Abstract
Objectives
Resin-based materials are applied in every branch of dentistry. Due to their tendency to release substances in the oral environment, doubts have been raised about their actual safety. This review aims to provide a comprehensive analysis of the last decade literature regarding the concentrations of elutable substances released from dental resin-based materials in different type of solvents.
Materials and methods
All the literature published on dental journals between January 2010 and April 2022 was searched using international databases (PubMed, Scopus, Web of Science). Due to strict inclusion criteria, only 23 papers out of 877 were considered eligible. The concentration of eluted substances related to surface and volume of the sample was analyzed, considering data at 24 h as a reference. The total cumulative release was examined as well.
Results
The most eluted substances were HEMA, TEGDMA, and BPA, while the less eluted were Bis-GMA and UDMA. Organic solvents caused significantly higher release of substances than water-based ones. A statistically significant inverse correlation between the release of molecules and their molecular mass was observed. A statistically significant positive correlation between the amount of released molecule and the specimen surface area was detected, as well as a weak positive correlation between the release and the specimen volume.
Conclusions
Type of solvent, molecular mass of eluates, and specimen surface and volume affect substances release from materials.
Clinical relevance
It could be advisable to rely on materials based on monomers with a reduced elution tendency for clinical procedures.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
The continuous demand for esthetic care and the improved properties of dental materials have led to the increasing use of resin-based composites as restorative material in dental practice. However, despite their growing popularity, many doubts have been raised over the last years about the actual safety of their use [1,2,3,4,5].
Resin-based composites consist of an organic matrix, reinforcing fillers, a silane coupling agent, pigments, catalysts, and inhibitors. Bis-GMA and other bisphenol A (BPA)-derived monomers are the most employed in methacrylate-based composite material fabrication, because of their relevant properties, such as flexural strength, volumetric shrinkage, water sorption/solubility, and viscosity [6]. However, they may induce genotoxicity and cytotoxicity probably through DNA damage, inhibition of cytokine release, and induction of apoptosis and necrosis [7, 8]. For example, Bis-GMA stimulates the production of PGE2 with the expression of COX2, induces pro-inflammatory activation, and increase of IL-1β, IL-6, and nitric oxide; the (co)monomer triethyleneglycoldimethacrylate (TEGDMA) is known instead to cause deoxyribonucleic acid (DNA) strand breakage [9,10,11].
The loss of substances from polymeric matrix mainly occurs following two mechanisms: free monomer release following the polymerization phase and intra-oral degradation [5, 12,13,14,15,16]. With a curing time usually not longer than 40 s and a temperature around 37 °C in the oral cavity, composites are never completely polymerized because of the propagation of the crosslinking reaction that drastically reduces the mobility of the monomers [17, 18]. Due to this incomplete polymerization, dental composites can release into the oral cavity residual monomers able to affect the biological compatibility of these materials [19,20,21,22,23]. As confirmed by many studies, the less the degree of conversion, the higher the amounts of elutable residual monomers [24, 25]. In addition, intra-oral degradation of resin-based restorations may induce additional release of components [26], whose majority have probably not been identified yet [27]. On one hand, they are an effect of mechanical, hydrolytic, and enzymatic scission, and, on the other hand, a result of composite aging that leads to more porosities, water sorption, and degradation [28,29,30]. Systemic intake of chemical substances released by resin-based restorations is possible by three main ways: diffusion to the pulp through dentinal tubules, gastro-intestinal ingestion, and uptake of volatile components in the lungs [31, 32].
In view of the progressive development of novel dental materials and the above-mentioned considerations, the idea of the present study was to review the recent literature in order to assess the quantifiable concentrations of elutable substances released from resin-based dental materials into oral environment. No up-to-date literature review regarding this argument has been published after the comprehensive analysis made by Van Landuyt et al. in 2010 [18], of which the present paper represents an update based on the literature of the last decade, aimed at taking into account also the behavior of new resin-based materials (and included elutable substances) that were not available at that time.
Materials and methods
Systematic review and meta-analysis protocol
The present study was conducted adhering to the guidance of PRISMA (Preferred Reporting Items of Systematic Reviews and Meta-Analyses) in order to follow a uniform and transparent methodology able to provide outcomes comparable with other meta-analytical studies.
Research resources and strategies
The systematic research strategy was conducted by three reviewers among multiple databases: PubMed, Scopus, and Web of Science. The object of this research was all international literature with no language restrictions, published among dental journals, in the decade from January 2010 to April 2022, regarding the topic of elution of monomers from resin-based dental materials. The inserted keywords were as follows: “resin-based,” “elution,” “eluate,” “dental composite,” “HPLC,” “LC,” LC–MS,” “quantification,” “release,” “substances,” “ingredients,” “components.” The search strategy used is summarized in Table 1.
Data collection
All the references obtained through the above-mentioned keyword searching were collected in EndNote X9 software (Clarivate, MA, USA), where the duplicates were removed. Subsequently, all the data were loaded into Rayyan [33], an online free tool for systematic reviews. A systematic methodology was used to label all the relevant information for the exclusion or the inclusion of the individual papers. Titles and abstracts were initially screened to identify studies that potentially met the eligibility criteria. Afterwards, full texts were reviewed assessing them on the basis of the inclusion/exclusion criteria specified in the following paragraph. The decision process was performed by two independent reviewers. In case of ambiguity or disagreement between the reviewers, the final decision was reached through consultation with a third reviewer, a senior experienced researcher. The results of the selected studies were analyzed to collect mean values (and standard deviations) for the concentration of eluted molecules in the soaking solvent (both per surface and per volume of the resin sample) at a specific incubation time. Those data were then subjected to the meta-analysis.
Inclusion and exclusion selection criteria
Only the results of the following studies were included in this research:
-
1.
Studies investigating monomer elution in resin-based dental materials as restorative composites, bulk-fill composites, flowable composites, adhesives, resin-modified glass-ionomer cements, resin cements, CAD/CAM resin-based materials, dental sealer. Studies conducted on provisional resin-based materials, acrylic-based resins for prosthodontics and orthodontics, root canal sealers, experimental resin-based materials, and fiber-reinforced composites were not included;
-
2.
In vitro studies. In vivo studies were excluded;
-
3.
Studies where the results were explicitly quantified, with clear information about mean and standard deviation values. Studies with qualitative or semi-quantitative results (for example the results referred to internal standard caffeine expressed in CF%) were not included, as well as studies where standard deviation was not mentioned;
-
4.
Studies which clearly expressed the unit of measurement of their results so as to allow an appropriate conversion into a common unit of measurement when needed. Studies using units of measurement that could not be properly converted were not included. Data for those molecules whose information about molecular weight could be gathered neither by searching the available scientific literature nor by contacting authors or material manufacturers had to be excluded as well;
-
5.
Studies in which the incubation time for every given elution measurement was clearly specified. Only studies providing results for an incubation time of 24 h were included. If elution data after longer incubations were also provided, those results were used to calculate the mean value of total cumulative release. Results of studies where the elution after 24 h was not reported or the measurement was just performed at a shorter time were not included;
-
6.
Studies that clearly reported the sample size (n);
-
7.
Studies that clearly described the manufacturing procedure and the dimensions of the specimens, thus allowing to calculate their exact surface and volume. Studies where shape and dimensions of the specimens were unclear were not included. Studies in which the specimens were manufactured as tooth fillings for a cavity of unspecified dimensions were excluded;
-
8.
Studies where the samples were polymerized and the methodology did not involve any pre-incubation time (for example leaving the specimen exposed to air or in any other medium) or any additional treatment (such as bleaching) before soaking;
-
9.
Studies clearly defining the volume and quality of the solvent. Studies where that information was not provided were excluded.
In case that the paper did not provide all the required information, the full text could not be obtained or there was the need for any clarification, the corresponding authors or the manufacturer of the tested materials were contacted by email in two attempts. If it was not possible to access the necessary data in this way, then even potentially relevant studies had to be excluded.
Recalculation
The collected elution data were inserted into MS Excel 2016 (Microsoft, WA, USA) software and prepared for statistical analysis. For those studies that did not present results numerically, but in a graph, the author of the article was contacted to supply the exact data. If it was not possible to obtain information in this way and the graph was sufficiently precise to accurately distinguish the recorded results, the online graphical tool Web Plot Digitizer [34] was used to extract them. In order to prevent data loss, if any study reported an eluate concentration “below the limit of detection,” this result was substituted by the actual value of the limit of detection specified by the author for that particular eluate. If the authors did not specify this limit, the result was substituted with the lowest measured concentration of released molecule among the results of all the included studies.
The included studies expressed the amounts of eluted monomers in several different units (mg/ml, μg/ml, ng/ml, mg/l, mmol/l, μmol/l, nmol/mm2). Therefore, in order to obtain uniform outcomes, it was necessary to convert them into a common unit of measurement, namely moles of eluted molecule per surface of resin specimen (μmol/mm2) and moles of eluted molecule per volume of resin specimen (μmol/mm3). The applied calculations were performed as previously suggested by Van Landuyt et al. [18] and are listed in Table 2.
Statistical analysis
Statistical analysis was performed using IBM SPSS Statistics 24 (IBM Corp., NY, USA) statistical software. The weighted means and standard deviations (SD) of concentration (per surface and per volume of tested specimen) of each eluted substance, in the different types of incubation solvent, were calculated for the release measurements collected at 24 h and for the total cumulative release (if further measurements were performed also after 24 h). If the study provided results only at 24 h, then no total cumulative release results were calculated. In case the solvent liquid was not refreshed after every measurement, then the total cumulative release was represented by the highest measured amount of eluted substance. In case of refreshing, the total cumulative release mean value was calculated as sum of mean values of all measurements and the SD was calculated as:
The fixed model was used in order to calculate the weighted mean. The 95% confidence interval (CI) for weighted mean was also computed, with its lower and upper limits calculated as follows [35]:
where T is weighted mean for study and SE is the standard error.
Additionally, the heterogeneity was estimated using Cochran Q Statistic as:
where wi is the weight of each study, Ti is the weighted mean of each study, Q is the chi-squared statistic, and df is its degree of freedom. The interpretation of heterogeneity I2 according to Cochrane Handbook for Systematic Reviews is as follows: 0 to 40%, might not be important; 30 to 60%, may represent moderate heterogeneity; 50 to 90%, may represent substantial heterogeneity; and 75 to 100%, considerable heterogeneity [36].
