Abstract
Water electrolysis is a sustainable and clean method to produce hydrogen fuel via hydrogen evolution reaction (HER). Using stable, effective and low-cost electrocatalysts for HER to substitute expensive noble metals is highly desired. In this paper, by using first-principles calculation, we designed a defect and N-, S-, P-doped penta-graphene (PG) as a two-dimensional (2D) electrocatalyst for HER, and its stability, electronic properties and catalytic performance were investigated. The Gibbs free energy (ΔGH), which is the best descriptor for the HER, is calculated and optimized, the calculation results show that the ΔGH can be 0 eV with C2 vacancies and P doping at C1 active sites, which should be the optimal performance for a HER catalyst. Moreover, we reveal that the larger charge transfer from PG to H, the closer ΔGH is to zero according to the calculation of the electron charge density differences and Bader charges analysis. Ulteriorly, we demonstrated that the HER performance prefers the Volmer–Heyrovsky mechanism in this study.
Avoid common mistakes on your manuscript.
Background
Because of the climate change and environmental pollution caused by fossil fuels usage, exploitation and utilization of clean and renewable energy are the mean way after nowadays [1,2,3,4]. As a clean, renewable and environmentally friendly energy source, hydrogen (H2) has been attracting considerable attention to fulfill human future energy needs [5, 6]. Water electrolysis is a sustainable and clean method to produce H2, and electrocatalysts can enhance the efficiency of water splitting observably [7, 8]. For hydrogen evolution reaction (HER), platinum-based nanomaterials are considered as the best electrocatalysts because of a small Tafel slope, a low overpotential, a slightly negative Gibbs free energy (ΔGH) and a high exchange current density [9, 10], but the scarcity and high cost hamper their industrial scale applications [11]. Therefore, developing effective, earth-abundant and low-cost electrocatalysts is essential for HER [12,13,14].
In fact, a wide range of earth-abundant electrocatalysts have been studied and designed for HER [15,16,17]. Among these materials, two-dimensional (2D) nanomaterials provide new opportunities for HER because of the compelling structural and electronic properties. To date, the transition metal dichalcogenides (TMDs) and the graphene-based materials are the biggest and most intensively studied groups of 2D electrocatalysts for HER [18,19,20,21,22,23]. The TMDs HER catalysts have low overpotential and small Tafel slope, unusual electronic properties and high air stability, exhibit high HER performance, and different methods were taken for enhancing their catalytic performance [24, 25]. The graphene-based HER catalysts have attracted considerable attention and persistent studying because of their distinctive structural merits, such as high electrical conductivity, large surface area and good chemical stability [26, 27]. Many methods were taken for enhancing the catalytic activity, such as heteroatom doping and defection engineering [28, 29]. Meanwhile, the intensive research on other new 2D carbon allotropes have also been developed, such as graphdiyne [30] and penta-graphene (PG) [31]. As a 2D carbon allotrope, PG is composed of only carbon pentagons and inherits many exceptional properties of 2D materials, such as finite electronic band gap, abundant active sites and large surface area, so it is anticipated to be a versatile material for lots of potential applications like other 2D graphene-based materials [32,33,34,35]. Since there are only applications in gas adsorption [36,37,38], H2 storage [39, 40], anode materials at present [41, 42], no report has ever been found on the application in HER. Therefore, research on HER by PG is of great significance and cannot only fill such a gap but also broaden the scope of graphene-based HER catalysts. However, the pristine PG is found to be inert for the HER with a relatively large ΔGH, which means that hydrogen adsorption is difficult and inhibits the HER. This is similar to the problems encountered by pristine graphene (ΔGH = 1.85 eV [43]). Heteroatom doping into graphene-based materials could adjust their electronic and catalytic properties, which makes them prospective catalysts for the practical applications [3]. Therefore, we managed to tailor the catalytic activity of PG by heteroatom doping [44,45,46] and defection engineering [47, 48].
