Abstract
When Ti(OiPr)4 was reacted with increasing proportions of methacrylic acid (McOH), the compounds Ti2(OiPr)6(OMc)2(iPrOH), Ti6O4(OiPr)8(OMc)8, Ti9O8(OiPr)4(OMc)16, and Ti8O8(OMc)16 were obtained in sequence. This allowed conclusions on the relative ratio of substitution and hydrolysis reactions, the latter being due to ester formation between the acid and cleaved alcohol. This ratio is also influenced by the reaction temperature, since Ti4O2(OiPr)6(OMc)6 was formed instead of Ti6O4(OiPr)8(OMc)8 at lower temperature with the same precursor ratio.
Graphical abstract
![](http://media.springernature.com/lw685/springer-static/image/art%3A10.1007%2Fs00706-015-1443-6/MediaObjects/706_2015_1443_Figa_HTML.gif)
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Metal oxo clusters, which are obtained by partial hydrolysis of a hydrolysable metal precursor, are valuable building blocks for inorganic–organic hybrid materials or metal–organic framework structures [1–4]. An efficient route is reaction of (functional or non-functional) carboxylic acids with early transition metal alkoxides. The carboxylic acids not only provide carboxylate ligands for stabilization of the metal-oxo cluster cores but also act as an in situ water source through esterification reactions.
A reasonable sequence of reactions is that (i) an OR group of the metal alkoxide, [M(OR)x]n, is substituted by a carboxylate ligand to give [M(OR)x−1(OOCR′)]m and ROH; (ii) the eliminated alcohol reacts with carboxylic acid to give an ester and water; (iii) the thus generated water hydrolyses part of the remaining OR groups to give a cluster MaOb(OR)c(OOCR)d. Although the first step is necessary for the overall reaction, only few (non-hydrolyzed) carboxylate-substituted metal alkoxides are known. For titanium alkoxides, which are subject of this article, carboxylate-substituted metal alkoxide derivatives were only isolated from reactions with the bulky pivalic acid [5]. Another derivative was obtained by reaction with phthalic anhydride, where only substitution, but no hydrolysis is possible [6]. Ester formation (step ii) is easily monitored by IR spectroscopy. The isolation of a few polynuclear compounds with coordinated water [7, 8] is strong evidence that water is concomitantly formed (instead of oxo group formation by a non-hydrolytic process). Cluster formation (step iii) must be a stepwise process, but details, such as intermediates, are still unknown. Empirical evidence suggests, however, that competition between the two carboxylic acid-consuming reactions, namely substitution and ester/water formation, is decisive for the outcome of the reaction. Any parameter influencing the relative reaction rate of the two processes, such as kind of OR group, acidity and steric bulk of the carboxylic acid, or the metal alkoxide:carboxylic acid ratio, influences the composition of the eventually formed cluster MaOb(OR)c(OOCR)d. Correspondingly, the degree of substitution (d:a ratio) and the degree of condensation (b:a ratio) are the two main parameters from which conclusions can be drawn on the cluster-forming processes.
A series of clusters was previously obtained from Zr(OBu)4 and methacrylic acid (McOH) when the molar ratio was varied. With a low proportion of McOH, the cluster Zr6O2(OBu)10(OMc)10 was obtained, with both a low O:Zr (0.33) and OMc:Zr ratio (1.66) [9], both limited by the available amount of McOH. A high McOH proportion resulted in the cluster Zr4O2(OMc)12 [10, 11] with a high degree of substitution (OMc:Zr = 3.0). The highest degree of condensation (O:Zr = 0.66 in Zr6(OH)4O4(OMc)12 [11]) was obtained for an intermediate Zr(OBu)4:McOH ratio, where the degree of substitution in the cluster (2.0) was not too high and thus allowed a higher degree of condensation.
The situation for titanium should be different, because OMc:Ti ratios >2.0 are not possible for compounds with octahedrally coordinated titanium atoms having bidentate carboxylate ligands. Reactions of Ti(OR)4 with carboxylic acids are particularly well investigated, and a great number of carboxylate-substituted titanium oxo/alkoxo clusters, with different OR/carboxylate combinations, are known [12–14]. In this article, the influence of a single parameter on the composition of the formed cluster was systematically investigated, namely the metal alkoxide:carboxylic acid ratio. All other parameters, especially the kind of metal alkoxide [Ti(OiPr)4] and the kind of acid (methacrylic acid) were unvaried.
