Abstract
Ultraviolet-ozone-treated poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS)was used as the anode buffer layer in copper phthalocyanine (CuPc)/fullerene-based solar cells. The power conversion efficiency of the cells with appropriated UV-ozone treatment was found to increase about 20% compared to the reference cell. The improved performance is attributed to the increased work function of the PEDOT:PSS layer, which improves the contact condition between PEDOT:PSS and CuPc, hence increasing the extraction efficiency of the photogenerated holes and decreasing the recombination probability of holes and electrons in the active organic layers.
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Background
Organic solar cells (OSCs) have attracted significant interests because of their potential for renewable energy source, low-cost and large-scale fabrication, and compatibility with large-area and flexible substrates [1]. In the past two decades, the power conversion efficiency (PCE) of OSCs has been steadily improved, and a PCE exceeding 8% has been demonstrated by using the materials that exhibit a broad absorption with high coefficient in the solar spectrum and by developing new device configurations that provide high exciton dissociation efficiency and charge carrier collection efficiency [2, 3]. The mechanism of OSCs involves the formation of excitons under illumination, the diffusion of excitons to the donor-acceptor interface, the dissociation of excitons into electrons and holes, and the collection of electrons and holes at opposite electrodes. One of the most important factors in determining the charge carrier collection efficiency is the interface property of electrode/organic layer. The buffer layer is often adopted in OSCs to improve the device performance. A lot of anode buffer layers have been demonstrated, such as MoO3[4], V2O5[4], NiO [5], WO3[6], and graphene oxide [7]. Conductive poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) film presents many advantages, such as high transparency in the visible range, high mechanical flexibility, and excellent thermal stability. These properties make it beneficial to be used as the anode buffer layer in OSCs [8]. However, phase separation of PEDOT and PSS is generally found with the insulating PSS grains atop the as-prepared PEDOT: PSS film cast from aqueous PEDOT:PSS solution, which leads to a low conductivity below 1 S/cm and an improper contact condition between PEDOT:PSS and the following organic layer [9]. Many strategies have been proposed to address such an issue, such as adding sorbitol [10–12], glycerol [11], N-methylpyrrolidone [12], isopropanol [12], dimethyl sulfoxide [13, 14], N,N-dimethyl formamide [13], tetrahydrofuran [13], ethylene glycol [14], 2-nitroethanol [14], 1-methyl-2-pyrrolidinone [14], mannitol [15], sodium p-toluenesulfonate [16], carbon nanotube [17], and pentacene [18] into PEDOT:PSS aqueous solution and treating the as-prepared PEDOT:PSS film with solvents [14, 19], thermal annealing [20], oxygen plasma [21], Ar ion sputtering [22], zwitterions [23], salt solution [24], and H2SO4[25]. However, these methods make the device construction process more complex and require careful control of the technologies to avoid the deterioration of the PEDOT:PSS film properties.
Increased work function and conductivity of PEDOT:PSS film have been demonstrated by ultraviolet light irradiation [26, 27], and the treated PEDOT:PSS has been adopted as the anode buffer layer in OSCs [28, 29]. Tengstedt et al. [30] have proposed that the work function of PEDOT:PSS film can be increased while maintaining reasonable conductivity by UV-ozone treatment, which is further confirmed by Helander et al. [31]. Nagata et al. [32] have clarified the respective roles of UV light irradiation and exposure to ozone gas on the PEDOT:PSS film, and they have found that the main role of UV light is to decompose the chemical bonds in the PEDOT:PSS film, resulting in a decrease of the conductivity, while the ozone and atomic oxygen are absorbed and oxidize the surface, leading to an increase of the work function. Thus, the UV-ozone treatment is capable of controlling the work function and conductivity of PEDOT:PSS film, hence allowing them to be adjusted to the device application. Such UV-ozone-treated PEDOT:PSS film has been adopted as the anode buffer layer in organic light-emitting diodes, and dramatic improvement of efficiency was observed [33, 34]. However, the application of UV-ozone-treated PEDOT:PSS in OSCs has not been exploited. In this paper, UV-ozone-treated PEDOT:PSS film is adopted as the anode buffer layer in copper phthalocyanine (CuPc)/fullerene (C60)-based small molecular OSCs. The power conversion efficiency of the cell was increased by more than 20%, compared with the reference cell without UV-ozone treatment. The improvement is primarily attributed to the increased work function of the PEDOT:PSS film, which improves the contact condition between PEDOT:PSS and CuPc, hence increasing the charge carrier collection efficiency and decreasing the charge carrier recombination probability in the bulk of organic layers.
