Combined effects of sea urchin-like structure and mixed Cu+/Cu0 states on promoting C2 formation in electrocatalytic CO2 reduction

  • Research Article
  • Published:
Frontiers of Chemical Science and Engineering Aims and scope Submit manuscript

Abstract

Surface engineering and Cu valence regulation are essential factors in improving the C2 selectivity during the electrochemical reduction of CO2. Herein, we present a sea urchin-like CuO/Cu2O catalyst derived from rhombic dodecahedra Cu2O through one-step oxidation/etching method where the mixed Cu+/Cu0 states are formed via in situ reduction during electrocatalysis. The combined effects of the morphology and the mixed Cu+/Cu0 states on C–C coupling are evaluated by the Faradaic efficiency of C2 and the C2/C1 ratio obtained in an H-cell. R-CuO/Cu2O exhibited 49.5% Faradaic efficiency of C2 with a C2/C1 ratio of 3.1 at −1.4 V vs. reversible hydrogen electrode, which are 1.5 and 3.2 times higher than those of R-Cu2O, respectively. Using a flow-cell, 68.0% Faradaic efficiency of C2 is achieved at a current density of 500 mA·cm−2. The formation of the mixed Cu+/Cu0 states was confirmed by in situ Raman spectra. Additionally, the sea urchin-like structure provides more active sites and enables faster electron transfer. As a result, the excellent C2 production on R-CuO/Cu2O is primarily attributed to the synergistic effects of the sea urchin-like structure and the stable mixed Cu+/Cu0 states. Therefore, this work presents an integrated strategy for developing Cu-based electrocatalysts for C2 production through electrochemical CO2 reduction.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

References

  1. Zhao Y J, Wang X Y, Sang X H, Zheng S X, Yang B, Lei L C, Hou Y, Li Z J. Spin polarization strategy to deploy proton resource over atomic-level metal sites for highly selective CO2 electrolysis. Frontiers of Chemical Science and Engineering, 2022, 16(12): 1772–1781

    Article  CAS  Google Scholar 

  2. Woldu A R, Huang Z, Zhao P, Hu L, Astruc D. Electrochemical CO2 reduction (CO2RR) to multi-carbon products over copper-based catalysts. Coordination Chemistry Reviews, 2022, 454: 214340

    Article  CAS  Google Scholar 

  3. Wang J, Wang H, Han Z, Han J. Electrodeposited porous Pb electrode with improved electrocatalytic performance for the electroreduction of CO2 to formic acid. Frontiers of Chemical Science and Engineering, 2016, 9(1): 57–63

    Article  Google Scholar 

  4. Qu J P, Cao X J, Gao L, Li J Y, Li L, Xie Y H, Zhao Y F, Zhang J Q, Wu M H, Liu H. Electrochemical carbon dioxide reduction to ethylene: from mechanistic understanding to catalyst surface engineering. Nano-Micro Letters, 2023, 15(1): 178

    Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

  5. Yao D, Tang C, Vasileff A, Zhi X, Jiao Y, Qiao S Z. The controllable reconstruction of Bi-MOFs for electrochemical CO2 reduction through electrolyte and potential mediation. Angewandte Chemie International Edition, 2021, 60(33): 18178–18184

    Article  CAS  PubMed  Google Scholar 

  6. Saha P, Amanullah S, Dey A. Selectivity in electrochemical CO2 reduction. Accounts of Chemical Research, 2022, 55(2): 134–144

    Article  CAS  PubMed  Google Scholar 

  7. Zhu J X, Li J T, Lu R H, Yu R H, Zhao S Y, Li C B, Lv L, Xia L X, Chen X, Cai W, et al. Surface passivation for highly active, selective, stable, and scalable CO2 electroreduction. Nature Communications, 2023, 14(1): 4670

    Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

  8. Chen P C, Chen C B, Yang Y, Maulana A L, Jin J B, Feijoo J L, Yang P D. Chemical and structural evolution of AgCu catalysts in electrochemical CO2 reduction. Journal of the American Chemical Society, 2023, 145(18): 10116–10125