Methacrylic acid is frequently used because of its small, rigid shape and the polymerizable group (for the preparation of class II hybrid materials). The only structures reported until present, obtained from reaction of Ti(OiPr)4 with methacrylic acid at different molar ratios, are Ti4O2(OiPr)(OMc)6 (Ti(OiPr)4:McOH ratio 1:2.3) [15] and Ti8O8(OMc)16 (ratio 1:4) [16] (Eq. (1)).
Results and discussion
The dimeric complex Ti2(µ2-OiPr)2(OiPr)4(µ2-OMc)(OMc)(iPrOH) (1, Fig. 1) crystallized from an equimolar mixture of Ti(OiPr)4 and McOH in 2-propanol at −10 °C. No esterification occurred at this temperature.
Compound 1 is isostructural to the other binuclear carboxylate-substituted titanium alkoxides mentioned above [5, 6]. The two octahedrally coordinated titanium atoms in 1 are bridged by two OiPr and one OMc ligands. A second OMc ligand is η1-coordinated to one titanium atom and stabilized by a hydrogen bond to an isopropanol molecule coordinated to the other titanium atom. We have pointed out earlier that the combination of a η1 carboxylate ligand and a neutral proton-donating ligand connected through a hydrogen bond is structurally equivalent to a mono-anionic bidentate ligand [7, 17].
In the reaction leading to 1, the carboxylic acid was completely consumed for substitution of OiPr groups, and consequently no ester and cluster formation was possible. The crystals of 1 dissolved when the reaction solution was warmed to room temperature, and after 48 h at room temperature, 1 did not crystallize again when cooled to −10 °C. This indicates that the substitution reaction might be reversible, with subsequent initiating of cluster-forming reactions.
When Ti(OiPr)4 was reacted with two equivalents of McOH at room temperature, i.e., when the McOH proportion was increased, the centrosymmetric cluster Ti6(µ3-O)2(µ2-O)2(µ2-OiPr)2(OiPr)6(OMc)8 was obtained (2, Fig. 2). The two equivalents of McOH are consumed to two-thirds for substitution (O:Ti ratio 0.67) and to one-third for ester/water formation (OMc:Ti ratio 1.33). Isostructural clusters were previously obtained with other combinations of alkoxo and/or carboxylate ligands (see review articles [12–14]). Cluster 2 consists of six nearly coplanar titanium atoms, where two Ti3O units are connected through four OMc and two µ2-oxo bridges in total.
A different cluster, viz. Ti4O2(OiPr)6(OMc)6 (3, Fig. 3), was previously obtained for a very similar Ti(OiPr)4:McOH ratio (1:2.3) [15]. Therefore, reaction of Ti(OiPr)4 with two molar equivalents of McOH was repeated, but the mixture was stored at 4 °C. Because no crystals were obtained after 6 months, the mixture was warmed to room temperature; crystals of 3 were then formed after one additional month. The structure of 3 is simpler than that of 2, as both oxygen atoms of the Ti4O2 core are µ3, all OMc ligands are bridging and all OiPr ligands are terminal.
Molecular structure of Ti4O2(OiPr)6(OMc)6 (3) [15]. Hydrogen atoms were omitted for clarity
In both reactions, the one leading to 2 and the one leading to 3, the two equivalents of McOH in the starting mixture were completely consumed. In 3, however, 75 % were consumed for substitution and only 25 % for ester formation (O:Ti ratio of 0.5 and OMc:Ti ratio of 1.5), compared to 67:33 % in 2. This shows that the reaction rate of ester formation was more strongly decreased by the lower temperature than that of the substitution reaction(s).
Reaction of Ti(OiPr)4 with McOH in a ratio of 1:4 or 1:6 led to Ti9(µ3-O)2(µ2-O)6(OiPr)4(µ2-OMc)16 (4, Fig. 4). While the carboxylic acid was completely consumed (for both substitution and ester formation) for Ti(OiPr)4:McOH ratios of 1:1 and 1:2 (leading to compounds 1–3), this is not possible for compound 4, and part of McOH must remain unreacted. The higher proportion of McOH, however, results in a lower proportion of residual OiPr groups.
