Abstract
Fine particles of calcium oxide doped cerium dioxide, 2–4 nm in diameter, were prepared by the chemical reaction of CeCl3-CaCl2 mixed aqueous solution and NaOH aqueous solution at pH 6–12 and 40°C followed by the oxidation with hydrogen peroxide. Doping of CaO with CeO2 resulted in decreasing the particle size and consequently, increasing UV shielding efficiency and transparency to visible light. The particle shape of ceria changed significantly depending on the reaction condition, i.e., rod-like particles and spherical particles were formed by the H2O2 oxidation of cerium trihydroxide pH above 8 and below 7, respectively.
Similar content being viewed by others
References
F. IMOTO, T. NANATAKI and S. KANEKO, Ceram. Trans. 1 (1988) 204.
W. P. HSU, L. RÖNNIQIST and E. MATIJEVIC, Langmuir 4 (1988) 31.
P. L. CHEN, I. W. CHEN and S. KANEKO, Am. Cerm. Soc. 76 (1993) 1577.
Y. C. ZHOU and M. N. RAHAMAN, J. Mater. Res. 8 (1993) 1680.
A. TSCH ÖPE and J. Y. YING, Nanostruct. Master. 4 (1994) 617.
Y. ZHOU, R. J. PHILLIPS and J. A. SWITZER, J. Amer. Ceram. Soc. 78 (1995) 981.
M. HIRANO and E. KATO, ibid. 79 (1996) 777.
W. CHEBGYUN, Q. YITAI, W. CHANGSUI, Y. LI and Z. GUIWEN, Mater. Sci. Eng. B39 (1996) 160.
T. MASUI, K. FUJIKAWA, K. MACHIDA, T. SAKATA, H. MORI and G. ADACHI, Chem. Mater. 9 (1997) 2197.
T. MASUI, K. M ACHIDA, T. SAKATA, H. MORI and G. ADACHI, J. Alloys Compounds (1997) 127.
X. YU, F. LI, X. YE, X. XIN and Z. XUE, J. Amer. Ceram. Soc. 83 (2000) 964.
S. YABE and S. MOMOSE, J. Soc. Cosmet. Chem. Jpn. 32 (1998) 372.
S. YABE, Rare Earth 35 (1999) 47.
E. MATIJEVIC, Langmuir 10 (1994) 8.
E. MATIJEVIC and W. P. HSU, J. Colloid Interface Sci. 118 (1987) 506. Received 3 May and accepted 2 October 2001 687
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Yamashita, M., Kameyama, K., Yabe, S. et al. Synthesis and microstructure of calcia doped ceria as UV filters. Journal of Materials Science 37, 683–687 (2002). https://doi.org/10.1023/A:1013819310041
Issue Date:
DOI: https://doi.org/10.1023/A:1013819310041