Abstract
Transmission electron microscopy and small-probe microanalysis have been used to investigate the microstructure and compositional profiles of CdTe(211)B/ZnTe/Si(211) heterostructures. Thin ZnTe buffer layers and subsequent thick CdTe layers were grown on Si(211) substrates using molecular beam epitaxy. Many {111}-type stacking faults were found to be present throughout the entire ZnTe layer, terminating near the point of initiation of CdTe growth. A rotation angle of about 3.5° was observed between lattice planes of the Si substrate and the final CdTe epilayer. Local lattice parameter measurement and elemental profiles indicated that some intermixing of Zn and Cd had taken place. The average widths of the ZnTe layer and the (Cd,Zn)Te transition region were found to be roughly 6.5 nm and 3.5 nm, respectively.
Similar content being viewed by others
References
M.A. Kinch, J. Electron. Mater. 39, 1043 (2010).
T.J. de Lyon, J.E. Jensen, M.D. Gorwitz, C.A. Cockrum, S.M. Johnson, and G.M. Venzor, J. Electron. Mater. 28, 705 (1999).
D.J. Smith, S.C.Y. Tsen, D. Chandrasekhar, P.A. Crozier, S. Rujirawat, G. Brill, Y.P. Chen, R. Sporken, and S. Sivananthan, Mater. Sci. Eng. B 77, 93 (2000).
Y. Chen, S. Farrell, G. Brill, P. Wijewarnasuriya, and N. Dhar, J. Cryst. Growth 310, 5303 (2008).
R.N. Jacobs, P.J. Smith, J.K. Markunas, J.D. Benson, and J. Pellegrino, J. Electron. Mater. 39, 1036 (2010).
Y.P. Chen, S. Sivananthan, and J.P. Faurie, J. Electron. Mater. 22, 951 (1993).
Y.P. Chen, J.P. Faurie, S. Sivananthan, G.C. Hua, and N. Otsuka, J. Electron. Mater. 24, 475 (1995).
Y. Xin, N.D. Browning, S. Rujirawat, S. Sivananthan, Y.P. Chen, P.D. Nellist, and S.J. Pennycook, J. Appl. Phys. 84, 4292 (1998).
H.Y. Wei, L. Salamance-Riba, and N.K. Dhar, Mater. Res. Soc. Symp. Proc. 484, 329 (1998).
N.K. Dhar, C.E.C. Wood, A. Gray, H.Y. Wei, L. Salamanca-Riba, and J.H. Dinan, J. Vac. Sci. Technol. B 14, 2366 (1996).
N.K. Dhar, P.R. Boyd, M. Martinka, J.H. Dinan, L.A. Almeida, and N. Goldsman, J. Electron. Mater. 29, 748 (2000).
N.K. Dhar, N. Goldsman, and C.E.C. Wood, Phys. Rev. B 61, 8256 (2000).
B. Brill, Y. Chen, N.K. Dhar, and R. Singh, J. Electron Mater. 32, 717 (2003).
M. Jaime-Vasquez, M. Martinka, R.N. Jacobs, and M. Groenert, J. Electron Mater. 35, 1455 (2006).
M. Jaime-Vasquez, M. Martinka, R.N. Jacobs, and J.D. Benson, J. Electron. Mater. 36, 905 (2007).
M. Jaime-Vasquez, R.N. Jacobs, J.D. Benson, A.J. Stoltz, L.A. Almeida, L.O. Bubulac, Y. Chen, and G. Brill, J. Electron. Mater. 39, 951 (2010).
W. Kern and D.A. Puotinen, RCA Rev. 31, 187 (1970).
R.N. Jacobs, J. Markunas, J. Pellegrino, L.A. Almeida, M. Groenert, M. Jaime-Vasquez, N. Mahadik, C. Andrews, and S.B. Qadri, J. Cryst. Growth 310, 2960 (2008).
C. Wang, D.J. Smith, S. Tobin, T. Parodos, J. Zhao, Y. Chang, and S. Sivananthan, J. Vac. Sci. Technol. A 24, 995 (2006).
S.J. Pennycook and D.E. Jesson, Ultramicroscopy 37, 14 (1991).
S. Rujirawat, Y. Xin, N.D. Browning, S. Sivananthan, D.J. Smith, S.C.Y. Tsen, Y.P. Chen, and V. Nathan, Appl. Phys. Lett. 74, 2346 (1999).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
ZHAO, W.F., JACOBS, R.N., JAIME-VASQUEZ, M. et al. Microstructural Characterization of CdTe(211)B/ZnTe/Si(211) Heterostructures Grown by Molecular Beam Epitaxy. J. Electron. Mater. 40, 1733–1737 (2011). https://doi.org/10.1007/s11664-011-1673-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-011-1673-2