Abstract
Cubic boron nitride (cBN) particles were mixed into superfine tungsten carbide (WC), and then cBN-WC-cobalt (Co) composites were prepared using spark plasma sintering method. The influence of the processing parameters on the microstructures and the mechanical properties of the cBN-WC-Co composites were investigated. The results indicated that the cBN particles arranged uniformly and had an excellent adhesion with WC matrix. There was no evidence of phase transformation from cBN to hBN. With the increasing of the sintering temperature, the liquid-phase Co was increased and entered the micro-pores between WC and cBN particles easily. Correspondingly, the density, the flexural strength, and the hardness of the cBN-WC-Co composites also increased. With the further increasing of the sintering temperature, WC grains grew leading to the reduction of the hardness. Therefore, the hardness of the samples increased to a maximum value of 2978 HV at 1250 °C, and then decreased with the sintering temperature. The experimental results also showed that the density, the flexural strength, and the hardness of cBN-WC-Co composites increased with the holding time, whereas the hardness presented a decreasing tendency when the holding time exceeded 7 min.
Similar content being viewed by others
References
G. Saurav, X.C. Luo, R.L. Reuben, and W.B. Rashid, Replacing Diamond Cutting Tools with CBN for Efficient Nanometric Cutting of Silicon, Mater. Lett., 2012, 68, p 507–509
G.F. Zhang, B. Zhang, Z.H. Deng, and Y.Q. Tan, An Experimental Study on a Novel Diamond Whisker Wheel, CIRP Annu. Manuf. Technol., 2010, 59, p 355–360
W.F. Ding, J.H. Xu, Z.Z. Chen, C.Y. Yang, C.J. Song, and Y.C. Fu, Fabrication and Performance of Porous Metal-Bonded CBN Grinding Wheels Using Alumina Bubble Particles as Pore-Forming Agents, Int. J. Adv. Manuf. Technol., 2013, 67, p 1309–1315
W.F. Ding, J.H. Xu, Z.Z. Chen, H.H. Su, and Y.C. Fu, Grain Wear of Brazed Polycrystalline CBN Abrasive Tools During Constant-Force Grinding Ti-6Al-4 V Alloy, Int. J. Adv. Manuf. Technol., 2011, 52, p 969–976
X.H. Zhang, W.K. An, and H. Cao, An Expert System of Cubic Nitride (cBN) Grinding Wheel Dressing in Cam Grinding, Mater. Manuf. Process., 2012, 27(10), p 1095–1100
X.H. Zhang, Z.H. Deng, W.K. An, and H. Cao, A Methodology for Contour Error Intelligent Precompensation in Cam Grinding, Int. J. Adv. Manuf. Technol., 2013, 64, p 165–170
Y.H. Ren, B. Zhang, and Z.X. Zhou, Specific Energy in Grinding of Tungsten Carbides of Various Grain Sizes, CIRP Annu. Manuf. Technol., 2009, 58, p 299–302
S.H. Chang and P.Y. Chang, Study on the Mechanical Properties, Microstructure and Corrosion Behaviors of Nano-WC-Co-Ni-Fe Hard Materials Through HIP and Hot-Press Sintering Processes, Mater. Sci. Eng., A, 2014, 618, p 56–62
V. Martínez and J. Echeberria, Hot isostatic Pressing of Cubic Boron Nitride-Tungsten Carbide/Cobalt (cBN-WC/Co) Composites: Effect of cBN Particle Size and some Processing Parameters on Their Microstructure and Properties, J. Am. Ceram. Soc., 2007, 90(2), p 415–424
M. Rosinski and A. Michalski, WCCo/cBN Composites Produced by Pulse Plasma Sintering Method, J. Mater. Sci., 2012, 47, p 7064–7071
