Abstract
To produce a highly stable wood-based product with increased mechanical properties, phenol formaldehyde (PF) resin impregnation was combined with the viscoelastic thermal compression (VTC) process. Dimensional stability and bending stiffness were evaluated. Two PF resins with weight average molecular weights of 172 and 780 were studied at three different concentrations, 5, 10 and 20%. After 24-h room temperature water soak and 2-h boil, both PF treatments at all concentration levels showed high levels of dimensional stability compared to non-impregnated VTC processed controls. The higher molecular weight PF provided greater stability with an average thickness swell value of 12% compared to 20 and 37% for the lower molecular weight PF resin treatment and control, respectively. High anti-swelling efficiency values were recorded for both low and high molecular weight resins, implying these modifications were effective at reducing the volumetric swelling which occurred in the unmodified control. PF treatments were also extremely effective at reducing irreversible swelling. The low and high molecular weight resin treatments had 1/5th and 1/7th the irreversible swelling than the unmodified VTC processed controls, respectively. All dimensional stability values improved as resin concentrations increased. Both resin types at all concentration levels reduced Young’s modulus.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
Abbreviations
- VTC:
-
Viscoelastic thermal compression
- PF:
-
Phenol formaldehyde
- PF1:
-
High molecular weight phenol formaldehyde
- PF2:
-
Low molecular weight phenol formaldehyde
- WPG:
-
Weight percent gain
- MOE:
-
Young’s modulus
- TS:
-
Thickness swell
- ASE:
-
Anti-swelling efficiency
- ASENorm :
-
Anti-swelling efficiency normalized
- IS:
-
Irreversible swelling
References
Deka M, Das P, Saikia CN (2000) Chemical modification of wood with thermosetting resin: effect on dimensional stability and strength property. Biosource Technol 73:179–181
Farmer RH (1967) Chemistry in the utilization of wood. Pergamon Press, New York
Furuno T, Imamura Y, Kajita H (2004) The modification of wood by treatment with low molecular weight phenol-formaldehyde resin: a properties enhancement with neutralized phenolic-resin and resin penetration into wood cell walls. Wood Sci Technol 37(5):349–361
Hill C (2006) Wood modification: chemical, thermal and other Processes. Wiley, England
Hsu WE, Schwald W, Schwald J, Shields JA (1988) Chemical and physical change required for producing dimensionally stable wood-based composites. Wood Sci Technol 22:281–289
Kamke FA (2006) Densified radiata pine for structural composites. MADERAS: Ciencia y Tecnología’ J 8(2):83–92
O’Conner JP (2007) Improving wood strength and stiffness through viscoelastic thermal compression. MS thesis, Oregon State University, Corvallis, pp 56–68
Ohmae K, Minato K, Norimoto M (2002) The analysis of dimensional changes due to chemical treatments and water soaking for Hinoki (Chamaecyparis obtusa) wood. Holzforschung 56(1):98–102
Reynolds MS (2005) Hydro-thermal stabilization of wood-based material. MS thesis, Virginia Polytechnic Institute and State University, Blacksburg. pp 73–88
Rowell RM (1999) Wood handbook: specialty treatments, Chap. 19. USDA general technical report FPL-GTR-113 USDA, Madison
Rowell RM (2005) Chemical modification of wood. In: Rowell RM (ed) Handbook of wood chemistry, wood composites, Chap. 14. CRC Press, Boco Raton, pp 381–420
Ryu JY, Imamura Y, Takahashi M, Kajita H (1993) Effects of molecular weight and some other properties of resin on biological resistance of phenolic resin treated wood. Mokuzai Gakkaishi 39(4):486–492
Shams MI, Kagemori N, Yano H (2004) Compressive deformation of wood impregnated with low molecular weight phenol formaldehyde (PF) resin I: effects of pressing pressure and pressure holding. J Wood Sci 50:337–342
Stamm AJ (1959) The dimensional stability of wood. For Prod J 9(10):375–381
Stamm AJ, Baechler RH (1960) Decay resistance and stability of five modified Woods. For Prod J 10(1):22–26
Stamm AJ, Elwin EH (1953) Chemical processing of wood. Chemical Publishing Co. Inc, New York
Stamm AJ, Seborg RM (1936) Minimizing wood shrinkage and swelling–treating with synthetic resin-forming materials. Ind Eng Chem 28(10):1164–1169
Wallström L, Lindberg KAH (1999) Measurement of cell wall penetration in wood of water-based chemicals using SEM/EDS and STEM/EDS technique. Wood Sci Technol 33:111–122
Wan H, Kim MG (2006) Impregnation of southern pine wood and strands with low molecular weight phenol-formaldehyde resins for stabilization of oriented strandboard. Wood Fiber Sci 38(2):314–324
Yano H, Hirose A, Inaba S (1997) High-strength wood-based materials. J Mat Sci 16:1906–1909
Yano H, Mori K, Collins PJ, Yazaki Y (2000) Effects of element size and orientation in production of high strength resin impregnated wood based materials. Holzforschung 54:443–447
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Gabrielli, C.P., Kamke, F.A. Phenol–formaldehyde impregnation of densified wood for improved dimensional stability. Wood Sci Technol 44, 95–104 (2010). https://doi.org/10.1007/s00226-009-0253-6
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00226-009-0253-6