The difference between weighted means of six most frequently detected monomers (Bis-EMA, Bis-GMA, BPA, HEMA, TEGDMA, UDMA) in water-based and organic solvents was examined through z-test. Pearson’s correlation coefficient was applied in order to assess correlations between the release of these six monomers and molecular mass, surface of specimen, volume of specimen, and volume of incubation solvent. The correlation coefficients were interpreted according to the following scale [37]: 0.00–0.10 as negligible correlation, 0.10–0.39 as weak, 0.40–0.69 as moderate, 0.70–0.89 as strong, 0.90–1.00 as very strong correlation.
Results
Systematic review
The electronic research through three different databases (PubMed, Scopus, Web of Science), inserting the keywords separately or in combination, generated a total of 1578 references, which were reduced to 877 after the duplicate removal. After the examination of titles and abstracts, 791 studies were excluded because of their study design incompatibility with this review (n = 653), wrong publication type (n = 70) or wrong type of material undergoing the research (n = 68). A total of 86 potentially relevant studies accessed the full-text evaluation phase resulting in a final number of 63 articles excluded with reasons [3, 38,39,40,41,42,43,44,45,46,47,48,49,50,51,52,53,54,55,56,57,58,59,60,61,62,63,64,65,66,67,68,69,70,71,72,73,74,75,76,77,78,79,80,81,82,83,84,85,86,87] (Table 3) and 23 publications included for further quantitative assessment (Fig. 1). A list of the included studies and their basic information is shown in Table 4. Extended information about the same studies, including more details regarding the protocols and the methodologies used, is provided in Online Resource 1.
The studied resin-based materials were all commercial products commonly used in dental treatments, most often resin-based composites for restorations, but also adhesives, resin modified glass-ionomer cements, resin cements, CAD/CAM resin-based materials, and dental sealers. The authors always indicated the product designation and manufacturer.
Most of the studies included in the present research had a similar protocol. When dealing with materials that had to undergo a polymerization process, authors applied them inside prefabricated molds with specified forms and dimensions. These were predominantly discs of various diameter and thickness (in most cases 5 mm diameter and 2 mm thickness). Subsequently, molds top were covered with glass slides or matrix strips. The polymerization was performed with different types of polymerization lamps (halogen and led lamps) operated with various intensity and power settings. However, a LED lamp on standard curing mode (with an output irradiance of 1200 mW/cm2 and a wavelength range of 430–480 nm) was prevalent through the included studies. The quality of irradiance was often confirmed with calibrated radiometer systems. The polymerization time respected the manufacturer’s recommendations and the distance was reduced to a minimum (mostly 0 mm). The protocol of some studies also included a surface polishing phase [80, 88, 89].
Once all specimens were prepared, they were soaked in several types of solvents divided into water-based media (distilled water, artificial saliva and cell culture mediums as fibroblast grow medium, minimum essential medium, and Dulbecco’s Modified Eagle Medium) and organic media (methanol, ethanol, and their dilutions with water). The most used solvents were distilled water, 75% ethanol-distilled water solution, and methanol. The volume of solvent used among the studies ranged between 0.4 and 10 ml (most commonly 1 ml). Many authors performed the elution measurements of multiple types of materials in multiple solvents simultaneously.
In some studies, multiple measurements were performed at different soaking times refreshing the solvent after each measurement; their results showed, therefore, a decreasing tendency over time. In other studies, the solvent was not refreshed: these papers reported increasing results due to the aggregate amounts of leached molecules over time. In all the selected studies, a common measurement time interval of 24 h was observed: even though some studies investigated the elution of monomers and additives after shorter times, such as after 1 h [53, 90], and other works followed the results up to 1 [53, 90, 91], 2 [92, 93], or 3 months [80, 94], the majority observed the elution between 1 day and 1 week.
Although some authors used gas chromatography/mass spectrometry (GC/MS) [46, 62, 72, 83, 84, 89, 91, 95,96,97,98,99] or liquid chromatography/mass spectrometry LC/MS [92, 100, 101], the release of monomers and additives was prevalently detected by the method of high performance liquid chromatography (HPLC). A list of the included studies together with detailed information on the technical parameters of their protocols is given in Online Resource 1. All the molecules detected in the solvents, mainly monomers and additives (as initiators, inhibitors, etc.), are listed in Table 5. The most detected molecules were as follows: triethylene glycol methacrylate (TEGDMA), bisphenol A diglycidyl methacrylate (Bis-GMA), ethoxylated bisphenol A glycol dimethacrylate (Bis-EMA), 2-hydroxyethyl methacrylate (HEMA), urethane dimetacrylate (UDMA), bisphenol A (BPA).
In some cases [80, 93,94,95, 99,100,101,102], the authors reported an elution that was below the limit of detection: to quantify such an information, the actual limit of detection value reported in the study was used as raw datum. In case the actual limit of detection was not published [72, 90, 95, 96, 99, 102,103,104] and not retrievable from the authors, it was substituted by the lowest measured result of concentration for every specific molecule among the included studies.
The present review included also studies comparing substance elution under various conditions, such as different solvent temperatures [88], different polymerization times, distances and settings [96, 101, 104, 105], polymerization through a barrier [106], experimental addition of antioxidants into the investigated material [98], and application of bleaching agents [83, 84, 103]. For those studies, however, only the data coming from the control groups, including specimens manufactured in basic conditions and strictly following the producer’s instructions, were collected.
Release
Tables 6 and 7 summarize the achieved results as weighted means (and SD) for the release measurements collected at 24 h and for the total cumulative release, per surface and per volume of tested specimens.
In such cases (BPA, DEGDMA, HPMA), where a high value of SD could be observed, a great heterogeneity of the original data could be assumed. For many eluates, a considerable heterogeneity of the resulting data (I2 > 75%) was evident, which might be due to several factors, such as different types of materials, materials manufacturers, study protocols, and analytical methods used to determine the amount of substance eluted together with various limits of detection that often had to be calculated.
The results were divided into two groups of water-based (distilled water, artificial saliva, and different types of cell media) and organic (methanol, ethanol solution) incubation solvents. In the majority of the results, a statistically significant difference between those two groups was detected, with a superior elution in organic solvents for most monomers. Bis-EMA, Bis-GMA, BPA, HEMA, TEGDMA, and UDMA were the most detected monomers, and their elution in organic and water-based solvents is summarized in Figs. 2 and 3. Conversely, for most additives, the results were rarely reported in more than one study. In some cases, the value was even derived from only one sample in a single study; therefore, the values of SD and heterogeneity could not be calculated for such molecules. Among the monomers, HEMA demonstrated the highest elution in both types of solvent (both per surface and per volume). A slightly reduced elution was recorded for TEGDMA, BPA, and Bis-EMA, depending on the solvent nature. Bis-GMA showed the lowest release (per volume and per surface) irrespective of the solvent, and a very low release was detected also for UDMA. The release of some additives appeared similarly high. For example, DMABEE (ethyl 4-dimethylamino benzoate), CQ (Camphoroquinone), CSA (Campheracid anhydride), BHT (Butylated hydroxytoluene), HMBP (2-hydroxy-4-methoxybenzophenone), and TINP (Tinuvin P) showed to elute at levels comparable to those of some monomers, especially in organic solvents.
The Pearson’s correlation test demonstrated a strong significant inverse correlation between the amount of released molecule and the molecular mass in organic solvents per surface (r = − 0.887; p = 0.046) and very strong correlation per volume (r = − 0.914; p = 0.011). Such correlation was not significant in water-based solvents (p > 0.05).
For results expressed as monomer elution per surface (μmol/mm2), a weak positive correlation was detected between the total surface area of the specimen and the amount of released eluate, both when data coming from all the different types of solvents were pooled together (r = − 0.283; p = 0.025) and for organic solvents alone (r = − 0.303; p = 0.037); such correlation was not evident when just water-based solvents were concerned (p > 0.05). For results expressed as monomer elution per volume (μmol/mm3), the same weak positive correlation between the release amount and the specimen surface was found when data coming from both types of solvents were pooled together (r = 0.0.223; p = 0.027). Such a correlation was detected even when the organic solvents were considered separately (r = − 0.302; p = 0.022), but it could not be confirmed (p > 0.05) for the results independently coming from the water-based solvents.
A weak positive correlation was found between the sample volume and the amount of released eluate per volume (μmol/mm3) considering data from organic solvents (r = − 0.278; p = 0.036), while there was not any correlation when considering water-based solvents (p > 0.05).No correlation (p > 0.05) was detected between the release of monomers (both per surface and per volume) and the volume of solvent, independently on the solvent nature.
Discussion
The present meta-analytical review included in vitro studies with the following common research protocol: preparation of resin-based dental materials specimens, soaking into different types of water-based or organic solvents (without any pre-incubation treatment), and quantification of the released compounds at different time intervals, with reference analysis at 24 h.
To determine the quantity of released compounds, the included studies performed the analysis prevalently through the HPLC (high-performance liquid chromatography) or GC–MS (gas chromatography mass spectrometry) methods. The analytical methods of LC–MS (liquid chromatography-mass spectrometry) and UPLC-MS/MS (ultraperformance liquid chromatography-tandem mass spectrometry) were used rarely. All the above-mentioned chemometric techniques are advanced methods able to detect singular molecules if used with correct calibration. HPLC and LC–MS are very versatile and popular methods because of their wide range of applications and their ability to detect molecules with high molecular weight [107]. Both UPLC- MS/MS and GC–MS (performed strictly with vaporized, volatile, and thermally stable molecules) [108] are instead particularly suitable methods for low molecular weight particle analysis [107].
The elution of a total of 36 substances could be observed within the included studies. The majority of data referred to monomers. Monomers are a significant component of resin-based composites as they represent about 20–40% of their content. Undesirable effects are attributed to monomers, which are released during incomplete monomer-polymer conversion [109]. The inorganic fillers as quartz, borosilicate, lithium–aluminum–silicate glasses, and amorphous silica, represent about 60–80% of resin-based composite content, but they do not seem to play a major role in the biocompatibility of these materials [5]. Additives, that usually play a role in promotion, modification, or inhibition of the polymerization reaction, represent only about 1–3% of the composition. Manufacturers are not obliged to disclose the ingredients in the composition of the materials if they do not exceed 1% of total volume [89]. Besides that, Material Safety Data Sheets (MSDS) of products are often incomplete [110, 111].
