Abstract
Graphite fiber reinforced magnesium composites have been fabricated by infiltration and liquid phase hot pressing techniques. Although pure magnesium does not wet graphite, weting and bonding were achieved by precoating the graphite fibers with titanium. Tensile strengths and elastic moduli of flat rectangular composite specimens were measured and compared with Rule of Mixtures strengths. Significant strengthening and stiffening were achieved. Tensile strength was increased by 170 pct and the elastic modulus by 100 pct. Measured elastic moduli were in good agreement with Rule of Mixtures values. The highest tensile strength was about 83 pct of the Rule of Mixtures strength. It is believed that specimen porosity and fiber misalignment account for the bulk of this difference and that an improved fabrication technique will yield specimens with higher strengths. Fracture modes are presented and discussed.
Similar content being viewed by others
References
W. H. Sutton and E. Feingold:Materials Science Research, W. W. Kriegel and Hayne Palmour III, eds., Vol. 3, Chapter 31, p. 577, Plenum Press, 1966.
S. M. Wolf, A. P. Levitt, and J. Brown:Wetting and Bonding Between Aluminum Alloys and Sapphire, Army Materials and Mechanics Research Center, TR 66-19, July 1966.
M. H. Richman and R. D. French: Investigation of the Role of the Interface in Composite Materials, Final Report No. AMMRC CR 68-13(F), Dec. 1968, DAAG 46-68-0036 with Brown University.
R. P. Elliott:Constitution of Binary Alloys, First Supplement, p. 600, McGraw- Hill, New York, 1965.
W. H. Sutton and J. Chorne:Fiber Composite Materials, 1964 Seminar, Ameri- can Society for Metals, Chapter 9, Table 9, p. 189.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Levitt, A.P., Cesare, E.D. & Wolf, S.M. Fabrication and properties of graphite fiber reinforced magnesium. Metall Trans 3, 2455–2459 (1972). https://doi.org/10.1007/BF02647049
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02647049