In this paper, by using first-principles calculation, we designed and demonstrated a defect and N-, S-, P-doped PG and investigated their stability and electronic properties and evaluated their performance as HER electrocatalysts. Our results reveal that the defect and doped PG can obviously enhance the catalytic activity toward HER, compared with the pristine PG. It is also shown that the ΔGH can be 0 eV with C2 vacancies and P doping at C1 active sites, which should be the optimal performance for a HER catalyst, so P-doped PG has the optimal ΔGH and activation energy barrier for the rate-determining step among the three counterparts, and it exhibits more favorable performance. We further show that the catalytic activity arises from the incorporated doping atoms, which can provide efficient pathway for charge transport during the electrolysis, resulting in the reduction in ΔGH. We also demonstrate that the Volmer–Heyrovsky mechanism is more preferred for HER on defect and doped PG. We compared our results with that of other researchers on graphene, and it can be found that the defection and doping engineering are more effective for PG in catalysis of HER. Thus, our effort on defect and doped PG makes it a high promising electrocatalyst for HER, and our findings provide a deep understanding in designing efficient and durable electrocatalysts. This method can be also applied to other graphene-based materials.
Computational Methods
Our first-principles calculations were performed using the Vienna Ab initio Simulation Package (VASP) [49]. The projected augmented wave (PAW) potentials were used to analyze the interactions between core electrons and valence electrons [50,51,52]. The electron exchange–correlation interactions were described by using the Perdew–Burke–Ernzerhof (PBE) functional within the generalized gradient approximation (GGA) [53]. The DFT-D3 exchange–correlation functional was introduced in structural optimization to take the van der Waals interaction into account. The vacuum space along the z-direction was set to 20 Å in order to eliminate the interactions between PG and its periodic images.
The plane-wave energy cutoff was set to be 500 eV. The convergence criterion was set as 10−5 eV for a total energy. All the atomic positions and lattice structures were fully relaxed with the threshold of a maximum force of 0.02 eV Å−1. In order to ensure the accuracy and efficiency of the calculation, a Gamma-centered k-point mesh with a Monkhorst–Pack method 5 × 5 × 1 was employed for all considered structures after convergence test [54]. The amount of the charge transfer between the C atoms and H atoms was calculated using Bader code [55]. We also calculated H* adsorption energy barriers using the climbing image-nudged elastic band (CI-NEB) method [56, 57]. The CI-NEB is an efficient method to determine the minimum energy path and saddle points between a given initial and final position [58,59,60], and in our CI-NEB calculations, the initial and the final structures were fully optimized.
The adsorption energy (ΔEH) is defined as
where E(*H) and E(*) are the total energy of structures with and without hydrogen adsorption, respectively, and E(H2) is the total energy of a H2 molecule.
The Gibbs free energy (ΔGH) is defined as:
where ΔEH is the adsorption energy, ΔEZPE is the difference in zero-point energy, T is the temperature (298.15 K) and ΔSH is the entropy difference of H adsorbed and H in the gas phase. We approximated the entropy of hydrogen adsorption as \(\Delta S_{{\text{H}}} \approx \frac{1}{2}(S_{{{\text{H}}_{2} }}^{ \circ } )\), where \(S_{{{\text{H}}_{2} }}^{ \circ }\) is the entropy of gas phase H2 at standard conditions, TΔSH was set to be − 0.202 eV after calculation in this study.
Results and Discussion
Structure and Catalytic Activity of Defect and Doped PG
The optimized structure of PG is shown in Fig. 1. For convenience of discussion, we hereafter group the sp3− and sp2− hybridized C atoms as C1 and C2, respectively. The distance between the C1 and C2 is 1.55 Å, and the C2–C2 bond length is 1.34 Å, which is consistent with the experimental result [31].
At the beginning, we first investigated the sites C1 and C2 in the basal plane of pristine PG for HER, the calculated ΔGH values are 2.43 eV and 2.72 eV, respectively. So our calculations show that the pristine PG is found to be inert for the HER with a relatively large ΔGH of H, which means that hydrogen adsorption is difficult and HER is inhibited. Therefore, we managed to use some methods to tailor the catalytic activity of PG. We researched the possible active sites for doping and we also investigated the active sites for C1 and C2 with N, S, P doping, respectively. The calculation results show that no obvious improvement of HER can be obtained if only doping engineering was introduced. In the case of the P-doped structure, the calculated ΔGH values of C1 and C2 sites are 1.24 eV and 1.40 eV, respectively. Ulteriorly, we investigated the defect PG with C vacancy sites. The calculation results reveal that C1 vacancy structure cannot improve the HER performance but C2 vacancy structure can decrease ΔGH obviously, so we use C2 vacancy structure in this study. The optimized structures with VC-UP and VC-DOWN C2 vacancies sites are shown in Fig. 2, the vacancy defects are built by removing C2 atoms from C2-UP or C2-DOWN site in a 24-atom supercell. The calculated ΔGH values are shown in Table 1, where C1 and C2 are the active sites for hydrogen adsorption.
