Abstract
The article presents research results focused on high-temperature gas corrosion of sections of EcoSoderberg electrolyzers’ gas-collecting bells (GCB) made of high-strength VCh50 cast iron with spherical graphite. The gravimetric method was used to study the specific mass losses of the sections due to corrosion. The microstructure of cast iron, structure, chemical and phase composition of corrosion products were studied using optical, electron microscopy and electron microprobe analysis. It was established that the specific weight loss of the sections during operation reaches 0.36–0.46 g/(cm2 month). Corrosion of cast iron sections of EcoSoderberg electrolyzers’ GCB is characterized by high unevenness by area. There are cases of decommissioning sections due to local through “burnouts” with a weight loss of 19–24 kg. With relatively uniform corrosion, the maximum allowable weight loss of the sections is 25–30 kg. To make predictive estimates based on experimental data, dependence of the sections’ mass loss on the operating time was obtained. It was found that the corrosion products of the sections consist of iron oxides and alloying elements of cast iron. Most samples are characterized by increased content of C, S, F, K, Al, and Na. Corrosion products have a pronounced layered structure and contain a large number of defects in the form of pores and cracks. The layers differ in chemical, phase composition, and macrostructure. All the studied samples are characterized by cyclic alternation of relatively dense layers of iron oxides Fe2O3 and Fe3O4 and more porous layers between them. The layers are characterized by increased content of C and F. Sulfur is evenly distributed over the thickness of corrosion products. The studied samples of corrosion products have high defectiveness, friability, large number of pores, cracks, discontinuities, and low adhesion to the surface of cast iron. This is due to the presence of phases and compounds with different coefficients of thermal expansion. The mechanism of corrosion product layer formation was established and scientifically proved.
![](http://media.springernature.com/m312/springer-static/image/art%3A10.3103%2FS0967091220120165/MediaObjects/11986_2021_1290_Fig1_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.3103%2FS0967091220120165/MediaObjects/11986_2021_1290_Fig2_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.3103%2FS0967091220120165/MediaObjects/11986_2021_1290_Fig3_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.3103%2FS0967091220120165/MediaObjects/11986_2021_1290_Fig4_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.3103%2FS0967091220120165/MediaObjects/11986_2021_1290_Fig5_HTML.gif)
Similar content being viewed by others
REFERENCES
Buzunov, V., Mann, V., Chuchuk, E., Frizorger, V., Pinaev, A., and Nikitin, E., The first results of the industrial application of the EcoSoderberg technology at the Krasnoyarsk aluminum smelter, in Light Metals 2013, Sadler, B.A., Ed., Chichester: Wiley, 2013, pp. 573–576.
Vinogradov, A.M., Pinaev, A.A., Vinogradov, D.A., Puzin, A.V., Shadrin, V.G., Zor’ko, N.V., and Somov, V.V., Improving the efficiency of Soderberg electrolyzers’ shelter, Metall. Tsvetn. Met., 2017, no. 1, pp. 19–30.
Shakhrai, S.G. and Sugak, E.V., Problems of cleaning gas emissions from aluminum plants and ways to solve them, Tekhn. Ekon. Vestn. Russ. Alyuminiya, 2006, no. 14, pp. 38–42.
Mintsis, M.Ya., Polyakov, P.V., and Sirazutdinov, G.A., Elektrometallurgiya alyuminiya (Electrometallurgy of Aluminum), Novosibirsk: Nauka, 2001.
Terent’ev, A.A. and Nozhko, S.I., Quality of raw aluminum for the production of aluminum wire rod, Sist., Metody, Tekhnol., 2018, vol. 37, no. 1, pp. 136–141.
Baranov, A.N., Guseva, E.A., Krasnoperov, A.N., Pobedash, A.S., and Yudin, A.N., Investigation of corrosion processes in aluminum production and development of new methods of protection of metals, Russ. J. Non-Ferrous Met., 2008, vol. 49, no. 4, pp. 5264–268.
