Abstract
Novel adsorbents are described for the preconcentration of chromium(VI). Graphene oxide (GO) was modified with various amino silanes containing one, two, or three nitrogen atoms in the molecule. These include 3-aminopropyltriethoxysilane (APTES), N-(3-trimethoxysilylpropyl)ethylenediamine (TMSPEDA), and N1-(3-trimethoxysilylpropyl)diethylenetriamine (TMSPDETA). The resulting GO derivatives were characterized by scanning electron microscopy, X-ray photoelectron spectroscopy, and energy-dispersive X-ray fluorescence spectrometry (EDXRF). Adsorption studies show that these GO based sorbents are highly selective for Cr(VI) in the presence of Cr(III) at pH 3.5. Although the amino silanes applied in modification of GO contain different numbers of nitrogen atoms, the maximum adsorption capacities of GO derivatives are very similar (13.3–15.1 mg·g−1). Such results are in accordance with spectroscopy studies which show that the amount of amino silanes attached to GO decreases in the order of APTES > TMSPEDA > TMSPDETA. The APTES-modified GO was applied to selective and sensitive extraction of Cr(VI) ions prior to quantitation by low-power EDXRF using the Cr Kα line. The Cr(VI) ions need not be eluted from the solid adsorbent. The method has a 0.17 ng·mL−1 detection limit, and the recovery is 99.7 ± 2.2% at a spiking level of 10 ng·mL−1. The method was successfully applied to the determination of Cr(VI) in water samples.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
Chromium is one of the environmental contaminant generated from industrial processes, such as leather tanning, dying, metallurgy, mining, and electroplating. Cr(III) and Cr(VI) are two main forms of chromium which exist in the water system. Both have a significant influence on human health: Cr(III) is an essential ion, whereas Cr(VI) compounds are highly toxic, mutagenic and carcinogenic. Taking this into consideration, it is very important to control hexavalent chromium (chromate) concentration in water. For this reason, the World Health Organization (WHO) has established an upper concentration limit for chromium in drinking water, which equals 50 ng⋅mL−1 [1]. Therefore, the development of new and sensitive analytical methods for chromium speciation in water samples is well-founded. Techniques which are used most commonly for the determination of Cr(VI) species are flame atomic absorption spectrometry (FAAS) [2, 3], electrothermal atomic absorption spectrometry (ETAAS) [4, 5], inductively coupled plasma optical emission spectrometry (ICP-OES) [6, 7], inductively coupled plasma mass spectrometry (ICP-MS) [8, 9], and X-ray fluorescence spectrometry (XRF) [10, 11]. Although, some of these techniques, e.g. ET-AAS or ICP-MS, offer excellent sensitivity and very low detection limits, the chromium speciation requires a preliminary separation of Cr(III) and Cr(VI). Apart from the hyphenated chromatographic techniques [12], the classical solid-phase extraction (SPE) and its miniaturized versions, such as solid-phase microextraction (SPME) or dispersive micro-solid phase extraction (DMSPE), are the most commonly employed techniques for the preconcentration/separation of chromium species. In these techniques, suitable selection of adsorbent is crucial to ensure quantitative retention of the trace elements and, in some cases, selective adsorption. The carbon-based nanomaterials, i.e. carbon nanotubes (CNTs), graphene and graphene oxide (GO), have become more important in SPME or DMSPE due to their excellent properties [13, 14]. However, they are not selective toward metal ions. The improvement of their selectivity can be realized by application of surfactant [15,16,17], suitable chelating agent [18, 19], or through chemical functionalization, e.g. via silanization [20,21,22] or creation of ester or amide bonds [23, 24]. In case of Cr(VI), the amino-functionalized GO seems to be the appropriate adsorbent because the protonated amino groups provide a positive surface charge that is suitable for the adsorption of Cr(VI) anions [25]. In comparison with non-modified GO, the point of zero charge (pHPZC) of amino-derivatives is shifted to the neutral position (pH 6–8). Therefore, the high adsorption of Cr(VI) is observed at pH lower than 6–8. The non-modified GO (pHPZC value of ca. 4) is much more suitable for adsorption of Cr(III) rather than Cr(VI). The adsorption of Cr(III) is observed at pH > 4 [10], whereas, the adsorption of Cr(VI) requires strong acidic solution, and it is not usually quantitative.