Though it is confirmed by our calculations that C2 vacancies are efficient to enhance the HER activity, PG with C2 vacancy structure is not yet optimal for a HER catalyst. Thus, we further investigated the defect and doped PG for HER. We used PG with C2 vacancy as initial structure, which is shown in Fig. 2 and then investigated all the different possible active sites with N, S, P doping, including C1, C2-UP and C2-DOWN sites. As a result, we found that better HER performance could be achieved with a combination of C2 vacancy and heteroatom doping. We investigated all the possible structures, and the results showed that there are two structures that can achieve better HER performance, one structure is a combination of the C2-UP vacancy and heteroatom doping in the C2-DOWN site, and the other is a combination of the C2-DOWN vacancy and heteroatom doping in the C2-UP site. So we focused on these two structures and found that they can shift the ΔGH values closer to zero. The optimized structures are shown in Fig. 3, and the calculated bond lengths are summarized in Table 2.
We can see that there is slight difference between the corresponding bond lengths of N-doped PG and that of pristine PG. Because of the large radius of S and P atoms, these two structures undergo much more distortion, but they can both maintain the structure of PG.
To investigate the stability of PG with C2 vacancy and heteroatom doping, we calculated the formation energy, which is defined as
where Et is the total energy of the defect and doped system, and EV is the energy of C2 vacancy PG, EC is the average energy per C atom of the pristine PG, Ed is the energy of doping atoms,\(\mu_{{\text{H}}}\) is taken from the total energy of the H2 molecule, respectively. One of our calculation results about the formation energies of preceding two structures with C1 active sites for HER is shown in Fig. 4. We can see that negative formation energies indicate energetically favorable and feasible defect and S-, P-doped PG. Similarly, Ef values of N-doped structures with active sites for HER are all positive. We investigated all the possible active sites and got the similar results as shown in Fig. 4, so we will investigate only the S- and P-doped PG. According to the definition, a more negative Ef value indicates higher stability of the structure, so P-doped PG has excellent stability, as well as good HER performance.
Origin of the HER Catalytic Activity
DOS and Band Structures
To achieve an in-depth understanding of the nature of C2 vacancy and doping engineering in the HER activity, we investigated the total and projected DOS, electronic band structure of the defect and S-, P-doped PG. Figure 5 is one of our calculation results about electronic band structures, total and projected DOS of pristine PG, VC-UP, VC-UPS-doped and VC-UPP-doped PG.
From the figure, we can see that when C2 vacancy is introduced, some new defect states highlighted by red curves appear in the forbidden band near the Fermi level. Obviously, these new states arise from the C2 vacancy. Furthermore, when S, P heteroatom doping is introduced, the band gap gets narrower (from 2.22 eV [31] to 0.37 eV) and the number of new defect states near the Fermi level increases, which can possibly improve the H* adsorption strength.
However, we found that the DOS of VC-UP near the Fermi level is much larger than that of pristine PG. In addition, the electron density near the Fermi level of C2 vacancy and S-, P-doped PG is further increased relative to pristine PG. We also found that the S 3p and P 3p orbitals undergo significant hybridization with the C1 and C2 states, leading to strong interactions between the heteroatoms and C, and the formation of S–C and P–C bonds. These results demonstrate that combination of the C2 vacancy and S, P heteroatoms doping may be a better engineering for improving HER activity.
Electron Density Difference and Charge Transfer
Moreover, to study the binding interaction between the H atom and PG, we calculated the electron charge density differences for defect and S-, P-doped PG with different active sites for hydrogen evolution. One of our calculation results about the electron charge density difference and Bader charges analysis for a C2-DOWN vacancy and P-doped PG with H* adsorbed at the different active sites for hydrogen adsorption is shown in Fig. 6. The yellow and blue colors represent charge accumulation and reduction, respectively. It is shown that the electrons accumulate around H atoms and reduce around the C atoms which are bonded to H atoms, indicating a charge transfer from PG to H*. The charge transfer is also confirmed by Bader charges analysis. The calculation results show that there are 0.18, 0.04, 0.02 and 0.01 electrons transferring to H* at C1, C2-DOWN, C2-DOWN(n) and C2-UP sites, respectively. We further show that the larger charge transfer from PG to H*, the closer ΔGH is to zero, which means the optimal performance for a HER catalyst, as shown in Fig. 7. It can be seen from Fig. 6 that electrons are transferred from PG to H*, resulting in increase in the charge density of the bonds, which means that the stabilization of the H* species in HER performance may originate from the enhanced charge density of P-doped C atoms, indicating that P atoms are inherently advantageous in interacting with H atoms than C atoms. We also noticed that H* is absorbed onto C instead of P, indicating that the increased charge density can contribute to the electrocatalyst on H atom. So our calculations show that P doping into the PG can lead to enhanced adsorption of H* on C atoms. As mentioned above, the DFT calculations also suggested that the P doping into PG could much more efficiently enhance the HER activity than that of S-doping.
