Abstract
For improving the ultraviolet (UV) protection property of cotton fabric and exploiting ecological cotton textiles, cotton fabric was modified with a kind of biocompatible and nontoxic of chitosan (CS)/nanocellulose (NCs) nanocomposites using a pad-dry-cure process. The effect of particle size of NCs on the morphology and property of CS/NCs cotton fabrics were carefully investigated by SEM, FTIR, and mechanical property, water wettability, UV protection and laundering durability analysis. The results revealed that the CS/NCs coated fabrics performed excellent UV protection ability as well as a good laundering durability. The UPF values of all the CS/NCs coated fabrics were much higher than that of untreated fabric even after 30 cycles of laundering. Moreover, the particle size of NCs had a negative effect on the UV protection ability of CS/NCs coated fabric. Meanwhile, coated with CS/NCs nanocomposites was benefit to enhance the mechanical property, and hydrophobicity of cotton fabric.
Similar content being viewed by others
References
L. Qu, M. Tian, X. Hu, Y. Wang, S. Zhu, X. Guo, G. Han, X. Zhang, K. Sun, and X. Tang, Carbon, 80, 565 (2014).
Y. Cao, H. Wang, C. Cao, Y. Sun, L. Yang, and Y. Zhang, Mater. Lett., 65, 340 (2011).
M. Yang, W. Liu, C. Jiang, Y. Xie, H. Shi, F. Zhang, and Z. Wang, Colloid. Surface A, 570, 172 (2019).
X. Hu, M. Tian, T. Xu, X. Sun, B. Sun, C. Sun, X. Liu, X. Zhang, and L. Qu, ACS Nano, 14, 559 (2020).
X. Hu, M. Tian, N. Pan, B. Sun, Z. Li, Y. Ma, X. Zhang, S. Zhu, Z. Chen, and L. Qu, Carbon, 152, 106 (2019).
Y. Lu, M. Tian, X. Sun, N. Pan, F. Chen, S. Zhu, X. Zhang, and S. Chen, Compos. Part A-Appl. S., 117, 202 (2019).
F. Sun, M. Tian, X. Sun, T. Xu, X. Liu, S. Zhu, X. Zhang, and L. Qu, Nano Lett., 19, 6592 (2019).
W. Y. Wong, J. K. C. Lam, C. W. Kan, and R. Postle, J. Text. Inst., 107, 1533 (2016).
M. Shabbir, L. Rather, and F. Mohammad, Ind. Crop. Prod., 119, 277 (2018).
M. Montazer and E. Pakdel, J. Photoch. Photobio. C, 12, 293 (2011).
M. Mahmoudifard and M. Safi, J. Text. Inst., 103, 893 (2012).
O. K. Alebeid and T. Zhao, J. Text. Inst., 108, 2027 (2017).
N. Abidi, L. Cabrales, and E. Hequet, ACS Appl. Mater. Inter., 1, 2141 (2009).
N. A. Ibrahim, R. Refaie, and A. F. Ahmed, J. Ind. Text., 40, 65 (2010).
M. M. Ibrahim, A. Mezni, H. S. El-Sheshtawy, A. A. Abu Zaid, M. Alsawat, N. El-Shafi, S. I. Ahmed, A. A. Shaltout, M. A. Amin, T. Kumeria, and T. Altalhi, Appl. Surf. Sci., 479, 953 (2019).
A. K. Jhatial, A. Khatri, S. Ali, and A. A. Babar, Cellulose, 26, 6365 (2019).
X. Hu, M. Tian, L. Qu, S. Zhu, and G. Han, Carbon, 95, 625 (2015).
X. Miao, J. Lin, F. Tian, X. Li, F. Bian, and J. Wang, Carbohyd. Polym., 136, 841 (2016).
H. Liu, D. Liu, F. Yao, and Q. Wu, Bioresource Technol., 101, 5685 (2010).
K. Missoum, F. Martoïa, M. N. Belgacem, and J. Bras, Ind. Crop. Prod., 48, 98 (2013).
H. Wang, X. Zhang, Z. Jiang, W. Li, and Y. Yu, Ind. Crop. Prod., 71, 80 (2015).
A. Hebeish, S. Farag, S. Sharaf, and T. I. Shaheen, Carbohyd. Polym., 151, 96 (2016).
R. Jafary, M. K. Mehrizi, S. H. Hekmatimoghaddam, and A. Jebali, J. Text. Inst., 106, 683 (2015).
V. Baheti, R. Mishra, J. Militky, and B. K. Behera, Fiber. Polym., 15, 1500 (2014).
S. Azizi, M. B. Ahmad, N. A. Ibrahim, M. Z. Hussein, and F. Namvar, Int. J. Mol. Sci., 15, 11040 (2014).
X. Yang, Y. Zhao, H. Mussana, M. Tessema, and L. Liu, Mater. Lett., 211, 300 (2018).
M. Gouda and S. M. A. S. Keshk, Carbohyd. Polym., 80, 504 (2010).
M. Tian, X. Tang, L. Qu, S. Zhu, X. Guo, and G. Han, Mater. Lett., 145, 340 (2015).
K. Shimoi, Y. Nakamura, I. Tomita, and T. Kada, Mutat. Res., 149, 17 (1985).
H. M. Fahmy and E. S. Abdel-Halim, J. Ind. Text., 40, 109 (2010).
Acknowledgments
This work was supported by Shanghai Science and Technology Commission (Project No.19YF1417900), National Natural Science Foundation of China (Project No.51903152), and the Research Initiation Funds of Shanghai University of Engineering Science (Project No. E3-0507-19-05164).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Yang, X., Wang, Z., Zhang, Y. et al. A Biocompatible and Sustainable Anti-ultraviolet Functionalization of Cotton Fabric with Nanocellulose and Chitosan Nanocomposites. Fibers Polym 21, 2521–2529 (2020). https://doi.org/10.1007/s12221-020-1339-x
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12221-020-1339-x