In the present work, GO was modified with three different amino silanes containing one, two and three nitrogen atoms in the molecule (GO-1 N, GO-2 N and GO-3 N) for selective adsorption of Cr(VI) ions. The amino-silanized derivatives of GO were characterized by microscopy and spectroscopy techniques. The adsorption of Cr(VI) on modified GO was investigated by batch adsorption experiment including influence of pH, kinetics, and Langmuir and Freundlich isotherm models. GO-1 N was used as an effective adsorbent in DMSPE in order to determine trace amounts of Cr(VI) ions by the energy-dispersive X-ray fluorescence spectrometry (EDXRF). Chromium was quantified directly on membrane, therefore, the Cr(VI) ions did not have to be eluted from the solid adsorbent. The method was applied for the determination of Cr(VI) in various types of environmental water samples.
Experimental
Reagents and solutions
Stock solutions (1 mg·mL−1 of Cr(III) and Cr(VI)), (3-aminopropyl)triethoxysilane (APTES, 99%), N-[3-(trimethoxysilyl)propyl]ethylenediamine (TMSPEDA, 97%) and N1-(3-trimethoxysilylpropyl)diethylenetriamine (TMSPDETA) were purchased from Sigma-Aldrich (Steinheim, Germany, www.sigmaaldrich.com); nitric acid (65%, p.a.), sulfuric acid (98%, p.a.), ethanol (p.a.), ammonium hydroxide solution (25%, p.a.), potassium permanganate (p.a.), sodium nitrite (p.a.) were from POCh (Gliwice, Poland, www.poch.com.pl). Standard solutions were diluted with high purity water obtained from Milli-Q system (Millipore, Molsheim, France, www.merckmillipore.com).
Instruments
The microstructural observations of the GO derivatives were conducted using JEOL-7600F (www.jeol.co.jp/en) scanning electron microscope (SEM) equipped with the Oxford X-ray energy-dispersive spectrometer (EDS). The chemical composition was confirmed by X-ray photoelectron spectroscopy (XPS). Photoelectron spectra were collected using a PHI 5700/660 Physical Electronic spectrometer (www.phi.com) with monochromated Al Kα radiation. The spectra were analyzed with a hemispherical mirror assuring an energy resolution of about 0.3 eV. Three hours after placing the samples in situ at 10−10 hPa vacuum, their surface was clean enough for measurements. The background was subtracted using the Tougaard’s approximation. The EDXRF measurements (chemical composition of GO derivatives and determination of Cr adsorbed on GO derivatives) were performed using an Epsilon 3 spectrometer (Panalytical, Almelo, The Netherlands, www.panalytical.com), equipped with Rh target X-ray tube of a 50 μm Be window and maximum power of 9 W. The X-ray spectra were collected using a thermoelectrically cooled silicon drift detector (SDD) with 8 μm Be window and 135 eV resolution at 5.9 keV. The system is also equipped with 10-position removable sample changer, spinner and five primary filters that can be selected to improve measuring conditions for determined element. Evaluation of spectra was performed using non-linear least squares fitting, based on the AXIL algorithm (Epsilon 3 software). The concentration of Cr in solutions (batch adsorption experiments: pH effect, isotherms, kinetics, sample volume) was determined by ICP-OES using Spectroblue spectrometer (Spectro Analytical Instruments GmbH, Germany, www.spectro.com) and following parameters: polychromator with focal length 750 mm, holographic master grating, wavelength range 165–770 nm; detector: 15 linear CCD arrays, 3648 pixels per array; generator: frequency 27.12 MHz, power 0.7–1.7 kW, air cooled; nebulizer Cross Flow type; exhaust system requirements: torch box: 200–300 m3⋅h−1, generator: 250–300 m3⋅h−1. The wavelength for Cr was 267.716 nm.
