Abstract
The surface tension, density, and viscosity of the Ni-based superalloy CMSX-4® have been determined in the temperature ranges of 1,650–1,850 K, 1,650–1,950 K, and 1,623–1,800 K, respectively. Each property has been measured in parallel by different techniques at different participating laboratories, and the results are compared with the aim to improve the reliability of data and to identify recommended values. The following relationships have been proposed: density-ρ (T) [kg· m−3] = 7,876 − 1.23(T − 1,654 K); surface tension-γ (T) [mN·m−1] = 1,773 − 0.56 (T − 1, 654 K); viscosity-η (T) [mPa·s] = 8.36 − 1.82 × 10−2(T − 1,654 K). For a comparison, surface-tension measurements on the Al-88.6 at% Ni liquid alloy with the same Al-content as the CMSX-4® alloy were also performed. In addition, the surface tension and density have been theoretically evaluated by different models, and subsequently compared with new experimental data as well as with those reported in the literature. The surface-tension experimental data for the liquid CMSX-4® alloy were found to be close to that of the Al-88.6 at% Ni alloy which is consistent with results from the compound formation model (CFM).
Similar content being viewed by others
References
V. Naidich, Progress in Surface and Membrane Science, vol. 14 (Academic Press, New York, 1981), p. 353
Eustathopoulos N., Nicholas M., Drevet B. (1999) Wettability at High Temperatures. Pergamon Materials Series, Oxford, UK
Keene B.J. (1997) . Int. Mater. Rev. 38, 157
B.J. Keene, DMM(A) 113, (1993)
Jakobsson A., Nasu M., Mangwiru J., Mills K.C., Seetharaman S. (1998) . Phil. Trans. R. Soc. Lond. A 356, 995
Brooks R.F., Monaghan B.J., Barnicoat A.J., McCabe A., Mills K.C., Quested P.N. (1996) . Int. J. Thermophys. 17, 1151
Ricci E., Arato E., Passerone A., Costa P. (2005) . Adv. Colloid Interface Sci. 117, 15
Vinet B., Schneider S., Garandet J.P., Marie B., Drevet B., Egry I. (2004) . Int. J. Thermophys. 25, 1889
Hayashi M., Jakobsson A., Tanaka T., Seetharaman S. (2003) . High Temp.-High Press. 35/36, 441
Li Z., Mills K.C., McLean M., Mukai K. (2005) . Metall. Mater. Trans. B 36B, 247
Wunderlich R., Fecht H. (2005) . Meas. Sci. Technol. 16, 402
C. Maze, G. Burnet, Surf. Sci. 13, 451 (1969); Surf. Sci. 24, 335 (1971)
Liggieri L., Passerone A. (1989) . High Temp. Technol. 7, 80
Eremenko V.N., Nizhenko V.I., Naidich Yu.V. (1961) . Izv. Akad. Nauk SSSR, Metallurgiya i Topivo 3, 150
Ayushina J.G.D., Levin E.S., Gel’dovich P.V. (1969) . Russ. J. Phys. Chem. 43, 1548
Aune R., Battezzati L., Egry I., Etay J., Fecht H.J., Giuranno D., Novakovic R., Passerone A., Ricci E., Schmidt-Hohagen F., Seetharaman S., Wunderlich R. (2006) . Microgravity Sci. Technol. XVIII-3/4, 5
Lin K.F., Lin C.C. (1998) . Scripta Mater. 39(10): 1333
Iida T., Guthrie R.I.L. (1993) The Physical Properties of Liquid Metals. Clarendon Press, Oxford
Ricci E., Passerone A., Joud J.C. (1988) . Surf. Sci. 206, 533
E. Ricci, D. Giuranno, E. Arato, P. Costa, in 5th Int. Conf. on High Temp. Capillarity, HTC 2007, March 21–24, Alicante, Spain (2007)
Molina J.M., Voytovvch R., Louis E., Eustathopoulos N. (2007) . Int. J. Adhes. Adhes. 27, 394
Mills K.C. (2002) Recommended Values of Thermophysical Properties for Commercial Alloys. Woodhead Pub., Cambridge, United Kingdom
Naidich J.V., Perevertailo V.M., Nevodnik G.M. (1972) . Russ. Metall. 2, 66
Lang G., Laty P., Joud J.C., Desré P. (1977) . Z. Metallkd. 68, 113
Knacke O., Kubashewski O., Hesselmann K. (1991) Thermochemical Properties of Inorganic Substances. Springer Verlag, Duesseldorf
Massalski T.B. (1986) Binary Alloy Phase Diagrams. Am. Soc. for Metals, Materials Park, Ohio
R.N. Singh, N.H. March, in Intermetallic Compounds, Principles and Practice, ed. by J.H. Westbrook, R.L. Fleischer (John Wiley & Sons, Chichester, UK, 1995)
Hume-Rothery W., Reynolds P.W. Raynor J.V. (1940) . J. Inst. Metals 66, 191
Mills K.C., Youssef Y.M., Li Z.S. (2006) . ISIJ Int. 46, 623
Brooks R., Day A.P., Andon R.J.L., Chapman L.A., Mills K.C., Quested P.N. (2001) . High Temp.-High Press. 33, 73
Roscoe R. (1958) . Proc. Phys. Soc. 72, 576
Brooks R., Egry I., Ricci E., Seetharaman S., Wunderlich R. (2006) . High Temp. Mater. Proc. 25, 303
Novakovic R., Ricci E., Gnecco F., Giuranno D., Borzone G. (2005) . Surf. Sci. 599, 230
Bhatia A.B., Hargrowe W.H., Thornton D.E. (1974) . Phys. Rev. B 9, 435
Butler J.A.V. (1932) . Proc. R. Soc. A 135, 348
Novakovic R., Tanaka T. (2006) . Physica B 371, 223
Novakovic R., Ricci E. (2002) Surface Properties of the Al–Co–Ni System. Calphad XXXI, Stockholm, Sweden
N. Dupin, Contribution à l’évaluation thermodynamique des alliages polyconstitués à base de nickel (Ph.D. thesis, Institut National Polytechnique de Grenoble, 1995)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ricci, E., Giuranno, D., Novakovic, R. et al. Density, Surface Tension, and Viscosity of CMSX-4® Superalloy. Int J Thermophys 28, 1304–1321 (2007). https://doi.org/10.1007/s10765-007-0257-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10765-007-0257-0