    Article  CAS  PubMed  Google Scholar 

  9. Li S M, Yan X D, Tang J Q, Cao D X, Sun X L, Tian G L, Tang X K, Guo H F, Wu Q Y, Sun J, et al. Cu26 nanoclusters with quintuple ligand shells for CO2 electrocatalytic reduction. Chemistry of Materials, 2023, 35(15): 6123–6132

    Article  CAS  Google Scholar 

  10. Wang M Y, Zhang S B, Li M, Han A G, Zhu X L, Ge Q F, Han J Y, Wang H. Facile synthesis of hierarchical flower-like Ag/Cu2O and Au/Cu2O nanostructures and enhanced catalytic performance in electrochemical reduction of CO2. Frontiers of Chemical Science and Engineering, 2020, 14(5): 813–823

    Article  CAS  Google Scholar 

  11. Wang J L, Tan H Y, Zhu Y P, Chu H, Chen H M. Linking the dynamic chemical state of catalysts with the product profile of electrocatalytic CO2 reduction. Angewandte Chemie, 2021, 133(32): 17394–17407

    Article  ADS  Google Scholar 

  12. Zhang Q, Wang J, Guo F, He G, Yang X, Li W, Xu J, Yin Z. Nitrogen cold plasma treatment stabilizes Cu0/Cu+ electrocatalysts to enhance CO2 to C2 conversion. Journal of Energy Chemistry, 2023, 84: 321–328

    Article  CAS  Google Scholar 

  13. Yuan X, Chen S, Cheng D, Li L, Zhu W, Zhong D, Zhao Z J, Li J, Wang T, Gong J. Controllable Cu0-Cu+ sites for electrocatalytic reduction of carbon dioxide. Angewandte Chemie International Edition, 2021, 60(28): 15344–15347

    Article  CAS  PubMed  Google Scholar 

  14. Sun L R, Han J Y, Ge Q F, Zhu X L, Wang H. Understanding the role of Cu+/Cu0 sites at Cu2O based catalysts in ethanol production from CO2 elcctroeeucctinn—a DFT study. RSC Advances, 2022, 12(30): 19394–19401

    Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

  15. Wang S N, Wang D, Tian B Q, Gao X X, Han L, Zhong Y, Song S C, Wang Z L, Li Y P, Gui J N, et al. Synergistic Cu+/Cu0 on Cu2O–Cu interfaces for efficient and selective C2+ production in electrocatalytic CO2 conversion. Science China Materials, 2023, 66(5): 1801–1809

    Article  CAS  Google Scholar 

  16. He T W, Tang C, Puente Santiago A R, Luque R, Pan H, Du A J. Tuning CO binding strength via engineering the copper/borophene interface for highly efficient conversion of CO into ethanol. Journal of Materials Chemistry A, 2021, 9(22): 13192–13199

    Article  CAS  Google Scholar 

  17. Kim C, Cho K M, Park K, Kim J Y, Yun G T, Toma F M, Gereige I, Jung H T. Cu/Cu2O interconnected porous aerogel catalyst for highly productive electrosynthesis of ethanol from CO2. Advanced Functional Materials, 2021, 31(32): 2102142

    Article  CAS  Google Scholar 

  18. Liu W, Zhai P B, Li A, Wei B, Si K P, Wei Y, Wang X G, Zhu G D, Chen Q, Gu X K, et al. Electrochemical CO2 reduction to ethylene by ultrathin CuO nanoplate arrays. Nature Communications, 2022, 13(1): 1877

    Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

  19. Jiang K, Huang Y F, Zeng G S, Toma F M, Goddard W A III, Bell A T. Effects of surface roughness on the electrochemical reduction of CO2 over Cu. ACS Energy Letters, 2020, 5(4): 1206–1214

    Article  CAS  Google Scholar 

  20. Sang J Q, Wei P F, Liu T F, Lv H F, Ni X M, Gao D F, Zhang J W, Li H F, Zang Y P, Yang F, et al. A reconstructed Cu2P2O7 catalyst for selective CO2 electroreduction to multicarbon products. Angewandte Chemie International Edition, 2021, 61(5): e202114238

