Abstract
A protective composite coating on an AZ31B magnesium alloy was prepared by anodic oxidation to form an oxide layer, followed by single immersion in maleic anhydride-g-liquid polybutadiene (MALPB) solution to cover a polymer coating on top. As a low-molecular weight polymer with low viscosity, MALPB had a tendency to infiltrate into the pores and cracks in the anodic layer to fill the defects among oxides so that a compact layer could be formed after it was cured by its hardeners, as observed by scanning electron microscopy (SEM). This compact layer, which was composed of anodic oxides integrated with solidified MALPB, possessed thickness around 0.7 μm as detected by energy dispersive X-ray (EDX). The anodized, MALPB-coated AZ31B alloy exhibited enhancement in corrosion resistance superior to that separately coated by anodizing oxides or MALPB, as reflected by its much higher corrosion potentials (E ccor) and lower corrosion current density (i corr) in DC polarization tests. Based on electrochemical impedance spectroscopy (EIS) data, we conclude that the anticorrosive performance of the composite coating can be attributed to the barrier effects provided by different layers when the electrolyte passed through the MALPB layer, compact layer, and then the inner anodic layer before it reached the surface of Mg alloy, and that among them, the compact layer acted as a much more effective barrier to the electrolyte. The appearance of damaged areas on the composite coating surface after a much longer duration in a salt spray environment revealed that the life-span of the AZ31B Mg alloy could be greatly prolonged if the pores and cracks on the anodizing films were properly sealed by suitable polymers.
Similar content being viewed by others
References
Zhao, M, Wu, SS, An, P, Luo, JR, Fukuda, Y, Nakae, H, “Microstructure and Corrosion Resistance of a Chromium-Free Multi-Elements Complex Coating on AZ91D Magnesium Alloy.” Mater. Chem. Phys., 99 (1) 54–60 (2006)
Zhao, H, Huang, ZH, Cui, JZ, “A Novel Method of Electroless Plating on AZ31 Magnesium Alloy Sheet.” J. Mater. Process. Technol., 203 (1–3) 310–314 (2008)
Gray, JE, Luan, B, “Protective Coatings on Magnesium and Its Alloys—A Critical Review.” J. Alloys Compd., 336 (1–2) 88–113 (2002)
Liu, JR, Guo, YN, Huang, WD, “Study on the Corrosion Resistance of Phytic Acid Conversion Coating for Magnesium Alloys.” Surf. Coat. Technol., 201 (3–4) 1536–1541 (2006)
Guo, HF, An, MZ, Xu, S, Huo, HB, “Microarc Oxidation of Corrosion Resistant Ceramic Coating on a Magnesium Alloy.” Mater. Lett., 60 (12) 1538–1541 (2006)
Hollstein, F, Weidemann, R, Scholz, J, “Characteristics of PVD-Coatings on AZ31hp Magnesium Alloys.” Surf. Coat. Technol., 162 (2–3) 261–268 (2003)
Mondal, AK, Kumar, S, Blawert, C, Dahotre, NB, “Effect of Laser Surface Treatment on Corrosion and Wear Resistance of ACM720 Mg Alloy.” Surf. Coat. Technol., 202 (14) 3187–3198 (2008)
Tian, XB, Wei, CB, Yang, SQ, Fu, RKY, Chu, PK, “Water Plasma Implantation/Oxidation of Magnesium Alloys for Corrosion Resistance.” Nucl. Instr. Meth. Phys. Res. B, 242 (1–2) 300–302 (2006)
Shi, ZM, Song, GL, Atrens, A, “The Corrosion Performance of Anodized Magnesium Alloys.” Corros. Sci., 48 (11) 3531–3546 (2006)
Zhang, YJ, Yan, CW, Wang, FH, Lou, HY, Cao, CN, “Study on the Environmentally Friendly Anodizing of AZ91D Magnesium Alloy.” Surf. Coat. Technol., 161 (1) 36–43 (2002)
