Summary
The dislocation structure evolution during isothermal recrystallization of Al has been followed by means of internal friction, modulus defect and X-ray diffraction analyses accompanying the microscopical observations. Many peaks ofQ −1 and of modulus defect and X-ray diffraction line width have been found, both in nucleation and grain growth, all referable to dislocations. The first of these peaks, at the beginning of recrystallization, presents recovery characteristics, different from those shown by the subsequent, secondary peaks. Secondary peaks are interpreted in terms of dislocation emission from grain boundaries, whereas the first peak appears connected with subboundaries, walls present in the initial stages of recrystallization.
Riassunto
Si è seguita l’evoluzione della struttura di dislocazioni durrante la ricristallizzazione isoterma di Al mediante misure di frizione interna, di difetto di modulo e analisi di diffrazione dei raggi X unitamente ad osservazioni di microscopia. Si sono trovati vari picchi diQ −1, di difetto di modulo e di larghezza di linea di diffrazione con raggi X, sia durante la nucleazione che durante la crescita dei grani, tutti riferibili a dislocazioni. Il primo di questi picchi, all’inizio della ricristallizzazione, presenta caratteristiche di recupero differenti da quelle mostrate dai picchi seguenti, secondari. I picchi secondari sono interpretati in termini di emissione di dislocazioni dai bordi di grano, mentre il primo picco sembra collegabile ai subcontorni, muri di dislocazioni presenti negli stadi iniziali della ricristallizzazione.
Similar content being viewed by others
References
A. Isoré, W. Benoit andP. Stadelman:Philos. Mag.,34, 811 (1976).
R. Kamel andE. A. Attia:Acta Metall.,9, 1047 (1961).
R. Schaller andW. Benoit:J. Phys. (Paris),44-C9, 17 (1983).
E. Bonetti, E. Evangelista, P. Gondi andR. Tognato:Phys. Status Solidi A,39, 661 (1977).
E. Bonetti, P. Gondi andR. Montanari:J. Phys. (Paris),46-C10, 363 (1985).
A. Isoré, Q. Mercier andW. Benoit:Mem. Sci. Rev., Met.70, 509 (1973).
C. Diallo, R. Schaller andW. Benoit:J. Phys. (Paris),44-C9, 765 (1983).
P. Gondi:Metall. Ital.,51, 185, 221 (1959).
J. E. Burke andD. Turnbull:Prog. Met. Phys.,3, 220 (1952).
P. Gondi, U. Valdré andA. Grilli:Nuovo Cimento,21, 834 (1961).
G. K. Williamson andR. A. Smallman:Philos. Mag.,1, 34 (1956).
B. E. Warren:Prog. Met. Phys.,8, 147 (1959).
A. S. Nowick andB. S. Berry:Anelastic Relaxation in Crystalline Solids (Academic Press, New York, N. Y., 1972), p. 358.
J. Woigard, J. P. Amirault andJ. de Fouquet:Proceedings of the V ICIFUAS (Aachen, 1973).
J. Woirgard andJ. de Fouquet:Scr. Metall.,8, 253 (1974).
P. Gondi, R. Tognato andE. Evangelista:Phys. Status Solidi A,33, 579 (1976).
E. Bonetti, E. Evangelista, P. Gondi andR. Tognato:Nuovo Cimento B,33, 409 (1976).
Author information
Authors and Affiliations
Additional information
To speed up publication, the authors of this paper have agreed to not receive the proofs for correction.
Rights and permissions
About this article
Cite this article
Gondi, P., Montanari, R. Dislocation emission in A1 during recrystallization. Il Nuovo Cimento D 8, 647–657 (1986). https://doi.org/10.1007/BF02451089
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02451089