Abstract
To achieve a better material for uncooled infrared (IR) detector, polycrystalline VO2(B) thin films with layered W-doping were fabricated on Si substrates by magnetron sputtering, and the best temperature coefficient of resistance (TCR) value reached −4.1%/K. The film synthesis was in a two-step route, first deposition at room temperature and then post-deposition annealing at 450 °C, to better control the crystallization behavior. Various transmission electron microscopy (TEM) methods were employed to investigate three sets of multi-layered films with different deposition time, 10, 20, and 30 min, with especial emphasis on the effect of layered W-doping scheme on the formation of multiple VO2(B) layers. Spatial-resolved energy dispersive X-ray spectroscopy (EDS) revealed the alternative patterns of W-rich layers and W-poor layers, while the thinner films exhibited better crystallinity and texturing. By comparison with an as-deposited film, it was found that the inter-diffusion between the two types of layers was completed in the deposition step while both remained in amorphous structure. A stable W solution of about 8 cat% in VO2(B) layers measured from all these films indicated that the layered doping can tailor the multi-layered microstructure to optimize the performance of VO2(B) films.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
Émond N, Hendaoui A, Chaker M. Low resistivity WxV1−xO2-based multilayer structure with high temperature coefficient of resistance for microbolometer applications. Appl Phys Lett 2015, 107: 143507.
Fieldhouse N, Pursel SM, Horn MW, et al. Electrical properties of vanadium oxide thin films for bolometer applications: Processed by pulse dc sputtering. J Phys D: Appl Phys 2009, 42: 055408.
Wang H, Yi X, Chen S. Low temperature fabrication of vanadium oxide films for uncooled bolometric detectors. Infrared Phys Techn 2006, 47: 273–277.
Venkatasubramanian C, Cabarcos OM, Allara DL, et al. Correlation of temperature response and structure of annealed VOx thin films for IR detector applications. J Vac Sci Technol A 2009, 27: 956.
Morin FJ. Oxides which show a metal-to-insulator transition at the neel temperature. Phys Rev Lett 1959, 3: 34–36.
Jian J, Chen A, Zhang W, et al. Sharp semiconductor-tometal transition of VO2 thin films on glass substrates. J Appl Phys 2013, 114: 244301.
Makarevich AM, Sadykov II, Sharovarov DI, et al. Chemical synthesis of high quality epitaxial vanadium dioxide films with sharp electrical and optical switch properties. J Mater Chem C 2015, 3: 9197–9205.
Takami H, Kawatani K, Kanki T, et al. High temperature-coefficient of resistance at room temperature in W-doped VO2 thin flms on Al2O3 substrate and their thickness dependence. Jpn J Appl Phys 2011, 50: 055804.
Wan D, Xiong P, Chen L, et al. High-performance thermal sensitive W-doped VO2(B) thin film and its identification by first-principles calculations. Appl Surf Sci 2017, 397: 30–39.
Leroux Ch, Nihoul G, Tendeloo GV. From VO2(B) to VO2(R) theoretical structures of VO2 polymorphs and in situ electron microscopy. Phys Rev B 1998, 57: 5111–5121.
Guinneton F, Sauques L, Valmalette JC, et al. Comparative study between nanocrystalline powder and thin of vanadium dioxide VO2: Electrical and infrared properties. J Phys Chem Solids 2001, 62: 1229–1238.
Mao Z, Wang W, Liu Y, et al. Infrared stealth property based on semiconductor (M)-to-metallic (R) phase transition characteristics of W-doped VO2 thin films coated on cotton fabrics. Thin Solid Films 2014, 558: 208–214.
Sahana MB, Subbanna GN, Shivashankar SA. Phase transformation and semiconductor–metal transition in thin films of VO2 deposited by low-pressure metalorganic chemical vapor deposition. J Appl Phys 2002, 92: 6495–6504.
Chen A, Bi Z, Zhang W, et al. Textured metastable VO2(B) thin films on SrTiO3 substrates with significantly enhanced conductivity. Appl Phys Lett 2014, 104: 071909.