Arrabal, R, Matykina, E, Viejo, F, Skeldon, P, Thompson, GE, “Corrosion Resistance of WE43 and AZ91D Magnesium Alloys with Phosphate PEO Coatings.” Corros. Sci., 50 (6) 1744–1752 (2008)
Mizutani, Y, Kim, SJ, Ichino, R, Okido, M, “Anodizing of Mg Alloys in Alkaline Solutions.” Surf. Coat. Technol., 169–170 (2) 143–146 (2003)
Guo, XW, Ding, WJ, Lu, C, Zhai, CQ, “Influence of Ultrasonic Power on the Structure and Composition of Anodizing Coatings Formed on Mg Alloys.” Surf. Coat. Technol., 183 (2–3) 359–368 (2004)
Wu, CS, Zhang, Z, Cao, FH, Zhang, LJ, Zhang, JQ, Cao, CN, “Study on the Anodizing of AZ31 Magnesium Alloys in Alkaline Borate Solutions.” Appl. Surf. Sci., 253 (8) 3893–3898 (2007)
Guo, Y, Wang, GX, Dong, GJ, Gong, F, Zhang, L, Zhang, ML, “Corrosion Resistance of Anodized AZ31 Mg Alloy in Borate Solution Containing Titania Sol.” J. Alloys Compd., 463 (1–2) 458–461 (2008)
Cheng, IC, Fu, EG, Liu, LD, Lee, CY, Lin, CS, “Effect of Fluorine Anions on Anodizing Behavior of AZ91 Magnesium Alloy in Alkaline Solutions.” J. Electrochem. Soc., 155 (5) C219–C225 (2008)
Wang, WM, Zhu, LO, Liu, HC, Li, WP, “Influence of Surface Pretreatment on the Anodizing Film of Mg Alloy and the Mechanism of the Ultrasound During the Pretreatment.” Surf. Coat. Technol., 202 (17) 4210–4217 (2008)
Hsiao, HY, Chung, P, Tsai, WT, “Baking Treatment Effect on Materials Characteristics and Electrochemical Behavior of Anodic Film Formed on AZ91D Magnesium Alloy.” Corros. Sci., 49 (2) 781–793 (2007)
Kannan, MB, Gomes, D, Dietzel, W, Abetz, V, “Polyoxadiazole-Based Coating for Corrosion Protection of Magnesium Alloy.” Surf. Coat. Technol., 202 (19) 4598–4601 (2008)
Kang, Z, Sang, J, Shao, M, Li, Y, “Polymer Plating on AZ31 Magnesium Alloy Surface and Film Evaluation of Corrosion Property.” J. Mater. Process. Technol., 209 (9) 4590–4594 (2009)
Truong, VT, Lai, PK, Moore, BT, Muscat, RF, Russo, MS, “Corrosion Protection of Magnesium by Electroactive Polypyrrole/Paint Coatings.” Synth. Met., 110 (1) 7–15 (2000)
Yfantis, AY, Paloumpa, I, Schmeizer, D, Yfantis, D, “Novel Corrosion-Resistant Films for Mg Alloys.” Surf. Coat. Technol., 151–152 (4) 400–404 (2002)
Sathiyanarayanan, S, Azim, SS, Venkatachari, G, “Corrosion Resistant Properties of Polyaniline–Acrylic Coating on Magnesium Alloy.” Appl. Surf. Sci., 253 (4) 2113–2117 (2006)
Khramov, AN, Balbyshev, VN, Kasten, LS, Mantz, RA, “Sol–Gel Coatings with Phosphonate Functionalities for Surface Modification of Magnesium Alloy.” Thin Solid Films, 514 (1–2) 174–181 (2006)
Lamaka, SV, Montemorc, MF, Galio, AF, Zheludkevich, ML, Trindade, C, Dick, LF, Ferreira, MGS, “Novel Hybrid Sol–Gel Coatings for Corrosion Protection of AZ31B Magnesium Alloy.” Electrochim. Acta, 53 (14) 4773–4783 (2008)
Rateick, RG, Xi, SJ, Birss, VI, “Sealing Methods for Enhanced Corrosion Protection of Anodized Magnesium Alloy WE43A-T6.” Magnesium Technology 2002 Symposium Held at the 2002 TMS Annual Meeting, Seattle, WA, Feb 2002
Mori, K, Hirahara, H, Oishi, Y, Kumagai, N, “Effect of Triazine Dithiols on the Polymer Plating of Magnesium Alloys.” International Workshop on Magnesium Platform Science and Technology, Nagaoka, Japon, July 2000
Mori, K, Kang, ZX, Oravec, J, Oishi, Y, “Corrosion Resistance of Polymer-Plated Magnesium Alloys.” 2nd International Conference on Platform Science and Technology for Advanced Magnesium Alloys, Osaka, Japan, Jan 2003