Synthesis of GO derivatives
GO was synthesized by the Hummers method. The GO was modified with the molecules containing different number of nitrogen atoms, i.e. APTES, TMSPEDA and TMSPDETA: (C2H5O)3Si(CH2)3NH2, (CH3O)3Si(CH2)3NH(CH2)2NH2 and (CH3O)3Si(CH2)3NH(CH2)2NH(CH2)2NH2. GO derivatives were denoted as GO-1 N, GO-2 N and GO-3 N, respectively. The synthesis of GO, GO-1 N, GO-2 N and GO-3 N is described in detail in Electronic Supplementary Materials.
Adsorption procedure
The batch adsorption experiments were carried out with 5 mg of GO derivatives (GO-1 N, GO-2 N or GO-3 N) and 25 mL of Cr(VI) aqueous solutions with the desired concentration and pH. The pH values of the suspensions were adjusted with nitric acid or ammonia solutions. Then, the suspensions were stirred for 3.0 h to achieve adsorption equilibrium (in the case of adsorption isotherms) or stirred within 30–300 min (kinetic study). The suspensions were filtered through a 0.45 μm membrane filters. The amount of Cr(VI) ions adsorbed on GO derivative q e or q t (mg⋅g−1) was calculated from the difference between the initial concentration C 0 (mg⋅L−1) and equilibrium concentration C e (mg⋅L−1) determined by ICP-OES after filtration: q e = (C 0 − C e )V/m adsorbent , where V is the volume of the suspension, and m adsorbent is the mass of GO derivative.
Preconcentration procedure
The pH value of samples (50 mL) was adjusted to 3.5 using 0.1 mol⋅L−1 HNO3 and/or 0.1 mol⋅L−1 NH3. Then, 1 mL of GO-1 N suspension (5 mg⋅mL−1 GO-1 N) was injected to the analyzed solution and stirred for 180 min. In the next step, the sample was passed through the membrane filter with the use of filtration assembly of 25 mm in diameter (deposit of GO-1 N on membrane filter of 16 mm in diameter). Subsequently, the membrane filter with GO-1 N and Cr(VI) adsorbed on its surface was dried under an IR heater and measured by EDXRF.
Real samples preparation
All environmental water samples were filtered through a Millipore cellulose acetate membrane filter (0.45 μm), acidified with concentrated nitric acid (pH 2) and stored in polyethylene bottles at 4 °C.
Results and discussion
Choice of materials
GO was selected for modification from among many adsorbents for two main reasons: (i) it possess large quantities of functional groups (much higher than oxidized CNTs [14]) that can be modified with amino silanes, (ii) it has serious advantages in the view of EDXRF measurements. The second reason was particularly important because adsorbent collected onto the membrane was directly measured without eluting step. In contrast to nano-oxides (including magnetic nanoparticles), GO contains only carbon, oxygen and hydrogen atoms. Therefore, characteristic radiation of adsorbent is not visible in EDXRF spectrum. Due to the low atomic number of carbon, oxygen, hydrogen, the attenuation of X-ray fluorescent radiation of chromium is very low. Moreover, such features of GO nanosheets as flexibility and softness allow obtaining smooth and durable thin sample after filtration process. These reasons make GO ideal adsorbent for direct EDXRF analysis. GO was modified with amino silanes containing amino groups that can be protonated in acidic solution and are responsible for interaction with anionic species of Cr(VI). The chemical modification significantly improves adsorptive properties of GO toward Cr(VI) but does not worsen its properties in the view of EDXRF measurement (characteristic radiation of nitrogen is not visible in EDXRF spectrum; Si Kα line can be observed in the low-energy EDXRF spectrum).
