Abstract
Shear punch mechanical testing was performed on neutron-irradiated HT-9 and 14YWT alloys, comparing the traditional ferritic/martensitic steel with the advanced oxide dispersion strengthened nanostructured ferritic alloy. The samples were irradiated at various temperatures between 380°C and 520°C. In HT-9, on increasing the irradiation temperature, the 1% offset shear stress and maximum shear stress decreased. The advanced 14YWT alloy was less sensitive to irradiation temperature with respect to irradiation hardening. However, it still exhibited irradiation hardening at each temperature.
Similar content being viewed by others
References
C.E. Lahm, J.F. Koenig, R.G. Pahl, D.L. Porter, and D.C. Crawford, J. Nucl. Mater. 204, 119 (1993).
D.S. Gelles, J. Nucl. Mater. 233, 293 (1996).
E. Aydogan, S.A. Maloy, O. Anderoglu, C. Sun, J.G. Gigax, L. Shao, F.A. Garner, I.E. Anderson, and J.J. Lewandowski, Acta Mater. 134, 116 (2017).
J.H. Kim, T.S. Byun, D.T. Hoelzer, S.-W. Kim, and B.H. Lee, Mater. Sci. Eng. A 559, 101 (2013).
J.H. Kim, T.S. Byun, D.T. Hoelzer, C.H. Park, J.T. Yeom, and J.K. Hong, Mater. Sci. Eng. A 559, 111 (2013).
G.R. Odette, JOM 66, 2427 (2014).
M.B. Toloczko, R.J. Kurtz, A. Hasegawa, and K. Abe, J. Nucl. Mater. 307, 1619 (2002).
R.K. Guduru, K.A. Darling, R. Kishore, R.O. Scattergood, C.C. Koch, and K.L. Murty, Mater Sci. Eng. A 395, 307 (2005).
R.K. Guduru, R.O. Scattergood, C.C. Koch, K.L. Murty, and A.V. Nagasekhar, Metall. Mater. Trans. A 37, 1477 (2006).
M.L. Hamilton, F.A. Garner, M.B. Toloczko, S.A. Maloy, W.F. Sommer, M.R. James, P.D. Ferguson, and M.R. Louthan, J. Nucl. Mater. 283, 418 (2000).
V. Karthik, P. Visweswaran, A. Vijayraghavan, K.V. Kasiviswanathan, and B. Raj, J. Nucl. Mater. 393, 425 (2009).
S.A. Maloy, T.J. Romero, P. Hosemann, M.B. Toloczko, and Y. Dai, J. Nucl. Mater. 417, 1005 (2011).
B.H. Sencer, J.R. Kennedy, J.I. Cole, S.A. Maloy, and F.A. Garner, J. Nucl. Mater. 393, 235 (2009).
T.S. Byun, M.B. Toloczko, T.A. Saleh, and S.A. Maloy, J. Nucl. Mater. 432, 1 (2013).
T.S. Byun, W.D. Lewis, M.B. Toloczko, and S.A. Maloy, J. Nucl. Mater. 421, 104 (2012).
O. Anderoglu, J. Van den Bosch, P. Hosemann, E. Stergar, B.H. Sencer, D. Bhattacharyya, R. Dickerson, P. Dickerson, M. Hartl, and S.A. Maloy, J. Nucl. Mater. 430, 194 (2012).
D.T. Hoelzer, K.A. Unocic, W. Tang, and Z. Feng, Oak Ridge Natl. Lab. (ORNL) (2015). https://doi.org/10.2172/1252141.
A. Izhutov, Y.M. Krasheninnikov, I.Y. Zhemkov, A.V. Varivtsev, Y.V. Naboishchikov, V.S. Neustroev, and V.K. Shamardin, Nucl. Eng. Technol 47, 253 (2015).
A.V. Varivtsev, I.Y. Zhemkov, A.V. Boev, O.V. Ishunina, Y.V. Naboyshchikov, N.S. Poglyad, and M.G. Sharonova, Nucl. Eng. Technol. 2, 126 (2016).
T. Lechtenberg, J. Nucl. Mater. 133, 149 (1985).
D.A. Terentyev, G. Bonny, and L. Malerba, Acta Mater. 56, 3229 (2008).
K.G. Field, X. Hu, K.C. Littrell, Y. Yamamoto, and L.L. Snead, J. Nucl. Mater. 465, 746 (2015).
J.J. Kai and G.L. Kulcinski, J. Nucl. Mater. 175, 227 (1990).
D.A. McClintock, D.T. Hoelzer, M.A. Sokolov, and R.K. Nanstad, J. Nucl. Mater. 386, 307 (2009).
E. Aydogan, J.S. Weaver, U. Carvajal-Nunez, M.M. Schneider, J.G. Gigax, D.L. Krumwiede, P. Hosemann, T.A. Saleh, N.A. Mara, D.T. Hoelzer, B. Hilton, and S.A. Maloy, Acta Mater. 167, 181 (2019).
M.J. Swenson, C.K. Dolph, and J.P. Wharry, J. Nucl. Mater. 479, 426 (2016).
Acknowledgements
Work was performed at Los Alamos National Laboratory. Los Alamos National Laboratory is an affirmative action/equal opportunity employer, and is operated by Triad National Security, LLC for the National Nuclear Security Administration of the US Department of Energy under Contract 89233218CNA000001. Also acknowledged is the SNAP program led by Dr. Gary Was at the University of Michigan, for preparing the samples and working with TerraPower LLC to organize this irradiation.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Eftink, B.P., Quintana, M.E., Romero, T.J. et al. Shear Punch Testing of Neutron-Irradiated HT-9 and 14YWT. JOM 72, 1703–1709 (2020). https://doi.org/10.1007/s11837-020-04011-z
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11837-020-04011-z