Yttrium-doped Y x Bi2−x Te3 (x = 0.15, 0.2, 0.25) flower-like nanopowders were synthesized by the hydrothermal method through careful adjustment of the amount of ethylenediaminetetraacetic acid surfactant. The flower-like nanopowders were hot pressed into bulk pellets, and the thermoelectric properties of the pellets were examined. The results showed that the optimized doped sample Y0.25Bi1.75Te3 had a relatively high Seebeck coefficient, a lower electrical resistivity, and a lower thermal conductivity. As a result, the figure of merit of the n-type Y0.25Bi1.75Te3 alloy reached 1.23 at 410 K.
Similar content being viewed by others
References
J.R. Sootsman, D.Y. Chung, and M.G. Kanatzidis, Angew. Chem. Int. Ed. 48, 8616 (2009).
A.J. Minnich, M.S. Dresselhaus, Z.F. Ren, and G. Chen, Energy Environ. Sci. 2, 466 (2009).
G.J. Snyder and E.S. Toberer, Nat. Mater. 7, 105 (2008).
J.R. Drabble and C.H.L. Goodman, J. Phys. Chem. Solids 5, 142 (1958).
Y.Q. Cao, T.J. Zhu, X.B. Zhao, X.B. Zhang, and J.P. Tu, Appl. Phys. A 324, 321 (2008).
S.Y. Wang, W.J. Xie, H. Li, and X.F. Tang, Intermetallics 19, 1024 (2011).
B. Poudel, Q. Hao, Y. Ma, Y. Lan, A. Minnich, B. Yu, X. Yan, D. Wang, A. Muto, D. Vashaee, X. Chen, J. Liu, M.S. Dresselhaus, G. Chen, and Z. Ren, Science 320, 634 (2008).
F. Wu, H.Z. Song, F. Gao, W.Y. Shi, J.F. Jia, and X. Hu, J. Electron. Mater. 42, 1140 (2013).
F. Wu, H.Z. Song, J.F. Jia, and X. Hu, Prog. Nat. Sci. Mater. Int. 23, 408 (2013).
Q. Zhao and Y.G. Wang, J. Alloys Compd. 497, 57 (2010).
X.B. Zhao, X.H. Ji, Y.H. Zhang, G.S. Cao, and J.P. Tu, Appl. Phys. A 80, 1567 (2005).
Z. Wang, F.Q. Wang, H. Chen, L. Zhu, H.J. Yu, and X.Y. Jian, J. Alloys Compd. 492, L50 (2010).
T. Sun, X.B. Zhao, T.J. Zhu, and J.P. Tu, Mater. Lett. 60, 2534 (2006).
H.L. Ni, X.B. Zhao, T.J. Zhu, X.H. Ji, and J.P. Tu, J. Alloys Compd. 397, 317 (2005).
M. Salavati-Niasari, M. Bazarganipour, and F. Davara, J. Alloys Compd. 489, 530 (2010).
Y. Deng, C.W. Nan, G.D. Wei, L. Guo, and Y.H. Lin, Chem. Phys. Lett. 374, 410 (2003).
Ö. Ceyda Yelgel and G.P. Srivastava, J. Appl. Phys. 113, 073709 (2013).
Y.C. Dou, X.Y. Qin, D. Li, L.L. Li, T.H. Zou, and Q.Q. Wang, J. Appl. Phys. 114, 044906 (2013).
Y.C. Lan, A.J. Minnich, G. Chen, and Z.F. Ren, Adv. Funct. Mater. 357, 20 (2010).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Shi, W., Wu, F., Wang, K. et al. Preparation and Thermoelectric Properties of Yttrium-Doped Bi2Te3 Flower-Like Nanopowders. J. Electron. Mater. 43, 3162–3168 (2014). https://doi.org/10.1007/s11664-014-3220-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-014-3220-4