Methods
Devices were fabricated on pattered indium tin oxide (ITO)-coated glass substrates with a sheet resistance of 15 Ω/sq. The substrates were routinely cleaned, followed by UV-ozone treatment for 10 min. The structure of the OSCs used here was ITO/PEDOT:PSS/CuPc (30 nm)/C60(40 nm)/4,7-diphenyl-1,10-phenanthroline (8 nm)/Al (100 nm). Two types of PEDOT:PSS (Clevios P VP Al 4083 (H. C. Starck, Clevios GmbH, Leverkusen, Germany) and 483095 (Aldrich, St. Louis, MO, USA) with PEDOT/PSS mass ratio of 1:6 and 1:1.6, respectively) were used here, and they were spin-coated onto the ITO anode with a speed of 4,000 rad/min, followed by baking in vacuum at 120 °C for 1 h, which forms a PEDOT:PSS layer of about 30 nm. The PEDOT:PSS films were then treated in a UV-ozone environment for different times(0, 2, 4, 6, and 10 min) before loading into a high-vacuum chamber. The other organic layers and the cathode were deposited onto the substrates via thermal evaporation in the vacuum chamber at a pressure of approximately 10−7 Torr. Deposition rates and thickness of the layers were monitored in situ using oscillating quartz monitors. The evaporation rates were kept at approximately 1 Å/s for organic layers and Al cathode. Current–voltage (I-V) characteristics of the devices were measured with a programmable Keithley 2400 power source (Keithley Instruments, Inc., Cleveland, OH, USA) both in dark and under illumination of a Xe lamp light source with an intensity of 100 mW/cm2. The surface characterization of PEDOT:PSS films was performed with a Bruker MultiMode 8 atomic force microscope (AFM; BRUKER, Ettlingen, Germany) in tapping mode. All the measurements were carried out at room temperature under ambient conditions.
Results and discussion
Figure 1 shows the I V characteristics of the cells under illumination with a PEDOT:PSS (Clevios P VP Al 4083) anode buffer layer treated with UV-ozone for various times. The parameters extracted from the I V curves are summarized in Table 1. The reference cell with untreated PEDOT:PSS film shows an open circuit voltage (VOC), short-circuit current density (JSC), fill factor (FF), and PCE of 0.496 V, 4.872 mA/cm2, 0.477, and 1.149%, respectively. It can be found in Figure 1 and Table 1 that the VOC of the cells with PEDOT:PSS anode buffer layer is almost constant regardless of the UV-ozone treatment time. The VOC of the CuPc/C60-based OSCs is reported to be determined by the energy offset of the highest occupied CuPc molecular orbital and the lowest unoccupied C60 molecular orbital [35]. The same VOC of the cells suggests that the UV-ozone treatment on PEDOT:PSS does not alter this energy offset. In contrast, the JSC and FF of the cells first increase and then decrease with further increase of the UV-ozone treatment time. The cell with 6-min UV-ozone-treated PEDOT:PSS shows the maximum JSC and FF of 5.897 mA/cm2 and 0.495, respectively. Consequently, a PCE of 1.429% was obtained, which was increased by 24% compared to the reference cell.