An isostructural compound was previously obtained from the reaction of Ti(OnPr)4 and McOH in a 1:4 ratio [18]. The structure of 4 is related to that of the known “titanyl carboxylates” Ti8(µ2-O)8(OOCR)16 (see below). Instead of a symmetric octanuclear ring system in the latter compounds, the structure of 4 has a “knot” as four of the nine [TiO6] octahedra (Ti1, Ti2, Ti3, and Ti9) are linked by two µ3-oxo bridges. All but two pairs of neighboring Ti octahedra are bridged by two methacrylate ligands. Ti7/Ti8 and Ti1/Ti2 are connected by only one methacrylate bridge; the second bridge is replaced by two OiPr ligands (one at each Ti atom). This unusual ring structure was previously discussed in detail [18].
Further increase of the McOH proportion in the reaction mixture (ratio 1:8 or 1:16) led to the formation of “titanyl methacrylate”, Ti8(µ2-O)8(µ2-OMc)16 (5, Fig. 5), where all OR groups of the starting metal alkoxide were either substituted or hydrolyzed. The well-known Ti8O8 ring structure [16, 19–22] with C 4v symmetry is built from eight [Ti(µ2-O)(µ2-OMc)2] units which are mutually interconnected by one µ2-oxo and two OMc bridges each. The molecular structure of 5 is the same as that of another (orthorhombic) polymorph described earlier [16].
Conclusions
When early transition metal alkoxides are reacted with carboxylic acid two carboxylic acid-consuming reactions compete with each other, namely substitution of part of the OR groups by carboxylate groups and ester formation with the eliminated alcohol. The thus generated water serves for (partial) hydrolysis of the OR groups.
Substitution without cocomitant hydrolysis was only achieved when Ti(OiPr)4 was reacted with methacrylic acid in a 1:1 molar ratio at low temperature, where the rate of substitution is apparently much faster than that of ester + water formation (it is assumed that hydrolysis and condensation are fast reactions). Ti2(OiPr)6(OMc)2(iPrOH) (1) appears to be kinetically favored, since it disappears when the reaction solution is warmed to room temperature.
Increasing the McOH:Ti(OiPr)4 ratio at constant reaction conditions (room temperature) results in the formation of the oxo clusters Ti6O4(OiPr)8(OMc)8 (2), Ti9O8(OiPr)4(OMc)16 (4), and Ti8O8(OMc)16 (5) in sequence, where the number of residual OR per Ti is steadily decreased (Table 1). Analysis of the degree of condensation (O/Ti ratio) and degree of substitution (OMc/Ti ratio) of these clusters shows, however, that the latter is always two-times higher than the former, i.e., two-thirds of the reacted McOH are consumed for substitution and to one-third for ester/water formation.
Changing the reaction temperature, however, also changes the relative rate of substitution and water formation (leading to condensation). With a constant McOH:Ti(OiPr)4 ratio of 2, Ti4O2(OiPr)6(OMc)6 (3) was formed at lower temperature instead of 2. As already stated for 1, the relative rate of the ester formation reaction is apparently slower when the temperature is decreased. This leads to a cluster (3) in which the degree of substitution is higher and the degree of condensation lower compared to 2, which was formed at higher temperature.
Experimental
All operations were carried out in a moisture- and oxygen-free argon atmosphere using standard Schlenk techniques. Ti(OiPr)4 and methacrylic acid were obtained from ABCR and used as received. Isopropanol was dried by distillation from sodium metal twice. The solvents for NMR spectroscopy (Eurisotop) were degassed prior to use and stored over molecular sieve. 1H and 13C solution NMR spectra were recorded on a Bruker AVANCE 250 (250.13 MHz for 1H, 62.86 MHz for 13C) equipped with a 5 mm inverse-broadband probe head and a z-gradient unit.
