Abstract
Diatomite was used as raw material to prepare sodium silicate with a modulus of 3.1 by alkali dissolution method and the resulted sodium silicate solution was employed as a precursor. Methyl methacrylate monomers were introduced in wet gels through solution-immersion, and upon heating at 70 °C, the mesoporous surfaces throughout the skeletal framework were coated with the polymer layer. PMMA modified silica aerogels were successfully synthesized via ambient pressure drying. The properties were investigated by FTIR, NMR, TGA, nitrogen adsorption-desorption, FESEM and nano-indentation, etc. Results indicate that with the increasing of PMMA incorporated into silica aerogels, the bulk density and the BET surface area increase, the porosity decreases. Through the observation of FESEM, it is found that the interconnecting pores and the big pores add, the pore size distribution expands from 5–17 to 28–150 nm. By comparison, the PMMA modified silica aerogels achieve a 52-fold increase in hardness and a 10-fold increase in modulus.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
N Hüsing, U Schubert. Aerogels [M]. Weinheim: Wiley, 2005
L W Hrubesh. Aerogel Application [J]. J. Non-cryst. Solids, 1998, 225: 335–342
D A Soleimani, M H Abbasi. Silica Aerogel: Synthesis, Properties and Characterization [J]. J. Mater. Process Tech., 2008, 199(1–3): 10–11
D Sharad, Bhagat, Y H Kim, et al. Rapid Synthesis of Water-glass Based Aerogels by in Situ Surface Modification of the Hydrogels [J]. Appl. Surf. Sci., 2007, 253(6): 3 231–3 236
A C Pierre, G M Pajonk. Chemistry of Aerogels and Their Applications [J]. Chem. Rev., 2002, 102: 4 243–4 265
M Reim, W Korner, J Manara, et al. Silica Aerogel Granulate Material for Thermal Insulation and Daylighting [J]. Solar Ener., 2005, 79(2): 131–139
L Jyoti Gurav, I K Jung, P H Hyung, et al. Silica Aerogel: Synthesis and Applications [J]. J. Nanomater, 2010, 2010: 1–11
J J Zhu, J Yao, X M Lu, et al. Synthesis and Characterization of Superhydrophobic Mesoporous Silica Aerogels by Ambient Pressure Drying [J]. J. Chinese Ceram. Soc., 2009, 37(4): 512–515
Y N Digambar, A V Rao. Methyltriethoxysilane: New Precursor for Synthesizing Silica Aerogels [J]. J. Alloys Compd., 2009, 467: 397–404
U K H Bangi, A V Rao, and A P Rao. A New Route for Preparation of Sodium-Silicate-Based Hydrophobic Silica Aerogels via Ambient-Pressure Drying [J]. Sci. Technol. Adv. Mater., 2008, 9:1–10
G W Liu, W B Zhou, X Y Ni, et al. Preparation of Super-Hydrophobic SiO2 Aerogel Monoliths from Sodium Silicate [J]. J. Chinese Ceram. Soc., 2012, 40(1): 160–164
G H Hou. Preparation of Silica Aerogels by Rice Husk [J]. J. Inorg. Mater., 2003, 02: 407–412
M A M Khralsheh, Y S Aldegs, W A Mcminn. Remediation of Waste Water Containing Heavy Metals using Raw and Modified Diatomite [J]. J. Chem. Eng., 2004, 99(29):177–184
J Liu, D F Zhao. The Present Situation and Development of Diatomite [J]. Environ. Sci. Manag., 2009, 34(5): 104–106
B M Wang, Y Han, K Song. Methods for Improving Strength and Toughness of Silica Aerogels [J]. Mater. Rev., 2011, 23: 55–58
B M Wang, K Song, Y Han. Synthesis and Characterization of Multi-walled Carbon Nanotube Doped Silica Aerogels [J]. J.Wuhan University of Technology -Mater.Sci.Ed., 2012, 27(3):1–4
H L Yang, X M Kong, E X Cao, et al. Advances in Studies on Polymer Modified Silica Aerogels [J]. Mater. Rev., 2011, 21:13–18+28
M A B Meador, L A Capadona, L M Corkle, et al. Structureproperty Relationships in Porous 3D Nanostructures as a Function of Preparation Conditions: Isocyanate Cross-linked Silica Aerogels [J]. Chem. Mater., 2007, 19: 2 247–2 260
F M Jia, J T Chen, S L Zheng. Study on Techniques of Preparation of Sodium Silicate by Diatomite [J]. Non-Metallic Mines, 2006, 29(4): 31–33
L J Wang, S Y Zhao. Synthesis and Characteristics of Mesoporous Silica Aerogels with One-step Solvent Exchange/Surface Modification [J]. J.Wuhan University of Technology -Mater.Sci.Ed., 2009, 24: 613–618
F Shi, L J Wang, J X Liu. Synthesis and Characterization of Silica Aerogels by a Novel Fast Ambient Pressure Drying Process [J]. Mater. Lett., 2006, 60(29–30) 3 718–3 722
H L Yang, X M Kong, Y R Zhang, et al. Mechanical Properties of Polymer-modified Silica Aerogels Dried under Ambient Pressure [J]. J. Non-cryst. Solids, 2011(357): 3 447–3 453
Hüsing N, Schubert U. Aerogels-airy Materials: Chemistry, Structure and Properties [J]. Angew. Chem. Int. Ed., 1998(37): 22–45
Ceballos L, Garrido M A, Fuentes V, et al. Mechanical Characterization of Resin Comments used for Luting Fibers Posts by Nanoimdentation [J]. Dental Mater., 2007, 23(1): 100–105
Author information
Authors and Affiliations
Corresponding author
Additional information
Supported by the the National Natural Science Foundation of China (No.51278086), PetroChina Innovation Fundation(No.2013D-5006-0606), the Program for New Century Excellent Talents in University by Ministry of Education of the People’s Republic of China (No.NCET-12-0084), Liaoning BaiQianWan Talents of Science and Technology Program (No.2012921073), Henan Open and Cooperation Project of Science and Technology (No.142106000023) and Dalian Plan Projects of Science and Technology (No. 2013A16GX113)
Rights and permissions
About this article
Cite this article
Ma, H., Wang, B., Zhao, L. et al. Preparation and properties of PMMA modified silica aerogels from diatomite. J. Wuhan Univ. Technol.-Mat. Sci. Edit. 29, 877–884 (2014). https://doi.org/10.1007/s11595-014-1013-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11595-014-1013-5