Abstract
Silver powder was fabricated by spray pyrolysis, using 2%–20% AgNO3 solution, 336–500 mL/h flux of AgNO3 solution, 0.28–0.32 MPa flux of carrier gas and in the 620–820 °C temperature range. The effects of furnace set temperature, concentration of AgNO3 aqueous solution, flux of AgNO3 aqueous solution as well as carrier gas on the morphology and particle size distribution of silver powder, were investigated. The experimental results showed that with the high concentration of AgNO3 aqueous solution, the average grain size of silver decreased with the increasing of furnace set temperature. But the gain size distribution was not homogenous, the discontinuous grain growth occurred. With the low concentration of AgNO3 aqueous solution, the higher furnace set temperature made the nano sliver grains sintered together to grow. Nano silver powder about 100 nm was fabricated by spray pyrolysis, using 2wt% AgNO3 solutions, 336 mL/h flux of AgNO3 aqueous solution, 0.32 MPa flux of carrier gas at 720 °C furnace set temperature.
Similar content being viewed by others
References
Nersisyan HH, Lee JH, Son HT, et al. A New and Effective Chemical Reduction Method for Preparation of Nanosized Silver Powder and Colloid Dispersion[J]. Mater. Res. Bull., 2003, 38(6): 949–956
Wang LS, Deng JC, Yang F, et al. Preparation and Catalytic Properties of Ag/CuO Nano-composites via a New Method[J]. Mater. Chem. Phys., 2008, 108(2–3): 165–169
Abu Bakar NHH, Ismail J, Abu Bakar M. Synthesis and Characterization of Silver Nanoparticles in Natural Rubber[J]. Mater. Chem. Phys., 2007, 104(2–3): 276–283
Singh N, Khanna PK. In situ Synthesis of Silver Nano-particles in Polymethylmethacrylate[J]. Mater. Chem. Phys., 2007, 104(2–3): 367–372
Pickering AL, Cooper GJT, Long DL, et al. Facile Synthesis and Structures of Infinite One-dimensional Silver(I) Coordination Polymers[J]. Polyhedron., 2004, 23(12): 2075–2079
Niu ZQ, Yan F. A New Surface-enhanced Raman Scattering System for C60 Fullerene: Silver Nano-Particles/C60/silver Film[J]. Vib Spectrosc., 2007, 43(2): 415–419
Shashikala V, Siva Kumar V, Padmasri AH, et al. Advantages of Nano-silver-carbon Covered Alumina Catalyst Prepared by Electro-chemical Method for Drinking Water Purification[J]. J. Mol. Catal. A Chem., 2007, 268(1–2): 95–100
Sobana N, Muruganadham M, Swaminathan M. Nano-Ag Particles Doped TiO2 for Efficient Photodegradation of Direct azo dyes [J]. J. Mol. Catal. A Chem., 2006, 258(1–2): 124–132
Lee SH, Oh SM, Park DW. Preparation of Silver Nanopowder by Thermal plasma[J]. Mater. Sci. Engin. C., 2007, 27(5–8): 1286–1290
Remita S, Fontaine P, Lacaze E, et al. X-ray Radiolysis Induced Formation of Silver Nano-particles: A SAXS and UV-visible Absorption Spectroscopy Study[J]. Nucl Instrum. Meth B., 2007, 263(2): 436–440
Raffi M, Akhter JI, Hasan MM. Effect of Annealing Temperature on Ag Nano-composite Synthesized by sol-gel[J]. Mater. Chem. Phys., 2006, 99(2–3): 405–409
Khanna PK, Subbarao VVVS. Nanosized Silver Powder via Reduction of Silver Nitrate by Sodium Formaldehydesulfoxylate in Acidic pH Medium[J]. Mater. Lett., 2003, 57(15): 2242–2245
Wu SP, Meng SY. Preparation of Ultrafine Silver Powder using Ascorbic Acid as Reducing Agent and Its Application in MLCI[J]. Mater. Chem. Phys., 2005, 89(2–3): 423–427
Huang CY, Chiang HJ, Huang JC, et al. Synthesis of Nanocrystalline Ag-Pd Alloys by Chemical Reduction Method[J]. Nanostruct. Mater., 1998, 10(8): 1393–1400
Korchagin AI, Kuksanov NK, Lavrukhin AV, et al. Production of Silver Nano-powders by Electron Beam Evaporation[ J]. Vacuum., 2005, 77(4): 485–491
Chau JLH, Hsu MK, Hsieh CC, et al. Microwave Plasma Synthesis of Silver Nanopowders[J]. Mater. Lett., 2005, 59(8–9): 905–908
Li R, Kim DJ, Yu K, et al. Study of Fine Silver Powder from AgOH Slurry by Hydrothermal Techniques[J]. Mater. Process Tech., 2003, 137(1–3): 55–59
Majumdar D, Glicksman HD, Kodas TT. Generation and Sintering Characteristics of Silver-copper (II) Oxide Composite Powders Made by Spray Pyrolysis[J]. Powder Tech-Nol., 2000, 110(1–2): 76–81
Yang SY, Kim SG. Characterization of Silver and Silver/Nickel Composite Particles Prepared by Spray Pyrolysis[J]. Powder Technol., 2004, 146(3): 185–192
Janackvic DJ, Jokanovic V, Kostic-Gvozdenovic LJ, et al. Synthesis of Mullite Nanostructured Spherical Powder by Ultrasonic Spray Pyrolysis[J]. Nanostruct. Mater., 1998, 10(3): 341–348
Liu ZH, Liu ZY, Li QH, et al. Morphology Control of Micro-sized Spherical Silver Powder Prepared by Spray Pyrolysis[J]. Chinese J. Nonferr. Metal., 2007, 17(1): 149–155 (in Chinese)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Zhang, Q., Liu, H., Wang, X. et al. Fabrication and characterization of nano silver powder prepared by spray pyrolysis. J. Wuhan Univ. Technol.-Mat. Sci. Edit. 24, 871–874 (2009). https://doi.org/10.1007/s11595-009-6871-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11595-009-6871-x