Kang, ZX, Li, YY, Mori, K, “Application of Polymer Plating to Inhibit Corrosion of Magnesium Alloy.” International Conference on Magnesium-Science, Technology and Applications, Beijing, China, Sep 2004
Herrera-Hernandez, H, Vargas-Garcia, JR, Hallen-Lopez, JM, Mansfeld, F, “Evaluation of Different Sealing Methods for Anodized Aluminum–Silicon Carbide (Al/SiC) Composites Using EIS and SEM Techniques.” Mater. Corros., 58 (11) 825–832 (2007)
Tang, JW, Wang, JW, He, YD, Tong, ZS, Shen, ZS, Li, XG, Li, BX, “Corrosion Protection of Galvanized Sheet by Maleic Anhydride-g-Liquid Polybutadiene Environmental Friendly Coatings.” Prog. Org. Coat., 63 (2) 195–200 (2008)
Wang, JW, Chen, L, He, YD, “Preparation of Environmental Friendly Coatings Based on Natural Shellac Modified by Diamine and Its Applications for Copper Protection.” Prog. Org. Coat., 62 (3) 307–312 (2008)
Guo, HF, An, MZ, Xu, S, Huo, HB, “Formation of Oxygen Bubbles and Its Influence on Current Efficiency in Micro-Arc Oxidation Process of AZ91D Magnesium Alloy.” Thin Solid Films, 485 (1–2) 53–58 (2005)
Zhu, YF, Lu, HM, Jiang, Q, Mimura, K, Isshiki, M, “Effect of Alloying Mg on Corrosion Resistance of Cu at High Temperature.” Electrochem. Soc., 154 (3) C153–C158 (2007)
Zhang, CH, Huang, XM, Zhang, ML, Gao, LL, Wu, RZ, “Electrochemical Characterization of the Corrosion of a Mg–Li Alloy.” Mater. Lett., 62 (14) 2177–2180 (2008)
Wang, XM, Zhu, LQ, Liu, HC, Li, WP, “Influence of Surface Pretreatment on the Anodizing Film of Mg Alloy and the Mechanism of the Ultrasound During the Pretreatment.” Surf. Coat. Technol., 202 (17) 4210–4217 (2008)
Zucchi, F, Frignani, A, Grassi, V, Balbo, A, Trabanelli, G, “Organo-Silane Coatings for AZ31 Magnesium Alloy Corrosion Protection.” Mater. Chem. Phys., 110 (2–3) 263–268 (2008)
Kannan, MB, Gomes, D, Dietzel, W, Abetz, V, “Polyoxadiazole-Based Coating for Corrosion Protection of Magnesium Alloy.” Surf. Coat. Technol., 202 (19) 4598–4601 (2008)
Duan, HP, Du, KQ, Yan, CW, Wang, FH, “Electrochemical Corrosion Behavior of Composite Coatings of Sealed MAO Film on Magnesium Alloy AZ91D.” Electrochim. Acta, 51 (14) 2898–2908 (2006)
Mansfeld, F, “Electrochemical Impedance Spectroscopy (EIS) as a New Tool for Investigating Methods of Corrosion Protection.” Electrochim. Acta, 35 (10) 1533–1544 (1990)
Chung, SC, Cheng, JR, Chiou, SD, “EIS Behavior of Anodized Zinc in Chloride Environments.” Corros. Sci., 42 (7) 1249–1268 (2000)
Ghasemi, A, Raja, VS, Blawert, C, Dietzel, W, Kainer, KU, “Study of the Structure and Corrosion Behavior of PEO Coatings on AM50 Magnesium Alloy by Electrochemical Impedance Spectroscopy.” Surf. Coat. Technol., 202 (15) 3513–3518 (2008)
Tepe, B, Gunay, B, “Evaluation of Pre-treatment Processes for HRS (Hot Rolled Steel) in Powder Coating.” Prog. Org. Coat., 62 (2) 134–144 (2008)
Poznyak, SK, Zheludkevich, ML, Raps, D, Gammel, F, Yasakau, KA, Ferreira, MGS, “Preparation and Corrosion Protective Properties of Nanostructured Titania-Containing Hybrid Sol–Gel Coatings on AA2024.” Prog. Org. Coat., 62 (2) 226–235 (2008)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Wang, J., Tang, J. & He, Y. Top coating of low-molecular weight polymer MALPB used for enhanced protection on anodized AZ31B Mg alloys. J Coat Technol Res 7, 737–746 (2010). https://doi.org/10.1007/s11998-010-9258-1
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11998-010-9258-1