Abstract
Ceramics in PMN–PZT system with formula xPb(Mg1/3Nb2/3)O3–(1 − x)Pb(Zr0.4Ti0.6)O3 (where x = 0.32, 0.35, 0.38, 0.41) were prepared by the conventional oxide-mixed method. The phase diagram, composition dependent ferroelectric, dielectric, field-induced strain and piezoelectric properties were systematically investigated. X-ray diffraction analysis indicated that as-prepared ceramics were of pure perovskite phase and the possible morphotropic phase boundary (MPB) between the tetragonal and pseudo-cubic phase compositions were located near the PMN content of x = 0.38, confirmed by their corresponding ferroelectric, dielectric, field-induced strain and piezoelectric properties. The composition with x = 0.38 possessed the optimum electrical properties since its composition locate close to the MPB where exist multiple polarization directions facilitates domain reorientation and consequently enables the superior electrical properties. The room temperature dielectric permittivity ε r , tangent loss tan δ, piezoelectric coefficient d 33, electromechanical coupling factor kp, remnant polarization P r , hysteresis loop squareness R sq and longitudinal strain of 0.38PMN–0.62PZT ceramics are 2441, 2.08 %, 662 pC/N, 63.5 %, 37.2 μC/cm2, 1.51 and 1.9 ‰, respectively, which mean it has a great promise for actuator applications.
Similar content being viewed by others
References
G.H. Haertling, J. Am. Ceram. Soc. 82, 797 (1999)
O. Hiromu, K. Nagano, S. Hayakawa, J. Am. Ceram. Soc. 48, 631 (1965)
B.J. Fang, C.L. Ding, J. Wu, Q.B. Du, J.N. Ding, X.Y. Zhao, H.Q. Xu, H.S. Luo, Eur. Phys. J. Appl. Phys. 57, 30101 (2012)
A. Glazounov, A. Tagantsev, A. Bell, Phys. Rev. B 53, 11282 (1996)
Q.Y. Yin, Z.Q. Sun, S.W. Shi, X.S. Jiang, C.G. Tian, M.L. Bao, J. Mater. Sci.: Mater. Electron. 24, 4258–4262 (2013)
L. Wang, R.H. Liang, C.L. Mao, M. Gao, G. Du, F. Cao, G.S. Wang, X.L. Dong, J. Am. Ceram. Soc. 95, 445 (2012)
L.E. Cross, Mater. Chem. Phys. 43, 108 (1996)
K. Vladimír, A. Carlos, B. Jaroslav, B. Helena, S. Karol, J. Eur. Ceram. Soc. 23, 1158–1163 (2003)
G. Srivastavan, A. Goswami, A.M. Umarji, Cream. Int. 39, 1978 (2013)
V. Koval, C. Alemany, J. Briancin, H. Brunckova, J. Electroceram. 10, 19–25 (2003)
Z.G. Xia, Q. Li, Solid State Commun. 142, 322 (2007)
S.M. Gupta, A.R. Kulkarni, Mater. Chem. Phys. 39, 98 (1994)
F.P. Sun, Z. Chaudhry, C. Liang, C.A. Rogers, J. Intel, Mater. Syst. Str. 6, 134 (1995)
R. Yimnirun, S. Ananta, P. Laoratanakul, Mater. Sci. Eng. B 112, 79 (2004)
M. Villegas, J.R. Jurado, C. Moure, P. Duran, J. Mater. Sci. 29, 1090 (1994)
S. Wongsaenmai, L. Yongyut, A. Supon, Y. Rattikorn, Mater. Sci. Eng. B 128, 85 (2006)
J.H. Gao, Q. Li, N.G. Luo, Q.F. Yan, Y.L. Zhang, X.C. Chu, Ceram. Int. 40, 487–492 (2014)
R. Yimnirun, S. Ananta, P. Laoratanakul, J. Eur. Ceram. Soc. 25, 3235 (2005)
J.Z. Du, J.H. Qiu, K.J. Zhu, H.L. Ji, Ceram. Int. 39, 9385 (2013)
M.S. Chae, J.H. Koh, Ceram. Int. 40, 2511 (2014)
L. Wang, R.H. Liang, C.L. Mao, G. Du, G.S. Wang, X.L. Dong, Ceram. Int. 39, 8572 (2013)
H. Fan, Z. Xu, L. Zhang, X. Yao, Chin. Sci. Bull. 42, 170 (1997)
G. Du, R.H. Liang, J.X. Wang, L. Wang, W.B. Zhang, G.S. Wang, Ceram. Int. 39, 9300 (2013)
B.M. Jim, J. Kim, S.C. Kim, Appl. Phys. A 65, 55 (1997)
K. Uchino, S. Nomura, Ferroelectrics 44, 57 (1982)
Q. Zhang, Z.R. Li, F. Li, Z. Xu, X. Yao, J. Am. Ceram. Soc. 92, 3331 (2010)
W. Chen, X. Yao, X.Y. Wei, Appl. Phys. Lett. 90, 182902 (2007)
Y.D. Hou, N.N. Wu, C. Wang, M.K. Zhu, X.M. Song, J. Am. Ceram. Soc. 93, 2753 (2010)
Z.P. Yang, B. Liu, L.L. Wei, Y.T. Hou, Mater. Res. Bull. 43, 85 (2008)
Acknowledgments
This work was financially supported by National Natural Science Foundation of China (51375228), NUAA Fundamental Funds (NS2013008), Fundamental Research Funds for the Central Universities (NJ20140012), The State Key Laboratory Program under Grant (MCMS-0514K01), A Project Funded by the Priority Academic Program Development of Jiangsu Higher Education Institutions (PAPD).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Wen, K., Qiu, J., Ji, H. et al. Investigation of phase diagram and electrical properties of xPb(Mg1/3Nb2/3)O3–(1 − x)Pb(Zr0.4Ti0.6)O3 ceramics. J Mater Sci: Mater Electron 25, 3003–3009 (2014). https://doi.org/10.1007/s10854-014-1974-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-014-1974-3