Rúa A, Díaz RD, Lysenko S, et al. Semiconductor-insulator transition in VO2(B) thin films grown by pulsed laser deposition. J Appl Phys 2015, 118: 125308.
Lee S, Ivanov IN, Keum JK, et al. Epitaxial stabilization and phase instability of VO2 polymorphs. Sci Rep 2016, 6: 19621.
Srivastava A, Rotella H, Saha S, et al. Selective growth of single phase VO2 (A, B, and M) polymorph thin films. APL Mater 2015, 3: 026101.
Sahana MB, Dharmaprakash MS, Shivashankar SA. Microstructure and properties of VO2 thin films deposited by MOCVD from vanadyl acetylacetonate. J Mater Chem 2002, 12: 333–338.
Wang X-J, Fei Y-J, Xiong Y-Y, et al. Vanadium oxide thin films deposited on indium tin oxide glass by radio-frequency magnetron sputtering. Chinese Phys 2002, 11: 737–740.
Miyazaki H, Utsuno F, Shigesato Y, et al. The structural characteristics of VOx films prepared by He-introduced reactive RF unbalanced magnetron sputtering. Thin Solid Films 1996, 281–282: 436–440.
Liu H, Wan D, Ishaq A, et al. Sputtering deposition of sandwich-structured V2O5/metal (V, W)/V2O5 multilayers for the preparation of high-performance thermally sensitive VO2 thin films with selectivity of VO2(B) and VO2(M) polymorph. ACS Appl Mater Interfaces 2016, 8: 7884–7890.
Wang XJ, Li HD, Fei YJ, et al. XRD and Raman study of vanadium oxide thin films deposited on fused silica substrates by RF magnetron sputtering. Appl Surf Sci 2001, 177: 8–14.
Xiong P. Study on the preparation and properties of tungsten graded doping vanadium oxide (V1−xWxO2) thermal films. Master Thesis. Shanghai University, 2016.
Pan M, Zhong HM, Wang SW, et al. Properties of VO2 thin film prepared with precursorVO(acac)2. J Cryst Growth 2004, 265: 121–126.
Desré PJ, Yavari AR. Suppression of crystal nucleation in amorphous layers with sharp concentration gradients. Phys Rev Lett 1990, 64: 1533–1536.
Liddiard CK, Reinhold O, Ringh U, et al. Test structures and performance analysis for uncooled resistance bolometer detector arrays. In: Proceedings of the SPIE 3379, Infrared Detectors and Focal Plane Arrays V, 1998: 115–125
Goodenough JB. The two components of the crystallographic transition in VO2. J Solid State Chem 1971, 3: 490–500.
Li J-H, Yi Y-N. Temperature coefficient of resistance of VO2 polycrystalline film formed by ion beam enhanced deposition. Acta Phys Sin 2004, 53: 2683–2686.
Felde B, Niessner W, Schalch D, et al. Plasmon excitation in vanadium dioxide films. Thin Solid Films 1997, 305: 61–65.
Acknowledgements
This work was financially supported by the National Natural Science Foundation of China under Grant Nos. 51532006 and 51325203, Shanghai Municipal Science and Technology Commission of Shanghai Municipality under Grant No. 16DZ2260600, and the 111 Project (D16002). We are grateful to the Shanghai Institute of Ceramics for technical assistance in TEM and SEM experiments, as well as to Prof. R. Huang of East China Normal University for TEM specimen preparations.
Author information
Authors and Affiliations
Corresponding author
Additional information
This article is published with open access at Springerlink.com
Rights and permissions
Open Access The articles published in this journal are distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Zhang, C., Hu, D., Gu, H. et al. Crystallization and inter-diffusional behaviors in the formation of VO2(B) thin film with layered W-doping. J Adv Ceram 6, 196–206 (2017). https://doi.org/10.1007/s40145-017-0231-7
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40145-017-0231-7