    Article  PubMed  Google Scholar 

  21. Li W, Feng X L, Zhang Z, Jin X, Liu D P, Zhang Y. A controllable surface etching strategy for well-defined spiny yolk@shell CuO@CeO2 cubes and their catalytic performance boost. Advanced Functional Materials, 2018, 28(49): 1802559

    Article  Google Scholar 

  22. Hua Q, Chen K, Chang S J, Ma Y S, Huang W X. Crystal plane-dependent compositional and structural evolution of uniform Cu2O nanocrystals in aqueous ammonia solutions. Journal of Physical Chemistry C, 2011, 115(42): 20618–20627

    Article  CAS  Google Scholar 

  23. Scholten F, Nguyen K L C, Bruce J P, Heyde M, Roldan Cuenya B. Identifying structure-selectivity correlations in the electrochemical reduction of CO2: a comparison of well-ordered atomically clean and chemically etched copper single-crystal surfaces. Angewandte Chemie International Edition, 2021, 60(35): 19169–19175

    Article  CAS  PubMed  Google Scholar 

  24. Yang P P, Zhang X L, Gao F Y, Zheng Y R, Niu Z Z, Yu X, Liu R, Wu Z Z, Qin S, Chi L P, et al. Protecting copper oxidation state via intermediate confinement for selective CO2 electroreduction to C2+ fuels. Journal of the American Chemical Society, 2020, 142(13): 6400–6408

    Article  CAS  PubMed  Google Scholar 

  25. Huang W C, Lyu L M, Yang Y C, Huang M H. Synthesis of Cu2O nanocrystals from cubic to rhombic dodecahedral structures and their comparative photocatalytic activity. Journal of the American Chemical Society, 2011, 134(2): 1261–1267

    Article  PubMed  Google Scholar 

  26. Huang J J, Chen Z, Cai J M, Jin Y Z, Wang T, Wang J H. Activating copper oxide for stable electrocatalytic ammonia oxidation reaction via in-situ introducing oxygen vacancies. Nano Research, 2022, 15(7): 5987–5994

    Article  ADS  CAS  Google Scholar 

  27. Yan X, Chen C, Wu Y, Liu S, Chen Y, Feng R, Zhang J, Han B. Efficient electroreduction of CO2 to C2+ products on CeO2 modified CuO. Chemical Science, 2021, 12(19): 6638–6645

    Article  CAS  PubMed  PubMed Central  Google Scholar 

  28. Alabsi M H, Wang X L, Zheng P, Ramirez A, Duan A J, Xu C M, Huang K W. Screening and design of active metals on dendritic mesoporous Ce0.3Zr0.7O2 for efficient CO2 hydrogenation to methanol. Fuel, 2022, 317: 123471

    Article  CAS  Google Scholar 

  29. Wang X Q, Chen Q, Zhou Y J, Li H M, Fu J W, Liu M. Cu-based bimetallic catalysts for CO2 reduction reaction. Advanced Sensor and Energy Materials, 2022, 1(3): 100023

    Article  Google Scholar 

  30. Luo H Q, Li B, Ma J G, Cheng P. Surface modification of Nano-Cu2O for controlling CO2 electrochemical reduction to ethylene and syngas. Angewandte Chemie International Edition, 2022, 61(11): e202116736

    Article  ADS  CAS  PubMed  Google Scholar 

  31. Chou T C, Chang C C, Yu H L, Yu W Y, Dong C L, Velasco Vélez J J, Chuang C H, Chen L C, Lee J F, Chen J M, et al. Controlling the oxidation state of the Cu electrode and reaction intermediates for electrochemical CO2 reduction to ethylene. Journal of the American Chemical Society, 2020, 142(6): 2857–2867