Performance of the cells under illumination with a PEDOT:PSS (Clevios P VP Al 4083) anode buffer layer treated with UV-ozone for various times. FF, fill factor; PCE, power conversion efficiency.
Figure 2 describes the I-V characteristics of the cells under illumination with a PEDOT:PSS (Aldrich 483095) anode buffer layer treated with UV-ozone for various times. The parameters extracted from the I-V curves are listed in Table 2. The VOC, JSC, FF, and PCE of the reference cell are 0.493 V, 5.334 mA/cm2, 0.483, and 1.271%, respectively. The superior performance of the cell with Aldrich 483095 PEDOT:PSS compared with Baytron P VP Al 4083 PEDOT:PSS is attributed to the higher conductivity of the former, which may increase the extraction efficiency of the photogenerated charge carriers. Similarly, the VOC of the cells are unaffected by the UV-ozone treatment on the PEDOT:PSS layer. In contrast, the JSC and FF are increased with UV-ozone treatment time. The maximum JSC and FF are found with 4-min UV-ozone treatment time, which are 6.099 mA/cm2 and 0.499, respectively. Correspondingly, the PCE reaches up to 1.529%, which is increased by 20% compared to the reference cell. These findings suggest that the improved performance of the CuPc/C60-based OSCs can be observed with UV-ozone-treated PEDOT:PSS as the anode buffer layer, and this effect is valid for the PEDOT:PSS film with different conductivities.
Performance of the cells under illumination with a PEDOT:PSS (Aldrich 483095) anode buffer layer treated with UV-ozone for various times. FF, fill factor; PCE, power conversion efficiency.
The improvement of the device performance by UV-ozone treatment may come from two factors: improved interface contact condition in PEDOT:PSS/CuPc and increased conductivity of the PEDOT:PSS film. Figure 3 displays the AFM image of the PEDOT:PSS (Clevios P VP Al 4083) films on ITO anode treated with UV-ozone for various times. The morphology of the PEDOT:PSS film without UV-ozone treatment is quite smooth with a root mean square (RMS) roughness of 1.06 nm, while the RMS roughnesses of the 2-, 4-, 6-, and 10-min UV-ozone-treated PEDOT:PSS films are 1.15, 1.10, 1.08, and 1.23 nm, respectively. This finding indicates that the UV-ozone treatment has little effect on the morphology of the PEDOT:PSS films. Thus, the PEDOT:PSS morphology change-induced alterations of the optical field distribution in the active organic layers, the CuPc molecule stacking mode, and the crystallinity of CuPc layer could be ruled out for the improved performance of the OSCs. Tengstedt et al. [30] have found that both the PEDOT and PSS moistures of the PEDOT:PSS film could be oxidized under UV-ozone treatment, which results in an increase of the work function of the PEDOT:PSS film. The effect was further confirmed by Helander et al. [31] and Nagata et al. [32]. Thus, increased work function of PEDOT:PSS film with UV-ozone treatment can be expected in this study. Such an effect improves the contact condition between PEDOT:PSS and CuPc, which increases the extraction efficiency of the photogenerated holes and decreases the recombination probability of holes and electrons in the active organic layers. As a result, both the JSC and FF and, hence, the PCE are enhanced in the optimized cells.
To exploit the UV-ozone treatment on the conductivity of the PEDOT:PSS film, the dark current of the cells with a PEDOT:PSS (Clevios P VP Al 4083) anode buffer layer treated with UV-ozone for various times was investigated, as shown in Figure 4. All five cells present almost the same the I V curves. A similar phenomenon was found in the cells with Aldrich 483095 PEDOT:PSS as the anode buffer layer (not shown here). Such a fact indicates that the UV-ozone treatment has little affect on the conductivity of the PEDOT:PSS film during the time scale investigated. Furthermore, this finding rules out the contribution of the increased conductivity of the PEDOT:PSS layer to the improved device performance. Thus, the improved device performance is attributed to the increased work function of the PEDOT:PSS layer under UV-ozone treatment, which increases the extraction efficiency of the photogenerated holes and decreases the recombination probability of holes and electrons in the active organic layers. The decreased performance of the cells with prolonged UV-ozone treatment time may result from the saturation in the change of the work function, decomposition of the chemical bonds, and/or formation of ping hole defects in the PEDOT:PSS layer [32, 33], which would decrease the extraction efficiency of the photogenerated charge carriers.
