Interfacial layers evolution during annealing in Ti-Al multi-laminated composite processed using hot press and roll bonding

  • Published:
Metals and Materials International Aims and scope Submit manuscript

Abstract

Ti-Al multi-laminated composites have great potential in high strength and low weight structures. In the present study, tri-layer Ti-Al composite was synthesized by hot press bonding under 40 MPa at 570 °C for 1 h and subsequent hot roll bonding at about 450 °C. This process was conducted in two accumulative passes to 30% and to 67% thickness reduction in initial and final passes, respectively. Then, the final annealing treatments were done at 550, 600, 650, 700 and 750 °C for 2, 4 and 6 h. Investigations on microstructural evolution and thickening of interfacial layers were performed by scanning electron microscopes, energy dispersive spectrometer, X-ray diffraction and micro-hardness tests. The results showed that the thickening of diffusion layers corresponds to amount of deformation. In addition to thickening of the diffusion layers, the thickness of aluminum layers decreased and after annealing treatment at 750 °С for 6 h the aluminum layers were consumed entirely, which occurred because of the enhanced interdiffusion of Ti and Al elements. Scanning electron microscope equipped with energy dispersive spectrometer showed that the sequence of interfacial layers as Ti3Al-TiAl-TiAl2-TiAl3 which are believed to be the result of thermodynamic and kinetic of phase formation. Micro-hardness results presented the variation profile in accordance with the sequence of intermetallic phases and their different structures.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Similar content being viewed by others

References

  1. J. H. Westbrook and R. L. Fleischer, Intermetallic Compounds, Vol. 1, p. 670, John Wiley & Sons, Inc., New Jersey, USA (1967).

    Google Scholar 

  2. J. Dutkiewicz, W. Maziarz, H. Heinrich, and G. Kostorz, Mater. Chem. Phys. 81, 414 (2003).

    Article  Google Scholar 

  3. M. Yoo, C. Fu, and J. Lee, J. de Physique III 1, 1065 (1991).

    Article  Google Scholar 

  4. F. Appel and R. Wagner, Mater. Sci. Eng. R: Reports 22, 187 (1998).

    Article  Google Scholar 

  5. D. Dimiduk, Mater. Sci. Eng. A 263, 281 (1999).

    Article  Google Scholar 

  6. S. Djanarthany, J.-C. Viala, and J. Bouix, Mater. Chem. Phys. 72, 301 (2001).

    Article  Google Scholar 

  7. F. Froes, C. Suryanarayana, and D. Eliezer, J. Mater. Sci. 27, 5113 (1992).

    Article  Google Scholar 

  8. D. Goda, N. Richards, W. Caley, and M. Chaturvedi, Mater. Sci. Eng. A 334, 280 (2000).

    Article  Google Scholar 

  9. L. Peng, J. Wang, H. Li, J. Zhao, and L. He, Scripta Mater. 52, 243 (2005).

    Article  Google Scholar 

  10. J. Baird, J. Nuclear Energy. Part A. Reactor Sci. 11, 81 (1960).

    Article  Google Scholar 

  11. J. Peng, Z. Liu, P. Xia, M. Lin, and S. Zeng, Mater. Lett. 74, 89 (2012).

    Article  Google Scholar 

  12. D. Yang, P. Hodgson, and C. E. Wen, Intermetallics 17, 727 (2009).

    Article  Google Scholar 

  13. W. C. Johnson and G. Martin, J. Appl. Phys. 68, 1252 (1990).

    Article  Google Scholar 

  14. J. Liu, Y. Su, Y. Xu, L. Luo, J. Guo, and H. Fu, Rare Metal. Mater. Eng. 40, 753 (2011).

    Article  Google Scholar 

  15. J.-P. Liu, L.-S. Luo, Y.-Q. Su, Y.-J. Xu, X.-Z. Li, R.-R. Chen, J.-J. Guo, and H.-Z. Fu, T. Nonferr. Metals Soc. 21, 598 (2011).

  16. Y. Wei, W. Aiping, Z. Guisheng, and R. Jialie, Mater. Sci. Eng. A 480, 456 (2008).

    Article  Google Scholar 

  17. L. Xu, Y. Y. Cui, Y. L. Hao, and R. Yang, Mater. Sci. Eng. A 435-436, 638 (2006).

    Article  Google Scholar 

  18. M. Mirjalili, M. Soltanieh, K. Matsuura, and M. Ohno, Intermetallics 32, 297 (2013).

    Article  Google Scholar 

  19. J. Oh, W. Lee, S. G. Pyo, W. Park, S. Lee, and N. J. Kim, Metall. Mater. Trans. A 33, 3649 (2002).

    Article  Google Scholar 

  20. Y.-B. Sun, Y.-Q. Zhao, D. Zhang, C.-Y. Liu, H.-Y. Diao, and C.-L. Ma, T. Nonferr. Metals Soc. 21, 1722 (2011).

    Article  Google Scholar 

  21. J.-G. Luo and V. L. Acoff, Mater. Sci. Eng. A 379, 164 (2004).

    Article  Google Scholar 

  22. C. Wagner, Acta Metall. 17, 99 (1969).

    Article  Google Scholar 

  23. H. Kim, H. Liou, and K. Tu, Appl. Phys. Lett. 66, 2337 (1995).

    Article  Google Scholar 

  24. H. Kim and K. Tu, Phys. Rev. B 53, 16027 (1996).

    Article  Google Scholar 

  25. I. Bataev, A. Bataev, V. Mali, and D. Pavliukova, Mater. Design 35, 225 (2012).

    Article  Google Scholar 

  26. F. Van Loo and G. Rieck, Acta Metall. 21, 73 (1973).

    Article  Google Scholar 

  27. Y. Mishin and C. Herzig, Acta Mater. 48, 589 (2000).

    Article  Google Scholar 

  28. U. Kattner, J.-C. Lin, and Y. Chang, Metall. Trans. A 23, 2081 (1992).

    Article  Google Scholar 

  29. A. Laik, K. Bhanumurthy, and G. Kale, Intermetallics 12, 69 (2004).

    Article  Google Scholar 

  30. A. Raman and K. Schubert, Z. Metallk. 56 (1965).

    Google Scholar 

  31. H. W. Kerr, J. Cisse, and G. Bolling, Acta Metall. 22, 677 (1974).

    Article  Google Scholar 

  32. J. Rawers and W. Wrzesinski, Scripta Metall. Mater. 24, 1985 (1990).

    Article  Google Scholar 

  33. W. Yang and G. Weatherly, J. Mater. Sci. 31, 3707 (1996).

    Article  Google Scholar 

  34. R. Bené, Appl. Phys. Lett. 41, 529 (1982).

Download references

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to B. Eghbali.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Assari, A.H., Eghbali, B. Interfacial layers evolution during annealing in Ti-Al multi-laminated composite processed using hot press and roll bonding. Met. Mater. Int. 22, 915–923 (2016). https://doi.org/10.1007/s12540-016-5647-z

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s12540-016-5647-z

Keywords

Navigation