Abstract
Magnesium alloys are potentially attractive biodegradable materials. However, their rapid corrosion rate limits their biomedical application. To slow down the rate of biodegradation, a protective calcium-phosphate coating was formed on a magnesium alloy substrate by a hydrothermal method. Scanning electron microscope results showed that the coating consisted of two layers with different crystalline characteristics. The loose outer layer showed a prism-like crystal structure, while the compact inner layer is a dense ultra-fine regular di-pyramid-like structure with an average grain dimension of ∼200 nm. The compositions of the inner layer and outer layer were calcium-deficient hydroxyapatite (Ca-def HA) and dicalcium phosphate (DCPa), respectively. The coating adhered well to the substrate with a thickness of about 15 μm. Immersion in Hank’s solution indicated that the coating could significantly improve the degradation properties of magnesium alloy. The pH of the solution containing the coated samples increased much more slowly than the untreated control. After 8 d immersion, the uncoated sample had corroded seriously while the coated sample was much less corroded. The Ca/P atom ratio in both the layers of the coating increased and the coating was still protecting the substrate. The two layers of the coating corroded differently because of differences in solubility. The outer layer was more severely attacked and many holes were formed on the surface, the inner layer suffered less attack. In addition, a growth of precipitate on the inner layer was observed, indicating that surface bioactivity was improved by the coating. Thus, magnesium alloys coated with a Ca-P coating prepared by a hydrothermal method are promising candidate biodegradable biomaterials, and further investigation of in vivo degradation behavior is suggested.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Witte F. The history of biodegradable magnesium implants. Acta Biomater, 2010, 6: 1680–1692
Staiger M P, Pietak A M, Huadmai J, et al. Magnesium and its alloys as orthopaedic biomaterials: A review. Biomaterials, 2006, 27: 1728–1734
Witte F, Kaese V, Haferkamp H, et al. In vivo corrosion of four magnesium alloys and the associated bone response. Biomaterials, 2005, 26: 3557–3563
Wen C L, Guan S K, Peng L, et al. Characterization and degradation behavior of AZ31 alloy surface modified by bone-like hydroxyapatite for implant applications. Appl Surf Sci, 2009, 255: 6433–6438
Geng F, Tan L L, Jin X X, et al. The preparation, cytocompatibility, and in vitro biodegradation study of pure beta-TCP on magnesium. J Mater Sci: Mater Med, 2009, 20: 1149–1157
Lin F H, Lin C C, Lu C M, et al. Mechanical-properties and histological-evaluation of sintered beta-Ca2P2O7 with Na4P2O7·10H2O addition. Biomaterials, 1995, 16: 793–802
He Y H, Tao H R, Zhang Y, et al. Biocompatibility of bio-Mg-Zn alloy within bone with heart, liver, kidney and spleen. Chin Sci Bull, 2009, 54: 484–491
Elia N, Sridhar T M, Kamachi M U, et al. Electrochemical and electrophoretic deposition of hydroxyapatite for orthopaedic application. Surf Eng, 2005, 21: 238–242
Park J H, Lee Y K, Kim K M. Bioactive calcium phosphate coating prepared on H2O2-treated titanium substrate by electrodeposition. Surf Coat Technol, 2005, 195: 252–257
Gibson L, Ashby M. Cellular solids. Structure and Properties. Sydney: Pergamon Press, 1988. 316–331
Author information
Authors and Affiliations
Corresponding author
Additional information
This article is published with open access at Springerlink.com
Rights and permissions
This article is published under an open access license. Please check the 'Copyright Information' section either on this page or in the PDF for details of this license and what re-use is permitted. If your intended use exceeds what is permitted by the license or if you are unable to locate the licence and re-use information, please contact the Rights and Permissions team.
About this article
Cite this article
Li, K., Wang, B., Yan, B. et al. Preparing Ca-P coating on biodegradable magnesium alloy by hydrothermal method: In vitro degradation behavior. Chin. Sci. Bull. 57, 2319–2322 (2012). https://doi.org/10.1007/s11434-012-5067-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11434-012-5067-5