    Article  CAS  PubMed  Google Scholar 

  32. Wu Z Z, Zhang X L, Niu Z Z, Gao F Y, Yang P P, Chi L P, Shi L, Wei W S, Liu R, Chen Z, et al. Identification of Cu(100)/Cu(111) interfaces as superior active sites for CO dimerization during CO2 electroreduction. Journal of the American Chemical Society, 2021, 144(1): 259–269

    Article  PubMed  Google Scholar 

  33. Park D G, Choi J W, Chun H, Jang H S, Lee H, Choi W H, Moon B C, Kim K H, Kim M G, Choi K M, et al. Increasing CO binding energy and defects by preserving Cu oxidation state via O2-plasma-assisted N doping on CuO enables high C2+ selectivity and long-term stability in electrochemical CO2 reduction. ACS Catalysis, 2023, 13(13): 9222–9233

    Article  CAS  Google Scholar 

  34. Fang M W, Wang M L, Wang Z W, Zhang Z X, Zhou H C, Dai L M, Zhu Y, Jiang L. Hydrophobic, ultrastable Cu6+ for robust CO2 electroreduction to C2 products at ampere-current levels. Journal of the American Chemical Society, 2023, 145(20): 11323–11332

    Article  CAS  PubMed  Google Scholar 

  35. Wordsworth J, Benedetti T M, Somerville S V, Schuhmann W, Tilley R D, Gooding J J. The influence of nanoconfinement on electrocatalysis. Angewandte Chemie International Edition, 2022, 61(28): e202200755

    Article  CAS  PubMed  Google Scholar 

  36. Lee S, Kim D, Lee J. Electrocatalytic production of C3–C4 compounds by conversion of CO2 on a chloride-induced Bi-phasic Cu2O–Cu catalyst. Angewandte Chemie International Edition, 2015, 54(49): 14701–14705

    Article  CAS  PubMed  Google Scholar 

  37. Kuang S Y, Li M L, Xia R, Xing L, Su Y Q, Fan Q, Liu J P, Hensen E J M, Ma X B, Zhang S. Stable surface-anchored Cu nanocubes for CO2 electroreduction to ethylene. ACS Applied Nano Materials, 2020, 3(8): 8328–8334

    Article  CAS  Google Scholar 

  38. Yang W, Liu H, Qi Y, Li Y, Cui Y, Yu L, Cui X, Deng D. Boosting C–C coupling to multicarbon products via high-pressure CO electroreduction. Journal of Energy Chemistry, 2023, 85: 102–107

    Article  CAS  Google Scholar 

  39. Sebastián-Pascual P, Escudero-Escribano M. Addressing the interfacial properties for CO electroreduction on Cu with cyclic voltammetry. ACS Energy Letters, 2019, 5(1): 130–135

    Article  Google Scholar 

  40. Choi C, Kwon S, Cheng T, Xu M J, Tieu P, Lee C, Cai J, Lee H M, Pan X Q, Duan X F, et al. Highly active and stable stepped Cu surface for enhanced electrochemical CO2 reduction to C2H4. Nature Catalysis, 2020, 3(10): 804–812

    Article  CAS  Google Scholar 

  41. Jiang Y W, Wang X Y, Duan D L, He C H, Ma J, Zhang W Q, Liu H J, Long R, Li Z B, Kong T T, et al. Structural reconstruction of Cu2O superparticles toward electrocatalytic CO2 reduction with high C2+ products selectivity. Advanced Science, 2022, 9(16): 2105292

    Article  CAS  PubMed  PubMed Central  Google Scholar 

  42. Liu P, Hensen E J M. Highly efficient and robust Au/MgCuCr2O4 catalyst for gas-phase oxidation of ethanol to acetaldehyde. Journal of the American Chemical Society, 2013, 135(38): 14032–14035

    Article  CAS  PubMed  Google Scholar 

  43. Lyu Z H, Zhu S Q, Xie M H, Zhang Y, Chen Z T, Chen R H, Tian M K, Chi M F, Shao M H, Xia Y N. Controlling the surface oxidation of Cu nanowires improves their catalytic selectivity and stability toward C2+ products in CO2 reduction. Angewandte Chemie International Edition, 2021, 60(4): 1909–1915

