Comparative Study of ENIG and ENEPIG as Surface Finishes for a Sn-Ag-Cu Solder Joint

  • Published:
Journal of Electronic Materials Aims and scope Submit manuscript

Abstract

Interfacial reactions and joint reliability of Sn-3.0Ag-0.5Cu solder with two different surface finishes, electroless nickel-immersion gold (ENIG) and electroless nickel-electroless palladium-immersion gold (ENEPIG), were evaluated during a reflow process. We first compared the interfacial reactions of the two solder joints and also successfully revealed a connection between the interfacial reaction behavior and mechanical reliability. The Sn-Ag-Cu/ENIG joint exhibited a higher intermetallic compound (IMC) growth rate and a higher consumption rate of the Ni(P) layer than the Sn-Ag-Cu/ENEPIG joint. The presence of the Pd layer in the ENEPIG suppressed the growth of the interfacial IMC layer and the consumption of the Ni(P) layer, resulting in the superior interfacial stability of the solder joint. The shear test results show that the ENIG joint fractured along the interface, exhibiting indications of brittle failure possibly due to the brittle IMC layer. In contrast, the failure of the ENEPIG joint only went through the bulk solder, supporting the idea that the interface is mechanically reliable. The results from this study confirm that the Sn-Ag-Cu/ENEPIG solder joint is mechanically robust and, thus, the combination is a viable option for a Pb-free package system.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. M. Abtew and G. Selvaduary, Mater. Sci. Eng. R 27, 95 (2000).

    Article  Google Scholar 

  2. C.M.L. Wu, D.Q. Yu, C.M.T. Law, and L. Wang, Mater. Sci. Eng. R 44, 1 (2004).

    Article  Google Scholar 

  3. G. Milad and D. Gudeczauskas, Met. Finish. 104, 33 (2006).

    Article  CAS  Google Scholar 

  4. G. Milad and M. Orduz, Met. Finish. 105, 25 (2007).

    Article  Google Scholar 

  5. Y.W. Yen, P.H. Tsai, Y.K. Fang, S.C. Lo, Y.P. Hsieh, and C. Lee, J. Alloys Compd. 503, 25 (2010).

    Article  CAS  Google Scholar 

  6. S.P. Peng, W.H. Wu, C.E. Ho, and Y.M. Huang, J. Alloys Compd. 493, 431 (2010).

    Article  CAS  Google Scholar 

  7. W.H. Wu, C.S. Lin, S.H. Huang, and C.E. Ho, J. Electron. Mater. 39, 2387 (2010).

    Article  CAS  Google Scholar 

  8. H.B. Kang, J.W. Lee, J.H. Bae, M.H. Park, J.W. Yoon, S.B. Jung, J.S. Ju, and C.W. Yang, J. Mater. Res. 23, 2195 (2008).

    Article  CAS  Google Scholar 

  9. H.S. Chun, J.W. Yoon, and S.B. Jung, J. Alloys Compd. 439, 91 (2007).

    Article  CAS  Google Scholar 

  10. J.W. Yoon and S.B. Jung, Z. Metallkd. 96, 1420 (2005).

    CAS  Google Scholar 

  11. J.W. Yoon, B.I. Noh, J.H. Yoon, H.B. Kang, and S.B. Jung, J. Alloys Compd. 509, L153 (2011).

    Article  CAS  Google Scholar 

  12. W.M. Chen, M. McCloskey, and S.C. O’Mathuna, Microelectron. Reliab. 46, 896 (2006).

    Article  CAS  Google Scholar 

  13. J.W. Yoon, J.H. Lim, W.C. Moon, H.J. Lee, J. Joo, and S.B. Jung, J. Mater. Res. 21, 3196 (2006).

    Article  CAS  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. School of Advanced Materials Science and Engineering, Sungkyunkwan University, 300 Cheoncheon-dong, Jangan-gu, Suwon, 440-746, Republic of Korea

    Jeong-Won Yoon, Bo-In Noh & Seung-Boo Jung

Authors
  1. Jeong-Won Yoon
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Bo-In Noh
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Seung-Boo Jung
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Jeong-Won Yoon.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Yoon, JW., Noh, BI. & Jung, SB. Comparative Study of ENIG and ENEPIG as Surface Finishes for a Sn-Ag-Cu Solder Joint. J. Electron. Mater. 40, 1950–1955 (2011). https://doi.org/10.1007/s11664-011-1686-x

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11664-011-1686-x

Keywords

Search

Navigation