Abstract
In this study surface-functionalized zirconium oxoclusters (ZrNBB), formed by reaction between vinylacetic acid and zirconium propoxide, were chemically modified through condensation with siloxane groups, so that the core integrity of ZrNBB was preserved. The direct coupling between zirconium oxo-clusters and siloxane moiety was performed by co-polymerisation with vinyl trimethoxysilane (VTMS) with Zr:Si molar ratio 1:2 in air at room temperature and benzoyl peroxide (BPO) was used as an initiator to start radical polymerization. The polymerisation was studied by differential scanning calorimetry (DSC) and Fourier Transform Infra Red (FTIR) spectroscopy. 29Si and 13C liquid and solid state NMR analyses were performed in order to study the microstructure of the hybrid material and the role of the clusters in polymerization and condensation. Beyond this, shear storage modulus (G′) and loss modulus (G′′), were investigated by dynamical mechanical spectroscopy (DMS). The results indicated a great stability at high temperature without any viscous flow during glass transition.
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10971-008-1754-8/MediaObjects/10971_2008_1754_Fig1_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10971-008-1754-8/MediaObjects/10971_2008_1754_Sch1_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10971-008-1754-8/MediaObjects/10971_2008_1754_Fig2_HTML.jpg)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10971-008-1754-8/MediaObjects/10971_2008_1754_Fig3_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10971-008-1754-8/MediaObjects/10971_2008_1754_Fig4_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10971-008-1754-8/MediaObjects/10971_2008_1754_Fig5_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10971-008-1754-8/MediaObjects/10971_2008_1754_Fig6_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10971-008-1754-8/MediaObjects/10971_2008_1754_Fig7_HTML.gif)
Similar content being viewed by others
References
Miller JB, Ko EI (1996) J Catal 159:58
Soppera O, Croutxe´-Barghorn C, Carre` C, Blanc D (2002) Appl Surf Sci 186:91
Saravanamuttu K, Min DX, Najafi SI, Andrews MP (1998) Can J Chem 76:1717
Park OK, Jung JI, Bae BS (2001) J Mater Res 16:2143
Armelao L, Eisenmenger-Sittner C, Groenewolt M, Gross S, Sada C, Schubert U, Tondello E, Zattin A (2005) J Mater Chem 15:1838
Schubert U (2004) J Sol–Gel Sci Techn 31:19
Kogler FR, Jupa M, Puchberger M, Schubert U (2004) J Mat Chem 14:3133
Schubert U (2003) J Sol–Gel Sci Technol 26:47
Kogler FR, Schubert U (2007) Polymer 48:4990
Kogler FR, Koch T, Peterlik H, Seidler S, Schubert U (2007) J Pol Sci (Part:B) 45:2215–2231
Acknowledgements
The Ministero dell’Università Italiana (MIUR) and PRIN05 are greatly acknowledged for funding the study.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Di Maggio, R., Dirè, S., Callone, E. et al. Si and Zr based NBBS for hybrid O/I macromolecular materials starting by preformed zirconium oxo-clusters. J Sol-Gel Sci Technol 48, 168–171 (2008). https://doi.org/10.1007/s10971-008-1754-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10971-008-1754-8