Abstract
The microstructure and mechanical properties of tailor-rolled blank (TRB) of medium-manganese steel during annealing were investigated. The annealing process of austenite-reverted transformation of the experimental steel was formulated. The effects of different morphologies on properties with different annealing temperatures in different thickness zones of TRB were analyzed. In the thin zone, the morphology is blocky, and in the thick zone, the morphology is lamellar. At the same annealing temperature, the tensile strength of the thick zone is lower than that of the thin zone, and the elongation and product of strength and elongation (PSE) of the thick zone are higher than those of the thin zone. With the increase in annealing temperature, the tensile strength increases, while the yield strength, the elongation and the PSE all decrease in the same thickness zone. Because the stability of lamellar austenite is higher than that of blocky austenite, the comprehensive mechanical properties in the thick zone are good. At the annealing temperature of 640 °C, the experimental steel has the best comprehensive mechanical properties, and the maximum PSE is more than 40.0 GPa% in different thickness zones. Particularly, PSE is up to 45.6 GPa% in the thickness zone of 2.0 mm.
Similar content being viewed by others
References
X.H. Liu, X. Liu, S.T. Fu, L.Z. Liu, Steel Rolling 32 (2015) No. 5, 1–7.
X.H. Liu, J. Iron Steel Res. Int. 18 (2011) No. 1, 1–7.
Y. Fukumoto, M. Nagai, Prog. Struct. Eng. Mater. 2 (2000) 34–40.
K. Fumimaru, M. Kazuyki, O. Tadashi, K. Tsutomu, T. Masahiro, K. Takahiro, JFE Tech. Rep. (2004) No. 2, 85–90.
S. Suzuki, R. Muraoka, T. Obinata, S. Endo, T. Horita, K. Omata, JFE Tech. Rep. (2004) No. 2, 41–48.
Y. Yuge, T. Hori, S. Nishida, Kawasaki Steel Giho 30 (1998) 137–141.
O. Tanigawa, T. Kohriyama, K. Amano, Kawasaki Steel Giho 32 (2000) 198–204.
P. Du, X.L. Hu, J. Wang, X.H. Liu, Steel Rolling 25 (2008) No. 1, 47–50.
B. Rooks, Assembly Auto. 21 (2001) No. 4, 323–328.
H. Hamatani, Y. Miyazaki, M. Ohara, Sci. Technol. Adv. Mater. 6 (2005) 712–719.
A. Meyer, B. Wietbrock, G. Hirt, Int. J. Mach. Tools Manuf. 48 (2008) 522–531.
M. Urban, M. Krahn, G. Hirt, R. Kopp, J. Mater. Process. Technol. 177 (2006) 360–363.
G.J. Zhang, X.H. Liu, Adv. Mater. Res. 418–420 (2012) 1232–1236.
X.H. Liu, Z.Q. Wu, Y. Zhi, P. Du, T. Sun, X.L. Hu, Automobile Technology & Material (2011) No. 1, 30–34.
X.H. Liu, Q.L. Zhao, L.Z. Liu, Acta Metall. Sin. (Engl. Lett.) 27 (2014) 483–493.
X.H. Liu, G.J. Zhang, Y. Zhi, Chinese Sci. Bull. 58 (2013) 1769–1774.
Y. Zhi, X.H. Liu, T. Sun, Z.Q. Wu, G.J. Zhang, J. Harbin Eng. Univ. 38 (2017) 602–609.
Y. Zhi, X.G. Wang, S. Wang, X.H. Liu, Int. J. Adv. Manuf. Technol. 94 (2018) 4507–4518.
P. Du, Research on rolling theory and control strategy for longitudinally profiled flat steel, Northeastern University, Shenyang, China, 2008.
X.H. Liu, Z.Q. Wu, Z. Fang, G.J. Zhang, Y. Zhi, Mater. Sci. Forum 706–709 (2012) 1448–1453.
P. Du, X.L. Hu, J. Wang, X.H. Liu, G.D. Wang, J. Iron Steel Res. 20 (2008) No. 12, 26–30.
J. Benedyk, Light Metal Age 58 (2000) Nos. 9–10, 34–35.
H. Dong, W.Q. Cao, J. Shi, C.Y. Wang, M.Q. Mao, Y.Q. Weng, Iron Steel 46 (2011) No. 6, 1–11.
J. Shi, X.J. Sun, M.Q. Wang, W.J. Hui, H. Dong, W.Q. Cao, Scripta Mater. 63 (2010) 815–818.
A. Arlazarov, M. Goune, O. Bouaziz, A. Hazotte, G. Petitgand, P. Barges, Mater. Sci. Eng. A 542 (2012) 31–39.
Z.B. Dai, R. Ding, Z.G. Yang, C. Zhang, H. Chen, Acta Mater. 144 (2018) 666–678.
Y. Zhi, Y. Tian, J.L. Zhang, X.H. Liu, J. Northeastern Univ. 35 (2014) 671–675.
X.C. Xiong, B. Chen, M.X. Huang, J.F. Wang, L. Wang, Scripta Mater. 68 (2013) 321–324.
G. Reisner, E.A. Werner, P. Kerschbaummayr, I. Papst, F.D. Fischer, JOM 49 (1997) No. 9, 62–83.
M. De Meyer, D. Vanderschueren, B.C. De Cooman, ISIJ Int. 39 (1999) 813–822.
Acknowledgements
Ying Zhi would like to thank the support from the National Natural Science Foundation of China (51504062) and the International Scientific and Technological Cooperation Projects of China (2015DFA50780).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Zhi, Y., Ke, Dw., Liu, Xh. et al. Effects of annealing temperature on microstructure and properties of tailor-rolled blank of medium-manganese steel. J. Iron Steel Res. Int. 27, 933–939 (2020). https://doi.org/10.1007/s42243-020-00371-7
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s42243-020-00371-7