Activity of Defect and Doped PG Toward HER
Gibbs Free Energies of HER
The ΔGH is the vital descriptor of the HER for a variety of electrocatalysts, the optimal ΔGH value for a electrocatalyst is zero, so the H* adsorption and desorption can occur spontaneously without activation energy barrier [61, 62]. To evaluate the HER activity of the PG and investigate the defection and doping engineering, we calculated the ΔGH of HER. One of our calculation results about ΔGH versus reaction coordinate of the HER for PG is shown in Fig. 8, where C1 and C2 inside the brackets are active sites for hydrogen adsorption.
Our calculations show that the pristine PG is found to be inert for the HER with a relatively large Gibbs free energy of H* (ΔGH = 2.72 eV(C2), ΔGH = 2.43 eV(C1)). When vacancies are introduced, there are two different C vacancy sites, C1 vacancy site and C2 vacancy site. We calculated the ΔGH on the two sites and found that C2 vacancy can notably decrease ΔGH (ΔGH = 0.24 eV), which indicates that H* preferentially adsorbs on C2 vacancy structures. The optimized structures with C2 vacancy sites (VC-UP and VC-DOWN) are shown in Fig. 2. Though C2 vacancies show significant improvement over the pristine PG, they are still not the optimal for the hydrogen adsorption, so doping engineering is explored to improve the HER performance. We show our effects of C2 vacancies and S, P heteroatom doping on the HER activity and optimize the HER performance. The ΔGH values are summarized in Table 3, and the active sites for hydrogen evolution are shown in Fig. 3.
The calculation results reveal that ΔGH decreases significantly, demonstrating that the defection and doping engineering are very effective in reducing ΔGH. Remarkably, we found that the ΔGH values of active sites C1, C2-UP and C2-UP(n) for VC-UP, active sites C1, C2-DOWN and C2-DOWN(n) for VC-DOWN are very close to zero, especially for two C1 sites, signifying the optimal conditions can be achieved, which are significantly superior to pristine PG. And we compared our results with previous work from other researchers on graphene, for instance, graphene with C vacancy (ΔGH = − 2.108 eV) [28], graphene with N-doped (ΔGH = − 0.693 eV) [28], graphene with C vacancy and N-doped (ΔGH = − 0.595 eV) [28], graphene with S-doped (ΔGH = − 0.30 eV) [29] and graphene with N/S co-doped (ΔGH = − 0.12 eV) [29]. We can find that the defection and doping engineering are more effective for PG. Thus, our results clearly suggest that the ΔGH of PG can be manipulated by applying defection and doping engineering to achieve the optimal HER activity.
The Reaction Pathways of Defect and Doped PG
The HER proceeds in a multistep electrochemical process, via one of two pathways which are known as the Volmer–Tafel and the Volmer–Heyrovsky mechanisms. The first step of HER is the H* adsorption on the electrocatalyst surface (i.e., Volmer reaction), which is described by H+ + e− → H*. Then, H* combines with H+ and an electron (e−) to form a H2 molecule, known as the Heyrovsky step, which is described by H* + H+ + e− → H2. Alternatively, H2 molecule can be formed via the Tafel step, i.e., the combination of two H* on the electrocatalyst surface, which is described by 2H* → H2 [63].