Characterization of GO-1 N, GO-2 N and GO-3 N
Amino-silanized GO derivatives were characterized by SEM/EDS, EDXRF and XPS. The SEM images presented in Fig. 1 show the highly wrinkled structure of GO derivatives. This structure in concert with the softness and flexibility of nanosheets allow achieving excellent contact with the analyzed solution. SEM/EDS analysis reveals that GO-1 N, GO-2 N and GO-3 N contain 4.3 ± 0.22, 4.3 ± 0.42 and 4.9 ± 0.14% N, respectively. Very similar concentration of N in GO derivatives suggests that TMSPDETA was attached to GO nanosheets in lower degree than TMSPEDA, and TMSPEDA lower than APTES, although GO-1 N, GO-2 N and GO-3 N were synthesized using the same amount of amino silanes. EDXRF analysis (Fig. S1a) confirms that the Si concentration decreases in the order of GO-1 N, GO-2 N and GO-3 N. The synthesized GO-1 N was also characterized by XPS. The results are discussed in Electronic Supplementary Materials (Fig. S1b).
Adsorption of chromium ions on GO-1 N, GO-2 N and GO-3 N
The acidity of sample solution is one of the most important parameters in the adsorption of metal ions. The acidity influences not only the adsorbent surface charge but also the metal species present in solution. The adsorption of Cr(VI) ions on GO modified with three different silanes, such as: APTES, TMSPEDA and TMSPDETA was investigated at pH ranging from 1 to 10. The experimental results for GO-1 N, shown in Fig. 2, indicate that adsorption of Cr(VI) increases at pH ranging from 1 to 3, remains constant at pH from 3 to 4, and decreases at pH 4–10. The maximum adsorption for GO-2 N and GO-3 N is shifted to a little higher pH value. At low pH, Cr(VI) assumes the anionic form, such as HCrO4−, Cr2O72− and CrO42−. Simultaneously, the large quantities of protons in acid solution can protonate amino groups onto the surface of modified GO, that are responsible for electrostatic interaction with anionic species of Cr(VI). Additionally, hydrogen bond interaction between HCrO4− and functional groups (Si-OH and -NH3+) of amino-modified GO can be formed [26, 27]. In basic solution, the negative charge is generated on the surface of adsorbent and electrostatic attraction is not possible. Taking into account the high adsorption of Cr(VI), pH 3.5 was chosen as the optimum pH for further studies (kinetics, adsorption isotherms, and determination of chromium by EDXRF). Adsorption of other metal ions at pH 3.5 is very low or even close to zero (Fig. S2). Fig. 2 also shows the effect of pH on the adsorption of Cr(VI) ions on the non-modified GO. As can be noticed, the maximum adsorption is shifted to acidic solution because GO is stronger acid than its amino-derivatives (pKa of -COOH in the range of 4–5, and pKa of -NH3+ in the range of 7–8 [25]). The efficiency of adsorption of Cr(VI) on GO decreases with the increase of sample pH. The highest value was achieved at pH 1, however, the adsorption is not quantitative. In strong acidic solution, Cr(VI) can be partially reduced to Cr(III): HCrO4− + 7H+ + 3e− → Cr3+ + 4H2O [28], which is not adsorbed on positively charged surface of GO, GO-1 N, GO-2 N and GO-3 N. The influence of pH on the adsorption of Cr(III) was also studied. As can be seen in Fig. 2, the adsorption is close to zero at pH 1–6. Such values can be explained by electrostatic repulsion between ionic species of Cr(III) such as: Cr(H2O)63+, Cr(OH)(H2O)52+, Cr(OH)2(H2O)4+ and the -NH3+ groups that are predominant at acidic solutions. At pH higher than 7 the adsorption % increases, because Cr(III) ions can be chelated through functional groups, as well as, can begin to precipitate as Cr(OH)3. In case of GO the adsorption increases quickly at pH 1–4 and remains constant in broad range of pH from 4 to 10. This is a result of strongly electrostatic interaction between cationic form of Cr(III) and negative surface charge of GO. Besides, Cr(III) ions can be chelated through functional groups on the GO surface.
The adsorption significantly depends on the adsorption time and sample volume. The effect of the sorption time and sample volume on the adsorption of Cr(VI) was investigated for 20–100 mL sample volume during 30–300 min. Fig. S3 shows that adsorption of Cr(VI) on the GO-1 N, GO-2 N and GO-3 N surfaces increases quickly at the beginning of the experiment and then reaches the equilibrium state. The adsorption decreases with increasing sample volume. As can be noticed, quantitative adsorption was achieved in the range of stirring time from 180 to 300 min for examined volumes of sample. From a practical point of view, the analysis of real water samples was performed using the sample volume of 50 mL and sorption time of 180 min. It is also noteworthy here that a dozen samples can be simultaneously prepared using one multiposition magnetic stirrer.