In the present study, HEMA (2-hydroxyethyl methacrylate) was the most released monomer. It can be described as a low molecular mass monomer (130 g/mol) with small dimensions, highly soluble in both types of solvents. Actually, in case of HEMA, no statistically significant difference between the release in organic and water-based solvents at 24 h was observed (Figs. 2 and 3). Due to its hydrophilic character, HEMA is a co-monomer frequently added in commercial resin-based materials in order to prevent the separation between water and hydrophobic co-monomers [112, 113]. On the other hand, some negative physic-mechanical features of HEMA (as low degree of conversion and water retention impairing a good polymerization) were reported [114]. Moreover, HEMA demonstrated a certain degree of cytotoxicity affecting cell viability [115,116,117], which might be aggravated by HEMA water solubility. Hydroxyethyl acrylamide (HEAA) and diethyl acrylamide (DEAA) are regarded as the two most promising alternatives to HEMA [114].
TEGDMA, BPA, and Bis-EMA revealed a quite high solubility (depending on the solvent) as well. TEGDMA demonstrated relatively high levels of release, specifically in organic solvents. TEGDMA is a low viscosity and low molecular mass (286.32 g/mol) molecule often added into composite materials in order to reduce the viscosity of the mixture [118, 119] and thus increase the degree of conversion (DC). Unfortunately, the higher DC determined by TEGDMA also increases the polymerization shrinkage of the material [120]. For this reason, TEGDMA is often at least partially substituted by another monomer of higher molecular mass and lower viscosity (for example Bis-EMA) [119]. Cytotoxic effects of TEGDMA on gingival and human fibroblasts clinically related to pulp inflammation and necrosis were reported [121, 122].
BPA demonstrated quite high values of release in results expressed as substance elution per volume (μmol/mm3), and significantly higher release was detected in organic solvents. Despite BPA is not directly present in resin-based composites, it still occurs in form of impurities [123]. Bis-DMA (bisphenol A dimethacrylate) can be converted into BPA by hydrolysis after its exposure to the esterase enzymes contained in saliva [124, 125]. Although Bis-GMA (synthetized from BPA and glycidyl methacrylate) does not undergo this reaction presumably because of its chemical structure which prevents hydrolysis at the ester linkage [118], Bis-GMA-based materials still showed detectable BPA release [126,127,128]. BPA molecule is insoluble in water but demonstrates a good solubility in organic solvents as alcohols, ethers, and fats [129]. BPA molecular mass corresponds to 228.28 g/mol. The European Food Safety Authority (EFSA) stated in 2015 that the temporary Tolerable Daily Intake (TDI) for BPA is 4 μg/kg/day [130]. During the measurements of a human BPA exposure, it was estimated that an average human organism directly or indirectly receives about 30.76 ng/kg per body weight per day [131,132,133,134]. Resin-based dental restorations are listed among the main sources of oral BPA intake [123, 135,136,137]. The negative human health effects of BPA are related to its endocrine disrupting activity [138,139,140,141,142] and have greater impact in early-life exposure [140, 143]. Alternative forms of bisphenol, as BPS (bisphenol S) and BPF (bisphenol F) were introduced to substitute BPA in order to avoid such an endocrine-disrupting chemical, but recent studies referred a similarly unfavorable behavior [142, 144].
High values in results expressed as monomer elution per surface (μmol/mm2) were detected for Bis-EMA in both types of solvents but the release was significantly increased in organic solvents. Bis-EMA is a hydrophobic analog of Bis-GMA used as a basis monomer of several dental resin materials in order to reduce their viscosity [17]. Low viscosity is caused by the absence of free hydroxyl groups which allows major incorporation of inorganic filler [47]. Bis-EMA is a low volatile hydrophobic molecule with a molecular mass of 452 g/mol. It was reported that also Bis-EMA containing materials released BPA as an impurity resulting from Bis-EMA degradation [128].
The records for UDMA release were generally very low, especially in water-based solvents. UDMA is another co-monomer commonly applied in dental resin-based materials to enhance the viscosity. Considered to be an alternative to Bis-GMA [145], UDMA usage is limited by its high molecular mass (470.56 g/mol), which results in a remarkable volumetric shrinkage clinically related to greater marginal gap between tooth and restoration [120]. Regarding its cytotoxicity, it has been reported that UDMA inhibits cell growth in vitro at the concentration of 0.1 mM [146].
The lowest release was demonstrated for Bis-GMA, which might be explained by its high molecular mass (512.599 g/mol) and very slight solubility in all types of solvents. Bis-GMA is a BPA derivate that is most frequently used as the base of resin-based composites. Bis-GMA molecule is composed by methyl methacrylate groups added to the hydroxyl groups of BPA via a glycidyl spacer [147]. Bis-GMA is a base matrix compound generally convenient for its low volumetric shrinkage after polymerization, good mechanical properties, high refractive index, low volatility, and diffusivity into tissues and excellent adhesion to enamel [127, 148]. Great voluminosity, strong molecular interactions driven by H-bonding, and large molecular mass are the determinants of its particularly high viscosity [149]. Nevertheless, the raised doubts about Bis-GMA low viscosity that might negatively affect mechanical properties of materials [150] and its possible cytotoxic effects linked to BPA [151, 152] have started the search for alternatives and led to the marketing of Bis-GMA resin-based materials [147, 153], such as Bis-EFMA-based composites [99].
The sequence of release of the substances corresponds to the order of their cytotoxic potential assessed by Reichl et al. [154]: HEMA < TEGDMA < UDMA < Bis-GMA. In that study, a 50% reduction in cell viability was reported after exposure of human gingival fibroblasts to Bis-GMA at a concentration of 0.087 mmol/L, to UDMA at 0.106 mmol/L, and for HEMA at 11.530 mmol/L. For TEGDMA, such viability decrease was detected at 3.460 mmol/L. The reduction of cell viability was related to the increased amount of reactive oxygen species and oxygen stress, and to DNA strand damage and cell cycle alterations [109]. Comparing the dental resin-based materials containing or non-containing Bis-GMA, a greater cytotoxic and genotoxic potential of materials releasing Bis-GMA and TEGDMA was observed [122]. The concrete effects of monomers applied in direct contact with dental pulp cells, as inflammation and inhibition of dentin mineralization, were described in many studies [155,156,157].
Among the included studies, the release of many additives was detected as well. Although the additives are present in the composition of resin-based materials only in a small percentage, some still showed quite high release, reaching the levels of frequently eluted monomers (Tables 6 and 7). However, the results for additives need to be considered with caution, as only few studies analyzed their elution and therefore the input data were not as strong as for monomers.
In the present study, results were given both for the elution at 24 h and for total cumulative release. The analysis at 24 h was considered the reference, as it is quite common in many studies and was present in all included studies. Concerning the total cumulative release, it must be underlined that the cumulative time period varied among the different studies from days to months.
The release among the included studies was confronted in different solvents. Most of the studies tested the materials in more than one solvent, prevalently diluted ethanol, distilled water, and methanol. Some protocols also tested elution in artificial saliva and in various types of media commonly used for cell culture growth. Most but not all studies clearly specified if the solution was refreshed after every analysis or if the results were of cumulative character. Water-based solvents as artificial saliva or distilled water can mimic intraoral conditions. Organic solvents are characterized by a major dissolution efficiency probably ascribable to their better penetration, sorption, and swelling of the polymer material [18]. Based on the outcome of this study, there was a significant difference between elution of water-based and organic solutions (Figs. 2 and 3), which offered a prevalently better environment for greater elution. Since monomers are generally hydrophobic, and the original studies declared similar differences between the major release in organic solvents and water-based ones, this outcome only confirmed the expectations.
Examining the influence of molecular mass on the amount of released molecules, a strong negative correlation was reported. This would mean that small molecular mass molecules tend to have greater mobility and polarity, and to release faster and more easily, unlike heavier and larger molecules. Such supposition corresponds to the results of the current paper considering the release of the six mainly examined monomers. HEMA, as a very light molecule, was released the most, followed by TEGDMA, BPA, and Bis-EMA. Lower release was detected for UDMA, and even lesser for Bis-GMA, the molecule with the highest molecular weight among these monomers.
The importance of the surface area exposed to the solvent was confirmed by the weak but statistically significant correlation between the amount of released molecule and the surface of specimens in the results for both surface and volume; this was valid for the results of both the type of solvents pooled together, and also for the organic ones separately. A faster elution from surface and subsurface layers compared with deeper layers was reported in previous studies [43, 158]. Therefore, it can be hypothesized that the more extensive the surface of the restoration is, the higher the risk of monomer elution becomes. Such theory might have an interesting clinical impact. Considering the minimal amount of intraorally polymerized resin-based material used for the cementation of indirect restorations, the created surface of material exposed to oral environment is minimal. From this point of view, indirect restorations would be the optimal solution regarding to the risk of monomer release and potential toxicity. Only two studies [92, 100] specified the actual surface area that was in contact with the solvent without considering the area contacting the bottom of the container all the time during the soaking phase. The rest of the studies did not mention this aspect.
A weak correlation between the release and the volume of specimens was detected when data for both solvents were pooled together. Such correlation may sustain the hypothesis that the major volume and so the major thickness of the material increment determines the major release. The descending efficiency of polymerization with the increasing thickness increment of cured material led to incomplete polymerization and reduced the degree of conversion in the deep layers. This results in the persistence of free monomers and their potential subsequent release [159, 160].
A correlation between the release of substances and the absence or presence of oxygen inhibition layer (OIL) could not be determined, as there were not enough data for such calculation. Only few studies [53, 90, 91, 99, 100] provided results in the presence of OIL; all the remaining studies clearly specified the steps taken to prevent the presence of the OIL (blocking the contact of the surface of material with oxygen before the curing process through glass, matrix strip, or glycerin gel). The presence of atmospheric oxygen may inhibit the correct polymerization of monomers and create a surface layer of unreacted monomers. The decrease of DC in the presence of the OIL was demonstrated [161], as well as an increase of DC after removing the OIL by polishing and finishing [162]. The correlation seemed to confirm the hypothesis that the release of monomers would be higher in the presence of OIL.
