Abstract
Zinc molybdate rod-like nanostructures have been successfully synthesized by precipitation method process in the presence of different surfactants. This study aimed to investigate the effects of different surfactant such as sodium dodecyl sulfate, polyethylene glycol, and cetyltrimethylammonium bromide and solvent on the morphology and particle size of final products. It was found that the size and morphology of the products could be greatly influenced by the aforementioned parameters. To the best of authors’ knowledge, this is the first report on the synthesis of ZnMoO4 nanostructure with different morphologies in the presence of ethanol as a solvent. The as-synthesized products were characterized by XRD, SEM, UV–Vis, and EDS techniques. To evaluate the photocatalyst properties of nanocrystalline zinc molybdate, the photocatalytic degradation of methyl orange under visible light irradiation was carried out.
Similar content being viewed by others
References
M. Ramezani, A. Davoodi, A. Malekizad, S.M. Hosseinpour-Mashkani, J. Mater. Sci. Mater. Electron. 26, 3957 (2015)
A. Javidan, S. Rafizadeh, S.M. Hosseinpour-Mashkani, Mater. Sci. Semicond. Process. 27, 468 (2014)
S.M. Hosseinpour-Mashkani, M. Ramezani, Mater. Lett. 130, 259 (2014)
F. Davara, M. Salavati-Niasari, J. Alloys Compd. 509, 2487 (2011)
W.S. Wang, L. Zhen, C.Y. Xu, W.Z. Shao, Z.L. Chen, J. Alloys Compd. 529, 17 (2012)
D. Li, Y.F. Zhu, Cryst. Eng. Commun. 14, 1128 (2012)
H.W. Liu, L. Tan, Ionics 16, 57 (2010)
L. Zhen, W.S. Wang, C.Y. Xu, W.Z. Shao, M.M. Ye, Z.L. Chen, Scripta Mater. 58, 461 (2008)
L. Zhou, W. Wang, H. Xu, S. Sun, Cryst. Growth Des. 8, 3595 (2008)
W.S. Wang, L. Zhen, C.Y. Xu, W.Z. Shao, Cryst. Growth Des. 9, 1558 (2009)
A. Phuruangrat, N. Ekthammathat, T. Thongtem, S. Thongtem, J. Phys. Chem. Solids 72, 176 (2011)
D. Zhu, K. Ki, X. Chen, T. Ying, J. Optoelectron. Adv. Mater. 5, 403 (2011)
Q.L. Dai, G.G. Zhang, P. Liu, J. Wang, J.K. Tang, Inorg. Chem. 51, 9232 (2012)
X. Jiang, J. Ma, B. Lin, Y. Ren, J. Liu, X. Zhu, J. Tao, J. Am. Ceram. Soc. 90, 977 (2007)
G. Zhanga, S. Yua, Y. Yanga, W. Jianga, S. Zhanga, B. Huang, J. Cryst. Growth 312, 1866 (2007)
L. Gironi, C. Arnaboldia, J.W. Beeman, O. Cremonesi, F.A. Danevich, V.Y. Degoda, L.I. Ivleva, L.L. Nagornaya, M. Pavan, G. Pessina, S. Pirro, V.I. Tretyak, I.A. Tupitsyna, J. Instrum. 5, 11007 (2010)
L. Lv, W. Tong, Y. Zhang, Y. Su, X. Wang, J. Nanosci. Nanotechnol. 11(11), 9506 (2011)
D.A. Spassky, A.N. Vasil’ev, I.A. Kamenskikh, V.V. Mikhailin, A.E. Savon, Y.A. Hizhnyi, S.G. Nedilko, P.A. Lykov, J. Phys. Condens. Matter 23(36), 365501 (2011)
L.I. Ivleva, I.S. Voronina, L.Y. Berezovskaya, P.A. Lykov, V.V. Osiko, L.D. Iskhakova, Crystallogr. Rep. 53, 1087 (2008)
G. Zhang, S. Yu, Y. Yang, W. Jiang, S. Zhang, B. Huang, J. Cryst. Growth 312, 1866 (2010)
S.C. Abrahams, J. Chem. Phys. 46, 2052 (1967)
M. Grzywa, W. Lasocha, W. Surga, J. Solid State Chem. 180, 1590 (2007)
S.M. Hosseinpour-Mashkani, M. Ramezani, M. Vatanparast, Mater. Sci. Semicond. Process. 26, 112 (2014)
Z. Shahri, M. Bazarganipour, M. Salavati-Niasari, Superlattices Microstruct. 63, 258 (2013)
K. Vinodgopal, Y. He, M. Ashokkumar, F. Grieser, J. Phys. Chem. B 110, 3849 (2006)
Y. Xie, X. Zheng, X. Jiang, J. Lu, L. Zhu, Inorg. Chem. 41, 387 (2002)
J. Zhong, J. Li, F. Feng, Y. Lu, J. Zeng, W. Hu, Z. Tang, J. Mol. Catal. A Chem. 357, 101 (2012)
Acknowledgments
Authors are grateful to council of University of Arak for providing financial support to undertake this work.
Conflict of interest
The author declares that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ramezani, M., Hosseinpour-Mashkani, S.M., Sobhani-Nasab, A. et al. Synthesis, characterization, and morphological control of ZnMoO4 nanostructures through precipitation method and its photocatalyst application. J Mater Sci: Mater Electron 26, 7588–7594 (2015). https://doi.org/10.1007/s10854-015-3395-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-015-3395-3