Abstract
The objective of this investigation is to assess the influence of graphite reinforcement on tribological behavior of ZA-27 alloy. The composite with 2 wt% of graphite particles was produced by the compocasting procedure. Tribological properties of unreinforced alloy and composite were studied, using block-on-disk tribometer, under dry and lubricated sliding conditions at different specific loads and sliding speeds. The worn surfaces of the samples were examined by the scanning electron microscopy (SEM). The obtained results revealed that ZA-27/graphite composite specimens exhibited significantly lower wear rate and coefficient of friction than the matrix alloy specimens in all the combinations of applied loads (F n ) and sliding speeds (v) in dry and lubricated tests. The positive tribological effects of graphite reinforcement of ZA-27 in dry sliding tests were provided by the tribo-induced graphite film on the contact surface of composite. In test conditions, characterized by the small graphite content and modest sliding speeds and applied loads, nonuniform tribo-induced graphite films were formed leading to the increase of the friction coefficient and wear rate, with increase of the sliding speed and applied load. In conditions of lubricated sliding, the very fine graphite particles formed in the contact interface mix with the lubricating oil forming the emulsion with improved tribological characteristics. Smeared graphite decreased the negative influence of F n on tribological response of composites, what is manifested by the mild regime of the boundary lubrication, as well as by realization of the mixed lubrication at lower values of the v/F n ratio, with respect to the matrix alloy.
Similar content being viewed by others
References
Vasiliev, V.V., Morozov, E.V.: Mechanics and Analysis of Composite Materials. Elsevier, Oxford (2001)
Pruthviraj, R.D., Krupakara, P.V.: Influence of SiC additions on mechanical properties of the Zn–Al alloy (ZA-27). Int J Mater Sci 2(1), 53–57 (2007)
Cahn, R.W., Haasen, P.: Physical Metallurgy, 4th edn. North-Holland, Amsterdam (1996)
Babic, M., Ninkovic, R., Rac, A.: Sliding Wear Behavior of Zn-Al Alloys in Conditions of Boundary Lubrication. The Annals of University “Dunarea De Jos” of Galati Fascicle VIII. Tribology, 60–64 (2005)
Sharma, S.C., Girish, B.M., Kamath, R., Satish, B.M.: Effect of SiC particle reinforcement on the unlubricated sliding wear behavior of ZA-27 alloy composites. Wear 213, 33–40 (1997)
Tjong, S.C., Chen, F.: Wear behavior of as-cast ZnAl27/SiC particulate metal-matrix composites under lubricated sliding condition. Metall Mater Trans A 28A, 1951–1955 (1997)
Prasad, B.K., Das, S., Jha, A.K., Modi, O.P., Dasgupta, R., Yegneswaran, A.H.: Factors controlling the abrasive wear response of a zinc-based alloy silicon carbide particle composite. Composites A 28(4), 301–308 (1997)
Prasad, B.K., Modi, O.P., Khaira, H.K.: High-stress abrasive wear behavior of a zinc-based alloy and its composite compared with a cast iron under varying track radius and load conditions. Mater Sci Eng A 381, 343–354 (2004)
Prasad, B.K.: Abrasive wear characteristics of a zinc-based alloy and zinc-alloy/SiC composite. Wear 252(3–4), 250–263 (2002)
Sastry, S., Krishna, M., Uchil, J.: A study on damping behavior of aluminate particulate reinforced ZA-27 alloy metal matrix composites. J Alloys Compd 346, 268–274 (2001)
Sharma, S.C., Sastry, S., Krishna, M.: Effect of aging parameters on the micro structure and properties of ZA-27/aluminate metal matrix composites. J Alloys Compd 346, 292–301 (2002)
Bobic, I., Jovanovic, M.T., Ilic, N.: Microstructure and strength of ZA-27 based composites reinforced with Al2O3 particles. Mater Lett 57, 1683–1688 (2003)