The kinetic data (the pseudo-second order rate adsorption kinetic model, Table S1, Fig. S3) and adsorption isotherms (Langmuir and Freundlich isotherm models, Table S2, Fig. S4) suggest that adsorption of Cr(VI) on GO-1 N, GO-2 N and GO-3 N nanosheets is monolayer coverage and it is controlled by electrostatic interaction between anionic species of Cr(VI) and protonated amino groups onto the surface of GO derivatives. The adsorption capacity is proportional to the number of active sites occupied on the surface of modified adsorbents. The maximum adsorption capacities q max of Cr(VI) on GO-1 N, GO-2 N and GO-3 N are very similar and equal 13.3, 15.1, 14.3 mg⋅g−1, respectively. Such results are in accordance with SEM/EDS analysis that reveals very similar contents of N in GO-1 N, GO-2 N and GO-3 N, i.e. the same number of active sites on the surface of GO derivatives. GO-1 N was selected for determination of Cr(VI) because of the best recovery at pH 3.5 (Fig. 2).
Application of GO-1 N in determination of trace Cr(VI) ions
The synthesized adsorbent was applied in determination of trace hexavalent chromium ions. The procedure is based on DMSPE and consists of following stages: (i) dispersing GO-1 N in aqueous sample adjusted to pH 3.5 and stirring, (ii), collecting GO-1 N with adsorbed Cr(VI) ions on membrane filter via vacuum filtration, (iii) measurement by EDXRF. The flexibility and softness of GO-1 N nanosheets allow preparing smooth and thin samples deposited onto a membrane, which is a crucial issue in XRF spectrometry. In order to study the analytical figures of merit of DMSPE/EDXRF procedure, the calibration curve was obtained by the preparation of a series of Cr(VI) standard solution. Results presented in Table 1 show the linear relationship between analytical signal (corrected peak area) and chromium concentration in aqueous samples in the range of 2–1400 ng·mL−1 range, which is reflected in a correlation coefficient R2 0.9996 (Fig. S5). The recovery value for Cr(VI) is ca. 100%. The relative standard deviation (RSD) characterizing precision of the method is 2.2%, which can be considered as very good for trace analysis. The limit of detection (LOD) and limit of quantification (LOQ) were calculated from the following equations: LOD = (3·k−1)·(R B ·t−1)1/2, where k is the sensitivity of the method, R B is the background count rate in counts·s−1 and t is the counting time, and LOQ = 3·LOD. It’s worth to emphasize that the LOD is ca. 300 times lower than the acceptable maximum contaminant levels for chromium that were established by WHO [1] and the Polish regulations for mineral and bottled water (50 ng⋅mL−1) [29]. The Table 2 shows the comparison of the analytical methods for determination of Cr(VI) using various adsorbents including amino-functionalized materials. The value of LOD depends on detection method used for quantification of chromium. The lowest LODs can be achieved using ICP-OES, and, most of all, ET-AAS. However, the LOD of EDXRF method (0.17 ng⋅mL−1) was obtained with the use of very low-power instrument (9 W X-ray tube) with no gas consumption. Moreover, the DMSPE/EDXRF method requires very small amount of adsorbent, i.e. 100 μg per 1 mL of the liquid sample. Therefore, it can be considered as environmentally friendly and lies in the green analytical chemistry rules. The maximum adsorption capacity (q max = 13.3 mg⋅g−1) is rather moderate. However, it is sufficient for determination of trace Cr(VI). The acidic solution (pH 3.5) is suitable for quantitative adsorption of Cr(VI) and simultaneously prevents the precipitation of some heavy metal ions present in real samples.