In general, the results of the current review are broadly consistent with Van Landuyt et al. [18] 10-year-old findings. However, slight differences deserve to be mentioned. The present work showed a statistically significant positive correlation (although weak) between the amount of released molecule and the specimen volume, which was not evident in Van Landuyt et al. article. In turn, their review revealed a weak but significant (positive) correlation between the released amount of each eluate and the amount of solution in which the resin-based specimen was immersed, which our findings failed to demonstrate.
The present meta-analytical review provided an exhaustive summary of the current evidence regarding substances elution from resin-based dental materials in vitro. Therefore, taking into account all the inherent drawbacks of in vitro studies, caution is recommended in generalizing the above-mentioned results. In vitro experiments regarding dental materials and their properties usually tend to mimic the environment of oral cavity, maintaining the reproducibility and stability of applied analytical methods. In the oral cavity, there is a constant influx of new saliva, which washes the surfaces of tooth and restorations, and which is subsequently drained by swallowing. The composition of natural human saliva is very complex and variable, depending on several individual factors (such as food intake, bacterial colonization, and others), which fundamentally affect intraoral pH. For those reasons, it is not exactly possible to create a synthetic formula identical to natural saliva [163]. However, the use of natural human saliva is unreliable as well, due to its lack of stability outside the oral cavity [164]. In case of monomer elution research, it would be therefore necessary to ensure an extraction solvent that resembles natural saliva and its constant exchange. It could be speculated that refreshing the extraction solvent could prevent reaching the chemical balance that progressively slows down monomer elution, thus letting this phenomenon run naturally without restrictions. On these bases, the protocols where the solvent was periodically refreshed after each measurement adhered more closely to the real intraoral conditions [18]. Nevertheless, reproducing the precise intraoral conditions seems very difficult, and this should be taken into account when evaluating the results of in vitro studies that may not fully correspond to the in vivo situation.
Finally, besides all the inherent drawbacks of in vitro studies, other potential limitations to the present review were related to the lack of standardization of the included studies: variability of original units of measurement, specimens size, samples polymerization and storage, and absence of limit of detection values, in fact, complicated the paper comparison.
The variability of the original units of measurement and their conversion into a common one were among the most important issues that needed to be solved in order to obtain uniform outcomes which could be subsequently compared and analyzed. The primary results were expressed mostly in concentration, while some of them were already related to surface and volume. The choice to express the outcomes into common units, moles per surface and volume, was based on the considerations given by Van Landuyt et al. [18]. These authors preferred this approach in order to express the amount of released molecules per surface and volume that may be confronted with actual dimensions of in vivo restorations.
There were other points in the selected original studies which were rarely standardized, thus making the comparability of the studies more difficult. Although the specimens were mostly disk-shaped, their size varied in every study. The details about the setting of the curing unit, the polymerization time (respecting or not the time recommended by the manufacturer), and the distance of the curing unit from the specimen surface were not always complete. Only some studies [62, 83, 84, 92, 94, 96,97,98, 101, 102, 165] provided very detailed information about the storage conditions during the soaking phase, namely the exact temperature and light-conditions. However, a clear specification of the solvent characteristics and its volume was one of the most important information that was required in the present review, and, if not clearly specified, represented an exclusion criterium. In the included papers, the specimens were soaked into the extraction liquid almost immediately, without any pre-incubation period.
Another important element that was often missing among studies was the limit of detection value. It was decided to supplement the original results under the limit of detection by the value of limit of detection itself. In case this was missing, then the lowest measured result within the included studies for the given molecule was used as a substitute value. This approach permitted not to lose but valorize data of measurements under the limit of detection; however, it might also represent a minor source of inaccuracy for the primary results. Moreover, some authors provided the results of their studies only in the form of graph and not in exact numbers. Only the studies where those graphs were clearly legible were included. Although a precise digital graphical tool was used to extract numerical values, this procedure might have still led to a minimal additional inaccuracy in obtained data.
In light of the above-mentioned limitations, the authors of the present paper emphasize the necessity for standardization, as already underlined by Van Landuyt et al. Despite their 10-year-old attempt to suggest several guidelines for study design standardization, in fact, no evident improvement has been detected in the literature regarding monomer elution from resin-based dental materials of the last 10 years. The authors of the present study recommend, therefore, that future works follow the above-mentioned guidelines and reaffirm the need to overcome the great heterogeneity ruling in the literature through the standardization of the following points: dimension and form of the specimen, specimen manufacturing protocol (including polymerization conditions such as intensity, modality, time of polymerization, and prevention of OIL), volume and types of soaking solvent (pH), soaking conditions (temperature, light, and real specimen surface exposure to the solvent), methodology of analysis, and units of measurement to quantify the results.
Conclusions
Based on the findings of this meta-analytical systematic review, it was possible to draw the following conclusions:
-
1.
The difference of monomer elution between organic and water-based solvents was evident, as organic solvents provoked major substances release.
-
2.
The strength of molecule elution is negatively correlated to its molecular mass: a lighter molecule elutes more, while molecule with higher molecular mass is released less.
-
3.
The surface area of specimen plays an important role: the major release of substances was observed in specimens of more extended surface.
-
4.
The volume of specimen may be an important factor as well: the more voluminous specimen demonstrated slightly major elution tendency.
It must be underlined, however, that the comparison of the different studies was not always effortless, given the wide variability of protocol set-ups, methodologies, and materials. In order to improve the homogeneity of future studies, it would be advisable to standardize the following aspects for in vitro experimental protocols on composite elution: specimen size, polymerization setting, solvent character, analytical method and results expressed numerically.
References
Murdoch-Kinch CA, McLean ME (2003) Minimally invasive dentistry. J Am Dent Assoc 134:87–95. https://doi.org/10.14219/jada.archive.2003.0021
Durner J, Schrickel K, Watts DC, Becker M, Draenert ME (2021) Direct and indirect monomer elution from an RBC product family. Dent Mater 37:1601–1614. https://doi.org/10.1016/j.dental.2021.08.011
Durner J, Wellner P, Hickel R, Reichl FX (2012) Synergistic interaction caused to human gingival fibroblasts from dental monomers. Dent Mater 28:818–823. https://doi.org/10.1016/j.dental.2012.04.031
Völkel W, Colnot T, Csanády GA, Filser JG, Dekant W (2002) Metabolism and kinetics of bisphenol a in humans at low doses following oral administration. Chem Res Toxicol 15:1281–1287. https://doi.org/10.1021/tx025548t
Goldberg M (2008) In vitro and in vivo studies on the toxicity of dental resin components: a review. Clin Oral Investig 12:1–8. https://doi.org/10.1007/s00784-007-0162-8
He J, Kopperud HM (2018) Preparation and characterization of Bis-GMA-free dental composites with dimethacrylate monomer derived from 9,9-Bis[4-(2-hydroxyethoxy)phenyl]fluorene. Dent Mater 34:1003–1013. https://doi.org/10.1016/j.dental.2018.03.007
Krifka S, Petzel C, Hiller KA, Frank EM, Bosl C, Spagnuolo G, Reichl FX, Schmalz G, Schweikl H (2010) Resin monomer-induced differential activation of MAP kinases and apoptosis in mouse macrophages and human pulp cells. Biomaterials 31:2964–2975. https://doi.org/10.1016/j.biomaterials.2010.01.005
