Abstract
Corrosion is a metallurgical problem that occurs frequently in a power plant, plant inevitable, especially in the present days, since higher efficiency of a power plant is required and thus the process temperature is increasing. Choosing the right materials for pipeline is very crucial since it is affecting the service life and operational reliability. The research is done to study the oxidation behaviour of ferritic alloy for power plant. A failed component from a gas combined cyclic thermal power plant was received and a failure analysis is done to investigate the cause of failure of the equipment. Results from the analysis suggested that the pipe was exposed to high temperature oxidation and metal dusting. Metal dusting mechanism and how it affects materials in high temperature condition is then identified and explained in this work.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
Abbreviations
- EDX:
-
Energy Dispersive X-ray
- SEM:
-
Scanning electron microscope
- XRD:
-
X-ray Diffractometer
References
Islam MM, Hasanuzzaman M, Pandey AK, Rahim NA (2020) Chapter 2–Modern energy conversion technologies. In: Hasanuzzaman MD, Rahim NA (eds) Energy for sustainable development. Academic Press, pp 19–39. https://doi.org/10.1016/B978-0-12-814645-3.00002-X
Tanner GM (1994) Metal dusting (catastrophic carburization) of a waste heat boiler tube. Eng Fail Anal 1(4):289–306. https://doi.org/10.1016/1350-6307(94)90004-3
AA Al-Meshari, J. Little (2009) Metal dusting behaviour of furnace tube alloys. ARPN J Eng Appl Sci 4(8):68–81, 2009. http://www.arpnjournals.com/jeas/research_papers/rp_2009/jeas_1009_256.pdf
ASM International Handbook Committee (1989) ASM Handbook In: Nondestructive Evaluation and Quality Control, vol 17.
Pippel E, Woltersdorf J, Schneider R (1998) Micromechanisms of metal dusting on Fe-base and Ni-base alloys. Mater Corros 49(5):309–316. https://doi.org/10.1002/(SICI)1521-4176(199805)49:5%3c309::AID-MACO309%3e3.0.CO;2-1
Al-Meshari AI (2008) ‘Metal dusting of heat-resistant alloys’. Thesis, University of Cambridge. https://doi.org/10.17863/CAM.14206
Herring DH (2003) What to do about metal dusting. Heat Treat Prog 20–24. http://www.heat-treat-doctor.com/documents/metaldusting.pdf
Natesan K, Zeng Z (2006) Development of materials resistant to metal dusting degradation–annual report for calendar year 2005. Energy Technology Division, Argonne National Laboratory, Argonne, Illinois, ANL-06/14, 2006. https://www.osti.gov/biblio/920980
Acknowledgements
This research was supported by Ministry of Higher Education, Malaysia and International Islamic University Malaysia with Grant Number MyLAB-001-0001.
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2023 The Author(s), under exclusive license to Springer Nature Singapore Pte Ltd.
About this paper
Cite this paper
Kaderi, A., Bakar, S.N.S.A., Ani, M.H., Illias, S., Osman, M.S. (2023). Metal Dusting Led Failure in a High-Temperature Condenser. In: Jalar, A., Embong, Z., Othman, N.K., Yaakob, N., Bakar, M.A. (eds) Proceedings of the 7th International Corrosion Prevention Symposium for Research Scholars . Lecture Notes in Mechanical Engineering. Springer, Singapore. https://doi.org/10.1007/978-981-19-1851-3_12
Download citation
DOI: https://doi.org/10.1007/978-981-19-1851-3_12
Published:
Publisher Name: Springer, Singapore
Print ISBN: 978-981-19-1850-6
Online ISBN: 978-981-19-1851-3
eBook Packages: EngineeringEngineering (R0)