The reliability of the procedure was verified by the analysis of five different types of natural water samples. The studies were carried out by the standard addition method on two levels of chromium concentration (10 and 20 ng⋅mL−1). The results presented in Table 3 show the recovery in the range of 89–100%. The advantage of the methodology is good resistance to sample matrix. Since GO-1 N is highly selective toward Cr(VI) at pH 3.5, the speciation analysis can also be performed (Table 4). The total concentration of Cr was calculated after oxidation of Cr(III) to Cr(VI) with KMnO4 according to procedure described in literature [37]. Then, the Cr(III) content was calculated as the difference between total chromium and Cr(VI) concentration. The results presented in Table 4 indicate that method can be successfully applied for speciation of chromium species in real water samples with good recovery and precision.
Conclusions
Novel adsorbents were synthesized by modification of GO with three amino silanes, APTES, TMSPEDA, and TMSPDETA containing one, two and three nitrogen atoms in molecule, respectively. Although GO was modified with amino silane containing different number of nitrogen atoms, the maximum adsorption capacities of synthesized adsorbents were very similar. It suggests that the amount of amino silanes attached to GO nanosheets decreases in the order of APTES > TMSPEDA > TMSPDETA. Such results are in accordance with spectroscopy studies. The maximum adsorption capacity of 13.3–15.1 mg⋅g−1 is rather moderate. However, it is sufficient for determination of trace Cr(VI). The selectivity of GO derivatives toward Cr(VI) ions indicates their potential application in chromium determination and speciation. The quantitative adsorption requires time of 180 min. However, a dozen samples can be simultaneously prepared using one multiposition magnetic stirrer. The adsorbent is collected onto the membrane and measured directly by EDXRF. Therefore, the Cr(VI) ions do not have to be eluted from the solid adsorbent. Very low LOD of 0.17 ng⋅mL−1 was achieved with the use of very small amount of adsorbent (100 μg per 1 mL of aqueous sample) and very low-power instruments (9 W X-ray tube) with no gas consumption. Therefore, the method can be considered as environmentally friendly and lies in the green analytical chemistry rules: reduction in the use of reagents and energy, waste minimization.
References
Guidelines for drinking-water quality, fourth edition. World Health Organization (2011) http://www.who.int/water_sanitation_health/publications/2011/dwq_guidelines/en/. Accessed 13 Dec 2017
Moreira Diniz K, Teixeira Tarley CR (2015) Speciation analysis of chromium in water samples through sequential combination of dispersive magnetic solid phase extraction using mesoporous amino-functionalized Fe3O4/SiO2 nanoparticles and cloud point extraction. Microchem J 123:185–195
Islam A, Ahmad H, Zaidi N, Kumar S (2016) A graphene oxide decorated with triethylene-tetramine-modified magnetite for separation of chromium species prior to their sequential speciation and determination via FAAS. Microchim Acta 183:289–296
Saboori A (2017) A nanoparticle sorbent composed of MIL-101(Fe) and dithiocarbamate-modified magnetite nanoparticles for speciation of Cr(III) and Cr(VI) prior to their determination by electrothermal AAS. Microchim Acta 184:1509–1516
Béni A, Karosi R, Posta J (2007) Speciation of hexavalent chromium in waters by liquid–liquid extraction and GFAAS determination. Microchem J 85:103–108
Munonde TS, Maxakato NW, Nomngongo PN (2017) Preconcentration and speciation of chromium species using ICP-OES after ultrasound-assisted magnetic solid phase extraction with an amino-modified magnetic nanocomposite prepared from Fe3O4, MnO2 and Al2O3. Microchim Acta 184:1223–1232
