Abstract
The effects of B2O3–CuO (BCu, the weight ratio of B2O3 to CuO is 1:1) addition on the sintering behavior, microstructure, and the microwave dielectric properties of 3Li2O–Nb2O5–3TiO2 (LNT) ceramics have been investigated. The low-amount addition of BCu can effectively lower the sintering temperature of LNT ceramics from 1125 to 900 °C and induce no obvious degradation of the microwave dielectric properties. Typically, the 2 wt% BCu-added ceramic sintered at 900 °C has better microwave dielectric properties of ε r = 50.1, Q × f = 8300 GHz, τ f = 35 ppm/°C. Silver powders were cofired with the dielectric under air atmosphere at 900 °C. The SEM and EDS analysis showed no reaction between the dielectric ceramic and silver powders. This result shows that the LNT dielectric materials are good candidates for LTCC applications with silver electrode.
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-008-9721-2/MediaObjects/10854_2008_9721_Fig1_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-008-9721-2/MediaObjects/10854_2008_9721_Fig2_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-008-9721-2/MediaObjects/10854_2008_9721_Fig3_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-008-9721-2/MediaObjects/10854_2008_9721_Fig4_HTML.jpg)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-008-9721-2/MediaObjects/10854_2008_9721_Fig5_HTML.jpg)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-008-9721-2/MediaObjects/10854_2008_9721_Fig6_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-008-9721-2/MediaObjects/10854_2008_9721_Fig7_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-008-9721-2/MediaObjects/10854_2008_9721_Fig8_HTML.gif)
Similar content being viewed by others
References
M. Abe, T. Nanataki, S. Yano, U.S. Patent 5,292,694 (1994)
M. Abe, T. Sugiura, T. Nanataki, S. Yano, U.S. Patent 5,332,984 (1994)
M. Abe, T. Nanataki, S. Yano, U.S. Patent 5,350,721 (1994)
J.B. Lim, K.H. Cho, S. Nahm, J.H. Paik, J.H. Kim, Mater. Res. Bull. 41, 1868 (2006). doi:10.1016/j.materresbull.2006.03.013
W.W. Cho, K.I. Kakimoto, H. Ohsato, Mater. Sci. Eng. B 121, 48 (2005). doi:10.1016/j.mseb.2005.02.061
A.Y. Borisevich, P.K. Davies, J. Am. Ceram. Soc. 87, 1047 (2004)
M.Z. Jhou, J.H. Jean, J. Am. Ceram. Soc. 89, 786 (2006). doi:10.1111/j.1551-2916.2005.00790.x
Y. Xu, G. Huang, Y. He, Ceram. Int. 31, 21 (2005). doi:10.1016/j.ceramint.2004.02.007
H·F. Zhou, H. Wang, X.Y. Ding, X. Yao, J. Mater. Sci. Mater. El. (2008). doi:10.1007/s10854-008-9600-x
M.I. Kim, S. Nahm, W.S. Lee, M.J. Yoo, N.K. Kang, H.T. Kim, H.J. Lee, Jpn. J. Appl. Phys. 44, 3091 (2005)
M.H. Kim, Y.H. Jeong, S. Nahm, H.T. Kim, H.J. Lee, J. Eur. Ceram. Soc. 26, 2139 (2006). doi:10.1016/j.jeurceramsoc.2005.09.072
J.B. Lim, S. Nahm, H.T. Kim, J.H. Kim, J.H. Paik, H.J. Lee, J. Electroceram. 17, 393 (2006)
L. Farber, I. Levin, A. Borisevich, I.E. Grey, R.S. Roth, P.K. Davies, J. Solid State Chem. 166, 81 (2002). doi:10.1006/jssc.2002.9563
Acknowledgment
This work was supported by National 863-project of China under grant 2006AA03Z0429, NCET-05-0840 and National 973-project of China under grant 2002CB613302.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Zhou, H., Wang, H., Li, K. et al. Effect of B2O3 and CuO additions on the sintering temperature and microwave dielectric properties of 3Li2O–Nb2O5–3TiO2 ceramics. J Mater Sci: Mater Electron 20, 283–288 (2009). https://doi.org/10.1007/s10854-008-9721-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-008-9721-2