Abstract
In the production of steel rollers, surface decarburization may occur in the course of heating before quenching. Means of more effective protection against such decarburization are considered in the case of the 35X CA steel barrel of wrapped rollers for the ShPS 30-80 ball-rolling mill. A technological protocol for the heat treatment of the rollers is developed. It is shown that protection by means of nitrogen + a carburizing agent + a muffle increases the likelihood of the desired outcome (no decarburized surface layer and hardness no less than 45 HRC) by 31.9% in comparison with protection by means of Barier protective compound + a carburizing agent + a muffle. On average, 450–470 t of grinding balls (diameter 40 mm; hardness groups III and IV) may be rolled in a complete run (to regrinding) on rollers heat-treated by the proposed protocol.
Similar content being viewed by others
References
Barabashin, B.M., Miller, V.V., Petrenko, V.G., et al., Heat treatment of the rolls of the ball-rolling mill 1040, Stal’, 1981, no. 10, pp. 74–75.
Kulak, V.Yu., Biler, V.A., Vasilenko, M.A., et al., The construction of the ball-rolling mill at the Donetsk Metal Rolling Company, Metall. Gornorudn. Prom-st’, 2014, no. 5, pp. 36–39.
Skoblo, T.S., Sidashenko, A.I., Avtukhov, A.K., et al., RF Patent 1722762, Byull. Izobret., 1992, no. 12.
Vrochinskii, S.L., Gerasimchuk, A.I., Medvedev, A.M., et al., Protection of iron-carbon and titan alloys against high-temperature corrosion during heat treatment. http://www.rg-nn.ru/zashhita-ot-vysokotemperaturnojkorrozii-zhelezouglerodistyx-i-titanovyx-splavov-pri-ixtermicheskoj-obrabotke.htm. Accessed February, 2015.
Author information
Authors and Affiliations
Corresponding author
Additional information
Original Russian Text © M.M. Lam, A.I. Serov, A.A. Ternavskiy, G.S. Bazarova, Y.N. Smyrnov, 2015, published in “Stal’,” 2015, No. 10, pp. 34–38.
About this article
Cite this article
Lam, M.M., Serov, A.I., Ternavskiy, A.A. et al. Heat treatment of rollers in the ShPS 30-80 ball-rolling mill at JSC DMPZ. Steel Transl. 45, 784–788 (2015). https://doi.org/10.3103/S0967091215100095
Received:
Published:
Issue Date:
DOI: https://doi.org/10.3103/S0967091215100095