Conclusions
In summary, UV-ozone-treated PEDOT:PSS film was used as the anode buffer layer in CuPc/C60-based OSCs. The morphology of the PEDOT:PSS film is unaffected by the UV-ozone treatment. However, the PCE is found to increase about 20% compared to the reference cell without UV-ozone treatment. The improved performance is attributed to the increased work function of the PEDOT:PSS layer, which increases the extraction efficiency of the photogenerated holes and decreases the recombination probability of holes and electrons in the active organic layers. This work provides a facile and cost-effective method to improve the performance of OSCs. Besides, such a strategy may have potential applications to improve the contact condition between PEDOT:PSS and metal anode in inverted OSCs where a PEDOT:PSS/metal bilayer anode is adopted.
References
Service RF: Outlook brightens for plastic solar cells. Science 2011, 332: 293. 10.1126/science.332.6027.293
He Z, Zhong C, Huang X, Wong WY, Wu HB, Chen L, Su S, Cao Y: Simultaneous enhancement of open-circuit voltage, short-circuit current density, and fill factor in polymer solar cells. Adv Mater 2011, 23: 4636–4643. 10.1002/adma.201103006
Chen G, Sasabe H, Wang Z, Wang XF, Hong Z, Yang Y, Kido J: Co-evaporated bulk heterojunction solar cells with >6.0% efficiency. Adv Mater 2012, 24: 2768–2773. 10.1002/adma.201200234
Shrotriya V, Li G, Yao Y, Chu CW, Yang Y: Transition metal oxides as the buffer layer for polymer photovoltaic cells. Appl Phys Lett 2006, 88: 073508. 10.1063/1.2174093
Yu W, Shen L, Ruan S, Meng F, Wang J, Zhang E, Chen W: Performance improvement of inverted polymer solar cells thermally evaporating nickel oxide as an anode buffer layer. Sol Energy Mater Sol Cells 2012, 98: 379–384.
Varnamkhasti MG, Fallah HR, Mostajaboddavati M, Ghasemi R, Hassanzadeh A: Comparison of metal oxides as anode buffer layer for small molecular organic photovoltaic cells. Sol Energy Mater Sol Cells 2012, 98: 212–215.
Yun JM, Yeo JS, Kim J, Jeong HG, Kim DY, Noh YJ, Kim SS, Ku BC, Na SI: Solution processable reduced graphene oxide as a novel alternative to PEDOT:PSS hole transport layers for highly efficient and stable polymer solar cells. Adv Mater 2011, 23: 4923–4928. 10.1002/adma.201102207
Peumans P, Forrest SR: Very-high-efficiency double-heterostructure copper phthalocyanine/C60photovoltaic cells. Appl Phys Lett 2001, 79: 126–128. 10.1063/1.1384001
Kemerink M, Timpanaro S, de Kok MM, Meulenkamp EA, Touwslager FJ: Three-dimensional inhomogeneities in PEDOT PSS films. J Phys Chem B 2004, 108: 18820–18825. 10.1021/jp0464674
Granlund T, Pettersson LAA, Inganäs O: Determination of the emission zone in a single-layer polymer light-emitting diode through optical measurements. J Appl Phys 2001, 89: 5897–5902. 10.1063/1.1350998
Zhang F, Johansson M, Anderssson MR, Hummelen JC, Inganäs O: Polymer photovoltaic cells with conducting polymer anode. Adv Mater 2002, 14: 662–665. 10.1002/1521-4095(20020503)14:9<662::AID-ADMA662>3.0.CO;2-N
