Abstract
The corrosion behaviour of two carbon-alloyed intermetallics of composition Fe-28.1Al-2.1C and Fe-27.5Al-3.7C has been studied and compared with that of binary intermetallics. Potentiodynamic polarization studies indicated that the intermetallics exhibited active-passive behaviour in an acidic solution of pH = 1, whereas they exhibited stable passivity in a buffer solution of pH 8.4. Corrosion rates were also obtained by immersion testing. The variation of corrosion rate as a function of time was similar for both the intermetallics. The variation in corrosion rate as a function of time has been explained based on the observed potentiodynamic polarization behaviour. Scanning electron microscopy of corroded surfaces indicated that the carbon-alloyed intermetallics were susceptible to galvanic corrosion, due to the presence of carbides.
Similar content being viewed by others
References
Babu N, Balasubramaniam R and Ramesh Kumar A V 2000 (to be published)
Baligdad R G, Prakash U, Ramakrishna Rao V, Rao P K and Ballal N B 1994Iron & Steel Making 21 324
Baligdad R G, Prakash U, Radhakrishna A and Ramakrishna Rao V 1997aScr. Mater. 36 667
Baligdad R G, Prakash U, Radhakrishna A and Ramakrishna Rao V 1997bScr. Mater. 36 105
Jones D A 1992Principles and prevention of corrosion (New York: Maxell Macmillan International)
Sen M and Balasubramaniam R 2000Scr. Mater. (accepted)
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Sen, M., Balasubramaniam, R. & Kumar, A.V.R. Corrosion of carbon-alloyed iron aluminides. Bull Mater Sci 23, 399–403 (2000). https://doi.org/10.1007/BF02708390
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02708390