Modi, O.P., Rathod, S., Prasad, B.K., Jha, A.K., Dixit, G.: The influence of alumina particle dispersion and test parameters on dry sliding wear behavior of zinc-based alloy. Tribol Int 40, 1137–1146 (2007)
Yu, S., He, Z., Chen, K.: Dry sliding frictional wear behavior of short fibre reinforced zinc-based alloy composites. Wear 198, 108–114 (1996)
Sharma, S.C., Girish, B.M., Kamath, R., Satish, B.M.: Sliding wear behavior of zircon particles reinforced ZA-27 alloy composite materials. Wear 224, 89–94 (1999)
Sharma, S.C., Satish, B.M., Girish, B.M., Kramath, R., Asanumat, H.: Dry sliding wear of short glass fiber reinforced zinc–aluminum composites. Tribol Int 31(4), 183–188 (1998)
Sharma, S.C., Girish, B.M., Satish, B.M., Kamath, R.: Aging characteristics of short glass fiber reinforced ZA-27 alloy composite material. J Mater Eng Perform 7, 747–750 (1998)
Ranganath, G., Sharma, S.C., Krishna, M.: Dry sliding wear of garnet reinforced zinc/aluminum metal matrix composites. Wear 251, 1408–1413 (2001)
Rohatgi, P.K., Ray, S., Lin, Y.: Tribological properties of metal matrix graphite particle composites. Int Mater Rev 37(3), 129–149 (1992)
Riahi, A.R., Alpas, A.T.: The role of tribo-layers on the sliding wear behavior of graphitic aluminum matrix composites. Wear 251, 1396–1407 (2001)
Yang, J.B., Lin, C.B., Wang, T.C., Chu, H.Y.: The tribological characteristics of A356.2Al alloy/Gr(p) composites. Wear 257, 941–952 (2004)
Akhlaghi, F., Zare-Bidaki, A.: Influence of graphite content on the dry sliding and oil impregnated sliding wear behavior of Al 2024-graphite composites produced by in situ powder metallurgy method. Wear 266, 37–45 (2009)
Seah, K.H.W., Sharma, S.C., Girish, B.M.: Mechanical properties of cast ZA-27/graphite particulate composites. Mater Des 16(5), 271–275 (1995)
Seah, K.H.W., Sharma, S.C., Girish, B.M.: Effect of artificial ageing on the hardness of cast ZA-27/graphite particulate composites. Mater Des 16(6), 337–341 (1995)
Seah, K.H.W., Sharma, S.C., Girish, B.M.: Corrosion characteristics of ZA-27-graphite particulate composites. Corros Sci 39(1), 1–7 (1997)
Seah, K.H.W., Sharma, S.C., Girish, B.M., Lim, S.C.: Wear characteristics of as-cast ZA-27/graphite particulate composites. Mater Des 17(2), 63–67 (1996)
Sharma, S.C., Girish, B.M., Kramath, R., Satish, B.M.: Graphite particles reinforced ZA-27 alloy composite materials for journal bearing applications. Wear 219, 162–168 (1998)
Vencl, A., Bobic, I., Jovanovic, M., Babic, M., Mitrovic, S.: Microstructural and tribological properties of A356 Al–Si alloy reinforced with Al2O3 particles. Tribol Lett 32, 159–170 (2008)
Babic, M., Vencl, A., Mitrović, S., Bobic, I.: Influence of T4 heat treatment on tribological behavior of ZA27 alloy under lubricated sliding condition. Tribol Lett. doi: 10.1007/s11249-009-9467-x
Liu, Y.B., Lim, S.C., Ray, S., Rohatgi, P.K.: Friction and wear of aluminum-graphite composites: the smearing process of graphite during sliding. Wear 159, 201–205 (1992)
Prasad, B.K.: Investigation into sliding wear performance of zinc-based alloy reinforced with SiC particles in dry and lubricated conditions. Wear 262, 262–273 (2007)
Acknowledgments
The results of this article are realized through the national project TR-14005B financially supported by the Ministry of Science of the Republic of Serbia (Project Coordinator: Prof. Dr. Miroslav Babic).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Babic, M., Slobodan, M., Džunic, D. et al. Tribological Behavior of Composites Based on ZA-27 Alloy Reinforced with Graphite Particles. Tribol Lett 37, 401–410 (2010). https://doi.org/10.1007/s11249-009-9535-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11249-009-9535-2