Khonkayan K, Sansuk S, Srijaranai S, Tuntulani T, Saiyasombat C, Busayaporn W, Ngeontae W (2017) New approach for detection of chromate ion by preconcentration with mixed metal hydroxide coupled with fluorescence sensing of copper nanoclusters. Microchim Acta 184:2965–2974
Peng H, Zhang N, He M, Chen B, Hu B (2015) Simultaneous speciation analysis of inorganic arsenic, chromium and selenium in environmental waters by 3-(2-aminoethylamino) propyl trimethoxysilane modified multi-wall carbon nanotubes packed microcolumn solid phase extraction and ICP-MS. Talanta 131:266–272
Vacchina V, De la Calle I, Séby F (2015) Cr(VI) speciation in foods by HPLC-ICP-MS: investigation of Cr(VI)/food interactions by size exclusion and Cr(VI) determination and stability by ion exchange on-line separations. Anal Bioanal Chem 407:3831–3839
Pytlakowska K (2016) Speciation of inorganic chromium in water samples by energy dispersive X-ray fluorescence spectrometry. J Anal At Spectrom 31:968–974
Margui E, Fontas C, Toribio M, Guillem M, Hidalgo M, Queralt I (2010) Determination of water-soluble hexavalent chromium in clinker samples by wavelength-dispersive X-ray fluorescence spectrometry after concentration in active layers. Appl Spectrosc 64:547–551
Markiewicz B, Komorowicz I, Sajnóg A, Belter M, Barałkiewicz D (2015) Chromium and its speciation in water samples by HPLC/ICP-MS - Technique establishing metrological traceability: A review since 2000. Talanta 132:814–828
Sitko R, Zawisza B, Malicka E (2012) Modification of carbon nanotubes for preconcentration, separation and determination of trace-metal ions. TrAC Trends Anal Chem 37:22–31
Sitko R, Zawisza B, Malicka E (2013) Graphene as a new sorbent in analytical chemistry. TrAC Trends Anal Chem 51:33–43
Aranda PR, Perino E, Bertolino FA, Raba J, De Vito IE (2012) Solid phase extraction of chromium(VI) using Aliquat336 immobilized on a thin film of multiwall carbon nanotubes. Microchim Acta 179:235–239
Aranda PR, Moyano S, Martinez LD, De Vito IE (2010) Determination of trace chromium(VI) in drinking water using X-ray fluorescence spectrometry after solid-phase extraction. Anal Bioanal Chem 398:1043–1048
Wu Y, Luo H, Wang H, Wang C, Zhang J, Zhang Z (2013) Adsorption of hexavalent chromium from aqueous solutions by graphene modified with cetyltrimethylammonium bromide. J Colloid Interf Sci 394:183–191
Tuzen M, Soylak M (2007) Multiwalled carbon nanotubes for speciation of chromium in environmental samples. J Hazard Mater 147:219–225
Sheikhmohammadi A, Mohseni SM, Khodadadi R, Sardar M, Abtahi M, Mahdavi S, Keramati H, Dahaghin Z, Rezaei S, Almasian M, Sarkhosh M, Faraji M, Nazari S (2017) Application of graphene oxide modified with 8-hydroxyquinoline for the adsorption of Cr (VI) from wastewater: Optimization, kinetic, thermodynamic and equilibrium studies. J Mol Liq 233:75–88
Sitko R, Janik P, Zawisza B, Talik E, Margui E, Queralt I (2015) Green approach for ultratrace determination of divalent metal ions and arsenic species using total-reflection X-ray fluorescence spectrometry and mercapto-modified graphene oxide nanosheets as a novel adsorbent. Anal Chem 87:3535–3542
Sitko R, Janik P, Feist B, Talik E, Gagor A (2014) Suspended aminosilanized graphene oxide nanosheets for selective preconcentration of lead ions and ultrasensitive determination by electrothermal atomic absorption spectrometry. ACS Appl Mater Interfaces 6:20144–20153
He C, Yang Z, Ding J, Chen Y, Tong X, Li Y (2017) Effective removal of Cr(VI) from aqueous solution by 3-aminopropyltriethoxysilane-functionalized graphene oxide. Colloid Surface A:Physicochem Eng Aspects 520:448–458
Zawisza B, Baranik A, Malicka E, Talik E, Sitko R (2016) Preconcentration of Fe(III), Co(II), Ni(II), Cu(II), Zn(II) and Pb(II) with ethylenediamine-modified graphene oxide. Microchim Acta 183:231–240