To investigate the defection and doping engineering effects on PG and further understand the mechanism of superior HER activity, the energy barriers of Tafel and Heyrovsky reactions with C2-UP and C2-DOWN vacancies, S-, P-doped PG for C1 site were calculated. The initial state (IS), the final state (FS) and the transition state (TS) are displayed in Fig. 9 with the corresponding energy barriers. For the Tafel reaction, the recombination of 2H* shows energy barriers of 1.51 eV (S-doped), 1.32 eV (P-doped), respectively. Whereas the release of a H2 molecule in the Heyrovsky reaction involved in a proton reacting with an adsorbed H* needs to overcome the energy barriers of 1.01 eV (S-doped), 0.99 eV (P-doped), respectively. The results reveal that the energy barriers of Tafel reaction are significantly higher than that of the Heyrovsky reaction. So the HER on defect and doped PG prefers the Volmer–Heyrovsky mechanism.
Conclusions
We theoretically designed a C vacancy and N-, S-, P-doped PG and investigated their stability and unique role of electrocatalyst toward HER systematically. We find that defection and doping engineering possess a superior HER performance over the pristine PG. Importantly, the optimal HER activity can be achieved with C2 vacancies and S, P heteroatoms doping, which indicates that the catalytic properties of the defect and doped PG can be tuned easily and effectively. Our calculations reveal that ΔGH decreases significantly with C2 vacancies and S, P heteroatom doping, and the optimal conditions can be achieved with P doping at C1 active sites, for which defection or doping engineering alone cannot achieve the optimal conditions. The electronic structure analysis shows that when C2 vacancy and S, P heteroatom doping are introduced, several new defection states move closer to the Fermi level, leading to the narrower band gap and an improvement of the hydrogen adsorption strength. We also find the charge transfer from PG to H* by calculating the electron charge density differences, the larger charge transfer to H*, the closer ΔGH values to zero by using Bader charges analysis, which indicates the optimal performance for a HER catalyst. And we further demonstrate the HER on defect and doped PG prefers the Volmer–Heyrovsky mechanism. So our study shows that the designed defect and doped PG is highly activated toward HER electrocatalyst, the optimal HER activity can be achieved, and abundant catalytic activity sites are provided. It is expected that the strategies developed in this paper may be applied for designing 2D graphene-based electrocatalysts for low-cost and high-performance HER applications.
Availability of data and materials
The datasets supporting the conclusions of this article are included within the article, and further information about the data and materials could be made available to the interested party under a motivated request addressed to the corresponding author.
Abbreviations
- HER:
-
Hydrogen evolution reaction
- PG:
-
Penta-graphene
- 2D:
-
Two dimensional
- ΔG H :
-
The Gibbs free energy
- TMDs:
-
The transition metal dichalcogenides
- VASP:
-
Vienna Ab initio Simulation Package
- PAW:
-
Projected augmented wave
- PBE:
-
The Perdew–Burke–Ernzerhof
- GGA:
-
The generalized gradient approximation
- CI-NEB:
-
The climbing image-nudged elastic band
- IS:
-
Initial state
- FS:
-
The final state
- TS:
-
The transition state
References
Chu S, Majumdar A (2012) Opportunities and challenges for a sustainable energy future. Nature 488:294–303
Hu GX, Fung V, Sang XH, Unocic RR, Ganesh P (2019) Superior electrocatalytic hydrogen evolution at engineered non-stoichiometric two-dimensional transition metal dichalcogenide edges. J Mater Chem A 7:18357–18364
