Abstract
Pure Ni and nickel matrix composite electrocoatings containing micron- and nano-SiC particles (1 μm and 20 nm respectively) were produced under direct and pulse current conditions from an additive-free Watts type bath. The effect of the particle size, codeposition percentage of SiC and type of imposed current on the microhardness as well as on the microstructure of the electrodeposits were investigated. Ni/SiC composite deposits prepared under either direct or pulse current conditions exhibited a considerable strengthening effect with respect to pure Ni coatings. The improved hardness of composite coatings was associated to specific structural modifications of Ni crystallites provoked by the adsorption of H+ on the surface of SiC particles, thus leading to a (211) texture mode of Ni crystal growth. Pulse electrodeposition significantly improved the hardness of the Ni/SiC composite coatings, especially at low duty cycles, in which grain refinement and higher SiC incorporation (vol. %) was achieved. The enhanced hardness of Ni/nano-SiC deposits, as compared to Ni/micron-SiC composites, was attributed to the increasing values of the number density of embedded SiC particles in the nickel matrix with decreasing particle size. In addition, the observed hardening effects of the SiC particles might be associated to the different embedding mechanisms of the particles, which could be characterized as inter-crystalline for micron-SiC and partially intra-crystalline for nano-SiC particles.
Similar content being viewed by others
References
Fransaer J., Celis J.P., Roos J.R. (1993). Met. Finish. 91:97
Hovestad A., Janssen L.J.J. (1995). J. Appl. Electrochem 25: 519
Musiani M. (2000). Electrochim. Acta 45:3397
Orlovskaja L., Periene N., Kurtinaitiene M., Surviliene S. (1999) Surf. Coat. Technol 111:234
Gyftou P., Pavlatou E.A., Spyrellis N., Hatzilyberis K.S. (2000) Trans. Inst. Met. Finish 78:223
Garcia I., Fransaer J., Celis J.-P. (2001)Surf. Coat. Technol 148:171
Zimmerman A.F., Palumbo G., Aust K.T, Erb U. (2002) Mater. Sci. Eng. A 328:137
Benea L., Bonora P.L., Borello A., Martelli S. (2002). Wear 249:995
Garcia I., Conde A., Langelaan G., Fransaer J., Celis J.P. (2003) Corros. Sci. 45:1173
Yeh S.H., Wan C.C. (1994) J. Appl. Electrochem 24:993
Maurin G., Lavanant A. (1995) J. Appl. Electrochem. 25:1113
Gyftou P., Stroumbouli M., Pavlatou E.A., Spyrellis N. (2002) Trans. Inst. Met. Finish 80:88
Zimmermann A.F., Clark D.G., Aust K.T., Erb U. (2002) Mater. Lett. 52:85
Kim S.K., Yoo H.J. (1998) Surf. Coat. Technol. 108–109:564
Wang S.-C., Wei W.-C.J., (2003) Mater. Chem. Phys. 78:574
M.-D. Ger (2004) Mater. Chem. Phys. 87:67
Hou K.H., Ger M.D., Wang L.M., Ke S.T. (2002) Wear 253:994
Shrestha N.K., Masuko M., Saji T. (2003) Wear 254:555
Nowak P., Socha R.P., Kaisheva M., Fransaer J., Celis J.-P., Stoinov Z. (2000) J. Appl. Electrochem. 30:429
Socha R.P., Nowak P., Laajalehto K., Väyrynen J. (2004) Coll. Surf. A 235:45
Kaisheva M., Fransaer J. (2004) J. Electrochem. Soc. 151:C89
Hu F., Chan K.C. (2004) Appl. Surf. Sci. 233:163
Kollia C., Spyrellis N., Amblard J., Froment M., Froment M., Maurin G. (1990) J. Appl. Electrochem. 20:1025
El-Sherik A.M., Erb U., Page J. (1996) Surf. Coat. Technol. 88:70
Tóth-Kádár E., Bakonyi I., Pogány L., Cziráki Á (1996) Surf. Coat. Technol. 88:57
Qu N.S., Zhu D., Chan K.C., Lei W.N. (2003) Surf. Coat. Technol 168:123
Boyer H.E., (eds) (1987) “Hardness Testing”. ASM International, Metals Park. OH
Mishra R., Basu B., Balasubramaniam R. (2004) Mater. Sci. Eng. A 373:370
Amblard J., Froment M., Maurin G., Spyrellis N. (1981) J. Microsc. Spectrosc. Electron. 6:311
Amblard J., Costavaras Th., Hugot-Le Goff A., Spyrellis N. (1977) Oberfläche-Surf. 1:18
Denise F., Leidheiser H. (1953) J. Electrochem. Soc. 100:490
Evans D.J. (1958) Trans. Far. Soc. 54:1086
Knödler A. (1966) Metalloberfläche 20:52
Lin C.S., Huang K.C. (2004) J. Appl. Electrochem. 34:1013
Amblard J., Froment M., Spyrellis N. (1977) Surf. Technol. 5:205
Psarrou S., Kollia C., Spyrellis N. (1999) Galvanotecnica e Nuove Finiture 4:224
Gyftou P., Pavlatou E.A., Spyrellis N. (2001) Galvanotecnica e Nuove Finiture 11:23
Acknowledgement
Part of this work was funded by the European Commission (project InMan, contract BRPR-CT98–0788).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Pavlatou, E., Stroumbouli, M., Gyftou, P. et al. Hardening effect induced by incorporation of SiC particles in nickel electrodeposits. J Appl Electrochem 36, 385–394 (2006). https://doi.org/10.1007/s10800-005-9082-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10800-005-9082-y