Abstract
The corrosion performances of rolled AZ31 alloy with addition of Y and Gd were comparatively investigated. The corrosion rates of AZ31 alloy modified with Y and Gd were 3.3 and 3.7 mm/y immersing for 24 h in 3.5 wt% NaCl solution, respectively, which were much lower than that of AZ31 alloy (23.6 mm/y). The remarkable improvement in corrosion performance by adding Y or Gd was ascribed to preferentially form less noble Al2Y or Al6GdMn6 and more protective corrosion product layer, resulting in the reduction in H2 evolution rate and the enhancement of passivity.
References
S. Pawar, T.J.A. Slater, T.L. Burnett, X. Zhou, G.M. Scamans, Z. Fan, G.E. Thompson, P.J. Withers, Acta Mater. 90, 133 (2017)
S. Yu, R. Jia, T. Zhang, F. Wang, J. Hou, H. Zhang, Acta Metall. Sin. Engl. Lett. 32, 433 (2019)
Y. Zhang, H. Jiang, S. Wang, Y. Wang, S. Tian, H. Lin, G. Zhang, Y. Yang, Z. Xu, Mater. Sci. Eng. A 140566, 804 (2021)
H. Niu, F. Cao, K. Deng, K. Nie, J. Kang, H. Wang, Acta Metall. Sin. Engl. Lett. 33, 362 (2020)
L. Yang, T. Wang, C. Liu, Y. Ma, L. Wu, H. Yan, X. Zhao, W. Liu, J. Alloys Compd. 159473, 870 (2021)
F. Zhong, H. Wu, Y. Jiao, R. Wu, J. Zhang, L. Hou, M. Zhang, J. Mater. Sci. Technol. 39, 124 (2020)
A. Atrens, S. Johnston, Z. Shi, M. S. Dargusch, Scr. Mater. 154 (2018)
L. Cui, R. Zeng, S. Gao, P. Li, F. Zhang, S. Li, Corros. Sci. 84, 118 (2017)
R. Arrabal, E. Matykina, A. Pardo, M.C. Merino, K. Paucar, M. Mohedano, P. Casajus, Corros. Sci. 2, 55 (2012)
S.M. Baek, J.S. Kang, H.J. Shin, C.D. Yim, B.S. You, H.Y. Ha, S.S. Park, Corros. Sci. 227, 118 (2017)
X. Peng, S. Xu, D. Ding, G. Liao, G. Wu, W. Liu, W. Ding, J. Mater. Sci. Technol. 16, 72 (2021)
J. Chen, L. Tan, X. Yu, K. Yang, J. Mater. Sci. Technol. 503, 35 (2019)
M. Mandal, A.P. Moon, G. Deo, C.L. Mendis, K. Mondal, Corros. Sci. 1, 78 (2014)
P. Wang, H. Jiang, Y. Wang, Y. Zhang, Y. Zhang, S. Tian, Z. Cao, Int. J. Miner. Metall. Mater. (2021). https://doi.org/10.1007/s1261302122684
H. Hao, X. Liu, C. Fang, X. Zhang, Mater. Sci. Eng. A 27, 698 (2017)
M.F. Hurley, C.M. Efaw, P.H. Davis, Corrosion 2, 71 (2015)
B. Mingo, R. Arrabal, M. Mohedano, C.L. Mendis, R. del Olmo, E. Matykina, N. Hort, M.C. Merino, A. Pardo, Mater. Des. 48, 130 (2017)
S. Baek, S. Lee, J.C. Kim, J. Kwon, H. Jung, S. Lee, K. Lee, S.S. Park, Corros. Sci. 108998, 178 (2021)
R.H. Buzolin, M. Mohedano, C.L. Mendis, B. Mingo, D. Tolnai, C. Blawert, K.U. Kainer, H. Pinto, N. Hort, Mater. Sci. Eng. A 682, 238 (2017)
F. Cao, Dissertation, Taiyuan University of Technology, 2019
J. Liu, L. Yang, C. Zhang, B. Zhang, T. Zhang, Y. Li, K. Wu, F. Wang, J. Alloys Compd. 648, 782 (2019)
R. Zeng, L. Sun, L. Sun, Y. Zheng, H. Cui, E. Han, Corros. Sci. 2, 79 (2014)
S. Leleu, B. Rives, J. Bour, N. Causse, N. Pebere, Electrochim. Acta 586, 290 (2018)
S. Yin, W. Duan, W. Liu, L. Wu, J. Bao, J. Yu, L. Li, Z. Zhao, J. Cui, Z. Zhang, Corros. Sci. 108962, 177 (2020)
S. Yin, W. Duan, W. Liu, L. Wu, J. Yu, Z. Zhao, M. Liu, P. Wang, J. Cui, Z. Zhang, Corros. Sci. 108419, 166 (2019)
M. Esmaily, D.B. Blücher, J.E. Svensson, M. Halvarsson, L.G. Johansson, Scr. Mater. 91, 115 (2016)
Y. Li, W. Xiao, F. Wang, T. Hu, C. Ma, J. Alloys Compd. 33, 745 (2018)
Acknowledgements
This work was financially supported by the Fundamental Research Funds for the Central Universities (No. FRF-IC-20-10).
Author information
Authors and Affiliations
Corresponding authors
Ethics declarations
Conflict of interest
The authors state that there are no conflicts of interest to disclose.
Additional information
Available online at http://link.springer.com/journal/40195.
Rights and permissions
About this article
Cite this article
Wang, P., Jiang, H., Wang, Y. et al. Role of Microalloyed Y and Gd in Improving the Corrosion Resistance of Rolled Mg-3Al-1Zn Alloy. Acta Metall. Sin. (Engl. Lett.) 35, 941–947 (2022). https://doi.org/10.1007/s40195-021-01332-z
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40195-021-01332-z