Huang FM, Kuan YH, Lee SS, Chang YC (2015) Cytotoxicity and genotoxicity of triethyleneglycol-dimethacrylate in macrophages involved in DNA damage and caspases activation. Environ Toxicol 30:581–588. https://doi.org/10.1002/tox.21935
Huang FM, Chang YC, Lee SS, Yeh CH, Lee KG, Huang YC, Chen CJ, Chen WY, Pan PH, Kuan YH (2016) BisGMA-induced cytotoxicity and genotoxicity in macrophages are attenuated by wogonin via reduction of intrinsic caspase pathway activation. Environ Toxicol 31:176–184. https://doi.org/10.1002/tox.22032
Kuan YH, Huang FM, Lee SS, Li YC, Chang YC (2013) Bisgma stimulates prostaglandin E2 production in macrophages via cyclooxygenase-2, cytosolic phospholipase A2, and mitogen-activated protein kinases family. PLoS ONE 8:e82942. https://doi.org/10.1371/journal.pone.0082942
Kuan YH, Huang FM, Li YC, Chang YC (2012) Proinflammatory activation of macrophages by bisphenol A-glycidyl-methacrylate involved NFκB activation via PI3K/Akt pathway. Food Chem Toxicol 50:4003–4009. https://doi.org/10.1016/j.fct.2012.08.019
Kleinsasser NH, Schmid K, Sassen AW, Harréus UA, Staudenmaier R, Folwaczny M, Glas J, Reichl FX (2006) Cytotoxic and genotoxic effects of resin monomers in human salivary gland tissue and lymphocytes as assessed by the single cell microgel electrophoresis (Comet) assay. Biomaterials 27:1762–1770. https://doi.org/10.1016/j.biomaterials.2005.09.023
Perduns R, Volk J, Schertl P, Leyhausen G, Geurtsen W (2019) HEMA modulates the transcription of genes related to oxidative defense, inflammatory response and organization of the ECM in human oral cells. Dent Mater 35:501–510. https://doi.org/10.1016/j.dental.2019.01.011
Kermanshahi S, Santerre JP, Cvitkovitch DG, Finer Y (2010) Biodegradation of resin-dentin interfaces increases bacterial microleakage. J Dent Res 89:996–1001. https://doi.org/10.1177/0022034510372885
Schmalz G, Krifka S, Schweikl H (2011) Toll-like receptors, LPS, and dental monomers. Adv Dent Res 23:302–306. https://doi.org/10.1177/0022034511405391
Mousavinasab SM (2011) Biocompatibility of composite resins. Dent Res J (Isfahan) 8:S21–S29
Sideridou I, Tserki V, Papanastasiou G (2002) Effect of chemical structure on degree of conversion in light-cured dimethacrylate-based dental resins. Biomaterials 23:1819–1829. https://doi.org/10.1016/s0142-9612(01)00308-8
Van Landuyt KL, Nawrot T, Geebelen B, De Munck J, Snauwaert J, Yoshihara K, Scheers H, Godderis L, Hoet P, Van Meerbeek B (2011) How much do resin-based dental materials release? A meta-analytical approach. Dent Mater 27:723–747. https://doi.org/10.1016/j.dental.2011.05.001
da Fonseca Roberti Garcia L, Pontes EC, Basso FG, Hebling J, de Souza Costa CA, Soares DG, (2016) Transdentinal cytotoxicity of resin-based luting cements to pulp cells. Clin Oral Investig 20:1559–1566. https://doi.org/10.1007/s00784-015-1630-1
Ferracane JL (2011) Resin composite–state of the art. Dent Mater 27:29–38. https://doi.org/10.1016/j.dental.2010.10.020
Longo DL, Paula-Silva FW, Faccioli LH, Gatón-Hernández PM, Queiroz AM, Silva LA (2016) Cytotoxicity and cytokine expression induced by silorane and methacrylate-based composite resins. J Appl Oral Sci 24:338–343. https://doi.org/10.1590/1678-775720150449
Peutzfeldt A (1997) Resin composites in dentistry: the monomer systems. Eur J Oral Sci 105:97–116. https://doi.org/10.1111/j.1600-0722.1997.tb00188.x
Roman A, Páll E, Moldovan M, Rusu D, Şoriţău O, Feştilă D, Lupşe M (2016) Cytotoxicity of experimental resin composites on mesenchymal stem cells isolated from two oral sources. Microsc Microanal 22:1018–1033. https://doi.org/10.1017/s1431927616011624
Miletic VJ, Santini A (2008) Remaining unreacted methacrylate groups in resin-based composite with respect to sample preparation and storing conditions using micro-Raman spectroscopy. J Biomed Mater Res B Appl Biomater 87:468–474. https://doi.org/10.1002/jbm.b.31128
Durner J, Obermaier J, Draenert M, Ilie N (2012) Correlation of the degree of conversion with the amount of elutable substances in nano-hybrid dental composites. Dent Mater 28:1146–1153. https://doi.org/10.1016/j.dental.2012.08.006
Finer Y, Santerre JP (2004) The influence of resin chemistry on a dental composite’s biodegradation. J Biomed Mater Res A 69:233–246. https://doi.org/10.1002/jbm.a.30000
Atkinson JC, Diamond F, Eichmiller F, Selwitz R, Jones G (2002) Stability of bisphenol A, triethylene-glycol dimethacrylate, and bisphenol A dimethacrylate in whole saliva. Dent Mater 18:128–135. https://doi.org/10.1016/s0109-5641(01)00031-8
Santerre JP, Shajii L, Tsang H (1999) Biodegradation of commercial dental composites by cholesterol esterase. J Dent Res 78:1459–1468. https://doi.org/10.1177/00220345990780081201
Koin PJ, Kilislioglu A, Zhou M, Drummond JL, Hanley L (2008) Analysis of the degradation of a model dental composite. J Dent Res 87:661–665. https://doi.org/10.1177/154405910808700712
Shajii L, Santerre JP (1999) Effect of filler content on the profile of released biodegradation products in micro-filled bis-GMA/TEGDMA dental composite resins. Biomaterials 20:1897–1908. https://doi.org/10.1016/s0142-9612(99)00087-3
Reichl FX, Seiss M, Kleinsasser N, Kehe K, Kunzelmann KH, Thomas P, Spahl W, Hickel R (2008) Distribution and excretion of BisGMA in guinea pigs. J Dent Res 87:378–380. https://doi.org/10.1177/154405910808700401
Gerzina TM, Hume WR (1996) Diffusion of monomers from bonding resin-resin composite combinations through dentine in vitro. J Dent 24:125–128. https://doi.org/10.1016/0300-5712(95)00036-4
Ouzzani M, Hammady H, Fedorowicz Z, Elmagarmid A (2016) Rayyan-a web and mobile app for systematic reviews. Syst Rev 5:210. https://doi.org/10.1186/s13643-016-0384-4
Drevon D, Fursa SR, Malcolm AL (2017) Intercoder reliability and validity of webplotdigitizer in extracting graphed data. Behav Modif 41:323–339. https://doi.org/10.1177/0145445516673998
Borenstein M, Hedges LV, Higgins JP, Rothstein HR (2010) A basic introduction to fixed-effect and random-effects models for meta-analysis. Res Synth Methods 1:97–111. https://doi.org/10.1002/jrsm.12
Higgins JP, Thompson SG, Deeks JJ, Altman DG (2003) Measuring inconsistency in meta-analyses. Bmj 327:557–560
Schober P, Boer C, Schwarte LA (2018) Correlation coefficients: appropriate use and interpretation. Anesth Analg 126:1763–1768. https://doi.org/10.1213/ane.0000000000002864
Bandarra S, Mascarenhas P, Luís AR, Catrau M, Bekman E, Ribeiro AC, Félix S, Caldeira J, Barahona I (2020) In vitro and in silico evaluations of resin-based dental restorative material toxicity. Clin Oral Investig 24:2691–2700. https://doi.org/10.1007/s00784-019-03131-4
Kopperud HM, Schmidt M, Kleven IS (2010) Elution of substances from a silorane-based dental composite. Eur J Oral Sci 118:100–102. https://doi.org/10.1111/j.1600-0722.2009.00697.x
Phan AC, Tang ML, Nguyen JF, Ruse ND, Sadoun M (2014) High-temperature high-pressure polymerized urethane dimethacrylate-mechanical properties and monomer release. Dent Mater 30:350–356. https://doi.org/10.1016/j.dental.2013.12.009
Randolph LD, Palin WM, Bebelman S, Devaux J, Gallez B, Leloup G, Leprince JG (2014) Ultra-fast light-curing resin composite with increased conversion and reduced monomer elution. Dent Mater 30:594–604. https://doi.org/10.1016/j.dental.2014.02.023
Wolff D, Coupek M, Erber R, Krueger T, Krisam J, Staehle HJ, Frese C (2016) Effect of aqueous storage on original and repair bond strength and residual monomer release of fiberreinforced composites. J Adhes Dent 18:535–543. https://doi.org/10.3290/j.jad.a37360
Manojlovic D, Radisic M, Vasiljevic T, Zivkovic S, Lausevic M, Miletic V (2011) Monomer elution from nanohybrid and ormocer-based composites cured with different light sources. Dent Mater 27:371–378. https://doi.org/10.1016/j.dental.2010.11.017
Gul P, Celik N, Ozgeris FB, Demirkaya-Miloglu F, Kiziltunc A, Seven N (2021) Effects of bisphenol A released from composite fillings on reproductive hormone levels in men. Int Dent J 71:343–351. https://doi.org/10.1016/j.identj.2020.12.008
Grenade C, De Pauw-Gillet MC, Pirard C, Bertrand V, Charlier C, Vanheusden A, Mainjot A (2017) Biocompatibility of polymer-infiltrated-ceramic-network (PICN) materials with Human Gingival Keratinocytes (HGKs). Dent Mater 33:333–343. https://doi.org/10.1016/j.dental.2017.01.001
Bationo R, Jordana F, Boileau MJ, Colat-Parros J (2016) Release of monomers from orthodontic adhesives. Am J Orthod Dentofacial Orthop 150:491–498. https://doi.org/10.1016/j.ajodo.2016.02.027
Durner J, Schrickel K, Watts DC, Ilie N (2015) Determination of homologous distributions of bisEMA dimethacrylates in bulk-fill resin-composites by GC-MS. Dent Mater 31:473–480. https://doi.org/10.1016/j.dental.2015.02.006
Durner J, Spahl W, Zaspel J, Schweikl H, Hickel R, Reichl FX (2010) Eluted substances from unpolymerized and polymerized dental restorative materials and their Nernst partition coefficient. Dent Mater 26:91–99. https://doi.org/10.1016/j.dental.2009.08.014
Koulaouzidou EA, Roussou K, Sidiropoulos K, Nikolaidis A, Kolokuris I, Tsakalof A, Tsitsimpikou C, Kouretas D (2018) Investigation of the chemical profile and cytotoxicity evaluation of organic components eluted from pit and fissure sealants. Food Chem Toxicol 120:536–543. https://doi.org/10.1016/j.fct.2018.07.042