Jönsson SKM, Birgerson J, Crispin X, Greczynski G, Osikowicz W, van der Gon AWD, Salaneck WR, Fahlman M: The effects of solvents on the morphology and sheet resistance in poly(3,4-ethylenedioxythiophene)/poly(4-styrenesulfonate) (PEDOT-PSS) films. Synth Met 2003, 139: 1–10. 10.1016/S0379-6779(02)01259-6
Kim JY, Jung JH, Lee DE, Joo J: Enhancement of electrical conductivity of poly(3,4-ethylenedioxythiophene)/poly(4-styrenesulfonate) by a change of solvents. Synth Met 2002, 126: 311–316. 10.1016/S0379-6779(01)00576-8
Ouyang JY, Xu Q, Chu CW, Yang Y, Li G, Shinar J: On the mechanism of conductivity enhancement in poly(3,4-ethylenedioxythiophene): poly(4-styrenesulfonate) film through solvent treatment. Polymer 2004, 45: 8443–8450. 10.1016/j.polymer.2004.10.001
Ko CJ, Lin YK, Chen FC, Chu CW: Modified buffer layers for polymer photovoltaic devices. Appl Phys Lett 2007, 90: 063509. 10.1063/1.2437703
Fan B, Mei X, Ouyang J: Significant conductivity enhancement of conductive poly(3,4-ethylenedioxythiophene):poly(4-styrenesulfonate) film by adding anionic surfactants into polymer solution. Macromolecules 2008, 41: 5971–5973. 10.1021/ma8012459
Su SH, Chiang WT, Hou CC, Kao LC, Yokoyama M: Enhancing efficiency of organic light-emitting diodes using a carbon nanotube doped hole injection layer. Jpn J Appl Phys 2010, 49: 04DK12. 10.1143/JJAP.49.04DK12
Kim H, Lee J, Ok S, Choe Y: Effects of pentacene-doped PEDOT:PSS as a hole-conducting layer on the performance characteristics of polymer photovoltaic cells. Nanoscale Res Lett 2012, 7: 5. 10.1186/1556-276X-7-5
Xia Y, Ouyang J: PEDOT:PSS films with significantly enhanced conductivities induced by preferential solvation with cosolvents and their application in polymer photovoltaic cells. J Mater Chem 2011, 21: 4927–4936. 10.1039/c0jm04177g
Kim Y, Ballatyne AM, Nelson J, Bradley DDC: Effects of thickness and thermal annealing of the PEDOT:PSS layer on the performance of polymer solar cells. Org Electron 2009, 10: 205–209. 10.1016/j.orgel.2008.10.003
Zhou Y, Yuan Y, Lian J, Zhang J, Pang H, Cao L, Zhou X: Mild oxygen plasma treated PEDOT:PSS as anode buffer layer for vacuum deposited organic light-emitting diodes. Chem Phys Lett 2006, 427: 394–398. 10.1016/j.cplett.2006.06.035
Hwang J, Amy F, Kahn A: Spectroscopic study on sputtered PEDOT·PSS: role of surface PSS layer. Org Electron 2006, 7: 387–396. 10.1016/j.orgel.2006.04.005
Xia Y, Zhang H, Ouyang J: Highly conductive PEDOT:PSS films prepared through a treatment with zwitterions and their application in polymer photovoltaic cells. J Mater Chem 2010, 20: 9740–9747. 10.1039/c0jm01593h
Xia Y, Ouyang JY: Anion effect on salt-induced conductivity enhancement of poly(3,4-ethylenedioxythiophene):poly(4-styrenesulfonate) films. Org Electron 2010, 11: 1129–1135. 10.1016/j.orgel.2010.04.007
Xia Y, Sun K, Ouyang J: Solution-processed metallic conducting polymer films as transparent electrode of optoelectronic devices. Adv Mater 2012, 24: 2436–2440. 10.1002/adma.201104795
Lin YJ, Yang FM, Huang CY, Chou WY, Chang J, Lien YC: Increasing the work function of poly(3,4-ethylenedioxythiophene) doped with poly(4-styrenesulfonate) by ultraviolet irradiation. Appl Phys Lett 2007, 91: 092127. 10.1063/1.2777147