X.L. Shi, H. Yang, G.Q. Shao, X.L. Duan, F.R. Zhou, and P. Sun, Improvement of Preparation of Cubic Boron Nitride Dispersed WC-10Co Composites, Mater. Mech. Eng., 2007, 31(4), p 71–73
B. Wang, Y. Qin, F. Jin, J.F. Yang, and K. Ishizaki, Pulse Electric Current Sintering of Cubic Boron Nitride/Tungsten Carbide-Cobalt (cBN/WC-Co) Composites: Effect of cBN Particle Size and Volume Fraction on Their Microstructure and Properties, Mater. Sci. Eng., A, 2014, 607, p 490–497
B. Ertuğ and F. Zhang, Sintering Applications, InTech, Rijeka, 2013
D. Sivaprahasam, S.B. Chandrasekar, and R. Sundaresan, Microstructure and Mechanical Properties of Nanocrystalline WC-12Co Consolidated by Spark Plasma Sintering, Int. J. Refract. Met. Hard Mater., 2007, 25, p 144–152
B. Wang, K. Matsumaru, J.F. Yang, Z.Y. Fu, and K. Ishizaki, The Effect of cBN Additions on Densification, Microstructure and Properties of WC-Co Composites by Pulse Electric Current Sintering, J. Am. Ceram. Soc., 2012, 95(8), p 2499–2503
B. Yaman and H. Mandal, Wear Performance of Spark Plasma Sintered Co/WC and cBN/Co/WC Composites, Int. J. Refract. Met. Hard Mater., 2014, 42, p 9–16
C. Mao, Y.H. Ren, H.Y. Gan, M.J. Zhang, J. Zhang, and K. Tang, Microstructure and Mechanical Properties of cBN-WC-Co Composites used for Cutting Tools, Int. J. Adv. Manuf. Technol., 2015, 76, p 2043–2049
Administration of Quality and Technology Supervision of PRC. GB/T14452-1993, Metallic Materials: Determination of Bending Mechanical Properties. The national standard of the People’s Republic of China, 1993, p 1–19.
C.H. Wu, Melting Point Temperature of Co Phase in a Series of WC-Co Cemented Carbides, Cem. Carbide, 1999, 16(4), p 201–205
S.W. Wang, L.D. Chen, Y.S. Kang, M. Niino, and T. Hirai, Effect of Plasma Activated Sintering (PAS) Parameters on Densification of Copper Powder, Mater. Res. Bull., 2000, 35(4), p 619–628
S.W. Wang, L.D. Chen, and T. Hirai, Densification of Al2O3 Powder Using Spark Plasma Sintering, J. Mater. Res., 2000, 15(4), p 982–987
X.L. Xi, X. Pi, Z. Nie, S.L. Song, X.Y. Xu, and T.Y. Zuo, Synthesis and Characterization of Ultrafine WC-Co by Freeze-Drying and Spark Plasma Sintering, Int. J. Refract. Met. Hard Mater., 2009, 27, p 101–104
F.M. Zhang, J. Shen, and J.F. Sun, The Effect of Phosphorus Additions on Densification, Grain Growth and Properties of Nanocrystalline WC-Co Composites, J. Alloys Compd., 2004, 385, p 96–103
H.Y. Rong, Z.J. Peng, X.Y. Ren, C.B. Wang, Z.Q. Fu, L.H. Qi, and H.Z. Miao, Microstructure and Mechanical Properties of Ultrafine WC-Ni-VC-TaC-cBN Cemented Carbides Fabricated by Spark Plasma Sintering, Int. J. Refract. Met. Hard Mater., 2011, 29, p 733–738
Acknowledgments
This project was sponsored by the National Natural Science Foundation of China (Grant Nos. 51375061, 51275436) and Changsha City Planned Science and Technology Project (Grant No. K1406031-11).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Mao, C., Zhang, M., Zhang, J. et al. The Effect of Processing Parameters on the Performance of Spark Plasma Sintered cBN-WC-Co Composites. J. of Materi Eng and Perform 24, 4612–4619 (2015). https://doi.org/10.1007/s11665-015-1777-6
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11665-015-1777-6