Methacrylate-substituted titanium propoxide Ti 2 (OiPr) 6 (OMc) 2 (iPrOH) ( 1 )
Ti(OiPr)4 (1 cm3, 3.45 mmol) was added to a solution of 291 mm3 methacrylic acid (3.45 mmol) in 3 cm3 of water-free isopropanol at 0 °C. A white precipitate formed immediately, which was dissolved by adding 1 cm3 of CH2Cl2. Crystals of 1 were obtained from the clear solution at −10 °C after 2 days. Yield 500 mg (43 %); 1H NMR (C6D6, 250 MHz): δ = 0.94–1.82 (m, 42H, CHCH 3), 1.95–2.29 (m, 6H, CCH3), 4.51 (br, 2H, OCH), 4.88–5.33 (m, 5H, OCH), 5.42 (br, 2H, C=CH2), 6.47 ppm (br, 2H, C=CH2) ppm; 13C NMR (C6D6, 62.90 MHz): δ = 18.22 (br, CCH3), 24.98 (CHCH3), 25.37 (br, CHCH3), 77.90 (OCH), 72.3–79.36 (br, OCH), 125.1–126.8 (br, CCH2) ppm.
Methacrylate-substituted titanium oxo clusters Ti 6 O 4 (OiPr) 8 (OMc) 8 ( 2 ), Ti 9 O 8 (OiPr) 4 (OMc) 16 ( 4 ), and Ti 8 O 8 (OMc) 16 ( 5 )
Methacrylic acid (2: 582 mm3, 6.90 mmol; 4: 1.75 cm3, 20.69 mmol; 5: 2.33 cm3, 27.58 mmol) was added to 1 cm3 of Ti(OiPr)4 (3.45 mmol) and the solution was stirred for 5 min. Crystals were obtained after 2–6 months at room temperature.
2: Yield 350 mg (40 %); 1H NMR (CDCl3, 200 MHz): δ = 1.00–1.44 (m, 48H, CHCH 3), 1.68–1.96 (m, 24H, CCH3), 3.97 (m, J = 6.16 Hz, 1H, CH), 4.30 (m, J = 6.06 Hz, 1H, CH), 4.58–4.85 (m, 4H, CH), 4.93–5.12 (m, 2H, CH), 5.24–5.56 (m, 8H, CH2), 5.90–6.27 ppm (m, 8H, CH2) ppm; 13C NMR (CDCl3, 50.3 MHz): δ = 18.17, 18.26, 18.48, 18.58, 18.64, 18.74, 18.81 (CCH3), 24.41, 24.52, 24.90, 25.25, 25.33, 25.40, 25.47, 77.20, 78.13, 78.40, 78.85, 80.27, 81.62, 81.75 (CHCH3), 125.81, 126.96, 127.90 (CH2), 137.45, 137.61, 138.12, 138.55, 138.75, 139.19, 139.29, 139.40 (C=CH2), 172.77, 173.14, 174.31, 174.71, 175.12, 175.81 (COO) ppm.
4: Yield 330 mg (39 %); 1H NMR (CDCl3, 250 MHz): δ = 0.88–1.11 (m, 3H, CHCH 3), 1.14 (d, J = 6.12 Hz, 6H, CHCH 3), 1.17–1.60 (m, 15H, CHCH 3), 1.64–1.96 (m, 48H, CCH3), 3.97 (m, J = 6.11 Hz, 1H, CH), 4.93–5.04 (m, 1H, CH), 5.20–5.58 (m, 16H, CH2), 5.61 (m, 3H, CH), 5.95–6.31 ppm (m, 16H, CH2) ppm.
5: Yield 80 mg (12 %); 1H NMR (CDCl3, 250 MHz): δ = 1.85–1.93 (m, 48H, CH3), 5.29–5.69 (m, 16H, CH2), 6.17–6.22 ppm (m, 16H, CH2) ppm; 13C NMR (CDCl3, 62.90 MHz): δ = 17.9–18.4 (CH3), 126.0–128.3 (CH2), 136.2–138.4 (C), 176.7 ppm (COO).
Methacrylate-substituted Ti 4 cluster Ti 4 O 2 (OiPr) 6 (OMc) 6 ( 3 )
Methacrylic acid (580 mm3, 6.87 mmol) was added to 1 cm3 of Ti(OiPr)4 (3.45 mmol) at room temperature. After 5 min of stirring, the reaction vessel was stored at 4 °C. After 6 months, no crystals were obtained; therefore, the mixture was warmed to room temperature. After one additional month, crystals of 3 were obtained. Yield 200 mg (21 %). Spectroscopic data were already reported in Ref. [15].
