Abstract
Vinyl acetate radical emulsion polymerization in water with GF51 silane co-monomer was performed by semi continuous way. The GF51 impacts on dispersion rheology as well on films and bonding strength properties were determined. It should be stated that even low quantities of GF51 (up to 6% from VAc) determined high viscosity of dispersions. The GF51 modified films have low water absorption and high affinity to glass. Molecular mass and thermal properties of GF51 modified polymers were determined accordingly.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
Tonnar, J., Pouget, E., Lacroix-Desmazers., P. and Boutevin, B., Eur. Polym. J., 2008, 44: 318
Maynard, D.H., Lyu, S.P., Fredrickson, H.G., Wudl, F. and Chmelka, F.B., Polymer, 2001, 42: 7567
Jia, X., Li, Y., Cheng, Q., Zhang, S. and Zhang, B., Eur. Polym. J., 2007, 43: 1123
Kruenate, J., Tongpool, R. and Kongrat, P., Journal of Metastable and Nanocrystalline Materials, 2005, 23: 227
Nguyen, V., Yoshida, W. and Cohen, Y., J. Appl. Polym. Sci., 2002, 87(2): 300
Geniosil GF51 Material Safety Data Sheet for US market, http://sdb.wacker.com/pf/e/result/report.jsp?PLANGU=E&PSYS=2&PSSN=490&PREP=00000000000000000030&PRES=1172&PSPEC=R, Cited 9 July 2012
Mitschka, P., Reological Acta, 1982, 21: 207
Brandrup, J., Immergut, E.H. and Grulke, E.A., in “Polymer handbook, fourth edition”, John Wiley & Sons, New York, VII-68, 1999
Sheen Pendulum Hardness Rocker datasheet, http://www.sheeninstruments.com/datasheets/pen2.pdf, Cited 9 July 2012
Woodward, P.R., Contact Angle Measurements Using the Drop Shape Method, http://www.firsttenangstroms.com/pdfdocs/CAPaper.pdf, Cited 9 July 2012
Naghash, H.J., Mallakpour, S. and Mokhtarian, N., Prog. Org. Coat., 2006, 55: 375
Petrie, E.M., in “Handbook of adhesives and sealants, Vol. 2”, McGraw-Hill, New York, 2007, p. 290
Liu, X.H., Yi, S.P., Li, H.B. and Huang, C., Iranian Polym. J., 2007, 16(3): 207
Zhou, X.H., Tu, W.P. and Xia, Z.P., J. Mater. Prot., 2004, 37: 21
O’Donnell, T., Mesrobian, R.B. and Woodward, A.E., J. Polym. Sci., 1958, 28(116): 171
Bataille, P., Van, B.T. and Pham, Q.B., J. Appl. Polym. Sci., 1978, 22: 3145
Friis, N., “A kinetic study of the emulsion polymerization of vinyl acetate”, Thesis, Technical University of Denmark, Lyngby, 1973
Donescu, D., Gosa, K., Diaconescu, I., Mazare, M. and Carp, N., in “Emulsion polymerization of vinyl acetate”, eds. by El-Aasser, M.S. and Vanderhoff, J.W., Applied Science Publishers, London, 1981, p. 203
Donescu, D., Gosa, K., Ciupitoiu, A. and Languri, I., J. Macromol. Sci., Chem., 1985, A22: 931
Zhu, M.Y., Qiao, W.H., Liu, H.Z. and Sun, Y.L., J. Appl. Polym. Sci., 2008, 107: 624
European Standard EN 204 “Classification of thermoplastic wood adhesives for non-structural applications”, 2005
Vick, C.B., “Adhesive bonding of wood materials”, in “Wood handbook: wood as an engineering material”, Chapter 9, Gen. Tech. Rept. FPL-GRT-113. USDA Forest Serv., Forest Prod. Lab., Madison, WI, 1999, p. 2, http://www.esf.edu/scme/wus/documents/WoodHandbook-fplgtr113.pdf, Cited 9 July 2012
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Dubininkas, M., Buika, G. Dispersion production by semi-continuous radical vinyl acetate emulsion polymerization with silane co-monomer and characterization of final products. Chin J Polym Sci 31, 346–354 (2013). https://doi.org/10.1007/s10118-013-1220-0
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10118-013-1220-0