35 mg). The C/N atomic ratio of P1 was 5.194/0.8307 (C/N mass ratio: 62.33/11.63), as calculated from elemental analysis, showing that the A/S ratio in P1 was determined to be 75:25. Gram scale synthesis of P1 was conducted using 5.40 g of 1S, generating 1.09 g of P1. Polymerization of A in 1S with different loading amounts of monomer was also performed according to the procedure described above after the co-introduction of acetonitrile into the host. For the synthesis of P2 in 1S, we used the same procedure other than the polymerization temperature (100 °C) and washing solvent (ethyl acetate).
Data availability
The X-ray crystallographic coordinates for the structure reported in this article have been deposited at the Cambridge Crystallographic Data Centre (CCDC), under deposition number CCDC 1430041. These data can be obtained free of charge from the Cambridge Crystallographic Data Centre via www.ccdc.cam.ac.uk/data_request/cif. All relevant data are available from the authors upon reasonable requests.
References
Alberts, B. et al. Molecular Biology of the Cell 4th edn (Garland Science, New York, 2002).
Merrifield, R. B. Solid phase peptide synthesis. I. The synthesis of a tetrapeptide. J. Am. Chem. Soc. 85, 2149–2154 (1963).
Barnes, J. C. et al. Iterative exponential growth of stereo- and sequence-controlled polymers. Nat. Chem. 7, 810–815 (2015).
Lee, I.-H., Kim, H. & Choi, T.-M. Cu-catalyzed multicomponent polymerization to synthesize a library of poly(N-sulfonylamidines). J. Am. Chem. Soc. 135, 3760–3763 (2013).
Solleder, S. C. & Meier, M. A. R. Sequence control in polymer chemistry through the Passerini three-component reaction. Angew. Chem. Int. Ed. 53, 711–714 (2014).
Xi, W. et al. Clickable nucleic acids: sequence-controlled periodic copolymer/oligomer synthesis by orthogonal thiol-X reactions. Angew. Chem. Int. Ed. 54, 14462–14467 (2015).
Satoh, K., Ozawa, S., Mizutani, M., Nagai, K. & Kamigaito, M. Sequence-regulated vinyl copolymers by metal-catalysed step-growth radical polymerization. Nat. Commun. 1, 6 (2010).
ten Brummelhuis, N. Controlling monomer-sequence using supramolecular templates. Polym. Chem. 6, 654–667 (2015).
Chen, G.-Q., Wu, Z.-Q., Wu, J.-R., Li, Z.-C. & Li, F.-M. Synthesis of alternating copolymers of N-substituted maleimides with styrene via atom transfer radical polymerization. Macromolecules 33, 232–234 (2000).
Rätzsch, M. Alternating maleic anhydride copolymers. Prog. Polym. Sci. 13, 277–337 (1988).
Hirai, H. Mechanism of alternating copolymerization of acrylic monomers with donor monomers in the presence of Lewis acid. J. Polym. Sci. Macromol. Rev. 11, 47–91 (1976).
Satoh, K., Matsuda, M., Nagai, K. & Kamigaito, M. AAB-sequence living radical chain copolymerization of naturally occurring limonene with maleimide: an end-to-end sequence-regulated copolymer. J. Am. Chem. Soc. 132, 10003–10005 (2010).
Hibi, Y., Tokuoka, S., Takaya, T., Ouchi, M. & Sawamoto, M. Design of AB divinyl “template monomers” toward alternating sequence control in metal-catalyzed living radical polymerization. Polym. Chem. 2, 341–347 (2011).
Hibi, Y., Ouchi, M. & Sawamoto, M. Sequence-regulated radical polymerization with a metal-templated monomer: repetitive ABA sequence by double cyclopolymerization. Angew. Chem. Int. Ed. 50, 7434–7437 (2011).
Zamfir, M. & Lutz, J.-F. Ultra-precise insertion of functional monomers in chain-growth polymerizations. Nat. Commun. 3, 1138 (2012).
Lutz, J.-F. Sequence-controlled polymerizations: the next Holy Grail in polymer science? Polym. Chem. 1, 55–62 (2010).
Schmidt, B. V. K. J., Fechler, N., Falkenhagen, J. & Lutz, J.-F. Controlled folding of synthetic polymer chains through the formation of positionable covalent bridges. Nat. Chem. 3, 234–238 (2011).
Zamfir, M., Theato, P. & Lutz, J.-F. Controlled folding of polystyrene single chains: design of asymmetric covalent bridges. Polym. Chem. 3, 1796–1802 (2012).
Yaghi, O. M. et al. Reticular synthesis and the design of new materials. Nature 423, 705–714 (2003).
Kitagawa, S., Kitaura, R. & Noro, S.-i Functional porous coordination polymers. Angew. Chem. Int. Ed. 43, 2334–2375 (2004).
Férey, G. & Serre, C. Large breathing effects in three-dimensional porous hybrid matter: facts, analyses, rules and consequences. Chem. Soc. Rev. 38, 1380–1399 (2009).