    Article  CAS  PubMed  Google Scholar 

  44. Xie M C, Shen Y, Ma W C, Wei D Y, Zhang B, Wang Z H, Wang Y H, Zhang Q H, Xie S J, Wang C, et al. Fast screening for copper-based bimetallic electrocatalysts: efficient electrocatalytic reduction of CO2 to C2+ products on magnesium-modified copper. Angewandte Chemie International Edition, 2022, 61(51): e202213423

    Article  CAS  PubMed  Google Scholar 

  45. Wang Y, Zhao J K, Cao C, Ding J, Wang R Y, Zeng J, Bao J, Liu B. Amino-functionalized Cu for efficient electrochemical reduction of CO to acetate. ACS Catalysis, 2023, 13(6): 3532–3540

    Article  CAS  Google Scholar 

  46. Duan G Y, Li X Q, Ding G R, Han L J, Xu B H, Zhang S J. Highly efficient electrocatalytic CO2 reduction to C2+ products on a poly(ionic liquid)-based Cu0–CuI tandem catalyst. Angewandte Chemie International Edition, 2022, 61(9): e202110657

    Article  CAS  PubMed  Google Scholar 

  47. Zhang J, Wang Y, Li Z, Xia S, Cai R, Ma L, Zhang T, Ackley J, Yang S, Wu Y, et al. Grain boundary-derived Cu+/Cu0 interfaces in CuO nanosheets for low overpotential carbon dioxide electroreduction to ethylene. Advanced Science, 2022, 9(21): 2200454

    Article  CAS  PubMed  PubMed Central  Google Scholar 

  48. Lei Q, Huang L, Yin J, Davaasuren B, Yuan Y, Dong X, Wu Z, Wang X, Yao K, Lu X, et al. Structural evolution and strain generation of derived-Cu catalysts during CO2 electroreduction. Nature Communications, 2022, 13(1): 4857

    Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

  49. Chen S, Li Y, Bu Z, Yang F, Luo J, An Q, Zeng Z, Wang J, Deng S. Boosting CO2-to-CO conversion on a robust single-atom copper decorated carbon catalyst by enhancing intermediate binding strength. Journal of Materials Chemistry A, 2021, 9(3): 1705–1712

    Article  CAS  Google Scholar 

  50. Liu H, Miao B Y, Chuai H, Chen X, Zhang S, Ma X B. Nanoporous tin oxides for efficient electrochemical CO2 reduction to formate. Green Chemical Engineering, 2022, 3(2): 138–145

    Article  Google Scholar 

Download references

Acknowledgements

This work was supported by the National Natural Science Foundation of China (Grant No. 22178266). We are grateful to Donghai Mei group of Tiangong University for providing in situ Raman spectroscopy tests. We thank Prof. Xiaolei Wang and Dr. Mahrima Majid of University of Alberta for polishing English language of the full text.

Author information

Authors and Affiliations

  1. Collaborative Innovation Center of Chemical Science and Engineering, Key Laboratory for Green Chemical Technology of the Ministry of Education, School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300354, China

    Mengqing Shan, Dongsheng Lu, Jiatong Dong, Shen Yan, Jinyu Han & Hua Wang

Authors
  1. Mengqing Shan
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Dongsheng Lu
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Jiatong Dong
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Shen Yan
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Jinyu Han
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Hua Wang
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Hua Wang.

Ethics declarations

Competing interests The authors declare that they have no competing interests.

Electronic Supplementary Material

11705_2024_2393_MOESM1_ESM.pdf

Combined effects of sea urchin-like structure and mixed Cu+/Cu0 states on promoting C2 formation in electrocatalytic CO2 reduction

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Shan, M., Lu, D., Dong, J. et al. Combined effects of sea urchin-like structure and mixed Cu+/Cu0 states on promoting C2 formation in electrocatalytic CO2 reduction. Front. Chem. Sci. Eng. 18, 30 (2024). https://doi.org/10.1007/s11705-024-2393-5

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1007/s11705-024-2393-5

Keywords

Search

Navigation