Abstract
A detailed study is presented of the structural, electrical, and optical properties of ErAs films grown on GaAs by molecular beam epitaxy (MBE). ErAs layers 1500Å thick were grown successfully over a relatively wide range of substrate temperatures (420-580° C), although overgrowth of GaAs on ErAs was found to be difficult. In-situ reflection highenergy electron diffraction (RHEED), x-ray diffraction, and Rutherford backscattering (RBS) measurements all indicate single crystal growth. Analysis of X-ray rocking curves reveals that, over the range of substrate temperatures studied, strain due to the lattice mismatch between ErAs and GaAs is completely inelastically relieved in the 1500Å thick ErAs layers. Variable-temperature Hall measurements reveal metallic behaviour in all samples, with no pronounced dependence on substrate temperature. Spectrally narrow (0.6 meV) intra 4f-shell transitions of Er3+ (4f11), at 1.54 μm, have been observed in ErAs epitaxial layers both in absorption (by Fourier transform infra-red spectroscopy, FTIR) and in emission (by cathodoluminescence). The crystal-field splittings observed in the FTIR spectra are consistent with the cubic(O h)symmetry expected for the Er lattice site in unstrained ErAs, in good agreement with the x-ray analyses.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
H. J. Richter, R. S. Smith, N. Herres, M. Seelmann-Eggebert and P. Wennekers, Appl. Phys. Lett.53, 99 (1988).
C. J. Palmstrøm, N. Tabatabaie and S. J. Allen, Jr., Appl. Phys. Lett.53, 2608 (1988).
C. J. Palmstrøm, K. C. Garrison, S. Mounier, T. Sands, C. L. Schwartz, N. Tabatabaie, S. J. Allen, Jr., H. L. Gilchrist and P. F. Miceli, J. Vac. Sci. Technol. B7, 747 (1989).
A. Hasegawa and A. Yanase, J. Phys. Soc. Jpn.42, 492 (1977).
S. J. Allen, Jr., N. Tabatabaie, C. J. Palmstrøm, G. W. Hull, T. Sands, F. DeRosa, H. L. Gilchrist and K. C. Garrison, Phys. Rev. Lett.62, 2309 (1989).
J. B. Taylor, L. D. Calvert, J. G. Despault, E. J. Gabe and J. J. Murray, J. Less-Common Metals37, 217 (1974).
G. H. Dieke,Spectra and Energy Levels of Rare Earth Ions in Crystals (Wiley-Interscience, New York, 1968).
H. Ennen and J. Schneider,Proceedings 13th Int. Conf. on Defects in Semiconductors, Coronado, CA, 12–17 August 1984, eds. L. C. Kimerling and J. M. Parsey, Jr., (The Metallurgical Society of AIME, New York, 1985) Vol. 14a, p. 115, and Refs. therein.
H. Ennen,Extended Abstracts of the 19th Conf. on Solid State Dev. and Mat, Tokyo, 1987 (Jap. Soc. Appl. Phys.) pp. 83–86 and Refs. therein.
H. Ennen, G. Pomrenke, A. Axmann, K. Eisele, W. Haydl and J. Schneider, Appl. Phys. Lett.46, 381 (1985).
W. T. Tsang and R. A. Logan, Appl. Phys. Lett.49, 1686 (1986).
J. Wagner, J. Windscheif and H. Ennen, Phys. Rev.B-30, 6230 (1984).
J. Wagner, H. Ennen and H. D. Müller, J. Appl. Phys.59, 1202 (1986).
H. Ennen, J. Wagner, H. D. Müller and R. S. Smith, J. Appl. Phys.61, 4877 (1987).
S. T. Picraux, L. R. Dawson, J. Y. Tsao, B. L. Doyle and S. R. Lee, Nucl. Instrum. Methods in Phys. Res.B 33, 891 (1988).
M. Hart, J. Cryst. Growth55, 409 (1981).
R. W. Vook,Epitaxial Growth Pt. A, ed. J. W. Matthews (Academic Press, New York, 1975) pp. 339–364.
R. S. Smith and P. Wennekers, Federal Republic of Germany, patent Nr. 3728135, awarded 1989.
J. Schneider et al., to be submitted.
K. R. Lea, M. J. M. Leask and W. P. Wolf, J. Phys. Chem. Solids23, 1381 (1962).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Ralston, J.D., Ennen, H., Wennekers, P. et al. Structural, electrical and optical characterization of singlecrystal ErAs layers grown on GaAs by MBE. J. Electron. Mater. 19, 555–560 (1990). https://doi.org/10.1007/BF02651278
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02651278