Ren CJ, Wen L, Magagula S, Jiang QY, Lin W, Zhang YF, Chen ZF, Ding KN (2020) Relative efficacy of Co-X4 embedded grapheme (X=N, S, B, and P) electrocatalysts towards hydrogen evolution reaction: is nitrogen really the best choice? ChemCatChem 12:536–543
Liang D, Zhang YW, Lu PF, Yu ZG (2019) Strain and defect engineered monolayer Ni-MoS2 for pH-universal hydrogen evolution catalysis. Nanoscale 11:18329–18337
Korotcenkov G, Han SD, Stetter JR (2009) Review of electrochemical hydrogen sensors. Chem Rev 109:1402–1433
Geng XM, Sun WW, Wu W, Chen B, Al-Hilo A, Benamara M, Zhu HL, Watanabe F, Cui JB, Chen TP (2016) Pure and stable metallic phase molybdenum disulfide nanosheets for hydrogen evolution reaction. Nat Commun 7:10672
Zhou YC, Leng YH, Zhou WJ, Huang JL, Zhao MW, Zhan J, Feng CH, Tang ZH, Chen SW, Liu H (2015) Sulfur and nitrogen self-doped carbon nanosheets derived from peanut root nodules as high-efficiency non-metal electrocatalyst for hydrogen evolution reaction. Nano Energy 16:357–366
Li Y, Wei XF, Chen LS, Shi JL, He MY (2019) Nickel-molybdenum nitride nanoplate electrocatalysts for concurrent electrolytic hydrogen and formate productions. Nat Commun 10:5335
Greeley J, Jaramillo TF, Bonde J, Chorkendorff IB, Nørskov JK (2006) Computational high-throughput screening of electrocatalytic materials for hydrogen evolution. Nat Mater 5:909–913
Greeley J, Stephens IEL, Bondarenko AS, Johansson TP, Hansen HA, Jaramillo TF, Rossmeisl J, Chorkendorff I, Nørskov JK (2009) Alloy of platinum and early transition metals as oxygen reduction electrocatalysts. Nat Chem 1:552–556
Zhang M, Dai LM (2012) Carbon nanomaterials as metal-free catalysts in next generation fuel cells. Nano Energy 1:514–517
You B, Liu X, Hu GX, Gul S, Yano J, Jiang DE, Sun YJ (2017) Universal surface engineering of transition metals for superior electrocatalytic hydrogen evolution in neutral water. J A Chem Soc 139:12283–12290
Xie JF, Zhang H, Li S, Wang RX, Sun X, Zhou M, Zhou JF, Lou XW, Xie Y (2013) Defect-rich MoS2 ultrathin nanosheets with additional active edge sites for enhanced electrocatalytic hydrogen evolution. Adv Mater 25:5807–5813
Ping XF, Liang D, Wu YY, Yan XX, Zhou SX, Hu DK, Pan XQ, Lu PF, Jiao LY (2021) Activating a two-dimensional PtSe2 basal plane for the hydrogen evolution reaction through the simultaneous generation of atomic vacancies and Pt clusters. Nano Lett 21:3857–3863
Jin HY, Guo CX, Liu X, Liu JL, Vasileff A, Jiao Y, Zheng Y, Qiao SZ (2018) Emerging two-dimensional nanomaterials for electrocatalysis. Chem Rev 118:6337–6408
Zhang X, Luo ZM, Yu P, Cai YQ, Du YH, Wu DX, Gao S, Tan CL, Li Z, Ren MQ, Osipowicz T, Chen SM, Jiang Z, Li J, Huang Y, Yang J, Chen Y, Yen Ang C, Zhao YL, Wang P, Song L, Wu XJ, Liu Z, Borgna A, Zhang H (2018) Lithiation-induced amorphization of Pd3P2S8 for highly efficient hydrogen evolution. Nat Catal 1:460–468
Cai YQ, Gao JF, Chen S, Ke QQ, Zhang G, Zhang YW (2019) Design of phosphorene for hydrogen evolution performance comparable to platinum. Chem Mater 31:8948–8956
Huang HJ, Yan MM, Yang CZ (2019) Graphene nanoarchitectonics: recent advances in graphene-based electrocatalysts for hydrogen evolution reaction. Ad Mater 31:1903415
Gawande MB, Fornasiero P, Zboril R (2020) Carbon-based single-atom catalysts for advanced applications. ACS Catal 10:2231–2259
Fei HL, Dong JC, Chen DL, Hu TD, Duan XD, Shakir I, Huang Y, Duan XF (2019) Single atom electrocatalysts supported on graphene or graphene-like carbons. Chem Soc Rev 48:5207–5241
He XY, Liu F, Lin FT, Shi WZ (2021) Tunable 3D Dirac-semimetals supported mid-IR hybrid plasmonic waveguides. Opt Lett 46:472–475
He XY, Feng Liu F, Lin FT, Shi WZ (2021) Tunable terahertz Dirac semimetal metamaterials. J Phys D: Appl Phys 54:235103
Peng J, He XY, Shi CYY, Leng J, Lin FT, Liu F, Zhang H, Shi WZ (2020) Investigation of graphene supported terahertz elliptical metamaterials. Phys E 124:114309