Moujoud A, Oh SH, Heo KY, Lee KW, Kim HJ: Indium zinc oxide ohmic contact to poly(3,4-ethylenedioxythiophene) poly(styrenesulfonate) induced by UV light. Org Electron 2009, 10: 785–790. 10.1016/j.orgel.2009.03.014
Lee HK, Kim JK, Park OO: Effects of UV light-irradiated buffer layer on the performance of polymer solar cells. Org Electron 2009, 10: 1641–1644. 10.1016/j.orgel.2009.09.010
Moujoud A, Oh SH, Hye JJ, Kim HJ: Improvement in stability of poly(3-hexylthiophene-2,5-diyl) [6,6]-phenyl-C61-butyric acid methyl ester bulk heterojunction solar cell by using UV light irradiation. Sol Energy Mater Sol cells 2011, 95: 1037–1041. 10.1016/j.solmat.2010.08.019
Tengstedt C, Kanciurzewska A, de Jong MP, Braun S, Salaneck WR, Fahlman M: Ultraviolet light–ozone treatment of poly(3,4-ethylenedioxy-thiophene)-based materials resulting in increased work functions. Thin Solid Films 2006, 515: 2085–2090. 10.1016/j.tsf.2006.07.005
Helander MG, Wang ZB, Greiner MT, Liu ZW, Lian K, Liu ZT: The effect of UV ozone treatment on poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate). Appl Phys Lett 2009, 95: 173302. 10.1063/1.3257382
Nagata T, Oh S, Chikyow T, Wakayama Y: Effect of UV–ozone treatment on electrical properties of PEDOT PSS film. Org Electron 2011, 12: 279–284. 10.1016/j.orgel.2010.11.009
Benor A, Takizawa SY, Chen P, Pérez-Bolívar C, Anzenbacher PJ: Dramatic efficiency improvement in phosphorescent organic light-emitting diodes with ultraviolet-ozone treated poly(3,4-ethylenedioxythiophene): poly(4-styrenesulfonate). Appl Phys Lett 2009, 94: 193301. 10.1063/1.3132059
Benor A, Takizawa SY, Pérez-Bolívar C, Anzenbacher PJ: Efficiency improvement of fluorescent OLEDs by tuning the working function of PEDOT:PSS using UV–ozone exposure. Org Electron 2010, 11: 938–945. 10.1016/j.orgel.2010.02.014
Liu ZT, Lo MF, Wang HB, Ng TW, Roy VAL, Lee CS, Lee ST: Influence of the donor/acceptor interface on the open-circuit voltage in organic solar cells. Appl Phys Lett 2009, 95: 093307. 10.1063/1.3222975
Acknowledgements
This work was supported by the National Natural Science Foundation of China grant numbers 11004187, 61076047, 61107082, and 60877027.
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors’ contributions
ZS participated in the design of the study, carried out the experiments, collected data, performed data analysis, and drafted the manuscript. LW and YL participated in collection of the data, performed data analysis, and helped draft the manuscript. HZ participated in the AFM image measurement and analysis. BC and WL participated in the design of the study and helped draft the manuscript. All authors read and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License ( https://creativecommons.org/licenses/by/2.0 ), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Su, Z., Wang, L., Li, Y. et al. Ultraviolet-ozone-treated PEDOT:PSS as anode buffer layer for organic solar cells. Nanoscale Res Lett 7, 465 (2012). https://doi.org/10.1186/1556-276X-7-465
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-7-465