Abstract
There is a need for next-generation, high-performance power electronic packages and systems employing wide-bandgap devices to operate at high temperatures in automotive and electric grid applications. Sintered silver joints are currently being evaluated as an alternative to Pb-free solder joints. Of particular interest is the development of joints based on silver paste consisting of nano- or micron-scale particles that can be processed without application of external pressure. The microstructural evolution at the interface of a pressureless-sintered silver joint formed between a SiC die with Ti/Ni/Au metallization and an active metal brazed (AMB) substrate with Ag metallization at 250°C has been evaluated using scanning electron microscopy (SEM), x-ray microanalysis, and x-ray photoelectron spectroscopy (XPS). Results from focused ion beam (FIB) cross-sections show that, during sintering, pores in the sintered region near to the Au layer tend to be narrow and elongated with long axis oriented parallel to the interface. Further densification results in formation of many small, relatively equiaxed pores aligned parallel to the interface, creating a path for easy crack propagation. X-ray microanalysis results confirm interdiffusion between Au and Ag and that a region with poor mechanical strength is formed at the edge of this region of interdiffusion.
Similar content being viewed by others
References
V.R. Manikam and K.Y. Cheong, IEEE Trans. Compon. Packag. Manuf. Technol. 1, 457 (2011).
G. Muralidharan, K. Kurumadali, A.K. Kercher, L. Walker, and S. Leslie, J. Electron. Mater. 42, 240 (2013).
K.S. Siow, J. Electron. Mater. 43, 947 (2014).
J.G. Bai and G.-Q. Lu, IEEE Trans. Device Mater. Rel. 6, 436 (2006).
J.G. Bai, J. Yin, Z. Zhang, G.-Q. Lu, and J.D. van Wyk, IEEE Trans. Adv. Packag. 30, 506 (2007).
J.G. Bai, J.N. Calata, and G.-Q. Lu, IEEE Trans. Electron. Packag. Manuf. 30, 241 (2007).
T. Wang, X. Chen, G.-Q. Lu, and G.-Y. Lei, J. Electron. Mater. 36, 1333 (2007).
T.G. Lei, J.N. Calata, G.-Q. Lu, X. Chen, and S. Luo, IEEE Trans. Compon. Packag. Technol. 33, 98 (2010).
T. Wang, M. Zhao, X. Chen, G.-Q. Lu, K. Ngo, and S. Luo, J. Electron. Mater. 41, 2543 (2012).
K. Xiao, J.N. Calata, H. Zheng, K.D.T. Ngo, and G.-Q. Lu, IEEE Trans. Compon. Packag. Manuf. Technol. 3, 1271 (2013).
H. Zheng, D. Berry, J.N. Calata, K.D.T. Ngo, S. Luo, and G.-Q. Lu, IEEE Trans. Compon. Packag. Manuf. Technol. 3, 915 (2013).
S. Wang, M. Li, H. Ji, and C. Wang, Scr. Mater. 69, 789 (2013).
F. Yu, R.W. Johnson, and M.C. Hamilton, IEEE Trans. Compon. Packag. Manuf. Technol. 5, 1258 (2015).
S.A. Paknejad, G. Dumas, G. West, G. Lewis, and S.H. Mannan, J. Alloys Compd. 617, 994 (2014).
C.H. Sha and C.C. Lee, IEEE Trans. Compon. Packag. Manuf. Technol. 1, 1258 (2011).
R.G. Kirsch, J.M. Poate, and M. Eibschutz, Appl. Phys. Lett. 29, 772 (1976).
Y. Liu and Y. Sun, Nanoscale 7, 13687 (2015).
H.L. Skriver and N.M. Rosengaard, Phys. Rev. B 46, 7157 (1992).
H.R. Gong, Mater. Chem. Phys. 123, 326 (2010).
Y. Liu, L. Zhang, D. Yu, and Y. Ge, J. Phase Equilib. Diffus. 29, 405 (2008).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Muralidharan, G., Leonard, D.N. & Meyer, H.M. Effect of Gold on the Microstructural Evolution and Integrity of a Sintered Silver Joint. J. Electron. Mater. 46, 4085–4092 (2017). https://doi.org/10.1007/s11664-016-5216-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-016-5216-8