Zhang Y, Xue LX, Liang CB, Chen YZ, Liu JJ, Shen C, Li Q, Duan YF, Yao LY, Zhang H, Cai YQ, Tan CL, Luo ZM (2021) Two-dimensional metallic MoS2-amorphous CoNi(OH)2 nanocomposite for enhanced electrochemical water splitting in alkaline solutions. Appl Surf Sci 561:150079
Liu G, Li JJ, Dong C, Wu LY, Liang D, Cao HW, Lu PF (2021) Hydrogen evolution reaction on in-plane platinum and palladium dichalcogenides via single-atom doping. Int J Hydrogen Energy 46:18294–18304
Huang CC, Li C, Shi G (2012) Graphene based catalysts. Energy Environ Sci 5:8848
Jia Y, Zhang LZ, Du AJ, Gao GP, Chen J, Yan XC, Brown CL, Yao XD (2016) Defect graphene as a trifunctional catalyst for electrochemical reactions. Adv Mater 28:9532–9538
Gao XP, Zhou YA, Tan YJ (2019) Single Mo atoms supported on N-doped carbon with N/C edge-site for enhanced electrochemical hydrogen evolution. Int J Hydrogen Energy 44:14861–14868
Ito Y, Cong WT, Fujita T, Tang Z, Chen MW (2014) High catalytic activity of Nitrogen and Sulfur co-doped nanoporous graphene in the hydrogen evolution reaction. Angew Chem Int Ed 54:2131–2136
Xue YR, Huang BL, Yi YP, Guo Y, Zuo ZC, Li YG, Jia ZY, Liu HB, Li YL (2018) Anchoring zero valence single atoms of nickel and iron on graphdiyne for hydrogen evolution. Nat Commun 9:1460
Zhang SH, Zhou J, Wang Q, Chen XS, Kawazoe Y, Jena P (2015) Penta-graphene: a new carbon allotrope. Proc Natl Acad Sci USA 112:2372–2377
Wang MH, ZhanZY GYQ, Zhou SN, Wang JH, Wang ZJ, Wei SX, Guo WY, Lu XQ (2020) Penta-graphene as a promising controllable CO2 capture and separation material in an electric field. Appl Surf Sci 502:144067
Qin HB, Feng C, Luan XH, Yang DG (2018) First-principles investigation of adsorption behaviors of small molecules on penta-graphene. Nanoscale Res Lett 13:264
Cheng MQ, Chen Q, Yang K, Huang WQ, Hu WY, Huang GF (2019) Penta-graphene as a potential gas sensor for NOx detection. Nanoscale Res Lett 14:306
Li B, Shao ZG (2020) Adsorption of DNA/RNA nucleobases and base pairs on penta-graphene from first principles. Appl Surf Sci 512:145635
Balasubramanian R, Chowdhury S (2015) Recent advances and progress in the development of graphene-based adsorbents for CO2 capture. J Mater Chem A 3:21968–21989
Lu XQ, Wang MH, Luo GW, Zhou SN, Wang JH, Xin HL, Wang ZJ, Liu SY, Wei SX (2020) High-efficiency CO2 capture and separation over N-2 in penta-graphene pores: insights from GCMC and DFT simulations. J Mater Sci 55:16603–16611
Zhang CP, Li B, Shao ZG (2019) First-principle investigation of CO and CO2 adsorption on Fe-doped penta-graphene. Appl Surf Sci 469:641–646
Sathishkumar N, Wu SY, Chen HT (2019) Charge-modulated/electric-field controlled reversible CO2/H2 capture and storage on metal-free N-doped penta-graphene. Chem Eng J 391:123577
Sathishkumar N, Wu SY, Chen HT (2019) Boron-and nitrogen-doped penta-graphene as a promising material for hydrogen storage: a computational study. Int J Energy Res 43:4867–4878
Xiao B, Li YC, Yu XF, Cheng JB (2016) Penta-graphene: a promising anode material as the Li/Na-ion battery with both extremely high theoretical capacity and fast charge/discharge rate. ACS Appl Mater Interfaces 8:35342–35352
Wang HW, Luo WW, Tian ZF, Ouyang CY (2019) First principles study of alkali and alkaline earth metal ions adsorption and diffusion on penta-graphene. Solid State Ion 342:115062
Zheng Y, Jiao Y, Li LH, Xing T, Chen Y, Jaroniec M, Qiao SZ (2014) Toward design of synergistically active carbon-based catalysts for electrocatalytic hydrogen evolution. ACS Nano 8:5290–5296
Zhang C, Cao Y, Dai X, Ding XY, Chen LL, Li BS, Wang DQ (2020) Ab-Initio study of the electronic and magnetic properties of boron- and nitrogen-doped penta-graphene. Nanomaterials 10:816
Einollahzadeh H, Fazeli SM (2021) The superconducting transition temperature for P-doped hydrogenated penta-graphene. Supercond Sci Tech 34:065003
