Effect of Polyurethane Treatment on the Interfacial and Mechanical Properties of Basalt Fiber-Reinforced Polymer Composite

  • Regular Article
  • Published:
Fibers and Polymers Aims and scope Submit manuscript

Abstract

Improving the interfacial bonding properties of basalt fiber-reinforced polymer (BFRP) to enhance the overall performance, keeping the existing technological flowsheet, meanwhile, fulfilling the product variety needs with a simple process are of great importance for both basalt fiber (BF) producer and its industry. In this study, polyurethane was coated as a coupling agent on the surface of BF to improve the bonding properties of BFRP interfaces, and the surface coating treatment process was also investigated. The results indicated that polyurethane treatment helped to enhance both the interfacial shear stress and the tensile properties of the BFRP; moreover, the treating process was particularly important, with the most significant improvement brought about by directly coating the surface of the original BF. SEM observation results illustrated that all samples treated with polyurethane had good interfacial adhesion between the fibers and polymeric matrix. In addition, chemical structural analysis of the BF surface based on FTIR and XPS results showed that polyurethane coating treatment could bring lots of polar functional groups to the fiber surface, especially the ones performed directly on the original BFs. Combining the experimental results and the interfacial functionary mechanisms, a discussion of the reinforcing mechanisms found that the introduction of polyurethane resulted in a mix of interfacial functionary mechanisms. In general, this work demonstrated that the approach of applying polyurethane directly on the original BF was a novel and facile concept and fulfilled the demands of both BF producers and downstream manufacturers.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8

Similar content being viewed by others

Data Availability

Data sets generated during the current study are available from the corresponding author on reasonable request.

References

  1. M. Altin Karataş, H. Gökkaya, Def. Technol. 14, 318 (2018)

    Article  Google Scholar 

  2. T.K. Das, P. Ghosh, N.C. Das, Adv. Compos. Hybrid. Mater. 2, 214 (2019)

    Article  CAS  Google Scholar 

  3. T. Sathishkumar, S. Satheeshkumar, J. Naveen, J. Reinf. Plast. Comp. 33, 1258 (2014)

    Article  CAS  Google Scholar 

  4. L. Yu, G. Liu, W. Wang, H. Hamada, Y. Yang, Polym. Compos.. Compos. 44, 2196 (2023)

    Article  CAS  Google Scholar 

  5. V.S.M. Francis Luther King, T. Purushothaman, Middle East J. Sci. Res. 22, 5 (2014)

    Google Scholar 

  6. V. Fiore, T. Scalici, G. Di Bella, A. Valenza, Compos. Part B Eng. 74, 74 (2015)

    Article  CAS  Google Scholar 

  7. H. Jamshaid, R. Mishra, J. Text. I. 107, 923 (2016)

    CAS  Google Scholar 

  8. V. Manikandan, J.W. Jappes, S.S. Kumar, P. Amuthakkannan, Compos. Part B Eng. 43, 812 (2012)

    Article  CAS  Google Scholar 

  9. V. Dhand, G. Mittal, K.Y. Rhee, S.-J. Park, D. Hui, Compos. Part B Eng. 73, 166 (2015)

    Article  CAS  Google Scholar 

  10. W. Ignaczak, A. Ladegaard Skov, M. El Fray, Polymers 12, 1486 (2020)

    Article  CAS  PubMed  PubMed Central  Google Scholar 

  11. S. Khandelwal, K.Y. Rhee, Compos. Part B Eng. 192, 108011 (2020)

    Article  CAS  Google Scholar 

  12. H. Liu, Y. Yu, Y. Liu, M. Zhang, L. Li, L. Ma, Y. Sun, W. Wang, Polymers 14, 2376 (2022)

    Article  PubMed  PubMed Central  Google Scholar 

  13. C. Yue, H. Looi, M. Quek, Int. J. Adhes. Adhes. 15, 73 (1995)

    Article  CAS  Google Scholar 

  14. P. Amuthakkannan, V. Manikandan, J.W. Jappes, M. Uthayakumar, Mater. Phys. Mech. 16, 107 (2013)

    CAS  Google Scholar 

  15. I. Živković, C. Fragassa, A. Pavlović, T. Brugo, Compos. Part B Eng. 111, 148 (2017)

    Article  Google Scholar 

  16. R. Zykaite, B. Purgleitner, W. Stadlbauer, C. Burgstaller, J. Compos. Mater. 51, 4091 (2017)

    Article  ADS  CAS  Google Scholar 

  17. C. Sergi, F. Sbardella, M. Lilli, J. Tirillò, A. Calzolari, F. Sarasini, Molecules 25, 4384 (2020)

    Article  CAS  PubMed  PubMed Central  Google Scholar 

  18. C. Arslan, M. Dogan, Compos. Part B Eng. 146, 145 (2018)

    Article  CAS  Google Scholar 

  19. B. Wei, H. Cao, S. Song, Compos. Part A-Appl. S. 42, 22 (2011)

    Article  Google Scholar 

  20. S.Y. Mun, J. Ha, S. Lee, Y. Ju, H.M. Lim, D. Lee, Compos. Part A-Appl. S. 142, 106208 (2021)

    Article  CAS  Google Scholar 

  21. Z. Chen, Y. Huang, J. Adhes. Sci. Technol. 30, 2175 (2016)

    Article  CAS  Google Scholar 

  22. A. Hinterreiter, J. Duchoslav, M. Kehrer, T. Truglas, A. Lumetzberger, C. Unterweger, C. Fürst, D. Stifter, Carbon 146, 97 (2019)

