Abstract
In order to obtain paper respirator with dust resistance performance and antibacterial property, silk photo-catalytic respirator paper was made by loading nano-TiO2 photo-catalyst on silk based respirator paper. The pore structure, surface topography and TiO2 distribution, and the filtration performance of silk respirator paper were studied by using a pore size meter (PSM), a field emission scanning electron microscope (FESEM), and a filter tester, respectively. In addition, the antibacterial property of silk respirator paper was also investigated. The results showed that the pore structure and filtration performance of silk respirator paper could be controlled by changing the degree of beating of silk pulp and the basis weight of silk paper. Silk respirator paper of 45 g/m2 made from silk pulp having beating degree of 85 oSR had high filtration efficiency and appropriate filtration resistance. Nano-TiO2 particles were mainly attached to the surface of silk paper, and the loading of nano-TiO2 photo-catalyst resulted in a slight decrease in filtration resistance and filtration efficiency of silk respirator paper. It, however, improved the antibacterial property of silk respirator paper effectively.
Article PDF
Similar content being viewed by others
References
K. Han and M. H. Yu, J. Appl. Polym. Sci., 100, 1588 (2006).
D. H. Cho, Fiber. Polym., 5, 326 (2004).
Y. H. Lu, H. Lin, Y. Y. Chen, C. Wang, and Y. R. Hua, Fiber. Polym., 18, 1 (2007).
M. L. Kaariainen, T. O. Kaariainen, and D. C. Cameron, Thin Solid Films, 517, 6666 (2009).
M. Montazer, E. Pakdel, and M. B. Moghadam, Fiber. Polym., 11, 967 (2010).
A. Fujishima and X. Zhang, C. R. Chim., 8, 750 (2005).
D. Chen, T. Wang, S. Yu, and Y. Jin, J. Mater. Eng., 11, 42 (2002).
O. Carp, C. L. Huisman, and A. Reller, Prog. Solid State Chem., 32, 33 (2004).
K. C. Wang, A. M. Morris, and J. D. Holmes, Chem. Mater., 17, 1269 (2005).
X. Yan, J. He, and D. G. Evans, J. Porous Mater., 11, 131 (2004).
Y. Hu, D. Rakhmawaty, M. Matsuoka, M. Takeuchin, and M. Anpo, J. Porous Mater., 13, 335 (2006).
T. Matsunaga and M. Okochi, Environ. Sci. Technol., 29, 501 (1995).
S. Ye, S. Liu, and M. He, Trans. Chin. Soc. Agric. Eng., 19, 180 (2009).
R. C. Brown, Ann. Occup. Hyg., 23, 367 (1980).
S. Shang, L. Zhu, W. Chen, L. Yi, D. Qi, and L. Yang, Fiber. Polym., 10, 807 (2009).
H. Akai, Int. J. Wild. Silkmoths Silk, 5, 255 (2000).
H. Tamako and K. Kato, J. Seric. Sci. Jpn., 66, 132 (1997).
K. Kato, J. Seric. Sci. Jpn., 67, 347 (1998).
H. Zhao and L. Sha, Pack. Eng., 29, 22 (2008).
H. Yamada, H. Nakao, Y. Takasu, and K. Tsubouchi, J. Mater. Sci. Eng. C, 14, 41 (2001).
Determining the Efficiency of Filter Element. High Efficiency Particulate Air Filter (HEPA and ULPA). BS EN 1822-5, 2000.
X. Jin, B. Yin, and H. Wu, Nonwovens, 11, 41 (2003).
S. Nagao, N. Mitani, M. Ikuta, and F. Kenji, U.S. Patent, 3,935,924 (1976).
S. Ruoyuan, K. Teruo, and I. Haruhiro, J. Text. Eng., 56, 71 (2010).
L. Sha and Z. Wang, Trans. Chin. Pulp. Pap., 20, 122 (2005).
L. Ruo, Chin. Personal Protection Equipment, 5, 13 (2004).
D. Han, Ind. Health, 38, 380 (2000).
G. Chi, S. Yao, J. Fan, W. Zhang, H. Wang, and G. Ren, Mater. Sci. Technol., 12, 52 (2004).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Sha, L., Zhao, H. Preparation and properties of Nano-TiO2 photo-catalytic silk respirator paper. Fibers Polym 13, 1159–1164 (2012). https://doi.org/10.1007/s12221-012-1159-8
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12221-012-1159-8