Janani K, Teja KV, Sandhya R, Alam MK, Al-Qaisi RK, Shrivastava D, Alnusayri MO, Alkhalaf ZA, Sghaireen MG, Srivastava KC (2021) Monomer elution from three resin composites at two different time interval using high performance liquid chromatography-an in-vitro study. Polymers (Basel) 13:4395. https://doi.org/10.3390/polym13244395
Roussou K, Nikolaidis AK, Ziouti F, Arhakis A, Arapostathis K, Koulaouzidou EA (2021) Cytotoxic evaluation and determination of organic and inorganic eluates from restorative materials. Molecules 26:4912. https://doi.org/10.3390/molecules26164912
Meyer-Lueckel H, Hartwig C, Börner HG, Lausch J (2020) Elution of monomers from an infiltrant compared with different resin-based dental materials. Oral Health Prev Dent 18:337–341. https://doi.org/10.3290/j.ohpd.a43354
Dursun E, Nguyen JF, Tang ML, Attal JP, Sadoun M (2016) HEMA release and degree of conversion from a resin-modified glass ionomer cement after various delays of light activation. Dent Mater 32:640–645. https://doi.org/10.1016/j.dental.2016.02.003
Pelourde C, Bationo R, Boileau MJ, Colat-Parros J, Jordana F (2018) Monomer release from orthodontic retentions: an in vitro study. Am J Orthod Dentofacial Orthop 153:248–254. https://doi.org/10.1016/j.ajodo.2017.06.021
Pongprueksa P, Miletic V, Janssens H, Van Landuyt KL, De Munck J, Godderis L, Van Meerbeek B (2014) Degree of conversion and monomer elution of CQ/amine and TPO adhesives. Dent Mater 30:695–701. https://doi.org/10.1016/j.dental.2014.03.007
Cokic SM, Duca RC, De Munck J, Hoet P, Van Meerbeek B, Smet M, Godderis L, Van Landuyt KL (2018) Saturation reduces in-vitro leakage of monomers from composites. Dent Mater 34:579–586. https://doi.org/10.1016/j.dental.2018.01.005
Durner J, Obermaier J, Ilie N (2014) Investigation of different bleaching conditions on the amount of elutable substances from nano-hybrid composites. Dent Mater 30:192–199. https://doi.org/10.1016/j.dental.2013.11.003
Hussain B, Thieu MKL, Johnsen GF, Reseland JE, Haugen HJ (2017) Can CAD/CAM resin blocks be considered as substitute for conventional resins? Dent Mater 33:1362–1370. https://doi.org/10.1016/j.dental.2017.09.003
Ilie N, Obermaier J, Durner J (2014) Effect of modulated irradiation time on the degree of conversion and the amount of elutable substances from nano-hybrid resin-based composites. Clin Oral Investig 18:97–106. https://doi.org/10.1007/s00784-013-0934-2
Kerezoudi C, Gogos C, Samanidou V, Tziafas D, Palaghias G (2016) Evaluation of monomer leaching from a resin cement through dentin by a novel model. Dent Mater 32:e297–e305. https://doi.org/10.1016/j.dental.2016.09.027
Kerezoudi C, Samanidou VF, Gogos C, Tziafas D, Palaghias G (2019) Evaluation of monomer leaching from a resin cement through dentin. Eur J Prosthodont Restor Dent 27:10–17. https://doi.org/10.1922/EJPRD_01854Kerezoudi09
Rothmund L, Shehata M, Van Landuyt KL, Schweikl H, Carell T, Geurtsen W, Hellwig E, Hickel R, Reichl FX, Högg C (2015) Release and protein binding of components from resin based composites in native saliva and other extraction media. Dent Mater 31:496–504. https://doi.org/10.1016/j.dental.2015.01.016
Putzeys E, Nys S, Cokic SM, Duca RC, Vanoirbeek J, Godderis L, Meerbeek BV, Van Landuyt KL (2019) Long-term elution of monomers from resin-based dental composites. Dent Mater 35:477–485. https://doi.org/10.1016/j.dental.2019.01.005
Putzeys E, Vercruyssen C, Duca RC, Saha PS, Godderis L, Vanoirbeek J, Peumans M, Van Meerbeek B, Van Landuyt KL (2020) Monomer release from direct and indirect adhesive restorations: a comparative in vitro study. Dent Mater 36:1275–1281. https://doi.org/10.1016/j.dental.2020.06.001
Yang Y, Reichl FX, Shi J, He X, Hickel R, Högg C (2018) Cytotoxicity and DNA double-strand breaks in human gingival fibroblasts exposed to eluates of dental composites. Dent Mater 34:201–208. https://doi.org/10.1016/j.dental.2017.10.002
Alamoush RA, Sung R, Satterthwaite JD, Silikas N (2021) The effect of different storage media on the monomer elution and hardness of CAD/CAM composite blocks. Dent Mater 37:1202–1213. https://doi.org/10.1016/j.dental.2021.04.009
Aldhafyan M, Silikas N, Watts DC (2022) Influence of curing modes on monomer elution, sorption and solubility of dual-cure resin-cements. Dent Mater 38:978–988. https://doi.org/10.1016/j.dental.2022.03.004
De Nys S, Putzeys E, Duca RC, Vervliet P, Covaci A, Boonen I, Elskens M, Vanoirbeek J, Godderis L, Van Meerbeek B, Van Landuyt KL (2021) Long-term elution of bisphenol A from dental composites. Dent Mater 37:1561–1568. https://doi.org/10.1016/j.dental.2021.08.005
Kincses D, Böddi K, Őri Z, Lovász BV, Jeges S, Szalma J, Kunsági-Máté S, Lempel E (2021) Pre-heating effect on monomer elution and degree of conversion of contemporary and thermoviscous bulk-fill resin-based dental composites. Polymers (Basel) 13:3599. https://doi.org/10.3390/polym13203599
Shahabi S, Sayyari M, Sadrai S, Valizadeh S, Hajizamani H, Sadr A (2021) Effect of volume and renewal of the storage media on the release of monomer from dental composites. Int J Dent 2021:9769947. https://doi.org/10.1155/2021/9769947
Hatipoǧlu Ö, Karadaş M, Er H, Turumtay EA (2019) Effect of thermocycling on the amount of monomer released from bulk fill composite resins. Dent Mater J 38:1019–1025. https://doi.org/10.4012/dmj.2018-377
Durner J, Stojanovic M, Urcan E, Hickel R, Reichl FX (2011) Influence of silver nano-particles on monomer elution from light-cured composites. Dent Mater 27:631–636. https://doi.org/10.1016/j.dental.2011.03.003
Durner J, Schrickel K, Watts DC, Becker M, Hickel R, Draenert ME (2020) An alternate methodology for studying diffusion and elution kinetics of dimethacrylate monomers through dentinal tubules. Dent Mater 36:479–490. https://doi.org/10.1016/j.dental.2020.02.008
Polydorou O, Rogatti P, Bolek R, Wolkewitz M, Kümmerer K, Hellwig E (2013) Elution of monomers from three different bonding systems and their antibacterial effect. Odontology 101:170–176. https://doi.org/10.1007/s10266-012-0071-4
Purushothaman D, Kailasam V, Chitharanjan AB (2015) Bisphenol A release from orthodontic adhesives and its correlation with the degree of conversion. Am J Orthod Dentofacial Orthop 147:29–36. https://doi.org/10.1016/j.ajodo.2014.09.013
Sunitha C, Kailasam V, Padmanabhan S, Chitharanjan AB (2011) Bisphenol A release from an orthodontic adhesive and its correlation with the degree of conversion on varying light-curing tip distances. Am J Orthod Dentofacial Orthop 140:239–244. https://doi.org/10.1016/j.ajodo.2010.02.037
Tak O, Usumez A (2015) Diffusion of HEMA from resin cements through different dentin thicknesses in vitro. Am J Dent 28:285–291
Khalid H, Syed MR, Rahbar MI, Iqbal H, Ahmad S, Kaleem M, Matinlinna JP, Khan AS (2018) Effect of nano-bioceramics on monomer leaching and degree of conversion of resin-based composites. Dent Mater J 37:940–949. https://doi.org/10.4012/dmj.2017-338
Song L, Sarikaya R, Ye Q, Misra A, Tamerler C, Spencer P (2020) Multifunctional monomer acts as co-initiator and crosslinker to provide autonomous strengthening with enhanced hydrolytic stability in dental adhesives. Dent Mater 36:284–295. https://doi.org/10.1016/j.dental.2019.11.007
Barutcigil K, Dündar A, Batmaz SG, Yıldırım K, Barutçugil Ç (2020) Do resin-based composite CAD/CAM blocks release monomers? Clin Oral Investig 25:329–336. https://doi.org/10.1007/s00784-020-03377-3
Hope E, Reed DR, Moilanen LH (2016) Potential confounders of bisphenol-a analysis in dental materials. Dent Mater 32:961–967. https://doi.org/10.1016/j.dental.2016.05.001
Yılmaz MN, Gul P (2022) Monomer release from dental restorative materials containing dimethacrylate resin after bleaching. Clin Oral Investig 26:4647–4662. https://doi.org/10.1007/s00784-022-04446-5
Schuster L, Reichl FX, Rothmund L, He X, Yang Y, Van Landuyt KL, Kehe K, Polydorou O, Hickel R, Högg C (2016) Effect of Opalescence(®) bleaching gels on the elution of bulk-fill composite components. Dent Mater 32:127–135. https://doi.org/10.1016/j.dental.2015.11.033
Schuster L, Rothmund L, He X, Van Landuyt KL, Schweikl H, Hellwig E, Carell T, Hickel R, Reichl FX, Högg C (2015) Effect of Opalescence® bleaching gels on the elution of dental composite components. Dent Mater 31:745–757. https://doi.org/10.1016/j.dental.2015.03.016
Tuna EB, Aktoren O, Oshida Y, Gencay K (2010) Elution of residual monomers from dental composite materials. Eur J Paediatr Dent 11:110–114
Mavishna MV, Venkatesh KV, Sihivahanan D (2020) The effect of leachable components of resin cements and its resultant bond strength with lithium disilicate ceramics. Indian J Dent Res 31:470–474. https://doi.org/10.4103/ijdr.IJDR_398_19
Tabatabaei MH, Arami S, Zandi S, Bassir SH (2011) Evaluation of Bis-GMA/TEGDMA monomers leaching from a hybrid dental composite resin. Minerva Stomatol 60:159–165
Atabek D, Aydintug I, Alaçam A, Berkkan A (2014) The effect of temperature on bisphenol: an elution from dental resins. J Contemp Dent Pract 15:576–580. https://doi.org/10.5005/jp-journals-10024-1582
Bezgin T, Cimen C, Ozalp N (2021) Evaluation of residual monomers eluted from pediatric dental restorative materials. Biomed Res Int 2021:6316171. https://doi.org/10.1155/2021/6316171
Cebe MA, Cebe F, Cengiz MF, Cetin AR, Arpag OF, Ozturk B (2015) Elution of monomer from different bulk fill dental composite resins. Dent Mater 31:e141–e149. https://doi.org/10.1016/j.dental.2015.04.008
