Abstract
Ferritic-martensitic 12Cr-MoWSiVNbB (EP-823) steel was irradiated with 7 MeV Ni++ ions within fluence interval 5 × 1018−5.4 × 1019 ions/m2 and with 30 and 70 keV He+ ions within fluence interval 1020–1021 ions/m2 at 500°C. Results from a comparative analysis of Cr and Si radiation-induced segregation profiles near the surface are presented. Dependence of the amount of surface segregation on damage dose, displacement generation rate, and radiation-induced point defects concentration is established.
Similar content being viewed by others
References
Mauri, F., Lucasson, P., Lucasson, A., et al., J. Phys. F: Metal. Phys., 1987, vol. 17, p. 1143.
Mathon, M.H., de Carlan, Y., Geoffroy, G., et al., J. Nucl. Mater., 2003, vol. 312, p. 236.
Olsson, P., J. Nucl. Mater., 2009, vols. 386–388, p. 86.
Wong, K.L., Lee, H.-J., Wirth, B.D., et al., Fusion Mater., 2007, vol. 43, p. 146.
Lysova, G.V., Birzhevoy, G.A., Solov’ev, N.P., et al., Fizika i khimiya obrabotki materialov, 2004, no. 4, p. 12.
Lysova, G.V., Birzhevoi, G.A., Zakharova, M.I., et al., Poverkhnost’. Rentgen., Sinkhrotron., Neutron. Issled., 2008, no. 3, p. 11 [J. Surface Invest. X-ray, Synchrotron Neutron Tech. (Engl. Transl.), 2008, vol. 2, no. 2, p. 178].
Terentyev, D.A., Malerba, L., Chakarova, R., et al., J. Nucl. Mater., 2006, vol. 349, p. 119.
Rehn, L.E. and Erck, R.A., J. Nucl. Mater., 1989, vol. 168, p. 208.
Author information
Authors and Affiliations
Corresponding author
Additional information
Original Russian Text © G.V. Lysova, G.A. Birzhevoy, 2010, published in Izvestiya Rossiiskoi Akademii Nauk. Seriya Fizicheskaya, 2010, Vol. 74, No. 2, pp. 135–138.
About this article
Cite this article
Lysova, G.V., Birzhevoy, G.A. Kinetics of radiation-induced segregation in 12Cr-MoWSiVNbB steel after Ni++ and He+ ion irradiation. Bull. Russ. Acad. Sci. Phys. 74, 118–121 (2010). https://doi.org/10.3103/S1062873810020048
Published:
Issue Date:
DOI: https://doi.org/10.3103/S1062873810020048