Abstract
The morphology and structure of the regenerated cellulose membranes prepared from its NaOH–urea aqueous solution by coagulating with 5 wt% H2SO4–10 wt% Na2SO4 aqueous solution with different temperatures and times were investigated. The pore size, water permeability and physical properties of the membranes were measured with scanning electron micrograph (SEM), wide X-ray diffraction (WXRD), Fourier transfer infrared spectroscopy (FTIR), flow rate method, and tensile testing. The SEM observation revealed that the structure and pore size of the membranes changed drastically as a function of the coagulation temperature. The membranes coagulated at lower temperatures tended to form the relatively small pore size than those at higher temperatures. On the contrary, the membranes coagulated at different times exhibited similar pore size. Interestingly, the mean pore size and water permeability of the membranes increased from 110 nm with standard deviation (SD) of 25 nm and 12 ml h−1 m−2 mmHg−1 respectively to 1,230 nm with SD of 180 nm and 43 ml h−1 m−2 mmHg−1 with an increase in coagulation temperature from 10 to 60°C. However, the membranes regenerated below 20°C exhibited the dense structure as well as good tensile strength and elongation at break. The result from FTIR and ultraviolet-visible (UV-vis) spectroscopy indicated that the relatively strong intermolecular hydrogen bonds exist in the cellulose membranes prepared at lower coagulation temperatures. This work provided a promising way to prepare cellulose materials with different pore sizes and physical properties by controlling the coagulation temperature.
Similar content being viewed by others
References
Abe Y, Mochizuki A (2002) Hemodialysis membrane prepared from cellulose/N-methylmorpholine-N-oxide solution. I. Effect of membrane preparation conditions on its permeation characteristics. J Appl Polym Sci 84:2302
Brown W, Wiskstön R (1965) Viscosity–molecular weight relationship for cellulose in cadoxen and hydrodynamic interpretation. Eur Polym J 1:1–10
Cai J, Zhang L (2005) Rapid dissolution of cellulose in LiOH/urea and NaOH/urea aqueous solution. Macromol Biosci 5:539
Cai J, Zhang L (2006) Unique gelation behavior of cellulose in NaOH/urea aqueous solution. Biomacromolecules 7: 183–189
Cai J, Zhang L, Zhou J, Qi H, Chen H, Tetsuo Kondo, Chen X, Chu B (2007) Multifilament fibers based on dissolution of cellulose in NaOH/Urea aqueous solution: structure and properties. Adv Mater (in press). doi:10.1002/adma.200601521
Cha W-I, Hyon S-H, Ikada Y (1994) Gel spinning of poly(vinyl alcohol) from dimethyl sulfoxide/water mixture. J Polym Sci Polym Phys 32:297–304
Cheng LP, Soh YS, Dwan A, Gryte CC (1994) An improved model for mass transfer during the formation of polymeric membranes by the immersion-precipitation process. J Polym Sci Polym Phys 32:1413–1425
Cho JJ, Hudson SH, Cuculo JA (1989) The coagulation of cellulose from anisotropic solution in the NH3/NH4SCN solvent system. J Polym Sci Polym Phys Ed 27:1699–1719
Fink HP, Weigel P, Purz HJ, Ganster J (2001) Structure formation of regenerated cellulose materials from NMMO-solutions. Prog Polym Sci 26:1473–1524
Isogai A, Usuda M, Koto T, Uryu T, Atalla RH (1989) Soild-state CP/MASS 13C NMR study of cellulose polymorphs. Macromolecules 22:3168
Kamide K, Okajima K, Kowsaka K (1992) Dissolution of natural cellulose into aqueous solution—role of super-molecular structure of cellulose. Polym J 24:71
Kaplan DL (1998) Biopolymers from renewable resources. Springer, Berlin, p 55
Klemm D, Heubletin B, Fink HP, Bohn A (2005) Cellulose: fascinating biopolymer and sustainable raw material. Angew Chem Int Ed 44:3358
Laity PR, Glover PM, Barry A, Hay JN (2001) Studies of non-solvent induced polymer coagulation by magnetic resonance imaging. Polymer 42:7701
Langan P, Nishiyama Y, Chanzy H (1999) A revised structure and hydrogen-bonding system in cellulose II from a neutron fiber diffraction analysis. J Am Chem Soc 121:9940
Liu CK, Cuculo JA, Smith B (1990) Diffusion competition between solvent and nonsolvent during the coagulation process of cellulose/ammonia/ammonium thiocyanate fiber spinning system. J Polym Sci Polym Phys Ed 28:449–465
Liu CK, Cuculo JA, Allen TC, Degroot AW (1991) Fiber formation via solution spinning of cellulose/ammonia/ammonium thiocyanate system. J Polym Sci Polym Phys Ed 29:181–196
Mao Y, Zhou J, Cai J, Zhang L (2006) Effects of coagulants on porous structure of membranes prepared from cellulose in NaOH/urea aqueous solution. J Membr Sci 279:246
Matsui T, Sano T, Yamane C, Kamide K, Okajima K (1995) Structure and morphology of cellulose films coagulated from novel cellulose/aqueous sodium hydroxide solutions by using aqueous sulfuric acid with various concentrations. Polym J 8:797
Mulder M (1992) Basic principles of membrane technology. Kluwer, Dordrecht
Nelson ML, O’Connor RT (1964) Relation of certain infrared bands to cellulose crystallinity and crystal lattice type. I. Spectra of lattice types I, II, III and of amorphous cellulose. J Appl Polym Sci 8:1311
Nues SP, Peinemann KV (2001) Membranes technology in the chemical industry. Wiley-VCH, Weinheim
Pereira S, Inoue T (1996) Evidence for spinodal decomposition and nucleation and growth mechanisms during membrane formation. J Membr Sci 111:93–103
Pusch W, Walch A (1982) Synthetic membranes—preparation, structure and application. Angew Chem Int Ed 21:660
Togawa E, Kondo T (1999) Change of morphological properties in drawing water-swollen cellulose films prepared from organic solutions. A view of molecular orientation in the drawing process. J Polym Sci Polym Phys 37:451–459
Yang G, Zhang L (1996) Regenerated cellulose microporous membranes by mixing cellulose cuoxam with a water soluble polymer. J Membr Sci 114:149–155
Zhang L, Cai J, Zhou J (2005a) CN ZL 03128386.1
Zhang L, Mao Y, Zhou J, Cai J (2005b) Effects of coagulation conditions on the properties of regenerated cellulose films prepared in NaOH/ urea aqueous solution. Ind Eng Chem Res 44:522
Zhang YP, Shao HL, Wu CS, Hu XC (2001) Formation and characterization of cellulose membranes from N-methylmorpholine-N-oxide solution. Macromol Biosci 1:141
Zhou J, Zhang L, Cai J, Shu H (2002) Cellulose microporous membranes prepared from NaOH/urea aqueous solution. J Membr Sci 210:77
Acknowledgements
This work was supported by the National High Technology Research and Development Program of China (863 Program, 2003AA333040), major grants of the National Natural Science Foundation of China (59933070), and Laboratory of Cellulose and Lignocellulosic Chemistry, Guangzhou Institute of Chemistry, Chinese Academy of Science, China.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Cai, J., Wang, L. & Zhang, L. Influence of coagulation temperature on pore size and properties of cellulose membranes prepared from NaOH–urea aqueous solution. Cellulose 14, 205–215 (2007). https://doi.org/10.1007/s10570-007-9106-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10570-007-9106-3