Reichl FX, Löhle J, Seiss M, Furche S, Shehata MM, Hickel R, Müller M, Dränert M, Durner J (2012) Elution of TEGDMA and HEMA from polymerized resin-based bonding systems. Dent Mater 28:1120–1125. https://doi.org/10.1016/j.dental.2012.06.010
Susila AV, Balasubramanian V (2016) Correlation of elution and sensitivity of cell lines to dental composites. Dent Mater 32:e63-72. https://doi.org/10.1016/j.dental.2015.11.011
Mourouzis P, Andreasidou E, Samanidou V, Tolidis K (2020) Short-term and long-term release of monomers from newly developed resin-modified ceramics and composite resin CAD-CAM blocks. J Prosthet Dent 123:339–348. https://doi.org/10.1016/j.prosdent.2019.01.012
Alshali RZ, Salim NA, Sung R, Satterthwaite JD, Silikas N (2015) Analysis of long-term monomer elution from bulk-fill and conventional resin-composites using high performance liquid chromatography. Dent Mater 31:1587–1598. https://doi.org/10.1016/j.dental.2015.10.006
Furche S, Hickel R, Reichl FX, van Landuyt K, Shehata M, Durner J (2013) Quantification of elutable substances from methacrylate based sealers and their cytotoxicity effect on with human gingival fibroblasts. Dent Mater 29:618–625. https://doi.org/10.1016/j.dental.2013.03.009
Högg C, Maier M, Dettinger-Maier K, He X, Rothmund L, Kehe K, Hickel R, Reichl FX (2016) Effect of various light curing times on the elution of composite components. Clin Oral Investig 20:2113–2121. https://doi.org/10.1007/s00784-015-1698-7
Rothmund L, Reichl FX, Hickel R, Styllou P, Styllou M, Kehe K, Yang Y, Högg C (2017) Effect of layer thickness on the elution of bulk-fill composite components. Dent Mater 33:54–62. https://doi.org/10.1016/j.dental.2016.10.006
Yang Y, Reichl FX, Ilie N, Shi J, Dhein J, Hickel R, Högg C (2019) Antioxidants as a novel dental resin-composite component: effect on elution and degree of conversion. Dent Mater 35:650–661. https://doi.org/10.1016/j.dental.2019.02.003
Hatipoğlu Ö, Turumtay EA, Saygın AG (2022) Evaluation of monomer elution, microhardness, and roughness of experimental dental composite resins prepared from Bis-EFMA, a novel monomer system. Polym Compos 43:584–592. https://doi.org/10.1002/pc.26401
De Nys S, Putzeys E, Vervliet P, Covaci A, Boonen I, Elskens M, Vanoirbeek J, Godderis L, Van Meerbeek B, Van Landuyt KL, Duca RC (2018) A novel high sensitivity UPLC-MS/MS method for the evaluation of bisphenol A leaching from dental materials. Sci Rep 8:6981. https://doi.org/10.1038/s41598-018-24815-z
Tichy A, Simkova M, Vrbova R, Roubickova A, Duskova M, Bradna P (2021) Bisphenol A release from dental composites and resin-modified glass ionomers under two polymerization conditions. Polymers (Basel) 14:46. https://doi.org/10.3390/polym14010046
Kurt A, Altintas SH, Kiziltas MV, Tekkeli SE, Guler EM, Kocyigit A, Usumez A (2018) Evaluation of residual monomer release and toxicity of self-adhesive resin cements. Dent Mater J 37:40–48. https://doi.org/10.4012/dmj.2016-380
Durner J, Stojanovic M, Urcan E, Spahl W, Haertel U, Hickel R, Reichl FX (2011) Effect of hydrogen peroxide on the three-dimensional polymer network in composites. Dent Mater 27:573–580. https://doi.org/10.1016/j.dental.2011.02.013
Gul P, Alp HH, Özcan M (2020) Monomer release from bulk-fill composite resins in different curing protocols. J Oral Sci 62:288–292. https://doi.org/10.2334/josnusd.19-0221
Kwon YR, Son KJ, Pandit S, Kim JE, Chang KW, Jeon JG (2010) Bioactivity-guided separation of anti-acidogenic substances against Streptococcus mutans UA 159 from Polygonum cuspidatum. Oral Dis 16:204–209. https://doi.org/10.1111/j.1601-0825.2009.01636.x
Nocca G, Iori A, Rossini C, Martorana GE, Ciasca G, Arcovito A, Cordaro M, Lupi A, Marigo L (2015) Effects of barriers on chemical and biological properties of two dual resin cements. Eur J Oral Sci 123:208–214. https://doi.org/10.1111/eos.12178
Sahu PK, Ramisetti NR, Cecchi T, Swain S, Patro CS, Panda J (2018) An overview of experimental designs in HPLC method development and validation. J Pharm Biomed Anal 147:590–611. https://doi.org/10.1016/j.jpba.2017.05.006
Honour JW (2006) Gas chromatography-mass spectrometry. Methods Mol Biol 324:53–74. https://doi.org/10.1385/1-59259-986-9:53
Krifka S, Spagnuolo G, Schmalz G, Schweikl H (2013) A review of adaptive mechanisms in cell responses towards oxidative stress caused by dental resin monomers. Biomaterials 34:4555–4563. https://doi.org/10.1016/j.biomaterials.2013.03.019
Kanerva L, Henriks-Eckerman ML, Jolanki R, Estlander T (1997) Plastics/acrylics: material safety data sheets need to be improved. Clin Dermatol 15:533–546. https://doi.org/10.1016/s0738-081x(97)00006-0
Schedle A, Ortengren U, Eidler N, Gabauer M, Hensten A (2007) Do adverse effects of dental materials exist? What are the consequences, and how can they be diagnosed and treated? Clin Oral Implants Res 18(Suppl 3):232–256. https://doi.org/10.1111/j.1600-0501.2007.01481.x
Spencer P, Wang Y (2002) Adhesive phase separation at the dentin interface under wet bonding conditions. J Biomed Mater Res 62:447–456. https://doi.org/10.1002/jbm.10364
Putzeys E, Duca RC, Coppens L, Vanoirbeek J, Godderis L, Van Meerbeek B, Van Landuyt KL (2018) In-vitro transdentinal diffusion of monomers from adhesives. J Dent 75:91–97. https://doi.org/10.1016/j.jdent.2018.05.023
Ahmed MH, Yoshihara K, Yao C, Okazaki Y, Van Landuyt K, Peumans M, Van Meerbeek B (2021) Multiparameter evaluation of acrylamide HEMA alternative monomers in 2-step adhesives. Dent Mater 37:30–47. https://doi.org/10.1016/j.dental.2020.10.002
Ginzkey C, Zinnitsch S, Steussloff G, Koehler C, Hackenberg S, Hagen R, Kleinsasser NH, Froelich K (2015) Assessment of HEMA and TEGDMA induced DNA damage by multiple genotoxicological endpoints in human lymphocytes. Dent Mater 31:865–876. https://doi.org/10.1016/j.dental.2015.04.009
Massaro H, Zambelli LFA, Britto AA, Vieira RP, Ligeiro-de-Oliveira AP, Andia DC, Oliveira MT, Lima AF (2019) Solvent and HEMA increase adhesive toxicity and cytokine release from dental pulp cells. Materials (Basel) 12:2750. https://doi.org/10.3390/ma12172750
Schweikl H, Gallorini M, Pöschl G, Urmann V, Petzel C, Bolay C, Hiller KA, Cataldi A, Buchalla W (2018) Functions of transcription factors NF-κB and Nrf2 in the inhibition of LPS-stimulated cytokine release by the resin monomer HEMA. Dent Mater 34:1661–1678. https://doi.org/10.1016/j.dental.2018.08.292
Söderholm KJ, Mariotti A (1999) BIS-GMA--based resins in dentistry: are they safe? J Am Dent Assoc 130:201–9. https://doi.org/10.14219/jada.archive.1999.0169
Gonçalves F, Kawano Y, Pfeifer C, Stansbury JW, Braga RR (2009) Influence of BisGMA, TEGDMA, and BisEMA contents on viscosity, conversion, and flexural strength of experimental resins and composites. Eur J Oral Sci 117:442–446. https://doi.org/10.1111/j.1600-0722.2009.00636.x
Floyd CJ, Dickens SH (2006) Network structure of Bis-GMA- and UDMA-based resin systems. Dent Mater 22:1143–1149. https://doi.org/10.1016/j.dental.2005.10.009
Stanislawski L, Lefeuvre M, Bourd K, Soheili-Majd E, Goldberg M, Périanin A (2003) TEGDMA-induced toxicity in human fibroblasts is associated with early and drastic glutathione depletion with subsequent production of oxygen reactive species. J Biomed Mater Res A 66:476–482. https://doi.org/10.1002/jbm.a.10600
De Angelis F, Mandatori D, Schiavone V, Melito FP, Valentinuzzi S, Vadini M, Di Tomo P, Vanini L, Pelusi L, Pipino C, Del Boccio P, D'Arcangelo C, Pandolfi A (2021) Cytotoxic and genotoxic effects of composite resins on cultured human gingival fibroblasts. Materials (Basel) 14:5225. https://doi.org/10.3390/ma14185225
Fleisch AF, Sheffield PE, Chinn C, Edelstein BL, Landrigan PJ (2010) Bisphenol A and related compounds in dental materials. Pediatrics 126:760–768. https://doi.org/10.1542/peds.2009-2693
Schmalz G, Preiss A, Arenholt-Bindslev D (1999) Bisphenol-A content of resin monomers and related degradation products. Clin Oral Investig 3:114–119. https://doi.org/10.1007/s007840050088
Arenholt-Bindslev D, Breinholt V, Preiss A, Schmalz G (1999) Time-related bisphenol-A content and estrogenic activity in saliva samples collected in relation to placement of fissure sealants. Clin Oral Investig 3:120–125. https://doi.org/10.1007/s007840050089
Kadoma Y, Tanaka M (2000) Acid and base-catalyzed hydrolysis of bisphenol A-related compounds. Dent Mater J 19:139–152. https://doi.org/10.4012/dmj.19.139
Pfeifer CS, Shelton ZR, Braga RR, Windmoller D, Machado JC, Stansbury JW (2011) Characterization of dimethacrylate polymeric networks: a study of the crosslinked structure formed by monomers used in dental composites. Eur Polym J 47:162–170. https://doi.org/10.1016/j.eurpolymj.2010.11.007
De Nys S, Duca RC, Vervliet P, Covaci A, Boonen I, Elskens M, Vanoirbeek J, Godderis L, Van Meerbeek B, Van Landuyt KL (2021) Bisphenol A as degradation product of monomers used in resin-based dental materials. Dent Mater 37:1020–1029. https://doi.org/10.1016/j.dental.2021.03.005
Sun J, Wang L, Ding S, Sun X, Xu L (2020) Solubility behavior and thermodynamic analysis of bisphenol A in 14 different pure solvents. J Chem Eng Data 65:2846–2858. https://doi.org/10.1021/acs.jced.0c00166
