Abstract
The morphological and electrochemical properties of nickel–cobalt double hydroxide (Ni-Co DH), cobalt hydroxide [Co(OH)2], and nickel hydroxide [Ni(OH)2] prepared directly on a transparent conductive oxide substrate via a simple one-pot wet-chemical method have been investigated and compared. All samples were composed of nanosheets vertically aligned on the substrate. Comparison of the results showed that Ni-Co DH with submicrometer-scale pores had more compact structure than Ni(OH)2 or Co(OH)2. Moreover, the highly symmetric cyclic voltammetry (CV) curves of Ni-Co DH indicated its good electrochemical reversibility. The specific capacitance value of Ni-Co DH was ∼ 286 F/g and ∼ 210 F/g at scan rate of 2 mV/s and 100 mV/s, respectively, indicating its better rate capability, particularly at high scan rate, than Ni(OH)2 or Co(OH)2. In addition, after CV cycling test, the Ni-Co DH nanosheets showed no noticeable morphological change. Furthermore, the electrochromic performance of Ni-Co DH was sustained over 10000 s. Thus, Ni-Co DH prepared via a facile one-step process exhibited promising characteristics as a cost-effective functional material for use in electrochemical devices.
Similar content being viewed by others
References
D.S. Hall, D.J. Lockwood, C. Bock, and B.R. MacDougall, Proc. R. Soc. A 471, 0792 (2014).
H. Li, Y. Yu, M.B. Starr, Z. Li, and X. Wang, J. Phys. Chem. Lett. 6, 3410 (2015).
Y. Wang, D. Zhang, and H. Liu, J. Power Sources 195, 3135 (2010).
E.G.C. Neiva, M.M. Oliveira, M.F. Bergamini, L.H. Marcolino Jr., and A.J.G. Zarbin, Sci. Rep. 6, 33806 (2016).
J. Pu, Y. Tong, S. Wang, E. Sheng, and Z. Wang, J. Power Sources 250, 250 (2014).
D. Zha, H. Sun, Y. Fu, X. Ouyang, and X. Wang, Electrochim. Acta 236, 18 (2017).
C. Xing, F. Musharavati, H. Li, E. Zalezhad, O.K.S. Hui, S. Bae, and B.-Y. Cho, RSC Adv. 7, 38945 (2017).
J.S. Chen, Y. Gui, and D.J. Blackwood, Electrochim. Acta 188, 863 (2016).
Z.-A. Hu, Y.-L. Xie, Y.-X. Wang, H.-Y. Wu, Y.-Y. Yang, and Z.-Y. Zhang, Electrochim. Acta 54, 2737 (2009).
R. Li, Z. Hu, X. Shao, P. Cheng, S. Li, W. Yu, W. Lin, and D. Yuan, Sci. Rep. 6, 18737 (2016).
W. Jiao and L. Zhang, Curr. Appl. Phys. 16, 115 (2016).
K.H. Kim, M. Mikami, Y. Abe, M. Kawamura, and T. Kiba, Thin Solid Films 654, 49 (2018).
K.H. Kim, M. Mikami, Y. Abe, M. Kawamura, and T. Kiba, Int. J. Electrochem. Sci. 13, 7655 (2018).
W.Q. Wang, Z.J. Yao, X.L. Wang, X.H. Xia, C.D. Gu, and J.P. Tu, J. Colloid Interface Sci. 535, 300 (2019).
Z. Bi, X. Li, Y. Chen, X. Xu, S. Zhang, and Q. Zhu, Electrochim. Acta 227, 61 (2017).
Y. Abe, S. Yamauchi, M. Kawamura, K.H. Kim, and T. Kiba, J. Vac. Sci. Technol. A 36, 02C102 (2018).
X. Wang, L. Wan, T. Yu, Y. Zhou, J. Guan, Z. Yu, Z. Li, and Z. Zou, Mater. Chem. Phys. 126, 494 (2011).
Y. Zhu, C. Cao, S. Tao, W. Chu, Z. Wu, and Y. Li, Sci. Rep. 4, 5787 (2014).
M.A. Vidales-Hurtado and A. Mendoza-Galván, Solid State Ion. 179, 2065 (2008).
Z. Pu, Q. Liu, A.H. Qusti, A.M. Asiri, A.O. Al-Youbi, and X. Sun, Electrochim. Acta 409, 252 (2013).
Q. Wang, S. Liu, H. Sun, and Q. Lu, RSC Adv. 5, 48181 (2015).
H. Wang, H.S. Casalongue, Y. Liang, and H. Dai, J. Am. Chem. Soc. 132, 7472 (2010).
D. Xia, H. Chen, J. Jiang, L. Zhang, Y. Zhao, D. Guo, and J. Yu, Electrochim. Acta 156, 108 (2015).
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
About this article
Cite this article
Kim, K.H., Motoyama, S., Abe, Y. et al. Comparative Study on Morphological and Electrochemical Properties of Nickel–Cobalt Double Hydroxide, Cobalt Hydroxide, and Nickel Hydroxide. J. Electron. Mater. 48, 3000–3005 (2019). https://doi.org/10.1007/s11664-019-07051-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-019-07051-7