Uemura, T., Yanai, N. & Kitagawa, S. Polymerization reactions in porous coordination polymers. Chem. Soc. Rev. 38, 1228–1236 (2009).
Uemura, T., Horike, S. & Kitagawa, S. Polymerization in coordination nanospaces. Chem. Asian J. 1, 36–44 (2006).
Uemura, T., Mochizuki, S. & Kitagawa, S. Radical copolymerization mediated by unsaturated metal sites in coordination nanochannels. ACS Macro Lett. 4, 788–791 (2015).
Uemura, T., Ono, Y. & Kitagawa, S. Radical copolymerizations of vinyl monomers in a porous coordination polymer. Chem. Lett. 37, 616–617 (2008).
Wei, Y.-S. et al. Coordination templated [2+2+2] cyclotrimerization in a porous coordination framework. Nat. Commun. 6, 8348 (2015).
Yang, S.-Y. et al. Crystallographic snapshots of the interplay between reactive guest and host molecules in a porous coordination polymer: stereochemical coupling and feedback mechanism of three photoactive centers triggered by UV-induced isomerization, dimerization, and polymerization reactions. J. Am. Soc. Chem. 136, 558–561 (2014).
Park, I.-H. et al. Formation of a syndiotactic organic polymer inside a MOF by a [2+2] photo-polymerization reaction (stereoregular polymerization). Angew. Chem. Int. Ed. 127, 7421–7425 (2015).
Mohideen, M. I. H. et al. Protecting group and switchable pore-discriminating adsorption properties of a hydrophilic–hydrophobic metal–organic framework. Nat. Chem. 3, 304–310 (2011).
Mallick, A., Garai, B., Díaz, D. D. & Banerjee, R. Hydrolytic conversion of a metal–organic polyhedron into a metal–organic framework. Angew. Chem. Int. Ed. 52, 13755–13759 (2013).
Sato, H. et al. Self-accelerating CO sorption in a soft nanoporous crystal. Science 343, 167–170 (2014).
Ōsawa, E., Wang, K. & Kurihara, O. p-Vinylbenzoic acid: a convenient preparation, copolymerization, and examination as dye receptive modifier for acrylic fibers and as ion exchange resin component. Makromol. Chem. 83, 100–112 (1965).
Bashir, Z. Co-crystallization of solvents with polymers: the X-ray diffraction behavior of solvent-containing and solvent-free polyacrylonitrile. J. Polym. Sci. B 32, 1115–1128 (1994).
Belov, P., Campanella, V. L., Smith, A. W. & Priefer, R. Microwave-assisted methylation of phenols with DMF-DMA. Tetrahedron Lett. 52, 2776–2779 (2011).
Williams, D. J. Nuclear magnetic resonance studies of poly(N-vinylcarbazole). Macromolecules 3, 602–605 (1970).
Kim, Y. & Harwood, H. J. Analysis of sequence distribution in methyl methacrylate–methyl acrylate copolymers by 13C NMR spectroscopy. Polymer 43, 3229–3237 (2002).
Brar, A. S. & Sunita. Determination by 13C-NMR spectroscopy of the microstructure of copolymers of acrylic acid with vinyl acetate. Eur. Polym. J. 1, 17–20 (1991).
Sugita, Y. & Okamoto, Y. Replica-exchange molecular dynamics method for protein folding. Chem. Phys. Lett. 314, 141–151 (1999).
Case, D. A. et al. The amber biomolecular simulation programs. J. Comput. Chem. 26, 1668–1688 (2005).
Frisch, M. J. et al. Gaussian09, Revision A.02 (Gaussian, Inc., Wallingford, CT, 2009).
Jantas, R. Copolymerization of multimethacrylate with vinyl monomers. Acta Polym. 42, 539–544 (1991).
Acknowledgements
This work was supported by CREST-JST (JPMJCR1321) and JSPS KAKENHI Grant Number JP16H06517 (Coordination Asymmetry). The authors would like to thank Dr. Hiroshi Sato (The University of Tokyo) for valuable technical discussions. We also acknowledge Dr. Nobuhiro Yasuda (Japan Synchrotron Radiation Research Institute, SPring-8) for single-crystal X-ray diffraction measurements.
Author information
Authors and Affiliations
Contributions
T.U. conceived and directed the project. T.U. and S.M. designed and performed the experiments. N.O. contributed to single-crystal X-ray diffraction analysis. M.T. and M.N. performed the computational analysis. S.M., S.K. and T.U. discussed the results and wrote the paper.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Mochizuki, S., Ogiwara, N., Takayanagi, M. et al. Sequence-regulated copolymerization based on periodic covalent positioning of monomers along one-dimensional nanochannels. Nat Commun 9, 329 (2018). https://doi.org/10.1038/s41467-017-02736-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-017-02736-1
- Springer Nature Limited
This article is cited by
-
Controlled assemblies of conjugated polymers in metal−organic frameworks
Polymer Journal (2022)