Lu PF (2020) Recent development of two-dimensional stanene. J Sichuan Normal Univ (Nat Sci) 43:1–20
Manjanath A, Hsu CP, Kawazoe Y (2020) Tuning the electronic and magnetic properties of pentagraphene through the C1 vacancy. 2D Mater 7:045024
Han TW, Wang XY, Zhang XY, Scarpa F, Tang C (2021) Mechanics of penta-graphene with vacancy defects under large amplitude tensile and shear loading. Nanotechnology 32:275706
Kresse GJ, Furthmuller J (1996) Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys Rev B 54:11169–11186
Kresse GJ, Joubert D (1999) From ultrasoft pseudopotentials to the projector augmented-wave method. Phys Rev B 59:1758–1775
Lin S, Liu JC, Li WZ, Wang D, Huang Y, Jia C, Li ZW, Murtaza M, Wang HY, SongJ N, Liu ZL, Huang K, Zu D, Lei M, Hong B, Wu H (2019) A flexible, robust and Gel-free electroencephalogram electrode for noninvasive brain–computer interfaces. Nano Lett 19:6853–6861
Lin S, Bai XP, Wang HY, Wang HL, Song JN, Huang K, Wang C, Wang N, Li B, Lei M, Wu H (2017) Roll-to-roll production of transparent silver nanofiber network electrode for flexible electrochromic smart windows. Adv Mater 29:1703238
PerdewJ P, Burke K, Ernzerhof M (1996) Generalized gradient approximation made simple. Phys Rev Lett 77:3865–3868
Monkhorst HJ, Pack JD (1976) Special points for brillouinzone integrations. Phys Rev B: Solid State 13:5188–5192
Tang W, Sanville E, Henkelman G (2009) A grid-based Bader analysis algorithm without lattice bias. J Phys: Condens Matter 21:084204
Henkelman G, Uberuaga BP, Jonsson H (2000) A climbing image nudged elastic band method for finding saddle points and minimum energy paths. J Chem Phys 113:9901–9904
Guan XN, Zhang R, Jia BN, Wu LY, Zhou B, Fan L, Liu G, Wang Y, Lu PF, Peng GD (2020) Fluorine passivation of ODC defects in amorphous germanium dioxide. J Non-Cryst Solids 550:120388
Tibbetts K, Miranda CR, Meng YS, Ceder G (2007) An ab Initio study of lithium diffusion in titanium disulfide nanotubes. Chem Mater 19:5302–5308
Peng B, Cheng FY, Tao ZL, Chen J (2010) Lithium transport at silicon thin film: Barrier for high-rate capability anode. J Chem Phys 133:034701
Bi K, Yang DQ, Chen J, Wang QM, Wu HY, Lan CW, Yang YP (2019) Experimental demonstration of ultra-large-scale terahertz all-dielectric metamaterials. Photonics Res 7:457–463
Hinnemann B, Moses PG, Bonde J (2005) Biomimetic hydrogen evolution: MoS2 nanoparticles as catalyst for hydrogen evolution. J Am Chem Soc 127:5308–5309
Jiao Y, Zheng Y, Jaroniec MT, Qiao SZ (2015) Design of electrocatalysts for oxygen- and hydrogen-involving energy conversion reactions. Chem Soc Rev 44:2060–2086
Wei JM, Zhou M, Long AC, Xue YM, Liao HB, We C, Xu ZCJ (2018) Heterostructured electrocatalysts for hydrogen evolution reaction under alkaline conditions. Nano-Micro Lett 10:75
Funding
This work was supported by the Fund of State Key Laboratory of IPOC (BUPT) (IPOC2019ZZ04 and IPOC2019A013), and the Open-Foundation of Key Laboratory of Laser Device Technology, China North Industries Group Corporation Limited (No. KLLDT202001).
Author information
Authors and Affiliations
Contributions
XHZ and DL conceived and designed the study. JBH, FW and LL performed the calculations and analyzed the result data; JBH and CLZ wrote the manuscript, XGM and PFL participated in the discussions and edited the manuscript. All authors read and approved the final manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare that they have no competing interests.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Hao, J., Wei, F., Zhang, X. et al. Defect and Doping Engineered Penta-graphene for Catalysis of Hydrogen Evolution Reaction. Nanoscale Res Lett 16, 130 (2021). https://doi.org/10.1186/s11671-021-03590-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-021-03590-3