Paula AB, Toste D, Marinho A, Amaro I, Marto CM, Coelho A, Marques-Ferreira M, Carrilho E (2019) Once resin composites and dental sealants release bisphenol-a, how might this affect our clinical management?-a systematic review. Int J Environ Res Public Health 16:1627. https://doi.org/10.3390/ijerph16091627
Huang RP, Liu ZH, Yuan SF, Yin H, Dang Z, Wu PX (2017) Worldwide human daily intakes of bisphenol A (BPA) estimated from global urinary concentration data (2000–2016) and its risk analysis. Environ Pollut 230:143–152. https://doi.org/10.1016/j.envpol.2017.06.026
Rezg R, El-Fazaa S, Gharbi N, Mornagui B (2014) Bisphenol A and human chronic diseases: current evidences, possible mechanisms, and future perspectives. Environ Int 64:83–90. https://doi.org/10.1016/j.envint.2013.12.007
Sabanayagam C, Teppala S, Shankar A (2013) Relationship between urinary bisphenol A levels and prediabetes among subjects free of diabetes. Acta Diabetol 50:625–631. https://doi.org/10.1007/s00592-013-0472-z
Huang YQ, Wong CK, Zheng JS, Bouwm an H, Barra R, Wahlström B, Neretin L, Wong MH (2012) Bisphenol A (BPA) in China: a review of sources, environmental levels, and potential human health impacts. Environ Int 42:91–99. https://doi.org/10.1016/j.envint.2011.04.010
Chen D, Kannan K, Tan H, Zheng Z, Feng YL, Wu Y, Widelka M (2016) Bisphenol analogues other than BPA: environmental occurrence, human exposure, and toxicity-a review. Environ Sci Technol 50:5438–5453. https://doi.org/10.1021/acs.est.5b05387
Marzouk T, Sathyanarayana S, Kim AS, Seminario AL, McKinney CM (2019) A systematic review of exposure to bisphenol A from dental treatment. JDR Clin Trans Res 4:106–115. https://doi.org/10.1177/2380084418816079
Olea N, Pulgar R, Pérez P, Olea-Serrano F, Rivas A, Novillo-Fertrell A, Pedraza V, Soto AM, Sonnenschein C (1996) Estrogenicity of resin-based composites and sealants used in dentistry. Environ Health Perspect 104:298–305. https://doi.org/10.1289/ehp.96104298
Tomza-Marciniak A, Stępkowska P, Kuba J, Pilarczyk B (2018) Effect of bisphenol A on reproductive processes: a review of in vitro, in vivo and epidemiological studies. J Appl Toxicol 38:51–80. https://doi.org/10.1002/jat.3480
Calaf GM, Ponce-Cusi R, Aguayo F, Muñoz JP, Bleak TC (2020) Endocrine disruptors from the environment affecting breast cancer. Oncol Lett 20:19–32. https://doi.org/10.3892/ol.2020.11566
Braun JM (2017) Early-life exposure to EDCs: role in childhood obesity and neurodevelopment. Nat Rev Endocrinol 13:161–173. https://doi.org/10.1038/nrendo.2016.186
Rochester JR (2013) Bisphenol A and human health: a review of the literature. Reprod Toxicol 42:132–155. https://doi.org/10.1016/j.reprotox.2013.08.008
Usman A, Ahmad M (2016) From BPA to its analogues: is it a safe journey? Chemosphere 158:131–142. https://doi.org/10.1016/j.chemosphere.2016.05.070
Ejaredar M, Lee Y, Roberts DJ, Sauve R, Dewey D (2017) Bisphenol A exposure and children’s behavior: A systematic review. J Expo Sci Environ Epidemiol 27:175–183. https://doi.org/10.1038/jes.2016.8
Eladak S, Grisin T, Moison D, Guerquin MJ, N’Tumba-Byn T, Pozzi-Gaudin S, Benachi A, Livera G, Rouiller-Fabre V, Habert R (2015) A new chapter in the bisphenol A story: bisphenol S and bisphenol F are not safe alternatives to this compound. Fertil Steril 103:11–21. https://doi.org/10.1016/j.fertnstert.2014.11.005
Papakonstantinou AE, Eliades T, Cellesi F, Watts DC, Silikas N (2013) Evaluation of UDMA’s potential as a substitute for Bis-GMA in orthodontic adhesives. Dent Mater 29:898–905. https://doi.org/10.1016/j.dental.2013.05.007
Wacławczyk A, Postek-Stefańska L, Pietraszewska D, Birkner E, Zalejska-Fiolka J, Wysoczańska-Jankowicz I (2018) TEGDMA and UDMA monomers released from composite dental material polymerized with diode and halogen lamps. Adv Clin Exp Med 27:469–476. https://doi.org/10.17219/acem/68382
Luo S, Zhu W, Liu F, He J (2016) Preparation of a Bis-GMA-free dental resin system with synthesized fluorinated dimethacrylate monomers. Int J Mol Sci 17:2014. https://doi.org/10.3390/ijms17122014
He J, Söderling E, Lassila LV, Vallittu PK (2014) Synthesis of antibacterial and radio-opaque dimethacrylate monomers and their potential application in dental resin. Dent Mater 30:968–976. https://doi.org/10.1016/j.dental.2014.05.013
Alrahlah A, Al-Odayni AB, Al-Mutairi HF, Almousa BM, Alsubaie FS, Khan R, Saeed WS (2021) A low-viscosity BisGMA derivative for resin composites: synthesis, characterization, and evaluation of its rheological properties. Materials (Basel) 14:338. https://doi.org/10.3390/ma14020338
Asmussen E, Peutzfeldt A (1998) Influence of UEDMA BisGMA and TEGDMA on selected mechanical properties of experimental resin composites. Dent Mater 14:51–56. https://doi.org/10.1016/s0109-5641(98)00009-8
Becher R, Wellendorf H, Sakhi AK, Samuelsen JT, Thomsen C, Bølling AK, Kopperud HM (2018) Presence and leaching of bisphenol a (BPA) from dental materials. Acta Biomater Odontol Scand 4:56–62. https://doi.org/10.1080/23337931.2018.1476869
Maserejian NN, Trachtenberg FL, Wheaton OB, Calafat AM, Ranganathan G, Kim HY, Hauser R (2016) Changes in urinary bisphenol A concentrations associated with placement of dental composite restorations in children and adolescents. J Am Dent Assoc 147:620–630. https://doi.org/10.1016/j.adaj.2016.02.020
Fugolin AP, de Paula AB, Dobson A, Huynh V, Consani R, Ferracane JL, Pfeifer CS (2020) Alternative monomer for BisGMA-free resin composites formulations. Dent Mater 36:884–892. https://doi.org/10.1016/j.dental.2020.04.009
Reichl FX, Esters M, Simon S, Seiss M, Kehe K, Kleinsasser N, Folwaczny M, Glas J, Hickel R (2006) Cell death effects of resin-based dental material compounds and mercurials in human gingival fibroblasts. Arch Toxicol 80:370–377. https://doi.org/10.1007/s00204-005-0044-2
Costa CA, Hebling J, Hanks CT (2000) Current status of pulp capping with dentin adhesive systems: a review. Dent Mater 16:188–197. https://doi.org/10.1016/s0109-5641(00)00008-7
Murray PE, Hafez AA, Windsor LJ, Smith AJ, Cox CF (2002) Comparison of pulp responses following restoration of exposed and non-exposed cavities. J Dent 30:213–222. https://doi.org/10.1016/s0300-5712(02)00021-0
Modena KC, Casas-Apayco LC, Atta MT, Costa CA, Hebling J, Sipert CR, Navarro MF, Santos CF (2009) Cytotoxicity and biocompatibility of direct and indirect pulp capping materials. J Appl Oral Sci 17:544–554. https://doi.org/10.1590/s1678-77572009000600002
Manojlovic D, Radisic M, Lausevic M, Zivkovic S, Miletic V (2013) Mathematical modeling of cross-linking monomer elution from resin-based dental composites. J Biomed Mater Res B Appl Biomater 101:61–67. https://doi.org/10.1002/jbm.b.32815
Pongprueksa P, De Munck J, Duca RC, Poels K, Covaci A, Hoet P, Godderis L, Van Meerbeek B, Van Landuyt KL (2015) Monomer elution in relation to degree of conversion for different types of composite. J Dent 43:1448–1455. https://doi.org/10.1016/j.jdent.2015.10.013
Kopperud HM, Johnsen GF, Lamolle S, Kleven IS, Wellendorf H, Haugen HJ (2013) Effect of short LED lamp exposure on wear resistance, residual monomer and degree of conversion for Filtek Z250 and Tetric EvoCeram composites. Dent Mater 29:824–834. https://doi.org/10.1016/j.dental.2013.04.022
Komurcuoglu E, Olmez S, Vural N (2005) Evaluation of residual monomer elimination methods in three different fissure sealants in vitro. J Oral Rehabil 32:116–121. https://doi.org/10.1111/j.1365-2842.2004.01405.x
Lee MJ, Kim MJ, Kwon JS, Lee SB, Kim KM (2017) Cytotoxicity of light-cured dental materials according to different sample preparation methods. Materials (Basel) 10:288. https://doi.org/10.3390/ma10030288
Jp-P J, Jakubik A, Przeklasa-Bierowiec A, Muszynska B (2017) Artificial saliva and its use in biological experiments. J Physiol Pharmacol 68:807–813
Mandel ID (1974) Relation of saliva and plaque to caries. J Dent Res 53:246–266. https://doi.org/10.1177/00220345740530021201
Bationo R, Rouamba A, Diarra A, Beugré-Kouassi MLA, Beugré JB, Jordana F (2020) Cytotoxicity evaluation of dental and orthodontic light-cured composite resins. Clin Exp Dent Res 7:40–48. https://doi.org/10.1002/cre2.337
Funding
Open access funding provided by Università degli Studi G. D'Annunzio Chieti Pescara within the CRUI-CARE Agreement.
Author information
Authors and Affiliations
Contributions
The authors listed in the attached paper have actively contributed to the work as shown below:
- Francesco De Angelis: conceptualization, methodology, data curation, investigation, writing — review & editing
- Nela Sarteur: conceptualization, methodology, data curation, investigation, writing — original draft
- Matteo Buonvivere: methodology, investigation, writing — review & editing
- Mirco Vadini: data curation, investigation, writing — original draft
- Michal Šteffl: data curation, formal analysis, visualization
- Camillo D’Arcangelo: conceptualization, supervision, project administration resources.
Corresponding author
Ethics declarations
Conflict of interest
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
De Angelis, F., Sarteur, N., Buonvivere, M. et al. Meta-analytical analysis on components released from resin-based dental materials. Clin Oral Invest 26, 6015–6041 (2022). https://doi.org/10.1007/s00784-022-04625-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00784-022-04625-4