    Article  CAS  Google Scholar 

  23. C. Ralph, P. Lemoine, E. Archer, A. Mcilhagger, Compos. Part B Eng. 176, 107260 (2019)

    Article  CAS  Google Scholar 

  24. C. Ralph, P. Lemoine, A. Boyd, E. Archer, A. McIlhagger, Appl. Surf. Sci. 475, 435 (2019)

    Article  ADS  CAS  Google Scholar 

  25. M. Lilli, M. Zvonek, V. Cech, C. Scheffler, J. Tirillò, F. Sarasini, Compos. Commun. 27, 100769 (2021)

    Article  Google Scholar 

  26. H. Wu, Y. Zhong, Y. Tang, Y. Huang, G. Liu, W. Sun, P. Xie, D. Pan, C. Liu, Z. Guo, Adv. Compos. Hybrid Mater. 5, 419–430 (2021)

    Article  Google Scholar 

  27. S.-H. Kim, J.-H. Lee, J.-W. Kim, S.-Y. Lee, S.-J. Park, Adv. Fiber Mater. 4, 1414 (2022)

    Article  CAS  Google Scholar 

  28. S. Vinay, M. Sanjay, S. Siengchin, C. Venkatesh, Mater. Today Proc. 52, 2460 (2022)

    Article  CAS  Google Scholar 

  29. T. Deák, T. Czigány, P. Tamás, C. Németh, Express Polym LettPolym. Lett. 4, 1 (2010)

    Article  Google Scholar 

  30. K.L. Kuzmin, I.A. Timoshkin, S.I. Gutnikov, E.S. Zhukovskaya, Y.V. Lipatov, B.I. Lazoryak, Compos. Interface 24, 13 (2017)

    Article  ADS  CAS  Google Scholar 

  31. L. Yu, Y. Ma, Compos. Part B Eng. 161, 285 (2019)

    Article  CAS  Google Scholar 

  32. P. Qiao, J. Wang, Int. J. Solids Struct. 41, 7423 (2004)

    Article  Google Scholar 

  33. J. Karger-Kocsis, H. Mahmood, A. Pegoretti, Prog. Mater. Sci. 73, 1 (2015)

    Article  CAS  Google Scholar 

  34. Y. Zhou, M. Fan, L. Chen, Compos. Part B Eng. 101, 31 (2016)

    Article  CAS  Google Scholar 

  35. F. De Luca, G. Sernicola, M.S. Shaffer, A. Bismarck, A.C.S. Appl, Mater. Interfaces 10, 7352 (2018)

    Article  Google Scholar 

  36. K. Balaji, K. Shirvanimoghaddam, G.S. Rajan, A.V. Ellis, M. Naebe, Mater. Today Chem. 17, 100334 (2020)

    Article  Google Scholar 

  37. Y. Pu, Z. Ma, L. Liu, Y. Bai, Y. Huang, Compos. Part B Eng. 236, 109846 (2022)

    Article  CAS  Google Scholar 

  38. M. Tanoglu, S.H. McKnight, G.R. Palmese, J. Gillespie Jr., Compos. Sci. Technol. 61, 205 (2001)

    Article  CAS  Google Scholar 

  39. M. Dey, J. Deitzel, J. Gillespie Jr., S. Schweiger, Compos. Part A-Appl. S. 63, 59 (2014)

    Article  CAS  Google Scholar 

  40. T. Osada, A. Nakai, H. Hamada, Compos. struct. 61, 333 (2003)

    Article  Google Scholar 

  41. O. Khondker, T. Fukui, M. Inoda, A. Nakai, H. Hamada, Compos. Part A-Appl. S. 35, 1195 (2004)

    Article  Google Scholar 

  42. Z. Li, L. Yu, Z. Yan, J. Polym. Environ. 30, 92 (2022)

    Article  CAS  Google Scholar 

Download references

Acknowledgements

This work was supported by the following: Applied Research Project of Huzhou City [Grant No: 2022GZ16].

Funding

Applied research project of Huzhou City, 2022GZ16, Ying YU.

Author information

Authors and Affiliations

  1. Huzhou Key Laboratory of Green Energy Materials and Battery Cascade Utilization, School of Intelligent Manufacturing, Huzhou College, Huzhou, 313000, China

    Ying Yu

  2. College of Material and Textile Engineering, Jiaxing University, Jiaxing, 314000, China

    Lichao Yu, Chenyang Wang & Ziyan Cui

Authors
  1. Ying Yu
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Lichao Yu
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Chenyang Wang
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Ziyan Cui
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Ying Yu.

Ethics declarations

Conflict of Interest

The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.

Rights and permissions

Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Yu, Y., Yu, L., Wang, C. et al. Effect of Polyurethane Treatment on the Interfacial and Mechanical Properties of Basalt Fiber-Reinforced Polymer Composite. Fibers Polym 25, 607–617 (2024). https://doi.org/10.1007/s12221-023-00436-w

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s12221-023-00436-w

Keywords

Search

Navigation