Pytlakowska K, Kozik V, Matussek M, Pilch M, Hachuła B, Kocot K (2016) Glycine modified graphene oxide as a novel sorbent for preconcentration of chromium, copper and zinc ions from water samples prior to energy dispersive X-ray fluorescence spectrometric determination. RSC Adv 6:42836–42844
Herrero-Latorre C, Barciela-García J, García-Martín S, Pena-Crecente RM (2017) Graphene and carbon nanotubes as solid phase extraction sorbents for the speciation of chromium: A review. Anal Chim Acta doi. https://doi.org/10.1016/j.aca.2017.11.042
Araghi SH, Entezari MH, Chamsaz M (2015) Modification of mesoporous silica magnetite nanoparticles by 3-aminopropyltriethoxysilane for the removal of Cr(VI) from aqueous solution. Micropror Mesopor Mater 218:101–111
Kumar ASK, Kakan SS (2013) A novel amine impregnated graphene oxide adsorbent for the removal of hexavalent chromium. Chem Eng J 230:328–337
Chen W, Zhang X, Mamadiev M, Zhao C, Wang Z, Xu H (2017) Synthesis of interstratified graphene/montmorillonite composite material through organics-pillared, delamination and co-stacking and its application in hexavalent chromium removal from aqueous solution. Adv Powder Technol 28:521–533
The Health Minister′s Regulation (2011) Dz.U.11.85.466. (The Official Journal of Law 11.85.466)
Shirkhanloo H, Khaligh A, Golbabaei F, Sadeghi Z, Vahid A, Rashidi A (2015) On-line micro column preconcentration system based on amino bimodal mesoporous silica nanoparticles as a novel adsorbent for removal and speciation of chromium (III, VI) in environmental samples. J Environ Heal Sci Eng 13:47
Qia X, Gao S, Ding G, Tang A-N (2017) Synthesis of surface Cr (VI)-imprinted magnetic nanoparticles for selective dispersive solid-phase extraction and determination of Cr (VI) in water samples. Talanta 162:345–353
Wang Z, Fang D-M, Li Q, Zhang L-X, Qian R, Zhu Y, Qu H-Y, Du Y-P (2012) Modified mesoporous silica materials for on-line separation and preconcentration of hexavalent chromium using a microcolumn coupled with flame atomic absorption spectrometry. Anal Chim Acta 725:81–86
Idris SA, Alotaibi K, Peshkur TA, Anderson P, Gibson LP (2012) Preconcentration and selective extraction of chromium species in water samples using amino modified mesoporous silica. J Colloid Interf Sci 386:344–349
Sereshti H, Farahani MV, Baghdadi M (2016) Trace determination of chromium(VI) in environmental water samples using innovative thermally reduced graphene(TRG) modified SiO2 adsorbent for solid phase extraction and UV–vis spectrophotometry. Talanta 146:662–669
Rezvani M, Asgharinezhad AA, Ebrahimzadeh H, Shekari N (2014) A polyaniline-magnetite nanocomposite as an anion exchange sorbent for solid-phase extraction of chromium(VI) ions. Microchim Acta 181:1887–1895
Bahadir Z, Bulut VN, Hidalgo M, Soylak M, Marguí E (2015) Determination of trace amounts of hexavalent chromium in drinking waters by dispersive microsolid-phase extraction using modified multiwalled carbon nanotubes combined with total reflection X-ray fluorescence spectrometry. Spectrochim Acta Part B 107:170–177
Tahmasebi Z, Davarani SSH (2016) Selective and sensitive speciation analysis of Cr(VI) and Cr(III), at sub-μg L−1 levels in water samples by electrothermal atomic absorption spectrometry after electro membrane extraction. Talanta 161:640–646
Acknowledgments
The project was supported by the National Science Centre (Poland) by the Grant No. 2015/17/B/ST4/03870.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
The author(s) declare that they have no competing interests.
Electronic supplementary material
ESM 1
(PDF 808 kb)
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Janik, P., Zawisza, B., Talik, E. et al. Selective adsorption and determination of hexavalent chromium ions using graphene oxide modified with amino silanes. Microchim Acta 185, 117 (2018). https://doi.org/10.1007/s00604-017-2640-2