X-ray structure analyses
All measurements were performed at 100 K using MoKα (λ = 71.073 pm) radiation. Data were collected on a Bruker Axs Smart Apex II four-circle diffractometer with κ-geometry, with φ and ω scans and different frame widths. The data were corrected for polarization and Lorentz effects, and an empirical absorption correction (Sadabs) was employed. The cell dimensions were refined with all unique reflections (Table 2). Saint Plus software (Bruker Analytical X-ray Instruments, 2007) was used to integrate the frames.
The structures were solved by the Patterson method (Shelxs97 [23]). Refinement was performed by the full-matrix least-squares method based on F 2 (Shelxl97) with anisotropic thermal parameters for all non-hydrogen atoms. Hydrogen atoms were inserted in calculated positions and refined riding with the corresponding atom. Three OiPr groups in 1 are disordered and were refined with around 80 % occupancy of the carbon atoms marked as “A” (e.g. C12A). One molecule of 2-propanol and two of methacrylic acid were found in the asymmetric unit of 4, of which the 2-propanol was refined with 50 % occupancy. The electron density in the void opened by the ring of 5 could not be refined and was removed using the Squeeze function in Platon.
CCDC-1024252 (1), -1024253 (2), -1024254 (4), and -1024255 (5) contain the supplementary crystallographic data for this paper. These data can be obtained free of charge from The Cambridge Crystallographic Data Center via www.ccdc.cam.ac.uk/data_request/cif.
References
Schubert U (2001) Chem Mater 13:3487
Sanchez C, Soler-Illia GJ de AA, Ribot F, Lalot T, Mayer CR, Cabuil V (2001) Chem Mater 13:3061
Schubert U (2011) Chem Soc Rev 40:575
Gross S (2011) J Mater Chem 21:15853
Boyle TJ, Tyner RP, Alam TM, Scott BL, Ziller JW, Potter BG (1999) J Am Chem Soc 121:12104
Czakler M, Artner C, Schubert U (2012) Eur J Inorg Chem 3485
Kogler FR, Jupa M, Puchberger M, Schubert U (2004) J Mater Chem 14:3133
Fric H, Jupa M, Schubert U (2006) Monatsh Chem 137:1
Moraru B, Gross S, Kickelbick G, Trimmel G, Schubert U (2001) Monatsh Chem 132:993
Trimmel G, Gross S, Kickelbick G, Schubert U (2001) Appl Organomet Chem 15:401
Kickelbick G, Schubert U (1997) Chem Ber 130:473
Schubert U (2005) J Mater Chem 15:3701
Rozes L, Steunou N, Fornasieri G, Sanchez C (2006) Monatsh Chem 137:501
Rozes L, Sanchez C (2011) Chem Soc Rev 40:1006
Moraru B, Hüsing N, Kickelbick G, Schubert U, Fratzl P, Peterlik H (2002) Chem Mater 14:2732
Artner C, Czakler M, Schubert U (2014) Chem Eur J 20:493
Artner C, Kronister S, Czakler M, Schubert U (2014) Eur J Inorg Chem 5596
Kickelbick G, Schubert U (1998) Eur J Inorg Chem 159
Barrow H, Brown DA, Alcock NW, Clase HJ, Wallbridge MGH (1995) J Chem Soc Chem Commun 1231
Piszczek P, Richert M, Grodzicki A, Glowiak T, Wojtczak A (2005) Polyhedron 24:663
Belli Dell’Amico D, Calderazzo F, Costa L, Franchi E, Gini L, Labella L, Marchetti F (2008) J Mol Struct 890:295
Frot T, Cochet S, Laurent G, Sassoye C, Popall M, Sanchez C, Rozes L (2010) Eur J Inorg Chem 5650
Sheldrick GM (1997) SHELXS-97, Program for crystal structure determination. University of Göttingen, Göttingen
Acknowledgments
This work was supported by the Fonds zur Förderung der wissenschaftlichen Forschung (FWF), Austria (Project P22915). The X-ray measurements were carried out at the X-Ray Center of the Vienna University of Technology.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution License which permits any use, distribution, and reproduction in any medium, provided the original author(s) and the source are credited.
About this article
Cite this article
Czakler, M., Artner, C. & Schubert, U. Influence of the Ti(OiPr)4: methacrylic acid ratio on the formed oxo/alkoxo clusters. Monatsh Chem 146, 897–902 (2015). https://doi.org/10.1007/s00706-015-1443-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00706-015-1443-6