Temlyantsev, M.V. and Mikhailenko, Yu.E., Okislenie i obezuglerozhivanie stali v protsessakh nagreva pod obrabotku davleniem (Oxidation and Decarburization of Steel at Heating for Pressure Treatment), Moscow: Teplotekhnik, 2006.
Bobro, Yu.G., Legirovannye chuguny (Alloyed Cast Iron), Moscow: Metallurgiya, 1976.
Foosnas, T., Naterstad, T., Bruheim, M., and Grjotheim, K., Anode dusting in Hall—Heroult cells, in Essential Readings in Light Metals: Electrode Technology for Aluminum Production, Chichester: Wiley, 2013, pp. 633–642.
Bugnion, L. and Fischer, J.C., Carbon dust in electrolysis pots-effect on the electrical resistivity of cryolite bath, Int. Aluminium J., 2016, vol. 92, nos. 1–2, pp. 44–47.
Bobro, Yu.G., Zharostoikie i rostoustoichivye chuguny (Heat- and Growth-Resistant Cast Iron), Moscow: Mashgiz, 1960.
Malyshev, G.P. and Volchok, I.P., Improving the operational stability of gas-collection bells of electrolysis baths with upper current lead, in Metallurgiya (Metallurgy), Zaporozhye: Zaporozh. Gos. Inzh. Akad., 2005, no. 12, pp. 129–133.
Shimanskii, I.A., Improving the corrosion resistance of cast iron products under high-temperature gas corrosion, Extended Abstract of Cand. Sci. (Eng.) Dissertation, Krasnoyarsk, 2012.
Gomes, A.S. and Heilgendorff, R.M., Carbon plant performance with blended coke, Proc. 134th TMS Annual Meeting “Light Metals 2005,” San Francisco, Pittsburgh, PA: Miner., Met. Mater. Soc., 2005, pp. 659–663.
Edwards, L.S., Neyrey, K.J., and Lossius, L.P., A review of coke and anode desulfurization, in Essential Readings in Light Metals, Vol. 4: Electrode Technology for Aluminum Production, Cham: Springer-Verlag, 2007, pp. 895–900.
Adams, A., Cahill, R., Belzile, Y., Cantin, K., and Gendron, M., Minimizing impact of low sulfur coke on anode quality, in Essential Readings in Light Metals, Vol. 4: Electrode Technology for Aluminum Production, Cham: Springer-Verlag, 2009, pp. 957–962.
Gendron, M., Whelan, S., and Cantin, K., Coke blending and fines circuit targeting at the Alcoa Deschambault smelter, in Essential Readings in Light Metals, Vol. 4: Electrode Technology for Aluminum Production, Cham: Springer-Verlag, 2008, pp. 861–864.
Vogt, F., Tonti, R., and Edwards, L.C., Global trends in anode grade coke availability & quality for Australasian aluminum industry, Proc. 7th Australasian Smelting Technology Conf., Melbourne, Australia, November 11–15, 2001, Melbourne, 2001.
Abbas, H., Khaji, K., and Sulaman, D., Desulphurization control during baking: Its impact on anode performance and operational Costs-Alba’s experience, in Light Metals 2010, Pittsburgh, PA: Miner., Met. Mater. Soc., 2010, pp. 1011–1014.
Grandfield, J.F. and Taylor, J.A., The downstream consequences of rising Ni and V concentrations in smelter grade metal and potential control strategies, in Essential Readings in Light Metals, Vol. 4: Electrode Technology for Aluminum Production, Cham: Springer-Verlag, 2009, pp. 1007–1011.
Author information
Authors and Affiliations
Corresponding authors
Additional information
Translated by K. Gumerov
About this article
Cite this article
Yur’ev, A.B., Temlyantsev, M.V., Deev, V.B. et al. Corrosion of Cast Iron Sections of Gas-Collecting Bells of Ecosoderberg Electrolyser. Steel Transl. 50, 827–833 (2020). https://doi.org/10.3103/S0967091220120165
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.3103/S0967091220120165